CN104005255A - Inflaming retarding type compound tipping paper and preparation method thereof - Google Patents

Abstract

The invention discloses inflaming retarding type compound tipping paper. The inflaming retarding type compound tipping paper is characterized by being prepared from following raw materials in parts by weight: 1-2 parts of antimonous oxide, 1-2 parts of titanium dioxide, 0.8-1 part of curcumine, 0.5-0.7 part of iron oxide red, 1-2 parts of propolis, 1-2 parts of soya bean lecithin, 43-46 parts of bamboo pulp, 50-54 parts of cotton pulp, 2-3 parts of edible gelatin, 1-2 parts of tomato seeds, 1-2 parts of crushed coconut shells, 2-3 parts of silicon sol, 2-3 parts of montmorillonite, 1-2 parts of an auxiliary agent and suitable amount of water. According to the inflaming retarding type compound tipping paper, the antimonous oxide with an inflaming retarding effect is added into a production process of the tipping paper, and substances including titanium dioxide, the crushed coconut shells and the like which have adsorption and filtering effects are added so as to further improve the effect of filtering smoke and increase the pleasant smell; the previous strong spicy feeling of the smoke is eliminated; the inflaming retarding type compound tipping paper has uniformly-distributed fibers, good air permeability and great strength and can avoid cracking.

Description

Compound cork paper of a kind of flame retardant type and preparation method thereof

Technical field

The present invention relates to cigarette technical field, particularly compound cork paper of a kind of flame retardant type and preparation method thereof.

Background technology

Along with the attention of country to fire safety evaluating problem, the raising of people's inherently safe consciousness, need to strengthen the security of cigarette product self for cigarette industry, reduce the fire safety evaluating hidden danger of cigarette product, preside over international public health treaty " Framework Convention on Tobacco Control " and State Tobacco Monopoly Bureau's " about suggestion of strengthening cigarette package management " of assigning for the World Health Organization simultaneously, containment excessive packaging, carry out saving and produce, cleaner production, advocate employing environment-friendly degradable, the packaging material of recyclable regenerative and recoverable, healthy, safety, the demand of environmentally friendly machine has become new development trend.

Smoking is the mankind's a hobby greatly, but in cigarette smoke, contain multiple noxious material, after smoking, these oxious components are deposited in human body and can cause the internal organs generation various diseases such as lung, respiratory tract and stomach, as cough asthma due to excessive phlegm, pharyngitis etc., often have a suck of cigarette and produce 100,000 free radicals to I haven't seen you for ages, just likely cause general cancer, accelerate growth of cancer cells, cause many chronic diseases.Smoking also can increase the incidence of disease of angiocardiopathy and cerebral apoplexy, and cigarette can stimulate liver generation drug metabolic enzyme, the metabolism of acceleration medicine, reduction blood substance concentration, thereby reduction curative effect of medication.So for the patient who is just taking medicine at ill needs, smoking is tantamount to make the matter worse.Although Smoking is harmful to your health, but smoker is still difficult to give up mostly, along with people are more and more higher to healthy concern, in recent years, " smoking is with healthy " problem more and more comes into one's own, people have higher requirement to cigarette, not only require it to have good mouthfeel, and want to reduce the harm of cigarette to human body.

Summary of the invention

The object of this invention is to provide compound cork paper of a kind of flame retardant type and preparation method thereof.

In order to realize object of the present invention, the present invention passes through following scheme implementation:

The compound cork paper of a kind of flame retardant type, is made up of the raw material of following weight portion: antimonous oxide 1-2, titanium dioxide 1-2, curcumin 0.8-1, iron oxide red 0.5-0.7, propolis 1-2, soybean lecithin 1-2, bamboo pulp 43-46, cotton pulp 50-54, edible gelatin 2-3, tomato seed 1-2, pulverizing cocoanut shell 1-2, Ludox 2-3, montmorillonite 2-3, auxiliary agent 1-2, water are appropriate;

Described auxiliary agent is made up of the raw material of following weight portion: tangerine peel freeze-dried powder 4-5, pineapple jelly dry powder 2-4, porous-starch 2-3, medical stone 3-5, peppermint essential oil 1-2, Tween-20 0.8-1, water are appropriate; Tangerine peel freeze-dried powder, pineapple jelly dry powder, porous-starch, medical stone mixed powder are broken into 60-80 object powder by preparation method, then add peppermint essential oil, a small amount of water to grind, grinding after 20-30 minute thin up, to become solid content be the solution of 10-15%, finally add Tween-20 to stir, obtain turbid liquid and get final product.

The compound cork paper of a kind of flame retardant type of the present invention, made by following concrete steps:

(1) Cotton Pulp, soft wood pulp are put into hydrabrusher size degradation, then through beater, beating consistency is controlled at 3.6-4.4%, beating degree is 67～73 ⁰sR, makes slurry;

(2) tomato seed, pulverizing cocoanut shell are dried, wear into 30-40 object powder, mix, reach compound;

(3) compound, antimonous oxide, titanium dioxide, montmorillonite are mixed, grind to form 40-60 object powder, add curcumin 0.8-1, iron oxide red, stir and within 25-30 minute, make compound, then 50-60 DEG C dry 1-1.5 hour stand-by;

(4) compound is added in slurry, add all the other residual componentss except auxiliary agent, stir, add in step (1) filtrate and appropriate water size mixing to solid content be 2.7-3.5%, be heated to 64-72 DEG C, by the slurry mixing up, through wet end and press section drainage and formation, l Water Paper page enters the front dry stage, at surface uniform brushing auxiliary agent;

(5) under the vacuum condition of 0.05-0.08Mpa, the l Water Paper after moulding is aspirated to dehydration, then electric heating forced air drying 5-6min finally carries out press polish on ray machine, obtains cork paper body paper after taking-up.

The invention has the beneficial effects as follows: the present invention not only adds the antimonous oxide with flame retardant effect in cork paper manufacturing process, and add titanium dioxide, pulverize cocoanut shell etc. and have the material of adsorption filtration effect, the interpolation of auxiliary agent, further increased the effect of filtering flue gas, pleasant smell, has eliminated the original strong pungent sense of flue gas, fiber of the present invention is evenly distributed, good permeability, intensity is large, prevents fracture.

Specific embodiments

Below by instantiation, the present invention is described in detail.

The compound cork paper of a kind of flame retardant type, by following weight portion (kilogram) raw material make: antimonous oxide 2, titanium dioxide 2, curcumin 0.8, iron oxide red 0.5, propolis 1, soybean lecithin 1, bamboo pulp 43, cotton pulp 50, edible gelatin 2, tomato seed 1, pulverizing cocoanut shell 1, Ludox 2, montmorillonite 2, auxiliary agent 1, water are appropriate;

Described auxiliary agent by following weight portion (kilogram) raw material make: tangerine peel freeze-dried powder 4, pineapple jelly dry powder 2, porous-starch 2, medical stone 3, peppermint essential oil 1, Tween-20 0.8, water are appropriate; Tangerine peel freeze-dried powder, pineapple jelly dry powder, porous-starch, medical stone mixed powder are broken into 60-80 object powder by preparation method, then add peppermint essential oil, a small amount of water to grind, grinding after 20-30 minute thin up, to become solid content be the solution of 10-15%, finally add Tween-20 to stir, obtain turbid liquid and get final product.

The compound cork paper of a kind of flame retardant type of the present invention, made by following concrete steps:

(1) Cotton Pulp, soft wood pulp are put into hydrabrusher size degradation, then through beater, beating consistency is controlled at 3.6-4.4%, beating degree is 67～73 ⁰sR, makes slurry;

(2) tomato seed, pulverizing cocoanut shell are dried, wear into 30-40 object powder, mix, reach compound;

(3) compound, antimonous oxide, titanium dioxide, montmorillonite are mixed, grind to form 40-60 object powder, add curcumin 0.8-1, iron oxide red, stir and within 25-30 minute, make compound, then 50-60 DEG C dry 1-1.5 hour stand-by;

(4) compound is added in slurry, add all the other residual componentss except auxiliary agent, stir, add in step (1) filtrate and appropriate water size mixing to solid content be 2.7-3.5%, be heated to 64-72 DEG C, by the slurry mixing up, through wet end and press section drainage and formation, l Water Paper page enters the front dry stage, at surface uniform brushing auxiliary agent;

(5) under the vacuum condition of 0.05-0.08Mpa, the l Water Paper after moulding is aspirated to dehydration, then electric heating forced air drying 5-6min finally carries out press polish on ray machine, obtains cork paper body paper after taking-up.

After testing, the machine direction tensile strength of the cork paper body paper that the present invention makes is 1.78KN/m, and air permeability is 65CU.

Claims (2)

1. the compound cork paper of flame retardant type, it is characterized in that, made by the raw material of following weight portion: antimonous oxide 1-2, titanium dioxide 1-2, curcumin 0.8-1, iron oxide red 0.5-0.7, propolis 1-2, soybean lecithin 1-2, bamboo pulp 43-46, cotton pulp 50-54, edible gelatin 2-3, tomato seed 1-2, pulverize cocoanut shell 1-2, Ludox 2-3, montmorillonite 2-3, auxiliary agent 1-2, water is appropriate;

Described auxiliary agent is made up of the raw material of following weight portion: tangerine peel freeze-dried powder 4-5, pineapple jelly dry powder 2-4, porous-starch 2-3, medical stone 3-5, peppermint essential oil 1-2, Tween-20 0.8-1, water are appropriate; Tangerine peel freeze-dried powder, pineapple jelly dry powder, porous-starch, medical stone mixed powder are broken into 60-80 object powder by preparation method, then add peppermint essential oil, a small amount of water to grind, grinding after 20-30 minute thin up, to become solid content be the solution of 10-15%, finally add Tween-20 to stir, obtain turbid liquid and get final product.

2. the compound cork paper of a kind of flame retardant type according to claim 1, is characterized in that, is made up of following concrete steps:

(1) Cotton Pulp, soft wood pulp are put into hydrabrusher size degradation, then through beater, beating consistency is controlled at 3.6-4.4%, beating degree is 67～73 ⁰sR, makes slurry;

(2) tomato seed, pulverizing cocoanut shell are dried, wear into 30-40 object powder, mix, reach compound;

(3) compound, antimonous oxide, titanium dioxide, montmorillonite are mixed, grind to form 40-60 object powder, add curcumin 0.8-1, iron oxide red, stir and within 25-30 minute, make compound, then 50-60 DEG C dry 1-1.5 hour stand-by;

(4) compound is added in slurry, add all the other residual componentss except auxiliary agent, stir, add in step (1) filtrate and appropriate water size mixing to solid content be 2.7-3.5%, be heated to 64-72 DEG C, by the slurry mixing up, through wet end and press section drainage and formation, l Water Paper page enters the front dry stage, at surface uniform brushing auxiliary agent;

(5) under the vacuum condition of 0.05-0.08Mpa, the l Water Paper after moulding is aspirated to dehydration, then electric heating forced air drying 5-6min finally carries out press polish on ray machine, obtains cork paper body paper after taking-up.