CN103952110B - 一种环氧树脂双喷的方法 - Google Patents

一种环氧树脂双喷的方法 Download PDF

Info

Publication number
CN103952110B
CN103952110B CN201410131090.8A CN201410131090A CN103952110B CN 103952110 B CN103952110 B CN 103952110B CN 201410131090 A CN201410131090 A CN 201410131090A CN 103952110 B CN103952110 B CN 103952110B
Authority
CN
China
Prior art keywords
epoxy resin
solution
binder solution
curing agent
sprayed onto
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410131090.8A
Other languages
English (en)
Other versions
CN103952110A (zh
Inventor
张小立
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Boyi Intellectual Property Operation Co ltd
Quzhou Huanya New Material Technology Co ltd
Original Assignee
Zhongyuan University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhongyuan University of Technology filed Critical Zhongyuan University of Technology
Priority to CN201410131090.8A priority Critical patent/CN103952110B/zh
Publication of CN103952110A publication Critical patent/CN103952110A/zh
Application granted granted Critical
Publication of CN103952110B publication Critical patent/CN103952110B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种环氧树脂双喷的方法，它的步骤如下：（1）将环氧树脂和乙醇按质量比为1：2-5：1均匀混合，形成粘结剂溶液，然后将粘结剂溶液喷到需要粘结的物体表面，使粘结剂溶液与被粘结物粘附，形成粘附物；（2）将改性异佛尔酮二胺固化剂与聚氨酯或有机硅按任意比例均匀混合，形成固化剂溶液，然后将固化剂溶液喷到步骤（1）中的粘附物表面，发生固化。本发明通过在环氧树脂粘结剂中添加乙醇、丙酮等有机溶剂，形成粘结剂溶液；在固化剂中添加有机硅溶剂等形成固化剂溶液；粘结剂溶液和固化剂溶液可以分开并实现喷涂使用。尤其可实现大量小尺寸物体和复杂异形物体的粘结。

Description

一种环氧树脂双喷的方法
技术领域
本发明涉及环氧树脂的改性利用，提高其适用范围和作业方法的技术领域。
背景技术
环氧树脂是常用的粘结剂，广泛用于玻璃、陶瓷、电子等领域，对金属及非金属材料都有很强的粘结能力。
现有的环氧树脂操作粘度大，这在施工方面显的有些不方便。而且使用时粘结剂和固化剂首先要按比例调配，然后只能采用在粘结界面涂刷，再胶粘的办法才能使用。对于一些复杂界面的胶粘，特殊形状物体的胶粘，尺寸很小的物体的胶粘，大量的小尺寸物体和其他材质的胶粘都很难操作，很不方便。
发明内容
本发明的目的在于改变现有环氧树脂的使用方法，更简单，粘附性能更强，适用于各种使用条件，方便，有效。
本发明的技术方案是：一种环氧树脂双喷的方法，它的步骤如下：
（1）将环氧树脂和乙醇按质量比为1：2-5：1均匀混合，形成粘结剂溶液，然后将粘结剂溶液喷到需要粘结的物体表面，使粘结剂溶液与被粘结物粘附，形成粘附物；
（2）将改性异佛尔酮二胺固化剂与聚氨酯或有机硅按任意比例均匀混合，形成固化剂溶液，然后将固化剂溶液喷到步骤（1）中的粘附物表面，发生固化。
所述步骤（1）中的环氧树脂为双酚A型环氧树脂或酚醛多环氧树脂。
所述步骤（1）中的乙醇的质量分数浓度为75-100%。
本发明的有益效果是：该方法通过在环氧树脂粘结剂中添加乙醇、丙酮等有机溶剂，形成粘结剂溶液；在固化剂中添加有机硅溶剂等形成固化剂溶液；粘结剂溶液和固化剂溶液可以分开并实现喷涂使用。尤其可实现大量小尺寸物体和复杂异形物体的粘结。并且粘结剂溶液和固化剂溶液都可以通过喷涂的办法实现常规涂胶的过程，可分开使用，粘附能力更强，固化后效果不降低。该方法适用于任意形状、尺寸的粘结对象，以及大量复杂及细小物体表面的粘结。
具体实施方式
实施例1
直径为0.5-3mm的安徽无为县花卉肥料厂生产的HF18速效粒状氮肥10g，将双酚A型环氧树脂和乙醇（浓度75%）按1：1混合均匀，并喷到均匀滚动的化肥表面；将上述喷有粘结剂溶液的化肥在煤矸石粉末上面均匀滚动，从而在化肥表面均匀粘附一层煤矸石粉末，将改性异佛尔酮二胺固化剂和邦乐澳BLA101有机硅溶液按质量比为1：1均匀混合，最后将上述固化剂溶液喷到粘附煤矸石粉末的化肥表面，3小时后发生固化，形成煤矸石包覆化肥。
实施例2
碰掉瓷的工艺瓷碗，表面呈现2-5mm尺寸凹凸不平的坑，将双酚A型环氧树脂和乙醇（浓度100%）按2：1混合均匀，并喷到瓷碗凹坑处；将掉瓷的碎片粘附到瓷碗表面，将改性异佛尔酮二胺固化剂和邦乐澳BLA101有机硅溶液按质量比为2：1均匀混合，最后将上述固化剂溶液喷到粘附有碎瓷片的瓷碗表面，3小时后发生固化，完成瓷碗的修补。
实施例3
直径为0.5-3mm的安徽无为县花卉肥料厂生产的HF18速效粒状氮肥10g，将酚醛多环氧树脂和乙醇（浓度100%）按1：1混合均匀，并喷到均匀滚动的化肥表面；将上述喷有粘结剂溶液的化肥在煤矸石粉末上面均匀滚动，从而在化肥表面均匀粘附一层煤矸石粉末，将改性异佛尔酮二胺固化剂和邦乐澳BLA101有机硅溶液按质量比为1：1均匀混合，最后将上述固化剂溶液喷到粘附煤矸石粉末的化肥表面，3小时后发生固化，形成煤矸石包覆化肥。
实施例4
直径为0.5-3mm的安徽无为县花卉肥料厂生产的HF18速效粒状氮肥10g，将酚醛多环氧树脂和乙醇（浓度100%）按1：1混合均匀，并喷到均匀滚动的化肥表面；将上述喷有粘结剂溶液的化肥在粉煤灰粉末上面均匀滚动，从而在化肥表面均匀粘附一层粉煤灰粉末，将改性异佛尔酮二胺固化剂和邦乐澳BLA101有机硅溶液按质量比为3：1均匀混合，最后将上述固化剂溶液喷到粘附粉煤灰粉末的化肥表面，3小时后发生固化，形成粉煤灰包覆化肥。
实施例5
直径为1-3mm的挪威进口复合肥10g，将酚醛多环氧树脂和乙醇（浓度100%）按2：1混合均匀，并喷到均匀滚动的化肥表面；将上述喷有粘结剂溶液的化肥在煤矸石粉末上面均匀滚动，从而在化肥表面均匀粘附一层煤矸石粉末，将改性异佛尔酮二胺固化剂和邦乐澳BLA101有机硅溶液按质量比为2：1均匀混合，最后将上述固化剂溶液喷到粘附煤矸石粉末的化肥表面，3小时后发生固化，形成煤矸石包覆化肥。
实施例6
一种环氧树脂双喷的方法，它的步骤如下：
（1）将双酚A型环氧树脂和质量分数浓度为75%的乙醇按质量比为1：2均匀混合，形成粘结剂溶液，然后将粘结剂溶液喷到需要粘结的物体表面，使粘结剂溶液与被粘结物粘附，形成粘附物；
（2）将改性异佛尔酮二胺固化剂与防水有机硅溶剂按质量比为1:1均匀混合，形成固化剂溶液，然后将固化剂溶液喷到步骤（1）中的粘附物表面，发生固化。
实施例7
一种环氧树脂双喷的方法，它的步骤如下：
（1）将酚醛多环氧树脂和质量分数浓度为100%的乙醇按质量比为5：1均匀混合，形成粘结剂溶液，然后将粘结剂溶液喷到需要粘结的物体表面，使粘结剂溶液与被粘结物粘附，形成粘附物；
（2）将改性异佛尔酮二胺固化剂与聚氨酯防水涂料按质量比为10:1混合，形成固化剂溶液，然后将固化剂溶液喷到步骤（1）中的粘附物表面，发生固化。
实施例8
一种环氧树脂双喷的方法，它的步骤如下：
（1）将双酚A型环氧树脂和质量分数浓度为95%的乙醇按质量比为1：1均匀混合，形成粘结剂溶液，然后将粘结剂溶液喷到需要粘结的物体表面，使粘结剂溶液与被粘结物粘附，形成粘附物；
（2）将改性异佛尔酮二胺固化剂与防水有机硅溶剂按任意比例均匀混合，形成固化剂溶液，然后将固化剂溶液喷到步骤（1）中的粘附物表面，发生固化。

Claims (4)

1.一种环氧树脂双喷的方法，其特征在于，它的步骤如下：
（1）将环氧树脂和乙醇按质量比为1：2-5：1均匀混合，形成粘结剂溶液，然后将粘结剂溶液喷到需要粘结的物体表面，使粘结剂溶液与被粘结物粘附，形成粘附物；
（2）将改性异佛尔酮二胺固化剂与聚氨酯或有机硅按任意比例均匀混合，形成固化剂溶液，然后将固化剂溶液喷到步骤（1）中的粘附物表面，发生固化。
2.根据权利要求1所述的环氧树脂双喷的方法，其特征在于：所述步骤（1）中的环氧树脂为双酚A型环氧树脂或酚醛多环氧树脂。
3.根据权利要求1所述的环氧树脂双喷的方法，其特征在于：所述步骤（1）中的乙醇的质量分数浓度为75-100%。
4.根据权利要求1所述的环氧树脂双喷的方法，其特征在于：所述步骤（2）中改性异佛尔酮二胺固化剂与聚氨酯或有机硅的质量比为10:1-1:1。
CN201410131090.8A 2014-04-03 2014-04-03 一种环氧树脂双喷的方法 Active CN103952110B (zh)