CN103898848A - Manufacturing method of traffic sign line sticker - Google Patents
Manufacturing method of traffic sign line sticker Download PDFInfo
- Publication number
- CN103898848A CN103898848A CN201410094614.0A CN201410094614A CN103898848A CN 103898848 A CN103898848 A CN 103898848A CN 201410094614 A CN201410094614 A CN 201410094614A CN 103898848 A CN103898848 A CN 103898848A
- Authority
- CN
- China
- Prior art keywords
- automatic
- film
- machine
- thickness
- dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a manufacturing method of a traffic sign line sticker. The manufacturing method comprises the steps that (1) pure aluminium is selected and laminating is conducted through an automatic combination machine; (2) adhesive stickers are selected, gumming is conducted on a film through an automatic gumming machine, and a debonding film is added; (3) spraying is conducted to form bottom oil through an automatic coating machine; (4) when paint is not dry, reflective glass beads are laid, and drying is conducted; (5) after the bottom oil is dry completely, transparent paint is added, and drying is conducted again; (6) slitting is conducted, and the debonding film is debonded and rolled. The method has the advantages that on-site laying can be conducted, aging resistance is achieved, service life is long, manufacturing cost is low, better abrasion resistance is achieved, surface friction force is large, color stability is good, and laying is convenient.
Description
Technical field
The present invention relates to the traffic mark field of road surface, relate in particular to a kind of preparation method of traffic mark sticker.
Background technology
Road traffic marking is to draw by mark the traffic safety facilities that various lines, arrow, word, object marking, protuberant guide post and delineator etc. on road surface form, and its effect is control and channel traffic, can be used in conjunction with mark, also can be used alone.Road traffic marking is mainly drawn and is located at road surface, stands to expose to the sun and rain, wind and snow is freezing, suffer the pounding wear of vehicle, therefore its performance is had to strict requirement; First, require drying time short, simple to operate, with reduce traffic disturb; Secondly, require that albedo is strong, in bright gay color, reflectance is strong, making has good visibility at daytime, night; The 3rd, should there is skid resistance and abrasion resistance, to ensure traffic safety and application life; Pavement marking paint can be divided into normal temperature solvent-borne type, thermal solvent type and heat molten type and two-component type four classes.
But existing road surface traffic mark mainly uses the method for the on-the-spot coating of quick drying paint to make, and needs certain hour to solidify after coating paint, affects traffic, marker line are shorter application life, need to often upgrade; Also have a kind of banded traffic mark of Pasting, can directly stick on road surface, but some environment application life shorter, easily come off, cost is high, in addition, mainly exists following defect: 1., in the time of construction, glue when rolling is sticky mutually with aluminium foil; 2. reflective for light direct projection and Pavement Skid Resistance effect is poor; 3. after end oil bone dry, lack corresponding processing mode.Therefore,, for above aspect, need to effectively innovate prior art.
Summary of the invention
For above defect, the invention provides a kind of while preventing rolling glue with aluminium foil mutually sticky, can avoid reflective to light direct projection and improve that Pavement Skid Resistance effect, cost of manufacture are lower, anti-aging, long service life, abrasion resistance are good, the cable laying operation preparation method of traffic mark sticker easily, to meet the needs of existing pavement marking.
For achieving the above object, the present invention is by the following technical solutions:
A preparation method for traffic mark sticker, is made up of following steps:
(1) choosing fine aluminium thickness is 0.3mm-0.5mm, carries out overlay film with Automatic complexing machine, and this film is that the thickness of PE film and film is 0.1-0.2mm;
(2) choosing adhesive sticker thickness is 0.25mm-0.4mm, utilizes automatic glue spreaders to carry out gluing to overlay film, utilizes on automatic glue spreaders fractal film glue when preventing rolling sticky mutually with aluminium foil simultaneously, and this fractal film thickness is 0.1 mm-0.3mm;
(3) utilize automatic spraying machine spraying to make end oil, the thickness of paint is determined on demand, determines finished color;
(4) in the time of Wet Paint, lay reflecting glass Bead so that overcome that light direct projection is reflective and road pavement is anti-skidding, bead size diameter is 0.1 mm-1mm, coats after reflecting glass Bead at end oil, enter automatic drier and dry 30 minutes, 100 DEG C-120 DEG C of temperature;
(5) after end oil bone dry, again return automatic spraying machine external surface is sprayed to the resistance to molten celluloid paint of a floor height, then enter automatic baking machine and dry 30 minutes, 100 DEG C-120 DEG C of temperature;
(6) above operation completed after 72 hours, cut with cutting machine, and cutting specification is width 10cm-12cm, and length is 38cm-45cm, fractal film was peeled off simultaneously, carried out rolling with winder.
Correspondingly, when carry out step (1)-(5) after, carrying out step (6) time, after cutting with cutting machine, directly carry out rolling with winder;
When carry out step (1)-(4) after, carrying out step (5) time, after end oil bone dry, directly enter again automatic baking machine and dry 30 minutes, 100 DEG C-120 DEG C of temperature; When end oil bone dry, directly enter again after automatic baking machine dries, cut with cutting machine, directly carry out rolling with winder.
The beneficial effect of the preparation method of traffic mark sticker of the present invention is: the method can be laid at the scene, anti-aging, long service life, cost of manufacture are lower, there is preferably abrasion resistance, long service life, skin friction is large, colour stability good, cable laying operation is convenient, can make different size specification and color according to unlike signal line, can make according to actual requirement the various marker line of road traffic.
Detailed description of the invention
embodiment 1
The preparation method of the traffic mark sticker described in the embodiment of the present invention, is mainly made up of following steps:
(1) choosing fine aluminium thickness is 0.3mm-0.5mm, carries out overlay film with Automatic complexing machine, and this film is that the thickness of PE film and film is 0.1-0.2mm;
(2) choosing adhesive sticker thickness is 0.25mm-0.4mm, utilizes automatic glue spreaders to carry out gluing to overlay film, utilizes on automatic glue spreaders fractal film glue when preventing rolling sticky mutually with aluminium foil simultaneously, and this fractal film thickness is 0.1 mm-0.3mm;
(3) utilize automatic spraying machine spraying to make end oil, the thickness of paint is determined on demand, determines finished color;
(4) in the time of Wet Paint, lay reflecting glass Bead so that overcome that light direct projection is reflective and road pavement is anti-skidding, bead size diameter is 0.1 mm-1mm, coats after reflecting glass Bead at end oil, enter automatic drier and dry 30 minutes, 100 DEG C-120 DEG C of temperature;
(5) after end oil bone dry, again return automatic spraying machine external surface is sprayed to the resistance to molten celluloid paint of a floor height, then enter automatic baking machine and dry 30 minutes, 100 DEG C-120 DEG C of temperature;
(6) above operation completed after 72 hours, cut with cutting machine, and cutting specification is width 10cm-12cm, and length is 38cm-45cm, fractal film was peeled off simultaneously, carried out rolling with winder.
embodiment 2
The preparation method of the traffic mark sticker described in the embodiment of the present invention, is mainly made up of following steps:
(1) choosing fine aluminium thickness is 0.3mm-0.5mm, carries out overlay film with Automatic complexing machine, and this film is that the thickness of PE film and film is 0.1-0.2mm;
(2) choosing adhesive sticker thickness is 0.25mm-0.4mm, utilizes automatic glue spreaders to carry out gluing to overlay film, utilizes on automatic glue spreaders fractal film glue when preventing rolling sticky mutually with aluminium foil simultaneously, and this fractal film thickness is 0.1 mm-0.3mm;
(3) utilize automatic spraying machine spraying to make end oil, the thickness of paint is determined on demand, determines finished color;
(4) in the time of Wet Paint, lay reflecting glass Bead so that overcome that light direct projection is reflective and road pavement is anti-skidding, bead size diameter is 0.1 mm-1mm, coats after reflecting glass Bead at end oil, enter automatic drier and dry 30 minutes, 100 DEG C-120 DEG C of temperature;
(5) after end oil bone dry, again return automatic spraying machine external surface is sprayed to the resistance to molten celluloid paint of a floor height, then enter automatic baking machine and dry 30 minutes, 100 DEG C-120 DEG C of temperature;
(6) above operation completed after 72 hours, cut with cutting machine, and cutting specification is width 10cm-12cm, and length is 38cm-45cm, carried out rolling with winder.
embodiment 3
The preparation method of the traffic mark sticker described in the embodiment of the present invention, is mainly made up of following steps:
(1) choosing fine aluminium thickness is 0.3mm-0.5mm, carries out overlay film with Automatic complexing machine, and this film is that the thickness of PE film and film is 0.1-0.2mm;
(2) choosing adhesive sticker thickness is 0.25mm-0.4mm, utilizes automatic glue spreaders to carry out gluing to overlay film, utilizes on automatic glue spreaders fractal film glue when preventing rolling sticky mutually with aluminium foil simultaneously, and this fractal film thickness is 0.1 mm-0.3mm;
(3) utilize automatic spraying machine spraying to make end oil, the thickness of paint is determined on demand, determines finished color;
(4) in the time of Wet Paint, lay reflecting glass Bead so that overcome that light direct projection is reflective and road pavement is anti-skidding, bead size diameter is 0.1 mm-1mm, coats after reflecting glass Bead at end oil, enter automatic drier and dry 30 minutes, 100 DEG C-120 DEG C of temperature;
(5) after end oil bone dry, then enter automatic baking machine and dry 30 minutes, 100 DEG C-120 DEG C of temperature;
(6) above operation completed after 72 hours, cut with cutting machine, and cutting specification is width 10cm-12cm, and length is 38cm-45cm, fractal film was peeled off simultaneously, carried out rolling with winder.
embodiment 4
The preparation method of the traffic mark sticker described in the embodiment of the present invention, is mainly made up of following steps:
(1) choosing fine aluminium thickness is 0.3mm-0.5mm, carries out overlay film with Automatic complexing machine, and this film is that the thickness of PE film and film is 0.1-0.2mm;
(2) choosing adhesive sticker thickness is 0.25mm-0.4mm, utilizes automatic glue spreaders to carry out gluing to overlay film, utilizes on automatic glue spreaders fractal film glue when preventing rolling sticky mutually with aluminium foil simultaneously, and this fractal film thickness is 0.1 mm-0.3mm;
(3) utilize automatic spraying machine spraying to make end oil, the thickness of paint is determined on demand, determines finished color;
(4) in the time of Wet Paint, lay reflecting glass Bead so that overcome that light direct projection is reflective and road pavement is anti-skidding, bead size diameter is 0.1 mm-1mm, coats after reflecting glass Bead at end oil, enter automatic drier and dry 30 minutes, 100 DEG C-120 DEG C of temperature;
(5) after end oil bone dry, then enter automatic baking machine and dry 30 minutes, 100 DEG C-120 DEG C of temperature;
(6) above operation completed after 72 hours, cut with cutting machine, and cutting specification is width 10cm-12cm, and length is 38cm-45cm, carried out rolling with winder.
Above embodiment is more preferably detailed description of the invention several of the present invention, and the common variation that those skilled in the art carry out within the scope of the technical program and replacing should be included in protection scope of the present invention.
Claims (4)
1. a preparation method for traffic mark sticker, is characterized in that, is made up of following steps:
(1) choosing fine aluminium thickness is 0.3mm-0.5mm, carries out overlay film with Automatic complexing machine, and this film is that the thickness of PE film and film is 0.1-0.2mm;
(2) choosing adhesive sticker thickness is 0.25mm-0.4mm, utilizes automatic glue spreaders to carry out gluing to overlay film, utilizes on automatic glue spreaders fractal film glue when preventing rolling sticky mutually with aluminium foil simultaneously, and this fractal film thickness is 0.1 mm-0.3mm;
(3) utilize automatic spraying machine spraying to make end oil, the thickness of paint is determined on demand, determines finished color;
(4) in the time of Wet Paint, lay reflecting glass Bead so that overcome that light direct projection is reflective and road pavement is anti-skidding, bead size diameter is 0.1 mm-1mm, coats after reflecting glass Bead at end oil, enter automatic drier and dry 30 minutes, 100 DEG C-120 DEG C of temperature;
(5) after end oil bone dry, again return automatic spraying machine external surface is sprayed to the resistance to molten celluloid paint of a floor height, then enter automatic baking machine and dry 30 minutes, 100 DEG C-120 DEG C of temperature;
(6) above operation completed after 72 hours, cut with cutting machine, and cutting specification is width 10cm-12cm, and length is 38cm-45cm, fractal film was peeled off simultaneously, carried out rolling with winder.
2. the preparation method of traffic mark sticker according to claim 1, is characterized in that: when carry out step (1)-(5) after, carrying out step (6) time, after cutting with cutting machine, directly carry out rolling with winder.
3. the preparation method of traffic mark sticker according to claim 1, is characterized in that: when carry out step (1)-(4) after, carrying out step (5) time, after end oil bone dry, directly enter again automatic baking machine and dry 30 minutes, 100 DEG C-120 DEG C of temperature.
4. the preparation method of traffic mark sticker according to claim 3, is characterized in that: when end oil bone dry, directly enter after automatic baking machine dries again, cut with cutting machine, directly carry out rolling with winder.