CN104002418B - 一种未拉伸流延pet覆铁膜的生产方法 - Google Patents
一种未拉伸流延pet覆铁膜的生产方法 Download PDFInfo
- Publication number
- CN104002418B CN104002418B CN201410227158.2A CN201410227158A CN104002418B CN 104002418 B CN104002418 B CN 104002418B CN 201410227158 A CN201410227158 A CN 201410227158A CN 104002418 B CN104002418 B CN 104002418B
- Authority
- CN
- China
- Prior art keywords
- film
- pet
- ferrum
- covers
- ferrum film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种未拉伸流延PET覆铁膜的生产方法，所述PET覆铁膜采用流延方法制造，流延温度260-270℃，所述PET覆铁膜包括6-7份均聚聚酯，3-4份共聚聚酯。本发明通过均聚聚酯和共聚聚酯的混合流延，对PET覆铁膜进行改性，使得PET薄膜的成型变得更加容易，能够制造出较薄的PET覆铁膜，由于采用流延方法制得，能够复合铁片冲压时的形变和延伸要求，不容易出现断裂的情况。
Description
技术领域
本发明涉及流延膜生产技术领域，具体是一种未拉伸流延PET覆铁膜的生产方法。
背景技术
覆膜加工由于不使用粘着剂、溶剂，所以不含甲醛，且塑料膜可经过美化装饰、抗菌、防染等处理，确保了人体的安全性和健康、同时又起到了环保的作用。应用于制罐行业的覆膜板，俗称为覆膜铁（LaminatedSteel），是采用PET，PVC，VCM或PP薄膜与金属板材（镀锌板，冷轧板，铝板，不锈钢板）进行覆合而成。传统的金属罐内侧都必须经过涂装加工，而涂装方法所含有的物质，对人体和环境都会产生有害影响，尤其是食用罐头,现在的处理方法是在罐的内壁采用树脂进行涂装。但是，因这种涂装工艺所使用的涂料里含有环境激素的有害物质―双酚A类（Bis-phenolA）物质，是一种国际公认的环境激素，而且可能出现溶出的问题,一旦溶出超标，会对人体产生不良影响。且这个问题导致的严重后果已经引起国内外的重视。金属板覆膜技术的诞生，是金属罐生产的革命性进步。随着它的广泛应用，传统金属罐生产工艺和技术将得到颠覆，生产率、生产成本、清洁卫生、环境保护等各个方面也都将前进一大步，覆合薄膜的材料也非常广泛，有PP、PE、PET、PVC、VCM、尼龙、布、镭射膜和纸等。
如果PET薄膜如果用流延方法生产，由于成型困难，那么PET膜的厚度会很大，作为覆铁膜成本较高，因此一般PET薄膜生产都是采用双向拉伸的方法生产的，而由于经过双向拉伸后的PET薄膜耐撕裂性能、拉伸性能很差，因此当覆膜后的铁板冲压后时覆在铁板上的PET膜会破损，那么就起不到覆膜后防锈、抗菌等的性能。
发明内容
本发明针对现有技术不足，提供一种未拉伸流延PET覆铁膜的生产方法，通过这种加工方法能够生产出具有较好的耐撕裂性能以及具有较好延伸性能的PET薄膜。
为了解决上述技术问题，本发明通过下述技术方案得以解决：一种未拉伸流延PET覆铁膜的生产方法，所述PET覆铁膜采用流延方法制造，流延温度260-270℃，所述PET覆铁膜包括6-7份均聚聚酯，3-4份共聚聚酯。
上述技术方案中，所述PET覆铁膜采用三层共挤流延法制造，将均匀混合的所述均聚聚酯与所述共聚聚酯混合物分成上表面层，中间层，下表面层，在上表面层和下表面层中加入活性有机硅，所述均聚聚酯与所述共聚聚酯的混合物与所述活性有机硅的比例为9：1。
本发明与现有技术相比，具有如下有益效果：本发明通过均聚聚酯和共聚聚酯的混合流延，对PET覆铁膜进行改性，使得PET薄膜的成型变得更加容易，能够制造出较薄的PET覆铁膜，由于采用流延方法制得，能够复合铁片冲压时的形变和延伸要求，不容易出现断裂的情况。
具体实施方式
下面结合具体实施方式对本发明作进一步详细描述：实施例一、一种未拉伸流延PET覆铁膜的生产方法，所述PET覆铁膜采用流延方法制造，流延温度260-270℃，所述PET覆铁膜包括6份均聚聚酯，3份共聚聚酯，所述PET覆铁膜采用三层共挤流延法制造，将均匀混合的所述均聚聚酯与所述共聚聚酯混合物分成上表面层，中间层，下表面层，在上表面层和下表面层中加入活性有机硅，所述均聚聚酯与所述共聚聚酯的混合物与所述活性有机硅的比例为9：1。
实施例二、一种未拉伸流延PET覆铁膜的生产方法，所述PET覆铁膜采用流延方法制造，流延温度260-270℃，所述PET覆铁膜包括7份均聚聚酯，4份共聚聚酯，所述PET覆铁膜采用三层共挤流延法制造，将均匀混合的所述均聚聚酯与所述共聚聚酯混合物分成上表面层，中间层，下表面层，在上表面层和下表面层中加入活性有机硅，所述均聚聚酯与所述共聚聚酯的混合物与所述活性有机硅的比例为9：1。
实施例三、一种未拉伸流延PET覆铁膜的生产方法，所述PET覆铁膜采用流延方法制造，流延温度260-270℃，所述PET覆铁膜包括6.5份均聚聚酯，3.5份共聚聚酯，所述PET覆铁膜采用三层共挤流延法制造，将均匀混合的所述均聚聚酯与所述共聚聚酯混合物分成上表面层，中间层，下表面层，在上表面层和下表面层中加入活性有机硅，所述均聚聚酯与所述共聚聚酯的混合物与所述活性有机硅的比例为9：1。
上述三个实施例中通过均聚聚酯和共聚聚酯的混合流延，对PET覆铁膜进行改性，使得PET薄膜的成型变得更加容易，能够制造出较薄的PET覆铁膜，由于采用流延方法制得，能够复合铁片冲压时的形变和延伸要求，不容易出现断裂的情况。并且通过三层共挤的方法在表面层中加入活性有机硅，从而使得PET覆铁膜表面之间的粘度降低，从而使得PET覆铁膜开卷更加顺利。
Claims (1)
1.一种未拉伸流延PET覆铁膜的生产方法，其特征在于：所述PET覆铁膜采用流延方法制造，流延温度260-270℃，所述PET覆铁膜包括6-7份均聚聚酯，3-4份共聚聚酯，所述PET覆铁膜采用三层共挤流延法制造，将均匀混合的所述均聚聚酯与所述共聚聚酯混合物分成上表面层，中间层，下表面层，在上表面层和下表面层中加入活性有机硅，所述均聚聚酯与所述共聚聚酯的混合物与所述活性有机硅的比例为9：1。