CN103962286A - Automatic powder injection line production process - Google Patents
Automatic powder injection line production process Download PDFInfo
- Publication number
- CN103962286A CN103962286A CN201410188722.4A CN201410188722A CN103962286A CN 103962286 A CN103962286 A CN 103962286A CN 201410188722 A CN201410188722 A CN 201410188722A CN 103962286 A CN103962286 A CN 103962286A
- Authority
- CN
- China
- Prior art keywords
- workpiece
- baking
- powder injection
- hardness
- automatic powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an automatic powder injection line production process. Workpieces after electrophoresis and cleaning are hung for water blowing and baking, and then the cleaned workpieces are placed in an automatic powder injection line for powder coating, wherein the chain speed of the automatic powder injection line is 24 revolutions per minute, the power injection quantity is 0.2 MPa, powder injection weighing ranges from 1.2kg to 1.6 kg, baking time is 30-40 minutes, and the baking temperature is between 215 DEG C and 225 DEG C; finished product inspection, hardness testing and smog testing are sequentially carried out on the workpieces to obtain products which meet production requirements. According to the automatic powder injection line production process, drying and baking for the workpieces can be automatically completed before powder injection processing, powder injection is automatically conducted on the workpieces during powder injection coating, quality of products is improved, and the production effectiveness of the products is improved.
Description
Technical field
The present invention relates to the one production technology of dusting, relate in particular to a kind of self-action spraying line production technology.
Background technology
Dusting is the electrostatic spraying treatment process for surface of workpiece, general production line is to be provided with workpiece to import and export in body both sides, chamber, and workpiece is fixed on a fixed mount, more manual shifting onto in powder spraying chamber, manually arrest spray gun, the application of dusting of certain position of alignment pieces or overall position.Before dusting, also need to carry out pre-process, need to carry out cleaning to the surface of workpiece, place greasy dirt or dust be attached on workpiece, dust with impact after the quality of production of workpiece, some factories adopt different operations to produce, clear up, need a dead lift, such mode of operation is to comparatively clumsy, and wasted a large amount of manpowers, affects operating efficiency.
Summary of the invention
For addressing the above problem, the invention provides a kind of self-action spraying line production technology.
The present invention solves the technical scheme that its technical problem takes: a kind of self-action spraying line production technology, comprises the following steps:
1) charging, will hang on the workpiece through electrophoresis, cleaning;
2) blow water, use air cannon to blow water to workpiece, blowing the water time is 30-40 minute, and blowing water pressure is 1-2kg/cm
2;
3) baking, is transported to workpiece in box baking oven and toasts via streamline stroke, and baking time is 45-50 minute, and baking temperature is 215 DEG C-225 DEG C, and chain speed is 12 rotating speeds, and electrophoresis is weighed as 6.5kg-7.0kg;
4) powder body coating, puts into automatic powder spraying line by workpiece and carries out powder body coating, and wherein the chain speed of automatic powder spraying line is 24 rotating speeds, and the amount of dusting is 0.2MPa, dusts and is weighed as 1.2kg-1.6kg, and baking time is 30-40 minute, and baking temperature is 215 DEG C-225 DEG C;
5) product inspection, whether visualize has defective products, and workpiece is placed on finished product district by bad not detecting, and what visualize was defective products is placed on defective products district;
6) lower satchel dress, according to requiring to use standard pack material to pack;
7) hardness test, is used hardness-testing device and 5B pencil to carry out hardness test to workpiece, and hardness-testing device is tested workpiece with the angle of 45° angle
8) salt spray test, uses salt spray test machine to carry out salt spray test to workpiece, and wherein brine strength is 50g/l, it is 33 DEG C-37 DEG C that laboratory temperature requires, and it is 45 DEG C-47 DEG C that saturated barrel temperature requires, and spray amount is 1.5 ± 0.5ml/80cm2/hr, atomisation pressure is 0.098MPa, and pH value is 6.5-7.2;
9) finished product shipment, estimates totally and packing slip carries out warehouse-in or the shipment of product.
Preferably, in the hardness test in described step 7, requiring hardness is 2H.
Beneficial effect of the present invention: the present invention can complete the pre-treatment of dusting automatically to the drying up and toasting of workpiece, and in the time dusting application, workpiece is carried out to automatic powder spraying, has improved the quality of product, has improved the productivity effect of product.
Detailed description of the invention
A kind of self-action spraying line production technology, comprises the following steps:
1) charging, will hang on the workpiece through electrophoresis, cleaning;
2) blow water, use air cannon to blow water to workpiece, blowing the water time is 30-40 minute, and blowing water pressure is 1-2kg/cm
2;
3) baking, is transported to workpiece in box baking oven and toasts via streamline stroke, and baking time is 45-50 minute, and baking temperature is 215 DEG C-225 DEG C, and chain speed is 12 rotating speeds, and electrophoresis is weighed as 6.5kg-7.0kg;
4) powder body coating, puts into automatic powder spraying line by workpiece and carries out powder body coating, and wherein the chain speed of automatic powder spraying line is 24 rotating speeds, and the amount of dusting is 0.2MPa, dusts and is weighed as 1.2kg-1.6kg, and baking time is 30-40 minute, and baking temperature is 215 DEG C-225 DEG C;
5) product inspection, whether visualize has defective products, and workpiece is placed on finished product district by bad not detecting, and what visualize was defective products is placed on defective products district;
6) lower satchel dress, according to requiring to use standard pack material to pack;
7) hardness test, is used hardness-testing device and 5B pencil to carry out hardness test to workpiece, and hardness-testing device is tested workpiece with the angle of 45° angle
8) salt spray test, uses salt spray test machine to carry out salt spray test to workpiece, and wherein brine strength is 50g/l, it is 33 DEG C-37 DEG C that laboratory temperature requires, and it is 45 DEG C-47 DEG C that saturated barrel temperature requires, and spray amount is 1.5 ± 0.5ml/80cm2/hr, atomisation pressure is 0.098MPa, and pH value is 6.5-7.2;
9) finished product shipment, estimates totally and packing slip carries out warehouse-in or the shipment of product.
Preferably, in the hardness test in described step 7, requiring hardness is 2H.
It is emphasized that, it is more than preferred embodiment of the present invention, not the present invention is done to any type of restriction in appearance, any simple modification, equivalent variations and modification that every foundation technical spirit of the present invention is done above embodiment, all still belong to the scope of technical solution of the present invention.
Claims (2)
1. a self-action spraying line production technology, is characterized in that: comprise the following steps:
1) charging, will hang on the workpiece through electrophoresis, cleaning;
2) blow water, use air cannon to blow water to workpiece, blowing the water time is 30-40 minute, and blowing water pressure is 1-2kg/cm
2;
3) baking, is transported to workpiece in box baking oven and toasts via streamline stroke, and baking time is 45-50 minute, and baking temperature is 215 DEG C-225 DEG C, and chain speed is 12 rotating speeds, and electrophoresis is weighed as 6.5kg-7.0kg;
4) powder body coating, puts into automatic powder spraying line by workpiece and carries out powder body coating, and wherein the chain speed of automatic powder spraying line is 24 rotating speeds, and the amount of dusting is 0.2MPa, dusts and is weighed as 1.2kg-1.6kg, and baking time is 30-40 minute, and baking temperature is 215 DEG C-225 DEG C;
5) product inspection, whether visualize has defective products, and workpiece is placed on finished product district by bad not detecting, and what visualize was defective products is placed on defective products district;
6) lower satchel dress, according to requiring to use standard pack material to pack;
7) hardness test, is used hardness-testing device and 5B pencil to carry out hardness test to workpiece, and hardness-testing device is tested workpiece with the angle of 45° angle
8) salt spray test, uses salt spray test machine to carry out salt spray test to workpiece, and wherein brine strength is 50g/l, it is 33 DEG C-37 DEG C that laboratory temperature requires, and it is 45 DEG C-47 DEG C that saturated barrel temperature requires, and spray amount is 1.5 ± 0.5ml/80cm2/hr, atomisation pressure is 0.098MPa, and pH value is 6.5-7.2;
9) finished product shipment, estimates totally and packing slip carries out warehouse-in or the shipment of product.
2. a kind of self-action spraying line production technology according to claim 1, is characterized in that: in the hardness test in described step 7, requiring hardness is 2H.