CN103937338A - Aging-resistance paint - Google Patents
Aging-resistance paint Download PDFInfo
- Publication number
- CN103937338A CN103937338A CN201410113601.3A CN201410113601A CN103937338A CN 103937338 A CN103937338 A CN 103937338A CN 201410113601 A CN201410113601 A CN 201410113601A CN 103937338 A CN103937338 A CN 103937338A
- Authority
- CN
- China
- Prior art keywords
- parts
- add
- paint
- raw material
- mix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses aging-resistance paint. The paint is composed of following raw materials which comprise, by weight, 73-83 parts of chlorinated polypropylene, 2-4 parts of polysiloxanes, 1-2 parts of 6-di-tert-butyl-4-methylphenol, 2-3 parts of ribbed smoked sheet, 1-2 parts of hexabromocyclododecane, 10-15 parts of nano calcium carbonate, 2-3 parts of ammonium biphosphate, 0.6-1 part of sulfonated lignin, 2-4 parts of polyvinyl butyral ester, 0.6-1 part of antioxidant SP, 3-5 parts of tailings, 1-2 parts of tetrabutylammonium bromide, 0.7-1 part of potassium dihydrogen phosphate and 12-20 parts of composite filling material. The paint is great in levelling property, strong in covering property and caking property, good in construction property and is environment friendly without pollution. The coating of the paint is free of cracking and being damaged after a manual aging process lasting for 8000 hours and the paint is long in service life.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of aging resistant coating.
Background technology
Object is exposed among atmosphere, is subject to the erosion of oxygen, moisture etc., causes the breakoff phenomenons such as corrosion of metal, foxy, cement weathering.Be coated with coating at article surface, form layer protecting film, can stop or postpone generation and the development of these breakoff phenomenons; extended the work-ing life of various materials; therefore a kind of coating efficiently can play good protection effect, reduces the wastage rate of object, economizes on resources.
Along with the development of coating industry; taking acrylate, PVC polymkeric substance etc. as the product of coating also a lot; but some coatings have slight corrodibility, dust suction, thermotolerance, weathering resistance poor; and the stable chemical performance of PE, good weatherability; nontoxic, pollution-free, density is low; the application of various materials can be widely used in, good protection effect can be played.
Summary of the invention
The object of the invention is just to provide a kind of aging resistant coating.
The present invention is achieved by the following technical solutions:
A kind of aging resistant coating, it is made up of the raw material of following weight parts:
Chlorinated Polypropylene III 73-83, polysiloxane 2-4,6-ditertbutylparacresol 1-2, smoke sheet rubber 2-3, hexabromocyclododecane 1-2, nano-calcium carbonate 10-15, primary ammonium phosphate 2-3, sulfonated lignin 0.6-1, polyvinyl butyral acetal ester 2-4, antioxidant SP 0.6-1, tailings 3-5, Tetrabutyl amonium bromide 1-2, potassium primary phosphate 0.7-1, compounded mix 12-20;
Described compounded mix is made up of the raw material of following weight parts:
Agalmatolite 25-30, fine hair powder 10-13, methylisothiazolinone 2-3, linear low density polyethylene 15-25, Xylo-Mucine 1-2, tricresyl phosphate (butoxyethyl group) ester 1-2, Terpineol 350 1-2;
Above-mentioned agalmatolite is calcined to 1-2 hour at 600-700 DEG C, after discharging is cooling, add methylisothiazolinone, linear low density polyethylene, pulverize, Xylo-Mucine is joined in 6-10 times of water, after stirring, add fine hair powder, at 60-70 DEG C, be uniformly mixed 4-6 minute, mix with powder obtained above, add the each raw material of residue, fully grind, dry, cross 60-80 mesh sieve, obtain described compounded mix.
A preparation method for aging resistant coating, comprises the following steps:
Above-mentioned ceramics powder, zinc borate, 16 Biphenyl Ethers are mixed, at 50-60 DEG C, be uniformly mixed 4-6 minute, add bone black, continue to be uniformly mixed 3-5 minute, add the each raw material of residue, mix, send into twin screw extruder, carry out melting, extrude, cross 60-100 mesh sieve, obtain described aging resistant coating.
Using method:
If be sprayed on the high temperature materials such as steel pipe, coating piece can be heated to suitable temperature, generally, between 200-350 DEG C, then coating of the present invention is dispersed on coating piece uniformly by electrostatic spraying, after coating melting, can be bonded in and on coating piece, forms plastic film;
If be sprayed on the material of the non-refractory such as cloth, fiberboard, can, by paint heating melting, then coating piece be infiltrated, can exert pressure to control by rubber rollers the thickness of glue-line to coating, then through plasticizing, cooling.
Advantage of the present invention is:
Coating good leveling property of the present invention, strong covering power, cohesiveness is strong, and application property is good, environment friendly and pollution-free, and resistance to artificial after old 8000 hours, coating is without cracking, without breakage, long service life.
Embodiment
Embodiment 1
A kind of aging resistant coating, it by following weight parts (kilogram) raw material form:
Chlorinated Polypropylene III 83, polysiloxane 2,6-ditertbutylparacresol 2, smoke sheet rubber 3, hexabromocyclododecane 2, nano-calcium carbonate 15, primary ammonium phosphate 3, sulfonated lignin 0.6, polyvinyl butyral acetal ester 4, antioxidant SP 0.6, tailings 5, Tetrabutyl amonium bromide 1, potassium primary phosphate 0.7, compounded mix 12;
Described compounded mix is made up of the raw material of following weight parts:
Agalmatolite 30, fine hair powder 13, methylisothiazolinone 3, linear low density polyethylene 25, Xylo-Mucine 2, tricresyl phosphate (butoxyethyl group) ester 2, Terpineol 350 2;
Above-mentioned agalmatolite is calcined 2 hours at 700 DEG C, after discharging is cooling, add methylisothiazolinone, linear low density polyethylene, pulverize, Xylo-Mucine is joined in 10 times of water, after stirring, add fine hair powder, at 70 DEG C, be uniformly mixed 4 minutes, mix with powder obtained above, add the each raw material of residue, fully grind, dry, cross 80 mesh sieves, obtain described compounded mix.
A preparation method for aging resistant coating, comprises the following steps:
Above-mentioned ceramics powder, zinc borate, 16 Biphenyl Ethers are mixed, at 60 DEG C, be uniformly mixed 6 minutes, add bone black, continue to be uniformly mixed 3 minutes, add the each raw material of residue, mix, send into twin screw extruder, carry out melting, extrude, cross 100 mesh sieves, obtain described aging resistant coating.
Performance test:
Shock resistance: >=50kg/cm;
Pencil hardness test: 2H is without scuffing.
Claims (2)
1. an aging resistant coating, is characterized in that what it was made up of the raw material of following weight parts:
Chlorinated Polypropylene III 73-83, polysiloxane 2-4,6-ditertbutylparacresol 1-2, smoke sheet rubber 2-3, hexabromocyclododecane 1-2, nano-calcium carbonate 10-15, primary ammonium phosphate 2-3, sulfonated lignin 0.6-1, polyvinyl butyral acetal ester 2-4, antioxidant SP 0.6-1, tailings 3-5, Tetrabutyl amonium bromide 1-2, potassium primary phosphate 0.7-1, compounded mix 12-20;
Described compounded mix is made up of the raw material of following weight parts:
Agalmatolite 25-30, fine hair powder 10-13, methylisothiazolinone 2-3, linear low density polyethylene 15-25, Xylo-Mucine 1-2, tricresyl phosphate (butoxyethyl group) ester 1-2, Terpineol 350 1-2;
Above-mentioned agalmatolite is calcined to 1-2 hour at 600-700 DEG C, after discharging is cooling, add methylisothiazolinone, linear low density polyethylene, pulverize, Xylo-Mucine is joined in 6-10 times of water, after stirring, add fine hair powder, at 60-70 DEG C, be uniformly mixed 4-6 minute, mix with powder obtained above, add the each raw material of residue, fully grind, dry, cross 60-80 mesh sieve, obtain described compounded mix.
2. a preparation method for aging resistant coating as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned tailings is mixed with ceramics powder, zinc borate, 16 Biphenyl Ethers, at 50-60 DEG C, be uniformly mixed 4-6 minute, add bone black, continue to be uniformly mixed 3-5 minute, add the each raw material of residue, mix, send into twin screw extruder, carry out melting, extrude, cross 60-100 mesh sieve, obtain described aging resistant coating.