CN104002519A - Adhesive-free solar film manufacturing process - Google Patents
Adhesive-free solar film manufacturing process Download PDFInfo
- Publication number
- CN104002519A CN104002519A CN201410225625.8A CN201410225625A CN104002519A CN 104002519 A CN104002519 A CN 104002519A CN 201410225625 A CN201410225625 A CN 201410225625A CN 104002519 A CN104002519 A CN 104002519A
- Authority
- CN
- China
- Prior art keywords
- adhesive
- coating
- free
- transparent base
- solar film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides an adhesive-free solar film manufacturing process which comprises the following steps: 1, coating a coating roller with a transparent base material PET (Polyethylene Terephthalate) in a roller coating mode at 160-180 DEG C for coloring; 2, performing vacuum coating (plating metal onto the coated transparent base material at 600-700 DEG C in vacuum); 3, performing oxidation treatment (performing fixation oxidation treatment on the surface of a metal layer at 120-150 DEG C by using coating, so as to prevent oxidation dissociation; 4, forming and compounding the transparent base material with a polyvinyl chloride film to obtain a compounded material; 5, performing adhesive-free static treatment on the compounded material; 6, compounding and forming the material after the static treatment with the transparent PET film; and 7, performing later treatment, namely, cutting, forming and packaging a compounded finished product into a finished product, namely, the adhesive-free solar film. The adhesive-free solar film is resistant to ultraviolet rays, is free of adhesive and environmentally-friendly and easy to tear and adhere, has a metal effect, is capable of reducing the indoor temperature, can be adhered without adhesive, and is capable of reducing glass breakage impact force.
Description
Technical field
The present invention relates to thermal isolation film technical field, be specifically related to glue-free solar film manufacturing process.
Background technology
Existing sun thermal isolation film is to be all placed with glue when production, and smell is dense heavy, in glue, contain other harmful substances such as benzene, when production, make troubles to workman, be unfavorable for user or consumer's health, produce high temperature at the irradiation lower-glass of the sun and also have pungent smell, to tear it down once be out of use and also be accompanied with gum spot above, bad cleaning, after tearing it down, cannot reuse, and in modern sun film production technology, often by vacuum evaporating or magnetron sputtering technique by aluminium, gold, copper, the metals such as silver are made the high heat insulating metal rete of multilayer, these products are all often thicker and increase cost.
Summary of the invention
For the deficiencies in the prior art, the object of this invention is to provide glue-free solar film manufacturing process, it has solved these above-mentioned problems.
The technical solution adopted in the present invention is as follows: glue-free solar film manufacturing process,
The first step, at 160 degree--at the temperature of 180 degree, by the mode of roller coat, coating roll is coated on transparent base PET and is painted;
Second step, vacuum coating (transparent base of first-class coating carries out vacuum metallization under the high temperature of 600--700 degree);
The 3rd step, oxidation processes (in the coating oxidation processes that fixes for layer on surface of metal, anti-oxidation departs from the temperature of 120--150 degree);
The 4th step, transparent base and polyvinyl chloride film moulding are compound;
The 5th step, carries out glue-free Electrostatic Treatment to compound good material;
The 6th step, the material after Electrostatic Treatment is complete again with the composite molding of clear PET film;
The 7th step, post-processed: by compound good finished product by cutting, moulding, packaging form the glue-free solar film of finished product.
Preferably, the metal of second step is aluminium or gold.
Beneficial effect of the present invention comprises:
The present invention has antiultraviolet, can reduce indoor temperature, glue-free environmental protection, easily tear easy subsides, can reduce glass breakage impulsive force, there is metal effect, do not need glue bonding, Electrostatic Absorption easily assembling, can Reusability, its compactedness and directionality have had significant raising, the fastness of film strengthens, light transmission is good, the overall performance of thermal isolation film is better, effect of heat insulation and light transmittance are also better, the shielding rate of visible region light transmittance and near infrared region light is higher, the strong illumination that skin is coated with metal color outside come all can the have effect of refracted ray, longer service life.Utilize the suction type of static, make atmospheric pressure be greater than the pressure of the air between screen and film, thereby produce adsorption capacity.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the present invention is described in detail.
Glue-free solar film manufacturing process,
The first step, at 160 degree--at the temperature of 180 degree, by the mode of roller coat, coating roll is coated on transparent base PET and is painted;
Second step, vacuum coating (transparent base of first-class coating carries out vacuum metallization under the high temperature of 600--700 degree);
The 3rd step, oxidation processes (in the coating oxidation processes that fixes for layer on surface of metal, anti-oxidation departs from the temperature of 120--150 degree);
The 4th step, transparent base and polyvinyl chloride film moulding are compound;
The 5th step, carries out glue-free Electrostatic Treatment to compound good material;
The 6th step, the material after Electrostatic Treatment is complete again with the composite molding of clear PET film;
The 7th step, post-processed: by compound good finished product by cutting, moulding, packaging form the glue-free solar film of finished product.
The metal of second step is aluminium or gold.
Above-mentioned embodiment is the preferred embodiments of the present invention; be not for limiting enforcement of the present invention and interest field; all equivalences of making according to the content described in the present patent application scope of patent protection change and modify, and all should be included in the present patent application the scope of the claims.
Claims (2)
1. glue-free solar film manufacturing process, is characterized in that,
The first step, at 160 degree--at the temperature of 180 degree, by the mode of roller coat, coating roll is coated on transparent base PET and is painted;
Second step, vacuum coating (transparent base of first-class coating carries out vacuum metallization under the high temperature of 600--700 degree);
The 3rd step, oxidation processes (in the coating oxidation processes that fixes for layer on surface of metal, anti-oxidation departs from the temperature of 120--150 degree);
The 4th step, transparent base and polyvinyl chloride film moulding are compound;
The 5th step, carries out glue-free Electrostatic Treatment to compound good material;
The 6th step, the material after Electrostatic Treatment is complete again with the composite molding of clear PET film;
The 7th step, post-processed: by compound good finished product by cutting, moulding, packaging form the glue-free solar film of finished product.
2. glue-free solar film manufacturing process according to claim 1, is characterized in that, the metal of second step is aluminium or gold.