CN103964728A - Novel cement hardening agent - Google Patents
Novel cement hardening agent Download PDFInfo
- Publication number
- CN103964728A CN103964728A CN201410182513.9A CN201410182513A CN103964728A CN 103964728 A CN103964728 A CN 103964728A CN 201410182513 A CN201410182513 A CN 201410182513A CN 103964728 A CN103964728 A CN 103964728A
- Authority
- CN
- China
- Prior art keywords
- parts
- sodium
- hardening agent
- cement
- novel cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a novel cement hardening agent which comprises the following components in parts by weight: 10-20 parts of calcium aluminate, 3-8 parts of gypsum, 4-8 parts of benzyl naphthalene sulfonic acid sodium, 2-4 parts of sodium fluosilicate, 1-3 parts of sodium stearate, 2-5 parts of calcium chloride, 1-3 parts of sodium carbonate, 3-5 parts of aluminum sulfate, 1-3 parts of citric acid and 60-80 parts of water. A preparation method for the novel cement hardening agent comprises the following steps: smashing the raw materials according to the ratio, and fully stirring so as to obtain the finished product. Compared with the prior art, the novel cement hardening agent has the benefits that (1) when the novel cement hardening agent is added into cement, the hardness of the cement can be greatly improved, after the novel cement hardening agent is added into cement for 3 hours, the compressive strength can reach 20 MPa, and the novel cement hardening agent is suitable for buildings needing pouring and quickly hardening; (2) the preparation technology is simple, and the cost is low.
Description
Technical field
The invention belongs to cement additire technical field, more specifically relate to a kind of novel concrete stiffening agent.
Background technology
Cement hardener refers to and is added in cement, to improve a kind of additive of cement hardness, can greatly improve the performance of cement, and use range is very extensive.
Summary of the invention
The object of the invention is to overcome the deficiency that prior art exists, a kind of novel concrete stiffening agent is provided.
For achieving the above object, the present invention has taked following technical scheme:
A novel concrete stiffening agent, in weight part, composed of the following components:
Calcium aluminate: 10～20, gypsum: 3～8, benzyl naphthalene sodium sulfonate: 4～8,
Sodium Silicofluoride: 2～4, sodium stearate: 1～3, calcium chloride: 2～5,
Sodium carbonate: 1～3, Tai-Ace S 150: 3～5, citric acid: 1～3, water: 60～80.
The preparation method of described novel concrete stiffening agent is: by proportioning, by described raw material pulverizing, after fully stirring, get final product to obtain finished product.
Compared with prior art, the present invention has following beneficial effect:
(1) the present invention adds in cement, can greatly improve the hardness of cement, add cement after 3 hours ultimate compression strength can reach 20MPa, be applicable to build the building of rapid sclerosis;
(2) preparation technology is simple, with low cost.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1
A novel concrete stiffening agent, in weight part, composed of the following components:
Calcium aluminate: 10, gypsum: 3, benzyl naphthalene sodium sulfonate: 4,
Sodium Silicofluoride: 2, sodium stearate: 1, calcium chloride: 2,
Sodium carbonate: 1, Tai-Ace S 150: 3, citric acid: 1, water: 60.
Embodiment 2
A novel concrete stiffening agent, in weight part, composed of the following components:
Calcium aluminate: 20, gypsum: 8, benzyl naphthalene sodium sulfonate: 8,
Sodium Silicofluoride: 4, sodium stearate: 3, calcium chloride: 5,
Sodium carbonate: 3, Tai-Ace S 150: 5, citric acid: 3, water: 80.
Embodiment 3
A novel concrete stiffening agent, in weight part, composed of the following components:
Calcium aluminate: 16, gypsum: 6, benzyl naphthalene sodium sulfonate: 6,
Sodium Silicofluoride: 3, sodium stearate: 2, calcium chloride: 3,
Sodium carbonate: 2, Tai-Ace S 150: 4, citric acid: 2, water: 70.
The preparation method of described novel concrete stiffening agent is: by proportioning, by described raw material pulverizing, after fully stirring, get final product to obtain finished product.
Claims (4)
1. a novel concrete stiffening agent, is characterized in that, in weight part, composed of the following components:
Calcium aluminate: 10～20, gypsum: 3～8, benzyl naphthalene sodium sulfonate: 4～8,
Sodium Silicofluoride: 2～4, sodium stearate: 1～3, calcium chloride: 2～5,
Sodium carbonate: 1～3, Tai-Ace S 150: 3～5, citric acid: 1～3, water: 60～80.
2. a kind of novel concrete stiffening agent according to claim 1, is characterized in that, in weight part, composed of the following components:
Calcium aluminate: 10, gypsum: 3, benzyl naphthalene sodium sulfonate: 4,
Sodium Silicofluoride: 2, sodium stearate: 1, calcium chloride: 2,
Sodium carbonate: 1, Tai-Ace S 150: 3, citric acid: 1, water: 60.
3. a kind of novel concrete stiffening agent according to claim 1, is characterized in that, in weight part, composed of the following components:
Calcium aluminate: 20, gypsum: 8, benzyl naphthalene sodium sulfonate: 8,
Sodium Silicofluoride: 4, sodium stearate: 3, calcium chloride: 5,
Sodium carbonate: 3, Tai-Ace S 150: 5, citric acid: 3, water: 80.
4. a kind of novel concrete stiffening agent according to claim 1, is characterized in that, in weight part, composed of the following components:
Calcium aluminate: 16, gypsum: 6, benzyl naphthalene sodium sulfonate: 6,
Sodium Silicofluoride: 3, sodium stearate: 2, calcium chloride: 3,
Sodium carbonate: 2, Tai-Ace S 150: 4, citric acid: 2, water: 70.