CN103966859A - Method for manufacturing novel flame-retardant negative ion curtain fabric - Google Patents
Method for manufacturing novel flame-retardant negative ion curtain fabric Download PDFInfo
- Publication number
- CN103966859A CN103966859A CN201410230492.3A CN201410230492A CN103966859A CN 103966859 A CN103966859 A CN 103966859A CN 201410230492 A CN201410230492 A CN 201410230492A CN 103966859 A CN103966859 A CN 103966859A
- Authority
- CN
- China
- Prior art keywords
- agent
- dyeing
- retardant
- fabric
- speed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for manufacturing a novel flame-retardant negative ion curtain fabric. A flame retardant finishing agent, a negative ion finishing agent and a coloring process are combined in the manufacturing process, and one-time inflaming retarding, negative ions and color dyeing and finishing treatment can be carried out on the fabric, so that the targets of inflaming retarding and releasing the negative ions are effectively achieved.
Description
Technical field
The present invention relates to a kind of fabric, belong to weaving face fabric field, relate in particular to a kind of manufacturing method of fabric of making curtain.
Background technology
Curtain is made by cloth, fiber crops, yarn, aluminium flake, wood chip, metal material etc., has the function of sunshading and heat-insulating and adjusting indoor light.The door curtain made of cloth divides and has cotton gauze by material, woven dacron, polyester cotton blending, cotton ramie blended spinning, nonwoven fabric etc., along with the development in epoch, consumer except original function, has also had new demand to curtain, as fire-retardant, reconcile air quality etc.
Airborne anion is referred to as airborne vitamin, as vitamin, human body and other vital movement is had to very important meaning, and airborne anion, with long-lived relevant, is referred to as long-lived element; Anion can make active acid disappear, and eliminates the active acid in body, eliminates fatigue, and activating cell strengthens immunity, makes human body freely comfortable, and blood is unobstructed, and delaying aging improves insomnia and dry skin.
Summary of the invention
Based on the technical problem of background technology existence, the present invention proposes the manufacture method of a kind of novel flame-retardant, anion window curtain fabric.
Technical scheme of the present invention is as follows:
A manufacture method for novel flame-retardant, anion window curtain fabric, comprises that pre-setting and dyeing arrange,
Described pre-setting, carries out: fabric is placed in to the pre-setting machine of 150-180 DEG C, with the speed of 20-50m/min, fabric is carried out to pre-setting according to the following steps;
Described dyeing arranges, and carries out according to the following steps:
1, boil step, the fabric that pre-setting is good is placed in dyeing machine, add form with the configuration of refining agent and chelated dispersants boil cloth liquid, at the temperature of 80-100 DEG C, boil cloth 10-40min, wherein, the addition of refining agent, chelated dispersants is to add 1-5g in 1L water.
2, colouring, under normal temperature, in dyeing machine, add dyeing dressing liquid, be warming up to 50-70 DEG C with the speed of 1-5 DEG C/min, continue insulation 20-40min to fabric paint, fire-retardant, anion processing, then be cooled to 45-55 DEG C with the speed of 0.5-3 DEG C/min, for subsequent use.
Each constituent mass of above-mentioned dyeing dressing liquid is respectively:
Deionized water: 1kg
Levelling agent: 0.5-4g
Chelated dispersants: 0.5-4g
Dyeing diluent: 5-80g
Coloring agent: 1-5g
Antiflaming finishing agent: 1-10g
Anionic finishing agent: 0.5-3g
3, wash water, is changed to deionized water by the water in dyeing machine, adds neutralizer and soaping agent in water, stir after 5-10min and be warming up to 80-100 DEG C with the speed of 1-10 DEG C/min, insulation 5-20min, then with the speed of 0.1-2 DEG C/min be cooled to 45-55 DEG C for subsequent use.
Preferably, described coloring agent is TEC series coloring agent, and described neutralizer is glacial acetic acid, and described dyeing diluent is glauber salt, and described levelling agent is cotton levelling agent.
Preferably, described fire retardant non-halogen flame retardant.
Preferably, described anionic finishing agent is nanoscale negative ion powder.
This programme is than the usefulness of traditional scheme:
1, will arrange and painted combination, production procedure is shorter than traditional handicraft, meets national industrial policies energy-conservation, that reduce discharging;
2, adopt nanoscale negative ion powder, fastness ability is good, and it is lasting to discharge;
3, fire resistance is good, limited oxygen index LOI>26%, and the long <15cm of charcoal, after flame time <10S, time <10S glows.
Detailed description of the invention
Embodiment 1:
A manufacture method for novel flame-retardant, anion window curtain fabric, comprises that pre-setting and dyeing arrange,
Described pre-setting, carries out: fabric is placed in to the pre-setting machine of 150 DEG C, with the speed of 30m/min, fabric is carried out to pre-setting according to the following steps;
Described dyeing arranges, and carries out according to the following steps:
1, boil cloth, the fabric that pre-setting is good is placed in dyeing machine, add form with the configuration of refining agent and chelated dispersants boil cloth liquid, at the temperature of 100 DEG C, boil cloth 20min, wherein, the addition of refining agent, chelated dispersants is to add 5g in 1L water.
2, colouring, under normal temperature, in dyeing machine, add dyeing dressing liquid, be warming up to 50 DEG C with the speed of 1 DEG C/min, continue insulation 20min to fabric paint, fire-retardant, anion processing, be then cooled to 50 DEG C with the speed of 3 DEG C/min, for subsequent use.
Each constituent mass of above-mentioned dyeing dressing liquid is respectively:
Deionized water: 1kg
Levelling agent: 0.5g
Chelated dispersants: 4g
Dyeing diluent: 16g
Coloring agent: 1g
Halogen-free flame-retardant finishing agent: 1g
Nanoscale anionic finishing agent: 3g
3, wash water, is changed to deionized water by the water in dyeing machine, adds neutralizer and soaping agent in water, stir after 8min and be warming up to 80 DEG C with the speed of 2 DEG C/min, insulation 5min, then with the speed of 2 DEG C/min be cooled to 50 DEG C for subsequent use.
Described coloring agent is TEC series coloring agent, and described neutralizer is glacial acetic acid, and described dyeing diluent is glauber salt, and described levelling agent is cotton levelling agent.
Embodiment 2:
A manufacture method for novel flame-retardant, anion window curtain fabric, comprises that pre-setting and dyeing arrange,
Described pre-setting, carries out: fabric is placed in to the pre-setting machine of 180 DEG C, the speed of 20m/min is carried out pre-setting to fabric according to the following steps;
Described dyeing arranges, and carries out according to the following steps:
1, boil cloth, the fabric that pre-setting is good is placed in dyeing machine, add form with the configuration of refining agent and chelated dispersants boil cloth liquid, at the temperature of 80 DEG C, boil cloth 40min, wherein, the addition of refining agent, chelated dispersants is to add 1g in 1L water.
2, colouring, under normal temperature, in dyeing machine, add dyeing dressing liquid, be warming up to 70 DEG C with the speed of 5 DEG C/min, continue insulation 30min to fabric paint, fire-retardant, anion processing, be then cooled to 55 DEG C with the speed of 0.5 DEG C/min, for subsequent use.
Each constituent mass of above-mentioned dyeing dressing liquid is respectively:
Deionized water: 1kg
Levelling agent: 4g
Chelated dispersants: 0.5g
Dyeing diluent: 5g
Coloring agent: 1g
Halogen-free flame-retardant finishing agent: 3g
Nanoscale anionic finishing agent: 0.5g
3, wash water, is changed to deionized water by the water in dyeing machine, adds neutralizer and soaping agent in water, stir after 5min and be warming up to 100 DEG C with the speed of 1 DEG C/min, insulation 20min, then with the speed of 0.1 DEG C/min be cooled to 55 DEG C for subsequent use.
Described coloring agent is TEC series coloring agent, and described neutralizer is glacial acetic acid, and described dyeing diluent is glauber salt, and described levelling agent is cotton levelling agent.
Embodiment 3:
A manufacture method for novel flame-retardant, anion window curtain fabric, comprises that pre-setting and dyeing arrange,
Described pre-setting, carries out: fabric is placed in to the pre-setting machine of 160 DEG C, the speed of 50m/min is carried out pre-setting to fabric according to the following steps;
Described dyeing arranges, and carries out according to the following steps:
1, boil cloth, the fabric that pre-setting is good is placed in dyeing machine, add form with the configuration of refining agent and chelated dispersants boil cloth liquid, at the temperature of 85 DEG C, boil cloth 10min, wherein, the addition of refining agent, chelated dispersants is to add 3g in 1L water.
2, colouring, under normal temperature, in dyeing machine, add dyeing dressing liquid, be warming up to 60 DEG C with the speed of 3 DEG C/min, continue insulation 30min to fabric paint, fire-retardant, anion processing, be then cooled to 45 DEG C with the speed of 1.5 DEG C/min, for subsequent use.
Each constituent mass of above-mentioned dyeing dressing liquid is respectively:
Deionized water: 1kg
Levelling agent: 2g
Chelated dispersants: 3g
Dyeing diluent: 80g
Coloring agent: 3g
Halogen-free flame-retardant finishing agent: 10g
Nanoscale anionic finishing agent: 1.5g
3, wash water, is changed to deionized water by the water in dyeing machine, adds neutralizer and soaping agent in water, stir after 10min and be warming up to 85 DEG C with the speed of 10 DEG C/min, insulation 10min, then with the speed of 1.2 DEG C/min be cooled to 45 DEG C for subsequent use.
Described coloring agent is TEC series coloring agent, and described neutralizer is glacial acetic acid, and described dyeing diluent is glauber salt, and described levelling agent is cotton levelling agent.
Embodiment 1-3 is detected:
| Test item | The mean value of embodiment 1-3 |
| Limited oxygen index (LOI) | 32 |
| The continuous right time (s) | 3 |
| (s) glows the time | 5 |
| Anion index (individual/cm3) | 9500 |
| Washing | 4.0 level |
| Washing | 4.2 |
This detects data only for above-mentioned detection sample.
The above; it is only preferably detailed description of the invention of the present invention; but protection scope of the present invention is not limited to this; any be familiar with those skilled in the art the present invention disclose technical scope in; be equal to replacement or changed according to technical scheme of the present invention and inventive concept thereof, within all should being encompassed in protection scope of the present invention.
Claims (5)
1. a manufacture method for novel flame-retardant, anion window curtain fabric, comprises pre-setting and dyeing, it is characterized in that:
Described pre-setting, carries out: fabric is placed in to the pre-setting machine of 150-180 DEG C, with the speed of 20-50m/min, fabric is carried out to pre-setting according to the following steps;
Described dyeing, carry out according to the following steps:
Boil step, the fabric that pre-setting is good is placed in dyeing machine, add form with the configuration of refining agent and chelated dispersants boil cloth liquid, at the temperature of 80-100 DEG C, boil cloth 10-40min, wherein, the addition of refining agent, chelated dispersants is to add 1-5g in 1L water;
Colouring, under normal temperature, in dyeing machine, add dyeing dressing liquid, be warming up to 50-70 DEG C with the speed of 1-5 DEG C/min, continue insulation 20-40min to fabric paint, fire-retardant, anion processing, be then cooled to 45-55 DEG C with the speed of 0.5-3 DEG C/min, for subsequent use;
Wash water, is changed to deionized water by the water in dyeing machine, adds neutralizer and soaping agent in water, stir after 5-10min and be warming up to 80-100 DEG C with the speed of 1-10 DEG C/min, insulation 5-20min, then with the speed of 0.1-2 DEG C/min be cooled to 45-55 DEG C for subsequent use.
2. the manufacture method of novel flame-retardant as claimed in claim 1, anion window curtain fabric, is characterized in that, each constituent mass of described dyeing dressing liquid is respectively:
Deionized water: 1kg;
Levelling agent: 0.5-4g;
Chelated dispersants: 0.5-4g;
Dyeing diluent: 5-80g;
Coloring agent: 1-5g;
Antiflaming finishing agent: 1-10g;
Anionic finishing agent: 0.5-3g.
3. the manufacture method of novel flame-retardant as claimed in claim 2, anion window curtain fabric, is characterized in that, described antiflaming finishing agent is halogen-free flame-retardant finishing agent.
4. the manufacture method of novel flame-retardant as claimed in claim 2, anion window curtain fabric, is characterized in that, described anionic finishing agent is nanoscale negative ion powder.
5. the manufacture method of novel flame-retardant as claimed in claim 2, anion window curtain fabric, is characterized in that described coloring agent is TEC series coloring agent, and described neutralizer is glacial acetic acid, and described dyeing diluent is glauber salt, and described levelling agent is cotton levelling agent.