CN103980550B - A kind of Composite thermal expansion material - Google Patents
A kind of Composite thermal expansion material Download PDFInfo
- Publication number
- CN103980550B CN103980550B CN201410237814.7A CN201410237814A CN103980550B CN 103980550 B CN103980550 B CN 103980550B CN 201410237814 A CN201410237814 A CN 201410237814A CN 103980550 B CN103980550 B CN 103980550B
- Authority
- CN
- China
- Prior art keywords
- thermal expansion
- composite thermal
- expansion material
- powder
- suction pipe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of Composite thermal expansion material, relate to be a kind of can the material of rapid expansion and a kind of suction pipe that can prevent hot drink suction at hot water.In order to overcome the deficiency of existing suction pipe----hot drink facilitates penetration of suction pipe, the invention provides a kind of suction pipe, and this suction pipe can block suction pipe in superheated liquid.The technical scheme that technical solution problem of the present invention adopts is: a kind of Composite thermal expansion material, it is characterized in that: this material is made up of following steps: the first step: auricularia auriculajudae powder, flower mushroom powder, Kelp Powder, jelly powder, starch, salt, peanut oil, be that 50:30:50:10:5:1:1 fully mixes according to mass ratio, second step: be that 10:1 fully mixes according to mass ratio the mixture obtained by the first step and water, the 3rd step: the mixture obtained by second step is dry.
Description
The divisional application that the application is the applying date is on November 13rd, 2012, application number is 2012104531852, denomination of invention is the patent application of " a kind of Composite thermal expansion material and a kind of suction pipe ".
Technical field
The present invention relates to a kind of matrix material and a kind of suction pipe, specifically, relate to be a kind of can the material of rapid expansion and a kind of suction pipe that can prevent hot drink suction at hot water.
Background technology
Suction pipe sipping liquids is usually used, such as fruit juice, coffee, vinegar, Yoghourt etc. in life, well-known: the behavior sucking superheated liquid with suction pipe is dangerous.In a lot of situation, use suction pipe sucking hot drink and cause health especially the damage in oral cavity be employ suction pipe because of carelessness, or wall of cup effect of heat insulation is better, cannot judge the temperature of liquid, employ suction pipe hastily.
Summary of the invention
In order to overcome the deficiency of existing suction pipe, the invention provides a kind of matrix material and a kind of suction pipe, this suction pipe can block suction pipe in superheated liquid.
The technical solution adopted for the present invention to solve the technical problems is:
A manufacture method for Composite thermal expansion material, the steps include:
Auricularia auriculajudae wash clean, then boil, then dry, then pulverize.This material designation is auricularia auriculajudae powder by the present invention.
Flower mushroom wash clean, then boil, then dry, then pulverize.This material designation is flower mushroom powder by the present invention.
Sea-tangle wash clean, then boil, then dry, then pulverize.This material designation is Kelp Powder by the present invention.
Gelatin is pulverized.This material designation is jelly powder by the present invention.
Auricularia auriculajudae powder, flower mushroom powder, Kelp Powder, jelly powder, starch, salt, peanut oil, be that 50:30:50:10:5:1:1 fully mixes according to mass ratio.The present invention is by this mixing material called after expansion dry powder.
Be that 10:1 fully mixes expansion dry powder and water according to mass ratio, obtain dope, the present invention is by this dope called after expansion wet-milling.
Expansion wet-milling is dry, obtain the solid material became one.The present invention is by this solid material called after Composite thermal expansion material.Composite thermal expansion material has such character: in the cold drink of 10 degrees Celsius, lasts 20 minutes volumes and obviously expands, and higher than in the hot drink of 60 degrees Celsius, lasting 5 seconds just can have obvious volumetric expansion.
A kind of Composite thermal expansion material, is characterized in that: be made up of auricularia auriculajudae powder, flower mushroom powder, Kelp Powder, jelly powder, starch, salt, peanut oil, its mass ratio is followed successively by 50:30:50:10:5:1:1.
Composite thermal expansion material is manufactured tubulose, and the present invention is by this pipe called after Composite thermal expansion material pipe.
A kind of suction pipe, is characterized in that: have at least one Composite thermal expansion material pipe in suction tube body.
The invention has the beneficial effects as follows: provide after one runs into hot water, the material that short period of time volume expands in a large number, is used for suction pipe this material, can prevents from drinking into hot drink.
Accompanying drawing explanation
Fig. 1 is suction-pipe structure schematic diagram.
Fig. 2 is suction pipe vertical view.
Fig. 3 is suction-pipe structure schematic diagram.
Fig. 4 is suction pipe vertical view.
In figure: 1-suction tube body, 2-Composite thermal expansion material pipe, 3-ring-type limiting plate.
Embodiment
Below in conjunction with accompanying drawing, further illustrate of the present invention.
First manufacture a kind of matrix material, the steps include:
Auricularia auriculajudae wash clean, remove silt and root wood chip, be then put in boiling water and boil, then dry, the results showed, dry, drying can.Find through test, be crushed to particle diameter at 30 microns---50 microns of better effects if.This material designation is auricularia auriculajudae powder by the present invention.
Flower mushroom wash clean: remove silt, be then put in boiling water and boil, then dry, the results showed, dry, drying can.Find through test, be crushed to particle diameter at 30 microns---50 microns of better effects if.This material designation is flower mushroom powder by the present invention.
Sea-tangle is processed equally: wash clean, then boil, then dry, be then crushed to particle diameter at 30 microns---50 microns.This material designation is Kelp Powder by the present invention.
Gelatin is pulverized.This material designation is jelly powder by the present invention.Find through overtesting, the particle diameter of jelly powder does not have a significant effect to technique effect, does not have materially affect to following process.
Auricularia auriculajudae powder, flower mushroom powder, Kelp Powder, jelly powder, starch, salt, peanut oil, be that 50:30:50:10:5:1:1 fully mixes according to mass ratio.The present invention is by this mixing material called after expansion dry powder.
Be that 10:1 fully mixes expansion dry powder and water according to mass ratio, obtain dope, the present invention is by this dope called after expansion wet-milling.During expansion dry powder and water mixing, can stir, while spray water with watering can, such operating method, what expansion dry powder and water can be made to mix is better.
Expansion wet-milling is dry, obtain the solid material became one.The present invention is by this solid material called after Composite thermal expansion material.Composite thermal expansion material has such character: in the cold drink of 10 degrees Celsius, lasts 20 minutes volumes and obviously expands, and in the hot drink of 60 degrees Celsius, lasting 5 seconds just can have obvious volumetric expansion.
Test finds, the seasoning of expansion wet-milling lucifuge, the character of heat drying to Composite thermal expansion material are had no significant effect.
Expansion wet-milling is made tubulose, and after drying, the product obtained is made up of Composite thermal expansion material and in a tubular form.This pipe, is named as in the present invention: Composite thermal expansion material pipe (2).
Find through test, starch effectively can improve the hardness of Composite thermal expansion material pipe (2), salt effectively can reduce the cracking of Composite thermal expansion material pipe (2), peanut oil both can improve the hardness of Composite thermal expansion material pipe (2), effectively can reduce again the cracking of Composite thermal expansion material pipe (2), simultaneously, peanut oil also slow down Composite thermal expansion material pipe (2) Bulking Time in cold drink, but too much peanut oil can cause Composite thermal expansion material pipe (2) Bulking Time in hot drink slack-off.So the content of peanut oil is strictly limited.
Find through test, in numerous produced mushroom, use the effect of flower mushroom better.
Find through test, reduce the consumption of Kelp Powder, the hardness of Composite thermal expansion material pipe (2) can decline, and increase the consumption of Kelp Powder, the hardness of Composite thermal expansion material pipe (2) also can decline, so, suitable Kelp Powder consumption be selected.
Find through test, auricularia auriculajudae powder content improves greatly, the time used of obviously expanding of volume in cold drink can be caused to shorten, can cause like this----in cold drink, Composite thermal expansion material pipe (2) very short time just can expand.
Find through test, gelatine content increases, and volume in hot drink can be caused obviously to expand time lengthening used, and can cause-----like this in hot drink, last for a long time, Composite thermal expansion material pipe (2) just can expand into enough large volume.
Find through test, gelatine content reduces, and volume in cold drink can be caused obviously to expand time shorten used.
Find through test: the ratio of Composite thermal expansion material pipe (2) internal diameter and thickness of pipe is 1:1 is preferred version, such Composite thermal expansion material pipe (2), in 10 DEG C water, lasts volumetric expansion in about 20 minutes to enough large, so that blocking suction pipe; In the water of 60 degrees Celsius, lasting 5 seconds just can have obvious volumetric expansion, so that blocking suction pipe.
Test also finds: Bulking Time and the beverage types relation of Composite thermal expansion material pipe (2) are little, such as: milk, water, Sucus Mali pumilae, orange juice, coffee, sucrose water, salt solution, as long as reason take water as the liquid (comprising solution, suspension liquid, emulsion) that primary solvent configures, identical effect can be played: rapid expansion in hot drink, in cold drink, slowly expand.
After usual people obtain suction pipe, suction pipe can be inserted in beverage, go to dining table from information desk, then drink.This time is often more than 5 seconds.
Find through test, Composite thermal expansion material pipe (2), in 4 DEG C water, lasts volumetric expansion in about 25 minutes to complete clogging suction pipe.Composite thermal expansion material pipe (2), in boiling water, lasts 2 seconds volumes and just expand into complete clogging suction pipe.
See accompanying drawing 1, a Composite thermal expansion material pipe (2) is had in suction tube body (1), Composite thermal expansion material pipe (2) is fixedly connected on the inwall of suction tube body (1), method of attachment can be bonding by edible gum, the internal diameter being a bit larger tham suction tube body (1) that also external diameter of Composite thermal expansion material pipe (2) can be made, then fills in suction tube body (1).
See accompanying drawing 2, accompanying drawing 2 is vertical views of accompanying drawing 1, and the ratio of the internal diameter (diameter of interior cylindrical cavity) of Composite thermal expansion material pipe (2) and the wall thickness of Composite thermal expansion material pipe (2) is 1 to 1 is preferred version.
In order to ensure that suction tube body (1) is inserted in beverage one end arbitrarily, there is Composite thermal expansion material pipe (2) to soak in the beverage, just needing to settle Composite thermal expansion material pipe (2) respectively at the two ends of suction tube body (1).
During for the ease of factory's segmentation cutting suction tube body (1), Composite thermal expansion material pipe (2) is always had in suction tube body (1), just need to settle multiple Composite thermal expansion material pipe (2) in suction tube body (1), such as, there is a Composite thermal expansion material pipe (2) every 5 centimetres, or have a Composite thermal expansion material pipe (2) every 3 centimetres.
See accompanying drawing 3, in order to better Composite thermal expansion material pipe (2) is fixed in suction tube body (1), two ring-type limiting plates (3) can be connected at suction tube body (1) internal fixtion, between two ring-type limiting plates (3), Composite thermal expansion material pipe (2) is installed.That is, suction pipe of the present invention can also comprise and is fixedly connected on suction tube body (1) inwall and two the ring-type limiting plates (3) being positioned at Composite thermal expansion material pipe (2) two ends.
Accompanying drawing 4 is vertical views of accompanying drawing 3, porose in the middle of ring-type limiting plate (3), is convenient to beverage and passes.
Same, in order to ensure that suction tube body (1) is inserted in beverage in one end arbitrarily, there is Composite thermal expansion material pipe (2) to soak in the beverage, just need to settle Composite thermal expansion material pipe (2) and the ring-type limiting plate (3) for fixing Composite thermal expansion material pipe (2) respectively at the two ends of suction tube body (1).
Same, for the ease of factory's segmentation cutting, settle multiple Composite thermal expansion material pipe (2) in suction tube body (1), each Composite thermal expansion material pipe is by ring-type limiting plate (3) restriction site.
The invention has the beneficial effects as follows: provide after one runs into hot water, the material that short period of time volume expands in a large number, is used for suction pipe this material, can prevents from drinking into hot drink.
Claims (1)
1. a Composite thermal expansion material, is characterized in that: described Composite thermal expansion material is formed by following steps manufacture:
The first step: auricularia auriculajudae powder, flower mushroom powder, Kelp Powder, jelly powder, starch, salt, peanut oil is that 50:30:50:10:5:1:1 fully mixes according to mass ratio,
Second step: be that 10:1 fully mixes according to mass ratio the mixture obtained by the first step and water,
3rd step: the mixture obtained by second step is dry.