CN103912631A - Highly-wear-resistant tight-up V-belt - Google Patents
Highly-wear-resistant tight-up V-belt Download PDFInfo
- Publication number
- CN103912631A CN103912631A CN201410136577.5A CN201410136577A CN103912631A CN 103912631 A CN103912631 A CN 103912631A CN 201410136577 A CN201410136577 A CN 201410136577A CN 103912631 A CN103912631 A CN 103912631A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- carbon black
- belt
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a highly-wear-resistant tight-up V-belt which comprises at least two V-belt bodies. The V-belt bodies are connected through a connection layer on the upper surface to form the tight-up V-belt, and the V-shaped outer side face of each V-belt body is coated with a wrapper layer which is made of a wrapper and adhered rubber. The highly-wear-resistant tight-up V-belt is characterized in that the adhered rubber is made by means of proportionally mixing, by weight, 100 parts of rubber, 20-25 parts of wear-resistant nano clay and 45-50 parts of wear-resistant carbon black. The adhered rubber of the wrapper layer is added with the wear-resistant nano clay and the wear-resistant carbon black so as to improve wear resistance of the wrapper layer, wear resistance of the entire tight-up V-belt is improved while service time of the entire tight-up V-belt is prolonged, and actual experiments prove that service life of the improved tight-up V-belt is generally between 2 years and 3 years.
Description
Technical field
The present invention relates to a kind of joint group V-type band, relate in particular to a kind of high abrasion joint group V-type band.
Background technique
Joint group V-type band is the V band group that the end face of several identical classical V-belts or narrow V belt is combined as a whole by tie layer.That each V strip length is consistent by one group of band of same material and once-through sulfuration, good integrity, stressed even, operate steadily, bearing capacity is high, and the life-span is long, is suitable for high-power transmission.Joint group V-type band is that single V band made-up belt is carried out and is unified into group again while production, and the outermost surface of single band is the infantees layer that is soaked with glue, infantees layer directly contacts with belt wheel, in use can produce friction, therefore depends on more the quality of infantees layer wear resistance the working life of joint group V-type band.
The shortcoming that existing joint group V-type band ubiquity wears no resistance, working life is short, take 3HB1970 as example, the 3HB1970 joint group V-type band major part of producing at present can only be used half a year, or shorter; Minority manufacturer production can use 1 year, but can use 2-3 seldom.
Summary of the invention
The object of the present invention is to provide a kind of high abrasion joint group V-type band, it has the feature of the good and long service life of wear resistance, with solve in prior art joint group V-type band exist wear no resistance and working life short problem.
For reaching this object, the present invention by the following technical solutions:
A kind of high abrasion joint group V-type band, it comprises at least two V-shape belts, described at least two V-shape belts connect to form joint group V-type band by the tie layer of upper surface, the V-type outer side surface of described every V-shape belt is coated with infantees layer, described infantees layer is made up of infantees and attached glue, and wherein, described attached glue adds nanometer antiwear potter's clay by rubber and abrasion resistant carbon black is mixed, three's mixed proportion (by weight), rubber: 100 parts; Nanometer potter's clay: 20~25 parts; Carbon black: 45~50 parts.
Especially, described infantees adopts wear-resisting stretchy nylon cloth.
Especially, the mixed proportion (by weight) of rubber, nanometer potter's clay and carbon black in described attached glue, rubber: 100 parts; Nanometer potter's clay: 20 parts; Carbon black: 45 parts.
Especially, the mixed proportion (by weight) of rubber, nanometer potter's clay and carbon black in described attached glue, rubber: 100 parts; Nanometer potter's clay: 22.5 parts; Carbon black: 47.5 parts.
Especially, the mixed proportion (by weight) of rubber, nanometer potter's clay and carbon black in described attached glue, rubber: 100 parts; Nanometer potter's clay: 25 parts; Carbon black: 50 parts.
Especially, described joint group V-type band is to comprise any of three, four, five, the six roots of sensation or seven V-shape belts.
Beneficial effect of the present invention is, compared with prior art described high abrasion joint group V-type band adds nanometer antiwear potter's clay and abrasion resistant carbon black to have improved the wear resistance of infantees layer in the attached glue of infantees layer, improved wear resistance and the service time of whole joint group V-type band, the joint group V-type band general service life after actual experiment proves to improve is between 2-3.
Accompanying drawing explanation
Fig. 1 is the structural representation of high abrasion joint group V-type band provided by the invention.
In figure:
1, V-shape belt; 2, tie layer; 3, infantees layer.
Embodiment
Further illustrate technological scheme of the present invention below in conjunction with accompanying drawing and by embodiment.
Embodiment one:
Refer to shown in Fig. 1, Fig. 1 is the structural representation of high abrasion joint group V-type band provided by the invention.
In the present embodiment, a kind of high abrasion joint group V-type band comprises three V-shape belts 1, described three V-shape belts 1 connect to form joint group V-type band by the tie layer 2 of upper surface, the V-type outer side surface of described every V-shape belt 1 is coated with infantees layer 3, described infantees layer 3 is made up of infantees and attached glue, and described infantees adopts wear-resisting stretchy nylon cloth.Described attached glue adds nanometer antiwear potter's clay by rubber and abrasion resistant carbon black is mixed, three's mixed proportion (by weight), rubber: 100 parts; Nanometer potter's clay: 20 parts; Carbon black: 45 parts.
Embodiment two:
Refer to shown in Fig. 1, Fig. 1 is the structural representation of high abrasion joint group V-type band provided by the invention.
In the present embodiment, a kind of high abrasion joint group V-type band comprises three V-shape belts 1, described three V-shape belts 1 connect to form joint group V-type band by the tie layer 2 of upper surface, the V-type outer side surface of described every V-shape belt 1 is coated with infantees layer 3, described infantees layer 3 is made up of infantees and attached glue, and described infantees adopts wear-resisting stretchy nylon cloth.Described attached glue adds nanometer antiwear potter's clay by rubber and abrasion resistant carbon black is mixed, three's mixed proportion (by weight), rubber: 100 parts; Nanometer potter's clay: 22.5 parts; Carbon black: 47.5 parts.
Embodiment three:
Refer to shown in Fig. 1, Fig. 1 is the structural representation of high abrasion joint group V-type band provided by the invention.
In the present embodiment, a kind of high abrasion joint group V-type band comprises three V-shape belts 1, described three V-shape belts 1 connect to form joint group V-type band by the tie layer 2 of upper surface, the V-type outer side surface of described every V-shape belt 1 is coated with infantees layer 3, described infantees layer 3 is made up of infantees and attached glue, and described infantees adopts wear-resisting stretchy nylon cloth.Described attached glue adds nanometer antiwear potter's clay by rubber and abrasion resistant carbon black is mixed, three's mixed proportion (by weight), rubber: 100 parts; Nanometer potter's clay: 25 parts; Carbon black: 50 parts.
Above embodiment has just set forth basic principle of the present invention and characteristic; the present invention is not limited by above-mentioned example; without departing from the spirit and scope of the present invention, the present invention also has various variations and change, and these variations and change all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (6)
1. a high abrasion joint group V-type band, it comprises at least two V-shape belts, described at least two V-shape belts connect to form joint group V-type band by the tie layer of upper surface, the V-type outer side surface of described every V-shape belt is coated with infantees layer, described infantees layer is made up of infantees and attached glue, it is characterized in that, described attached glue adds nanometer antiwear potter's clay by rubber and abrasion resistant carbon black is mixed, three's mixed proportion (by weight), rubber: 100 parts; Nanometer potter's clay: 20~25 parts; Carbon black: 45~50 parts.
2. high abrasion joint group V-type band according to claim 1, is characterized in that, described infantees adopts wear-resisting stretchy nylon cloth.
3. high abrasion joint group V-type band according to claim 1 and 2, is characterized in that, the mixed proportion (by weight) of rubber, nanometer potter's clay and carbon black in described attached glue, rubber: 100 parts; Nanometer potter's clay: 20 parts; Carbon black: 45 parts.
4. high abrasion joint group V-type band according to claim 1 and 2, is characterized in that, the mixed proportion (by weight) of rubber, nanometer potter's clay and carbon black in described attached glue, rubber: 100 parts; Nanometer potter's clay: 22.5 parts; Carbon black: 47.5 parts.
5. high abrasion joint group V-type band according to claim 1 and 2, is characterized in that, the mixed proportion (by weight) of rubber, nanometer potter's clay and carbon black in described attached glue, rubber: 100 parts; Nanometer potter's clay: 25 parts; Carbon black: 50 parts.
6. high abrasion joint group V-type band according to claim 1, is characterized in that, described joint group V-type band is to comprise any of three, four, five, the six roots of sensation or seven V-shape belts.