CN103980694B - A kind of sponge matress containing silica gel - Google Patents
A kind of sponge matress containing silica gel Download PDFInfo
- Publication number
- CN103980694B CN103980694B CN201410233678.4A CN201410233678A CN103980694B CN 103980694 B CN103980694 B CN 103980694B CN 201410233678 A CN201410233678 A CN 201410233678A CN 103980694 B CN103980694 B CN 103980694B
- Authority
- CN
- China
- Prior art keywords
- silica gel
- sponge
- sponge matress
- mattress
- matress
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of sponge matress containing silica gel, comprise urethane 75 ~ 90 parts; 15 ~ 20 parts, silica gel; Silicone oil 0.2 ~ 0.3 part; Linking agent 0.1 ~ 0.2 part; Whipping agent 0.2 ~ 0.3 part; Catalyzer 0.1 ~ 0.15 part; Suds-stabilizing agent 0.05 ~ 0.2 part; 1.5 ~ 2.5 parts, water.The invention also discloses the preparation method of the sponge matress containing silica gel, taken by feed components, silica gel is worn into lower than 100 object particles, is mixed by all components, puts into foaming machine and foams rear and cool, then conventionally manufacture mattress; Sponge matress containing silica gel of the present invention, by adding silica gel in starting material, in conjunction with the advantage of sponge and silica gel, making the sponge matress made cool in summer and warm in winter, and keeping constant temperature effect, is unlikely to too cool or too hot in winter of cold and torridity summer.Silica gel need be worn into lower than 100 object particles containing the making method of silica-gel sponge mattress in the present invention, cooled by all raw material mixing post-foamings, conveniently produce mattress method and manufacture mattress, the method operation sequence is simple, applicable scale operation.
Description
Technical field
The present invention relates to family product, particularly a kind of sponge matress containing silica gel.
Background technology
In daily life, the time of the nearly half of people is spent in sleep, mattress is one of important bedding, at present, the mattress that domestic people's majority uses is that coating layer and spring layer are formed, its shortcoming is: the spring on the one hand in conventional mattresses, in the process of compression, has certain noise; Spring on the other hand in mattress, after using for a long time, easily follows the string, easily causes mattress to be partially formed recess, and traditional mattress is ventilative poor, and mattress is short for work-ing life, makes troubles to life.In addition, in existing technology, mattress just meets basic sleep request, lacks the nourishing function to human body.Especially in the summer of sweltering heat, common mattress heat radiation is slow, and poor air permeability, easily causes uncomfortable.
Sponge general reference foam material, the foaming product of resin, rubber, plastics all claims sponge.Polyurethane sponge is exactly foamed polyurethane material.The elasticity of the existing rubber of urethane, there are again the intensity of plastics and excellent processing characteristics, can for the preparation of polyurethane low resilience urethane foam resilient foam, this polyurethane low resilience urethane foam resilient foam is memory foam again, can be used for the manufacture of mattress, but current sponge mattress function singleness, does not also possess comfortable function and nourishing function.
Summary of the invention
The object of this invention is to provide a kind of cool in summer and warm in winter, the sponge matress containing silica gel of constant temperature can be kept.
For achieving the above object, the present invention is by the following technical solutions:
Adopt above structure,
Containing a sponge matress for silica gel, described sponge matress is formed by the component mixed foaming of following parts by weight:
Urethane 75 ~ 90 parts;
15 ~ 20 parts, silica gel;
Silicone oil 0.2 ~ 0.3 part;
Linking agent 0.1 ~ 0.2 part;
Whipping agent 0.2 ~ 0.3 part;
Catalyzer 0.1 ~ 0.15 part;
Suds-stabilizing agent 0.05 ~ 0.2 part;
1.5 ~ 2.5 parts, water.
Described catalyzer is organotin, one or both in sodium-chlor.
Described whipping agent is methylene dichloride, more than one the mixture in ethylene dichloride or pentane.
Described linking agent is ethylene glycol, more than one the mixture in dipropylene glycol or triglycol.
As claimed in claim 1 containing a preparation method for the sponge matress of silica gel, it comprises the following steps:
1) each component is taken according to the weight part ratio of raw material;
2) silica gel is worn into lower than 100 object particles, and be mixed into compound with other components, for subsequent use;
3) above-mentioned compound is pumped into foaming machine to foam, blowing temperature is 90 ~ 120 DEG C, forms cavernous body;
4), after being cooled at 20 ~ 25 DEG C by cavernous body, the method processing mattress of sponge matress is conveniently produced.
Sponge and silica gel are applied in the production of mattress by the present invention simultaneously, make the mattress of production in conjunction with sponge and the common advantage of silica gel, produced mattress flexibility and rebound resilience just right, user lies on mattress, mattress can adjust according to according to human body different sites, has reached the degree of human comfort of allowing.
Silica gel discharges after surging force can being absorbed at leisure again.Utilize this character to be used on mattress by silica gel, the effect of pressure of relaxing will be had.In addition, because silica gel is in different temperature, its soft durometer will change thereupon (thermal change is soft cold hardening).
Sponge matress containing silica gel of the present invention also comprises fire retardant, to prevent raw material temperature in foaming process too high, causes burning.
Sponge matress containing silica gel of the present invention, by adding silica gel in starting material, in conjunction with the advantage of sponge and silica gel, making the sponge mattress made cool in summer and warm in winter, and keeping constant temperature effect, is unlikely to too cool or too hot in winter of cold and torridity summer.Silica gel need be worn into lower than 100 object particles containing the making method of silica-gel sponge mattress in the present invention, cooled by all raw material mixing post-foamings, conveniently produce mattress method and manufacture mattress, the method operation sequence is simple, applicable scale operation.
Embodiment
Below in conjunction with embodiment, the present invention is further detailed explanation:
A kind of sponge matress containing silica gel of the present invention, described sponge matress is formed by the component mixed foaming of following parts by weight:
Urethane 75 ~ 90 parts;
15 ~ 20 parts, silica gel;
Silicone oil 0.2 ~ 0.3 part;
Linking agent 0.1 ~ 0.2 part;
Whipping agent 0.2 ~ 0.3 part;
Catalyzer 0.1 ~ 0.15 part;
Suds-stabilizing agent 0.05 ~ 0.2 part;
1.5 ~ 2.5 parts, water.
Described catalyzer is organotin, one or both in sodium-chlor.
Described whipping agent is methylene dichloride, more than one the mixture in ethylene dichloride or pentane.
Described linking agent is ethylene glycol, more than one the mixture in dipropylene glycol or triglycol.
As claimed in claim 1 containing a preparation method for the sponge matress of silica gel, it comprises the following steps:
1) each component is taken according to the weight part ratio of raw material;
2) silica gel is worn into lower than 100 object particles, and be mixed into compound with other components, for subsequent use;
3) above-mentioned compound is pumped into foaming machine to foam, blowing temperature is 90 ~ 120 DEG C, forms cavernous body;
4), after being cooled at 20 ~ 25 DEG C by cavernous body, the method processing mattress of sponge matress is conveniently produced.
Embodiment 1
Containing a preparation method for the sponge matress of silica gel, it comprises the following steps:
1) each component is taken according to the weight part ratio of raw material;
Urethane 75 parts;
20 parts, silica gel;
Silicone oil 0.2 part;
Linking agent 0.1 part;
Whipping agent 0.3 part;
Catalyzer 0.1 part;
Suds-stabilizing agent 0.2 part;
1.5 parts, water.
2) silica gel is worn into lower than 100 object particles, and be mixed into compound with other components, for subsequent use;
3) above-mentioned compound is pumped into foaming machine to foam, blowing temperature is 90 DEG C, forms cavernous body;
4), after being cooled at 20 ~ 25 DEG C by cavernous body, the method processing mattress of sponge matress is conveniently produced.
Embodiment 2
Containing a preparation method for the sponge matress of silica gel, it comprises the following steps:
1) each component is taken according to the weight part ratio of raw material;
Urethane 90 parts;
15 parts, silica gel;
Silicone oil 0.3 part;
Linking agent 0.2 part;
Whipping agent 0.2 part;
Catalyzer 0.15 part;
Suds-stabilizing agent 0.05 part;
2.5 parts, water.
2) silica gel is worn into lower than 100 object particles, and be mixed into compound with other components, for subsequent use;
3) above-mentioned compound is pumped into foaming machine to foam, blowing temperature is 120 DEG C, forms cavernous body;
4), after being cooled at 20 ~ 25 DEG C by cavernous body, the method processing mattress of sponge matress is conveniently produced.
Embodiment 3
Containing a preparation method for the sponge matress of silica gel, it comprises the following steps:
1) each component is taken according to the weight part ratio of raw material;
Urethane 80 parts;
18 parts, silica gel;
Silicone oil 0.25 part;
Linking agent 0.15 part;
Whipping agent 0.25 part;
Catalyzer 0.13 part;
Suds-stabilizing agent 0.1 part;
1.7 parts, water.
2) silica gel is worn into lower than 100 object particles, and be mixed into compound with other components, for subsequent use;
3) above-mentioned compound is pumped into foaming machine to foam, blowing temperature is 110 DEG C, forms cavernous body;
4), after being cooled at 20 ~ 25 DEG C by cavernous body, the method processing mattress of sponge matress is conveniently produced.
Claims (2)
1., containing a sponge matress for silica gel, it is characterized in that: described sponge matress is formed by the component mixed foaming of following parts by weight:
Urethane 75-90 part;
Silica gel 15-20 part;
Silicone oil 0.2-0.3 part;
Linking agent 0.1-0.2 part;
Whipping agent 0.2-0.3 part;
Catalyzer 0.1-0.15 part;
Suds-stabilizing agent 0.05-0.2 part;
Water 1.5-2.5 part;
Described whipping agent is methylene dichloride, more than one the mixture in ethylene dichloride or pentane;
Described linking agent is ethylene glycol, more than one the mixture in dipropylene glycol or triglycol;
The preparation method of described sponge matress comprises the following steps:
1) each component is taken according to the weight part ratio of raw material;
2) silica gel is worn into lower than 100 object particles, and be mixed into compound with other components, for subsequent use;
3) above-mentioned compound is pumped into foaming machine to foam, blowing temperature is 90-120 DEG C, forms cavernous body;
4), after being cooled at 20-25 DEG C by cavernous body, the method processing mattress of sponge matress is conveniently produced.
2. a kind of sponge matress containing silica gel according to claim 1, is characterized in that: described catalyzer is organotin.