CN103961744A - Method for making simvastatin drug-containing hydroxyapatite coating on surface of pure titanium - Google Patents
Method for making simvastatin drug-containing hydroxyapatite coating on surface of pure titanium Download PDFInfo
- Publication number
- CN103961744A CN103961744A CN201310043285.2A CN201310043285A CN103961744A CN 103961744 A CN103961744 A CN 103961744A CN 201310043285 A CN201310043285 A CN 201310043285A CN 103961744 A CN103961744 A CN 103961744A
- Authority
- CN
- China
- Prior art keywords
- pure titanium
- simvastatin
- preparation
- hydroxyapatite coating
- electrochemical deposition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for depositing a simvastatin drug-containing hydroxyapatite coating on the surface of pure titanium by utilizing an electrochemical deposition process. The method comprises the following steps: polishing the surface of a pure titanium implant, sand-blasting, acid-etching, and depositing by utilizing an electrochemical deposition station, a simple apparatus and cheap materials to make the simvastatin drug-containing hydroxyapatite coating on the surface of the implant. The method has the advantages of simple preparation process, simple apparatus, low making cost, high making efficiency and the like, and the obtained coating has good biocompatibility and osteogenic cell proliferation differentiation promotion ability. A platform for making the drug-containing coating on the surface of pure titanium is established.
Description
Technical field
The present invention relates to a kind of method of preparing pastille hydroxyapatite coating layer on pure titanium surface.Especially, relate to a kind of electrochemical deposition method, method of the hydroxyapatite coating layer that contains simvastatin medicine at pure titanium surface deposition used.
Background technology
Constantly perfect along with planting technology, increasing agomphosis patient selects to plant repairing and treating.But because agomphosis overlong time or some systemic diseases as osteoporosis etc. may cause bone quantity not sufficient or the sclerotin change of planting area, thereby affect plantation success rate and long-time stability.Existing many studies confirm that, the surface topography of implantation body and chemical composition are integrated important role for the bone of implantation body.Simvastatin is a kind of fat-soluble statins, can induce expression and the stimulation bone formation of the mRNA of BMP-2.And hydroxyapatite is a kind of widely used coating material, because itself and bone have similar chemical composition, there is good biological activity simultaneously, therefore there is energy directly and the potentiality of bone surface combination.Widely used implantation body clinically at present, the general SLA technology that adopts in surface, i.e. sandblast acid etching coarse surface, its clinical application effect is better, but for the poor patient of local bone situation, still has the situation that plantation is failed.Therefore how can pass through to change implant surface pattern or composition, thereby effectively improve the poor patient's of bone condition plantation success rate, become the important research direction of global implantology.
Summary of the invention
What the object of the present invention is to provide a kind of high-biocompatibility and bone active forms the method containing the hydroxyapatite coating layer of simvastatin medicine on pure titanium surface.
The object of the invention is to be achieved through the following technical solutions: a kind of method that contains the hydroxyapatite coating layer of simvastatin medicine in the surface preparation of pure titanium, it is characterized in that, comprise the following steps:
(1) by pure titanium implant roughness be the polishing respectively of 320 orders, 500 orders and 800 object sand paper; With green silicon carbide sand grains under 4MPa pressure to the titanium surface sand-blasting after polishing; Use respectively acetone, 75% ethanol and distilled water, ultrasonic cleaning 15 minutes, and 50 DEG C of oven dry in baking oven;
(2) sample after cleaning is put into containing the Fluohydric acid. of 0.11mol/L and the salpeter solution of 0.09mol/L, and soaking at room temperature 10 minutes is rear with distilled water supersonic vibration cleaning 15 minutes twice, and 50 DEG C of oven dry in baking oven; Put into containing the hydrochloric acid of 5.8mol/L and the sulfuric acid solution of 8.96mol/L, 80 DEG C are soaked 30 minutes again, and rear taking-up is cleaned 15 minutes twice with distilled water sonic oscillation, and in baking oven 50 DEG C dry 24 hours;
(3) configuration simvastatin solution: 42 milligrams of simvastatins are dissolved in 1 milliliter of 95% alcoholic solution, add 0.1mol/L sodium hydroxide, with 0.1mol/L hydrochloric acid solution adjusting pH value to 7.2, deionized water is settled to 10 milliliters.
(4) electrochemical deposition: using pure titanium implant after treatment as the work utmost point (negative electrode), get one section of platinum filament as anode.Electrolyte is the lime nitrate 0.6mmol/L that contains AG, the deionized water solution of Ammonium biphosphate 0.36mmol/L, thus ensure that calcium-phosphorus ratio is 1.67, then add the Chile saltpeter of 0.1mol/L to increase electrolytical electric conductivity, add simvastatin solution, making its final concentration is 10 again
-6mol/L.Deposition process built in 3.0 volts, 85 DEG C, deposits 30 minutes by computer controlled.
The present invention has following technique effect, instrumental characterizing demonstration, and pure titanium implant surface forms column crystal, contains simvastatin medicine in crystal.In vitro cell experiment confirmation, there is not toxic action to cell in the standby coating of this legal system, preosteoblast is had to the effect that promotes proliferation and differentiation simultaneously.The present invention is by the electrochemical deposition of single, in the short period of time, prepared the hydroxyapatite coating layer containing simvastatin, preparation process material requested apparatus is comparatively simple, cost is lower, has realized the requirement of the artificial material of the short osteogenesis of low cost, high efficiency, high-biocompatibility.
Detailed description of the invention
By to after pure titanium implant surface finish, sandblast acid etching, utilize electrochemical deposition station, with comparatively simple apparatus and comparatively cheap material, the hydroxyapatite coating layer that contains simvastatin medicine in the preparation of implant surface deposition.In view of other surface treatment modes are for adding medicine to have some limitations, therefore the present invention selects electrochemical deposition method, thereby sets up comparatively easy drug deposition platform.
Feature of the present invention is to process pure titanium implant with sandblast aciding, the hydroxyapatite coating layer that contains simvastatin medicine is prepared in implant surface by electrochemical process, thus the pastille coating production that finds a kind of easy operating of low-cost high-efficiency to complete.
Claims (3)
1. the method containing the hydroxyapatite coating layer of simvastatin medicine in the surface preparation of pure titanium, is characterized in that, comprises the following steps: (1) is to the sand paper polishing of pure titanium implant surface, the sandblast of carborundum sand grains, cleaning, drying.(2) carry out secondary acid etching, cleaning, drying with different acid.(3) by ethanol, sodium hydroxide and hydrochloric acid preparation simvastatin solution for standby.(4) use electrochemical deposition station, by the electrolyte with simvastatin, the hydroxyapatite coating layer that preparation contains simvastatin medicine.
2. preparation method according to claim 1, is characterized in that: pure titanium surface is used to sand paper polishing, use the sandblast of green silicon carbide sand grains, use the mixed acid of special proportioning to carry out the pure titanium of secondary acid etching surface.
3. preparation method according to claim 1, is characterized in that: use electrochemical deposition station, simvastatin solution is added in electrolyte, thereby preparation is containing medicine coating.