CN104028313A - 一种scr脱硝催化剂的端部硬化处理方法 - Google Patents

一种scr脱硝催化剂的端部硬化处理方法 Download PDF

Info

Publication number
CN104028313A
CN104028313A CN201410202244.8A CN201410202244A CN104028313A CN 104028313 A CN104028313 A CN 104028313A CN 201410202244 A CN201410202244 A CN 201410202244A CN 104028313 A CN104028313 A CN 104028313A
Authority
CN
China
Prior art keywords
catalyst
parts
ammonium
solution
dissolved
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410202244.8A
Other languages
English (en)
Other versions
CN104028313B (zh
Inventor
周伟
沈阳浩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lohuis Environmental Protection Equipment Shanghai Co ltd
Zhou Dongyu
Original Assignee
Wuxi Li Xin Environmental Protection Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Li Xin Environmental Protection Technology Co Ltd filed Critical Wuxi Li Xin Environmental Protection Technology Co Ltd
Priority to CN201410202244.8A priority Critical patent/CN104028313B/zh
Publication of CN104028313A publication Critical patent/CN104028313A/zh
Application granted granted Critical
Publication of CN104028313B publication Critical patent/CN104028313B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种SCR脱硝催化剂的端部硬化处理方法，其使得催化剂的端部硬度提高，使得催化剂更耐磨，增加了催化剂的使用寿命。其具体步骤如下：（1）配置活性溶液：分别秤取1～5份偏钨酸铵，0.5～1份硝酸铈，1～2份七钼酸铵，溶解于100份去离子水中；（2）秤取20～35份磷酸二氢铵，溶解于100份去离子水中；（3）将步骤（1）和步骤（2）二种溶液混合，升温至80℃，并搅拌均匀；（4）将需要硬化的蜂窝催化剂模块一端或者两端浸渍在步骤（3）溶液中5s～10s；（5）将步骤（4）取出浸渍好的催化剂放入马弗炉中110℃煅烧30min，使其中的组分和催化剂发生反应，确保催化剂一端或两端边缘硬化。

Description

一种SCR脱硝催化剂的端部硬化处理方法
技术领域
本发明涉及SCR脱硝催化剂的技术领域，具体为一种SCR脱硝催化剂的端部硬化处理方法。
背景技术
随着国家对氮氧化物排放的控制越来越严，以燃煤锅炉为主的固定源向大气中排放氮氧化物的量会得到越来越严格的控制，单纯依靠低氮燃烧技术已无法满足严格的排放标准。
目前应用最广泛的是SCR脱硝催化剂，其所处的烟气环境条件比较恶劣，粉尘和重金属浓度高，对催化剂冲刷比较严重，催化剂也比较容易被磨损、堵塞，这大大缩短了催化剂的使用寿命。
发明内容
针对上述问题，本发明提供了一种SCR脱硝催化剂的端部硬化处理方法，其使得催化剂的端部硬度提高，使得催化剂更耐磨，增加了催化剂的使用寿命。
一种SCR脱硝催化剂的端部硬化处理方法，其特征在于：
其具体步骤如下：
（1）配置活性溶液：分别秤取1～5份偏钨酸铵，0.5～1份硝酸铈，1～2份七钼酸铵，溶解于100份去离子水中；
（2）秤取20～35份磷酸二氢铵，溶解于100份去离子水中；
（3）将步骤（1）和步骤（2）二种溶液混合，升温至80℃，并搅拌均匀；
（4）将需要硬化的蜂窝催化剂模块一端或者两端浸渍在步骤（3）溶液中5 s ～10s；
（5）将步骤（4）取出浸渍好的催化剂放入马弗炉中110℃煅烧30min，使其中的组分和催化剂发生反应，确保催化剂一端或两端边缘硬化。
一种SCR脱硝催化剂的端部硬化液，其特征在于：其为活性溶液和磷酸二氢铵溶液的混合液，所述活性溶液的成分具体为1～5份偏钨酸铵、0.5～1份硝酸铈、1～2份七钼酸铵溶解于100份去离子水中混和均匀而成；所述磷酸二氢铵溶液具体为20～35份磷酸二氢铵溶解于100份去离子水中混和均匀而成。
采用本发明后，将催化剂模块端部浸渍在SCR脱硝催化剂的端部硬化液中5 s ～10s后，再将浸渍好的催化剂放入马弗炉中110℃煅烧30min，使其中的组分和催化剂发生反应，确保催化剂一端或两端边缘硬化，做硬化处理后，其使得催化剂的端部硬度提高，使得催化剂更耐磨，增加了催化剂的使用寿命。
具体实施方式
具体实施例一
一种SCR脱硝催化剂的端部硬化处理方法，其具体步骤如下：
（1）配置活性溶液：分别秤取10g偏钨酸铵，5g硝酸铈，15g七钼酸铵，溶解于1000g去离子水中；
（2）秤取200g磷酸二氢铵，溶解于1000g去离子水中；
（3）将步骤（1）和步骤（2）二种溶液混合，升温至80℃，并搅拌均匀；
（4）将需要硬化的蜂窝催化剂模块一端或者两端浸渍在步骤（3）溶液中10s；
（5）将步骤（4）取出浸渍好的催化剂放入马弗炉中110℃煅烧30min，使其中的组分和催化剂发生反应，确保催化剂一端或两端边缘硬化。
具体实施例二
一种SCR脱硝催化剂的端部硬化处理方法， 其具体步骤如下：
（1）配置活性溶液：分别秤取25g偏钨酸铵，7g硝酸铈，20g七钼酸铵，溶解于1000g去离子水中；
（2）秤取350g磷酸二氢铵，溶解于1000g去离子水中；
（3）将步骤（1）和步骤（2）二种溶液混合，升温至80℃，并搅拌均匀；
（4）将需要硬化的蜂窝催化剂模块一端或者两端浸渍在步骤（3）溶液中7s；
（5）将步骤（4）取出浸渍好的催化剂放入马弗炉中110℃煅烧30min，使其中的组分和催化剂发生反应，确保催化剂一端或两端边缘硬化。
具体实施例三
一种SCR脱硝催化剂的端部硬化处理方法， 其具体步骤如下：
（1）配置活性溶液：分别秤取50g偏钨酸铵，10g硝酸铈，15g七钼酸铵，溶解于1000g去离子水中；
（2）秤取275g磷酸二氢铵，溶解于1000g去离子水中；
（3）将步骤（1）和步骤（2）二种溶液混合，升温至80℃，并搅拌均匀；
（4）将需要硬化的蜂窝催化剂模块一端或者两端浸渍在步骤（3）溶液中5s；
（5）将步骤（4）取出浸渍好的催化剂放入马弗炉中110℃煅烧30min，使其中的组分和催化剂发生反应，确保催化剂一端或两端边缘硬化。

Claims (2)

1.一种SCR脱硝催化剂的端部硬化处理方法，其特征在于：
其具体步骤如下：
（1）配置活性溶液：分别秤取1～5份偏钨酸铵，0.5～1份硝酸铈，1～2份七钼酸铵，溶解于100份去离子水中；
（2）秤取20～35份磷酸二氢铵，溶解于100份去离子水中；
（3）将步骤（1）和步骤（2）二种溶液混合，升温至80℃，并搅拌均匀；
（4）将需要硬化的蜂窝催化剂模块一端或者两端浸渍在步骤（3）溶液中5 s ～10s；
（5）将步骤（4）取出浸渍好的催化剂放入马弗炉中110℃煅烧30min，使其中的组分和催化剂发生反应，确保催化剂一端或两端边缘硬化。
2.一种SCR脱硝催化剂的端部硬化液，其特征在于：其为活性溶液和磷酸二氢铵溶液的混合液，所述活性溶液的成分具体为1～5份偏钨酸铵、0.5～1份硝酸铈、1～2份七钼酸铵溶解于100份去离子水中混和均匀而成；所述磷酸二氢铵溶液具体为20～35份磷酸二氢铵溶解于100份去离子水中混和均匀而成。
CN201410202244.8A 2014-05-14 2014-05-14 一种scr脱硝催化剂的端部硬化处理方法 Expired - Fee Related CN104028313B (zh)