CN103897525A - Acrylic anti-corrosion paint - Google Patents
Acrylic anti-corrosion paint Download PDFInfo
- Publication number
- CN103897525A CN103897525A CN201210569266.9A CN201210569266A CN103897525A CN 103897525 A CN103897525 A CN 103897525A CN 201210569266 A CN201210569266 A CN 201210569266A CN 103897525 A CN103897525 A CN 103897525A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic
- corrosion paint
- corrosion
- acrylic anti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an acrylic anti-corrosion paint which comprises the following components: 60-80 parts of an acrylic emulsion, 4-10 parts of zinc phosphate, 2-8 parts of dibutyl phthalate, 1-7 parts of butyl acetate, 10-15 parts of alcohol ester-12, 1-4 parts of aqua ammonia, and 1-4 parts of titanium dioxide. The butyl acetate content is 3 parts. The acrylic anti-corrosion paint is a pure acrylic anti-corrosion paint which realizes combination of a primer and a topcoat, has single component, is a self-drying type, has good corrosion resistance, and accords with environmental protection requirements; the acrylic anti-corrosion paint can be blended with any color, is convenient to construct, and can be constructed at the temperature of 0 DEG C or more; and the acrylic anti-corrosion paint has strong salt fog resistance, and can provide required anti-corrosion performance for steel materials.
Description
Technical field
The present invention relates to a kind of paint, especially a kind of vinylformic acid antifouling paste.
Background technology
The rust-inhibiting paint protective system overwhelming majority of domestic use is solvent based coating, and the shortcoming of these coating maximums is exactly contaminate environment, inflammable and explosive, harmful, and wastes a large amount of resources and the energy.In market, use now and have widely water-based anticorrosive paint to have the rich zinc of aqueous inorganic, aqueous epoxy coating etc., these coating are to be all used in priming paint, high to substrate treatment requirement, construct loaded down with trivial details.Water soluble acrylic acid protective system has some producers producing abroad, but poor effect on anticorrosion salt spray resistance and sticking power, and the main anti-corrosion paints such as red iron oxide and composite iron-titanium powder that use, are not suitable for toning in water soluble acrylic acid is anticorrosion, use into finish paint effect bad.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of vinylformic acid antifouling paste.
For solving the problems of the technologies described above, vinylformic acid antifouling paste of the present invention, it comprises following component, ACRYLIC EMULSION 60-80 part, zinc phosphate 4-10 part, dibutyl phthalate 2-8 part, N-BUTYL ACETATE 1-7 part, lauryl alcohol ester 10-15 part, ammoniacal liquor 1-4 part, titanium dioxide 1-4 part.
The content of described N-BUTYL ACETATE is 3 parts.
Vinylformic acid antifouling paste of the present invention bottom surface unification, the pure acrylic acid protective system that single component, self-drying type, antiseptic property be good, meet environmental requirement, can be made into random color, and easy construction, all can construct above at 0 DEG C; Salt spray resistance is strong, can provide steel required resistance to antiseptic property.
Embodiment
Embodiment 1
Vinylformic acid antifouling paste of the present invention, it comprises following component, 60 parts of ACRYLIC EMULSION, 10 parts of zinc phosphates, 8 parts of dibutyl phthalates, 1 part of N-BUTYL ACETATE, 15 parts of lauryl alcohol esters, 1 part of ammoniacal liquor, 4 parts of titanium dioxide.
Embodiment 2
Vinylformic acid antifouling paste of the present invention, it comprises following component, 80 parts of ACRYLIC EMULSION, 10 parts of zinc phosphates, 2 parts of dibutyl phthalates, 7 parts of N-BUTYL ACETATEs, 10 parts of lauryl alcohol esters, 4 parts of ammoniacal liquor, 1 part of titanium dioxide.
Embodiment 3
Vinylformic acid antifouling paste of the present invention, it comprises following component, 75 parts of ACRYLIC EMULSION, 4 parts of zinc phosphates, 4 parts of dibutyl phthalates, 5 parts of N-BUTYL ACETATEs, 12 parts of lauryl alcohol esters, 2 parts of ammoniacal liquor, 2 parts of titanium dioxide.
The above, be only to preferred embodiment of the present invention, not the present invention done to other forms of restriction, and any those skilled in the art may utilize the technology contents of above-mentioned announcement to be changed or be modified as the equivalent embodiment of equal variation.Every the present invention program's content that do not depart from,, all drops in protection scope of the present invention any simple modification made for any of the above embodiments, equivalent variations and remodeling according to technical spirit of the present invention.
Claims (2)
1. a vinylformic acid antifouling paste, is characterized in that: it comprises following component, ACRYLIC EMULSION 60-80 part, zinc phosphate 4-10 part, dibutyl phthalate 2-8 part, N-BUTYL ACETATE 1-7 part, lauryl alcohol ester 10-15 part, ammoniacal liquor 1-4 part, titanium dioxide 1-4 part.
2. according to vinylformic acid antifouling paste claimed in claim 1, it is characterized in that: the content of described N-BUTYL ACETATE is 3 parts.