CN103923564B - Class coating material of the anti-finger prints processing in a kind of stainless steel plate surface and preparation method thereof - Google Patents
Class coating material of the anti-finger prints processing in a kind of stainless steel plate surface and preparation method thereof Download PDFInfo
- Publication number
- CN103923564B CN103923564B CN201410062669.3A CN201410062669A CN103923564B CN 103923564 B CN103923564 B CN 103923564B CN 201410062669 A CN201410062669 A CN 201410062669A CN 103923564 B CN103923564 B CN 103923564B
- Authority
- CN
- China
- Prior art keywords
- oil
- minutes
- additive
- stainless steel
- coating material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Class coating material of the anti-finger prints processing in a kind of stainless steel plate surface and preparation method thereof, mixes by following weight part, additive 10-20, oxidation inhibitor 1-3, oil-soluble resin 5-8, water-holding agent 0.5-1, machinery oil 50-70.The preparation method of this class coating material, comprises the steps: 1) in stirrer, first add machinery oil, additive, oil-soluble resin and oxidation inhibitor, stirrer stirs 30 ~ 40 minutes with the speed of 1000 ~ 2000 revs/min; 2) add water-holding agent again, stirrer stirs 5 ~ 10 minutes with the speed of 500 ~ 700 revs/min; 3) 10 ~ 20 minutes are incubated under last normal temperature.This coated material increases the snappiness of coating by adding the good oil-soluble resin of amalgamation in machinery oil; change the coated material of original metal decking; propose a resin and the oily new ideas being mixed into coating protection layer; making metal decking touch is no longer completely hard sensation; and add antirust function, the effect of original anti-fingerprint is also strengthened greatly.
Description
Technical field
The present invention relates to the material of metal material surface process, especially for the class coating material of the anti-finger prints processing on stainless steel plate surface.
Background technology
Now commercially the use range of stainless steel plate is more and more wider, more and more press close to usual life, and people it is also proposed higher requirement to its aesthetic property.The surface of stainless steel plate, easily by fingerprint pollution, makes stainless steel plate surface tarnish gradually.
As anti-fingerprint stainless steel decorated sheet and the production technique thereof of application publication number CN101386006, be made up of stainless steel decorated sheet surface-coated film layer, comprise and selecting materials, pre-treatment, the production stages such as configuration mixed solution.Film layer is hard firmly smooth, and anti-fingerprint is effective.But this technique is very simple, and form the hard protective film of one deck dense uniform after drying, be not the outside surface being suitable as life household goods, protective film should be tried one's best softer, preferably also has etch-proof function.
Summary of the invention
Object of the present invention solves the problems of the technologies described above, the protective layer providing a kind of resin to mix with oil, and make the elasticity of the existing resin of coated material have again the oilness of oil, and preparation method is simple, cost is low.
Technical solution of the present invention is: the class coating material of the anti-finger prints processing in a kind of stainless steel plate surface, mixes by following weight part,
Additive 10-20,
Oxidation inhibitor 1-3,
Oil-soluble resin 5-8,
Water-holding agent 0.5-1
Machinery oil 50-70.
As preferably, described additive is one or more of silicon, aluminium, carbon and oxide compound thereof, and their mean particle size is less than 100 nanometers.These materials of silicon, aluminium, carbon are conducive to the intensity improving coating, improve wear resistance.
As preferably, described oxidation inhibitor is antioxidant BHT.Antioxidant BHT can suppress or delays the oxidative degradation of plastics or rubber and increase the service life, and can also prevent the acid number of oil or the rising of viscosity.
As preferably, described oil-soluble resin be Gum Rosin, dammar gum, soluble phenolic resin, petroleum resin one or more.
As preferably, described oil-soluble resin is Gum Rosin and soluble phenolic resin mass ratio is the mixture of 1:1.
As preferably, described water-holding agent is polyacrylic acid potassium or ammonium polyacrylate.Water-holding agent is the functional high molecule material that a kind of water-retaining capacity is strong especially, nontoxic, repeatedly releases water, water suction.He can keep the good absorption of moisture in machinery oil, if when other additives need moisture content, can well release water again.And when some bad weather, also good regulating effect can be played.
As preferably, described machinery oil is 7# or 10# or 100# machinery oil.
The preparation method of above-mentioned class coating material, comprises the steps:
1) in stirrer, first add machinery oil, additive, oil-soluble resin and oxidation inhibitor, stirrer stirs 30 minutes with the speed of 1000 revs/min;
2) add water-holding agent again, stirrer stirs 5 minutes with the speed of 500 revs/min;
3) 20 minutes are incubated under last normal temperature.
Beneficial effect of the present invention is: this coated material increases the snappiness of coating by adding the good oil-soluble resin of amalgamation in machinery oil; change the coated material of original metal decking; propose a resin and the oily new ideas being mixed into coating protection layer; making metal decking touch is no longer completely hard sensation; and add antirust function, the effect of original anti-fingerprint is also strengthened greatly.
Use the surface of the stainless steel plate of this coated material to form one deck and possess elasticity, smooth colloid protective membrane, improve the effect of anti-fingerprint pollution greatly, be beneficial to antirust, easily clean, and do not have bubble in coating.
Embodiment
This specific embodiment is only explanation of the invention; it is not limitation of the present invention; those skilled in the art can make to the present embodiment the amendment not having creative contribution as required after reading this specification sheets, as long as but be all subject to the protection of patent law in right of the present invention.
1, embodiment 1, the class coating material of the anti-finger prints processing in a kind of stainless steel plate surface, the composition comprising following weight part mixes:
Additive 10, oxidation inhibitor 1, oil-soluble resin 5, water-holding agent 0.5,7# machinery oil 50.Described additive-package is containing the silicon below 100 nanometers and oxide compound thereof.Described oxidation inhibitor is antioxidant BHT.Described oil-soluble resin is Gum Rosin.Water-holding agent is polyacrylic acid potassium.
The preparation method of above-mentioned class coating material, comprises the steps:
1) in stirrer, first add the 7# machinery oil of 50 kilograms, 10 kilograms of additives, 5 kg of oil soluble resins and 1 kilogram of oxidation inhibitor, stirrer with 1000 ~ rev/min speed stir 30 minutes;
2) add 0.5 kilogram of water-holding agent again, stirrer stirs 5 minutes with the speed of 500 revs/min;
3) 10 minutes are incubated under last normal temperature.
Through salt-fog test, the stainless steel plate after using this class coating material 20 days, common stainless steel plate 2 days.
Ball impact test, the steel ball of unified mass above test sample two meters of freely falling bodies to the surface three times repeatedly of test sample, sample for reference surface.Stainless steel plate after film has indenture slightly, and common stainless steel plate has obvious indenture phenomenon.
2, embodiment 2, the class coating material of the anti-finger prints processing in a kind of stainless steel plate surface, the composition comprising following weight part mixes:
Additive 15, oxidation inhibitor 2, oil-soluble resin 7, water-holding agent 0.7,10# machinery oil 60.Described additive-package is containing the silicon below 100 nanometers and oxide compound thereof.Described oxidation inhibitor is antioxidant BHT.Described oil-soluble resin is dammar gum.Water-holding agent is polyacrylic acid potassium.
The preparation method of above-mentioned class coating material, comprises the steps:
1) in stirrer, first add the 10# machinery oil of 60 kilograms, 15 kilograms of additives, 7 kg of oil soluble resins and 2 kilograms of oxidation inhibitor, stirrer with 1500 ~ rev/min speed stir 36 minutes;
2) add 0.7 kilogram of water-holding agent again, stirrer stirs 8 minutes with the speed of 600 revs/min;
3) 15 minutes are incubated under last normal temperature.
Through salt-fog test, the stainless steel plate after using this class coating material 25 days, common stainless steel plate 2 days.
Ball impact test, the steel ball of unified mass above test sample two meters of freely falling bodies to the surface three times repeatedly of test sample, sample for reference surface.Stainless steel plate after film is without indenture, and common stainless steel plate has obvious indenture phenomenon.
3, embodiment 3, the class coating material of the anti-finger prints processing in a kind of stainless steel plate surface, the composition comprising following weight part mixes:
Additive 20, oxidation inhibitor 3, oil-soluble resin 8, water-holding agent 1,100# machinery oil 70.Described additive-package is containing the silicon below 100 nanometers and oxide compound thereof.Described oxidation inhibitor is antioxidant BHT.Described oil-soluble resin is Gum Rosin and soluble phenolic resin mass ratio is the mixture of 1:1.Water-holding agent is ammonium polyacrylate.
The preparation method of above-mentioned class coating material, comprises the steps:
1) in stirrer, first add the 100# machinery oil of 70 kilograms, 20 kilograms of additives, 8 kg of oil soluble resins and 3 kilograms of oxidation inhibitor, stirrer with 2000 ~ rev/min speed stir 40 minutes;
2) add 1 kilogram of water-holding agent again, stirrer stirs 10 minutes with the speed of 700 revs/min;
3) 10 minutes are incubated under last normal temperature.
Through salt-fog test, the stainless steel plate after using this class coating material 30 days, common stainless steel plate 2 days.
Ball impact test, the steel ball of unified mass above test sample two meters of freely falling bodies to the surface three times repeatedly of test sample, sample for reference surface.Stainless steel plate after film is without indenture, and common stainless steel plate has obvious indenture phenomenon.
Claims (2)
1. a class coating material for the anti-finger prints processing in stainless steel plate surface, is characterized in that the composition comprising following weight part:
Additive 10-20,
Oxidation inhibitor 1-3,
Oil-soluble resin 5-8,
Water-holding agent 0.5-1,
Machinery oil 50-70;
Described additive is one or more of silicon, aluminium, carbon and oxide compound thereof, and the mean particle size of described additive is less than 100 nanometers, described oxidation inhibitor is antioxidant BHT, described oil-soluble resin be Gum Rosin, dammar gum, soluble phenolic resin, petroleum resin one or more, described water-holding agent is polyacrylic acid potassium or ammonium polyacrylate, and described machinery oil is 7# or 10# or 100# machinery oil.
2., by the preparation method of the class coating material described in the claims 1, it is characterized in that comprising the steps:
1) in stirrer, first add machinery oil, additive, oil-soluble resin and oxidation inhibitor, stirrer stirs 30 ~ 40 minutes with the speed of 1000 ~ 2000 revs/min;
2) add water-holding agent again, stirrer stirs 5 ~ 10 minutes with the speed of 500 ~ 700 revs/min;
3) 10 ~ 20 minutes are incubated under last normal temperature.