CN103892615A - Health-care cushion - Google Patents
Health-care cushion Download PDFInfo
- Publication number
- CN103892615A CN103892615A CN201410082034.XA CN201410082034A CN103892615A CN 103892615 A CN103892615 A CN 103892615A CN 201410082034 A CN201410082034 A CN 201410082034A CN 103892615 A CN103892615 A CN 103892615A
- Authority
- CN
- China
- Prior art keywords
- layer
- health
- care
- parts
- bamboo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a cushion article for daily use, and in particular relates to a health-care cushion. The cushion comprises a base layer and a cushion layer arranged above the base layer, wherein at least a first health-care layer and a second health-care layer are sequentially arranged below the cushion layer; the first health-care layer comprises a bamboo charcoal layer and a tourmaline particle and/or anion power layer which are mutually staggered; the specific arrangement mode is that the bamboo charcoal layer is arranged on one side of the upper part of the first health-care layer, and the tourmaline particle and/or anion power layer are/is arranged on the other side side of the upper part of the first health-care layer; the tourmaline particle and/or anion power layer are/is arranged at the lower part of the first health-care layer and right below the bamboo charcoal layer; the bamboo charcoal layer is arranged at the lower part of the first health-care layer and right below the tourmaline particle and/or anion power layer; the second health-care layer comprises flexible magnet massage beads and flexible magnetic stripes arranged along the circumferential direction of the second health-care layer; the flexible magnetic stripes are connected in the base layer or on the surface of the base layer in a penetrating manner through elastic lines; the flexible magnetic stripes are fixed on the base layer in an inlaying, cladding or adhering way. By means of the cushion disclosed by the invention, the health preserving mode of comprehensively coordinating health can be realized.
Description
Technical field
The present invention relates to a kind of cushion daily necessities, relate in particular to a kind of health-care cushion.
Background technology
Influence of magnetic field body current distributes, motion, the permeability of film system and the magnetic moment orientation of boiomacromolecule etc. of Charge particle, and histiocytic physiology, biochemical process are changed, and produces analgesia, detumescence, promotes the effects such as blood and Lymphatic Circulation.Magnetic therapy is that to adapt to symptom extensive due to it obtaining developing rapidly in recent years, and health-care effect is remarkable, without wound, very little, safe without pain, side effect, reliably.
CN101638117B (2013-9-4) discloses a kind of seat cushion, drives class instrument but this seat cushion is mainly provided to bicycle etc., can not meet the demand of health care.
Summary of the invention
The object of this invention is to provide a kind of healthy health-care cushion that is conducive to.
Above-mentioned technical purpose of the present invention is achieved by the following technical programs:
A kind of health-care cushion, comprises a basic unit and a bed course that is arranged on described basic unit top, and described in it, bed course below is at least disposed with the first heath care layer and the second heath care layer;
Described the first heath care layer comprises bamboo-carbon layer and tourmaline particle and/or the anion bisque of interlaced arrangement; Concrete arrangement mode is that described the first heath care layer top one side is bamboo-carbon layer, and opposite side is tourmaline particle and/or anion bisque; Described heath care layer bottom and to be positioned under described bamboo-carbon layer be tourmaline particle and/or anion bisque, described heath care layer bottom and be positioned at described tourmaline particle and/or anion bisque under be bamboo-carbon layer;
The flexible magnetic strips that described the second heath care layer comprises flexible magnet massage bead and circumferentially arranges along described the second heath care layer, described flexible magnetic strips is worn to connect by elastica and is arranged on described basic unit inside or substrate surface; Described flexible magnetic strips by inlaying, mode coated or adhesion is fixed in described basic unit.
The present invention, by the setting of flexible magnet massage bead, flexible magnetic strips and bamboo-carbon layer, tourmaline particle and/or anion bisque, reaches the healthy Curing Method of comprehensive coordination;
Human body is by absorbing the rear far infrared discharging of tourmaline heating, anion, sub-ion, mineral element etc., skin metabolism harmful substance, improve skin elasticity, promote systemic blood circulation and metabolism, thereby reach the effect of beauty treatment, body beautification and some chronic diseases for the treatment of.
In addition, bamboo charcoal has and de-tastes and antibacterial functions, and dirt is had to suction-operated, assists in removing the peculiar smell in environment, makes air cleaning; Conductance is high, and not containing dust impurity, far infrared effect is good, can promote health insulation and peripheral blood circulation, has good health care function.
As preferably, described flexible magnet massage bead entirety is Tai Ji and distributes.
This structure setting can make the present invention meet base of principle of human engineering, and massage effect is better.
As preferably, described bed course hooks face and VELCRO hair side by including VELCRO VELCRO with described the first heath care layer is removably connected, described VELCRO hooks face by the bonding described bed course back side that is arranged on of glue, and described VELCRO hair side is arranged on described the first heath care layer surface by glue is bonding.
As preferably, described glue is made up of the raw material of following parts by weight:
Phthalic anhydride 25-35 part, triethylene glycol 10-12 part, glutaric acid 15-18 part, butantriol 8-10 part, Zinc Oxide 5-7 part, magnesia 3-5 part, neoprene 15-25 part, elastic plastic 70-95 part, softening oil 2-3 part, dimethyl carbonate 15-20 part, ethylbenzene 20-30 part, fire retardant 1-3 part.
Adopt glue of the present invention, have advantages of that tack is good, fastness is high.
More preferably, described fire retardant is counted composed of the following components by weight: 20～50 parts of ammonium low polyphosphates, 10～25 parts, ammonium phosphate, 6～12 parts of ammonium pyrophosphates, 5～20 parts, ammonium sulfate, 5～10 parts of boric acid, 10～25 parts, water.
Not only good flame retardation effect of fire retardant of the present invention, and can with glue in all the other component Synergistics, increase the tack of glue.
?as preferably, described bamboo charcoal is prepared from by following steps:
?(1) raw material pre-treatment: plant material is sent in microwave vacuum tank, be evacuated to vacuum for-0.02MPa～-0.001MPa, then carry out microwave treatment, microwave frequency is 300MHz～950MHz, and microwave treatment time is 1～3min;
?(2) elementary charcoal preparation: will experience successively dry, pre-charing, charing, calcining and cooling through the plant material of raw material pre-treatment gained, control combustion is warming up to 700-750 ℃ or 900-1000 ℃ and is incubated 40-80min with the speed of 5-15 ℃/min, and then be warming up to 1000-1500 ℃ or 1600-1800 ℃ and be incubated 2-8h with the speed of 5-15 ℃/min, then be cooled to 300-400 ℃ with the speed of 18-25 ℃/min, cool to again room temperature with the furnace, obtain elementary charcoal;
?(3) then activation processing: the Potassium Oxalate Solution that is 8-10% with mass fraction by elementary gained charcoal is 1:3-4 mixing submergence 3-5h is in mass ratio neutral by washed with de-ionized water to pH value;
?(4) dipping flame treatment: adopt vacuum pressed flame treatment, in processing procedure, first the elementary charcoal of gained after activation processing is packed into vacuum pressed tank and vacuumize and make its vacuum for-0.015MPa～-0.025MPa, then fire retardant is added in tank and by pressure to add to 0.1MPa～0.8MPa;
?(5) bamboo vinegar processing: comprise a bamboo vinegar processing and the processing of secondary bamboo vinegar, a bamboo vinegar processing is that the charcoal after flame treatment is immersed in 20-40min in the bamboo vinegar treatment fluid of 40-50 ℃ by dipping, the processing of secondary bamboo vinegar is submergence 10-30min in the secondary bamboo vinegar treatment fluid of 55-80 ℃, the bamboo vinegar aqueous solution that a described bamboo vinegar treatment fluid is 20-30g/L, the mixed solution of bamboo vinegar, chelating agent and water composition that described secondary bamboo vinegar treatment fluid is weight ratio 1:0.1-0.2:60-100;
?(6) microwave treatment: bamboo vinegar is processed to gained material and carry out microwave treatment, microwave frequency is 500～650MHz, and microwave treatment time is 1～3min;
(7) carbon granule preparation: the material after microwave treatment is made to the charcoal particle that diameter is 0.5-2mm with pulverizer or hydraulic press.
Advantage of the present invention is:
1. can control moisture and the perforate of plant material by pre-treatment, contribute to the preparation of follow-up elementary charcoal, can improve the conduction of elementary charcoal and de-taste function, the plant charcoal sheet resistance of preparation is high, there is good electric conductivity, the antistatic behaviour of air-conditioned room is had to facilitation;
2. this plant charcoal particle and having de-tastes and antibacterial functions, and dirt is had to suction-operated, assists in removing the peculiar smell in environment, makes air cleaning;
The carbon granule conductance of 3. passing through activation processing is high, and not containing dust impurity, far infrared effect is good, can promote health insulation and peripheral blood circulation, has good health care function;
4. inventor finds activation processing after, to flood fire-retardantly again, can strengthen the antibacterial ability of charcoal particle, and the negative ion releasing function of carbon granule of the present invention is improved, and can improve user's lung capacity, raising sleep quality;
5. flood flame treatment and adopt vacuum pressed flame treatment, can overcome the mobile resistances of fire retardant such as conduit in plant microstructure, test-tube baby, pit, extract filling or aspiration, make fire retardant can deeply be penetrated into bamboo wood the inside, effectively prevented the loss of fire retardant; Vacuum pressed flame treatment also has the advantages such as fire retardant infiltration efficiency is high, resistance leachability is strong, environmentally friendly;
6. bamboo vinegar processing method of the present invention and bamboo vinegar treatment fluid can make carbon granule further activate, and improve bacteriostasis rate and the antibacterial value of charcoal;
7. microwave vacuum processing of the present invention, there is fuel factor and non-thermal effect in each component simultaneously, when carry out microwave radiation heating, electromagnetic field in microwave is with several hundred million even billions of inferior frequency inverted directions per second, make polarization and this polarization of the different electric charges of material internal not possess the ability of catching up with rapidly alternating electric field, cause material internal friction and generate heat, i.e. so-called " interior heating ", each component is blended mutually, and may there are some reactions, there is synergistic function, improve carbon granule Air purification.
As preferably, described step (1) plant material is corncob, bamboo or pine tree.
As preferably, described negative ion powder is made up of following components in mass portion: sea-gull stone 15-20 part; Tourmaline 5-10 part; Opal 30-35 part; Serpentine 2-6 part; Medical stone 4-6 part; Strange ice stone 4-6 part; Hokutolite 1-2 part; Doctor Wang Shi 5-7 part; Shell 1-3 part; Diatomite 12-18 part; Zirconia 5-8 part; Basic zirconium phosphate 4-6 part.
The airion concentration that adopts negative ion powder that raw material proportioning of the present invention makes to produce is high, has calmness, hypnosis, antibechic, antipruritic, diuresis, increasing appetite, hypotensive effect, and it is happy that user feels.
As preferably, described sea-gull stone, Tourmaline, opal, serpentine, medical stone, strange ice stone, hokutolite, doctor Wang Shi, shell, diatomite, zirconia and basic zirconium phosphate are mixed, ultra-fine grinding to grain diameter is 15-30nm, sieves, microwave treatment.
As preferably, microwave frequency is 500～650MHz, and microwave treatment time is 1～3min.
By microwave treatment, can further strengthen the efficacy effect of anion.
Accompanying drawing explanation
Fig. 1 is health-care cushion schematic diagram of the present invention;
Fig. 2 is the present invention's the first heath care layer structural representation;
Fig. 3 is the present invention's the second heath care layer structural representation;
Fig. 4 is bed course and the first heath care layer connection diagram of a kind of embodiment.
The specific embodiment
Below in conjunction with accompanying drawing, the present invention is described in further detail.
As shown in Figure 1,2,3, 4, health-care cushion comprises a basic unit 1 and a bed course 2 that is arranged on basic unit 1 top, and bed course 2 belows are at least disposed with the first heath care layer 3 and the second heath care layer 4;
The first heath care layer 3 comprises bamboo-carbon layer 31 and tourmaline particle and/or the anion bisque 32 of interlaced arrangement; Concrete arrangement mode is that the first heath care layer 3 top one sides are bamboo-carbon layer 31, and opposite side is tourmaline particle and/or anion bisque 32; Heath care layer 3 bottoms and to be positioned under bamboo-carbon layer 31 be tourmaline particle and/or anion bisque 32, heath care layer 3 bottoms and be positioned at tourmaline particle and/or anion bisque 32 under be bamboo-carbon layer 31;
The flexible magnetic strips 42 that the second heath care layer 4 comprises flexible magnet massage bead 41 and circumferentially arranges along the second heath care layer 4, flexible magnetic strips 42 is arranged on basic unit 1 inside or basic unit 1 surface by elastica 43 companies of wearing; Flexible magnetic strips 42 by inlaying, mode coated or adhesion is fixed in basic unit 1; Flexible magnet massage bead 41 entirety are Tai Ji and distribute;
The mode of removably connecting of bed course 2 and the first heath care layer 3 has multiple, and the mode that for example can inhale mutually by Magnetic hasp connects; Also can be that the VELCRO 5 that bed course 2 is hooked to face 51 and VELCRO hair side 52 with the first heath care layer 3 by including VELCRO is removably connected, VELCRO hooks face 51 by bonding bed course 2 back sides that are arranged on of glue, and VELCRO hair side 52 is by bonding first heath care layer 3 surfaces that are arranged on of glue.
Following embodiment is shown in respectively in the preparation of the formula of glue, the preparation of bamboo charcoal and negative ion powder.
Embodiment mono-
Glue is made up of the raw material of following parts by weight: 25 parts of phthalic anhydrides, 10 parts of triethylene glycols, 15 parts of glutaric acids, 8 parts of butantriols, 5 parts of Zinc Oxides, 3 parts, magnesia, 15 parts of neoprenes, 70 parts of elastic plastics, 2 parts of softening oils, 15 parts of dimethyl carbonates, 20 parts, ethylbenzene, 1 part of fire retardant.
Fire retardant is counted composed of the following components by weight: 20 parts of ammonium low polyphosphates, 10 parts, ammonium phosphate, 6 parts of ammonium pyrophosphates, 5 parts, ammonium sulfate, 5 parts of boric acid, 10 parts, water.
The plant material that the preparation of the present embodiment bamboo charcoal adopts is bamboo chip (being about 40cm).
Plant material is sent in microwave vacuum tank, be evacuated to vacuum for-0.001MPa, then carry out microwave treatment, microwave frequency is 950MHz, and microwave treatment time is 3min;
To experience successively dry, pre-charing, charing, calcining and cooling through the plant material of pre-treatment gained, the temperature of each point for measuring temperature, dry section temperature is 150 ℃, pre-char zone is 275 ℃, and the temperature of combustion zone diverse location is observed in 450 ℃ of char zone when intensification, control the combustion zone temperature experiencing in bamboo folding process, control combustion is warming up to 750 ℃ and be incubated 80min with the speed of 15 ℃/min, and then heats up 1500 ℃ and be incubated 8h with the speed of 15 ℃/min
Then be cooled to 300-330 ℃ with the speed of 18-23 ℃/min, then cool to room temperature with the furnace, obtain elementary charcoal; Then carrying out activation processing: the Potassium Oxalate Solution that is 10% with mass fraction by elementary gained charcoal is 1:4 mixing submergence 5h in mass ratio, is then neutral by washed with de-ionized water to pH value; Then adopt vacuum pressed flame treatment, in processing procedure, first the elementary charcoal of gained after activation processing being packed into vacuum pressed tank vacuumizes and makes its vacuum for-0.025Mpa, then fire retardant is added in tank and by pressure in tank and adds to 0.8Mpa, the fire retardant of use is counted composed of the following components by weight: 50 parts of ammonium low polyphosphates, 25 parts, ammonium phosphate, 12 parts of ammonium pyrophosphates, 20 parts, ammonium sulfate, 10 parts of boric acid, 25 parts, water;
Then carry out bamboo vinegar processing, bamboo vinegar processing comprises a bamboo vinegar processing and the processing of secondary bamboo vinegar, a bamboo vinegar processing is that charcoal is immersed in to 20min in the bamboo vinegar treatment fluid of 40 ℃, the bamboo vinegar aqueous solution that bamboo vinegar treatment fluid is 20g/L, the processing of secondary bamboo vinegar is to continue charcoal to be immersed in 10min in the secondary bamboo vinegar treatment fluid of 55 ℃, and secondary bamboo vinegar treatment fluid is the mixed solution of bamboo vinegar, disodium edta chelating agent and the water composition of weight ratio 1:0.2:60;
And then carry out microwave treatment, and microwave frequency is 500～550MHz, microwave treatment time is 1～1.2min; Finally make with pulverizer the charcoal particle that diameter is 2-4mm.
Negative ion powder formula: 18 parts, sea-gull stone; 8 parts of Tourmalines; 33 parts, opal; 4 parts, serpentine; 5 parts of medical stones; 5 parts, strange ice stone; 1.5 parts of hokutolites; 6 parts of doctor Wang Shis; 2 parts, shell; 15 parts, diatomite; 7 parts of zirconias; 5 parts of basic zirconium phosphates.
Negative ion powder preparation: described sea-gull stone, Tourmaline, opal, serpentine, medical stone, strange ice stone, hokutolite, doctor Wang Shi, shell, diatomite, zirconia and basic zirconium phosphate are mixed, ultra-fine grinding to grain diameter is 20nm, sieve, microwave treatment: microwave frequency is 550MHz, microwave treatment time is 2min.
Embodiment bis-
Glue is made up of the raw material of following parts by weight: 35 parts of phthalic anhydrides, 12 parts of triethylene glycols, 18 parts of glutaric acids, 10 parts of butantriols, 7 parts of Zinc Oxides, 5 parts, magnesia, 25 parts of neoprenes, 95 parts of elastic plastics, 3 parts of softening oils, 20 parts of dimethyl carbonates, 30 parts, ethylbenzene, 3 parts of fire retardants.
Fire retardant is counted composed of the following components by weight: 50 parts of ammonium low polyphosphates, 25 parts, ammonium phosphate, 12 parts of ammonium pyrophosphates, 20 parts, ammonium sulfate, 10 parts of boric acid, 25 parts, water.
The plant material that the preparation of the present embodiment bamboo charcoal adopts is corncob.
Plant material is sent in microwave vacuum tank, be evacuated to vacuum for-0.02MPa, then carry out microwave treatment, microwave frequency is 300MHz, and microwave treatment time is 1min; To experience successively dry, pre-charing, charing, calcining and cooling through the plant material of pre-treatment gained, the temperature of each point for measuring temperature, dry section is 150 ℃, pre-char zone is 275 ℃, char zone is 450 ℃, controls the combustion zone temperature experiencing in bamboo folding process, and control combustion is warming up to 700 ℃ and be incubated 40min with the speed of 5 ℃/min, and then be warming up to 1600 ℃ and be incubated 2h with the speed of 5 ℃/min
Then be cooled to 380-400 ℃ with the speed of 23-25 ℃/min, then cool to room temperature with the furnace, obtain elementary charcoal; Then carrying out activation processing: the Potassium Oxalate Solution that is 8% with mass fraction by elementary gained charcoal is 1:3 mixing submergence 3h in mass ratio, is then neutral by washed with de-ionized water to pH value; Then adopt vacuum pressed flame treatment, in processing procedure, first the elementary charcoal of gained after activation processing being packed into vacuum pressed tank vacuumizes and makes its vacuum for-0.015MPa, then fire retardant is added in tank and by pressure in tank and adds to 0.1MPa, the fire retardant of use is counted composed of the following components by weight: 20 parts of ammonium low polyphosphates, 10 parts, ammonium phosphate, 6 parts of ammonium pyrophosphates, 5 parts, ammonium sulfate, 5 parts of boric acid, 10 parts, water;
Then carry out bamboo vinegar processing, bamboo vinegar processing comprises a bamboo vinegar processing and the processing of secondary bamboo vinegar, a bamboo vinegar processing is that gained charcoal is immersed in to 30min in the bamboo vinegar treatment fluid of 45 ℃, the bamboo vinegar aqueous solution that bamboo vinegar treatment fluid is 25g/L, the processing of secondary bamboo vinegar is to be immersed in 20min in the secondary bamboo vinegar treatment fluid of 70 ℃, and secondary bamboo vinegar treatment fluid is the mixed solution of bamboo vinegar, ethylenediamine tetra-acetic acid chelating agent and the water composition of weight ratio 1:0.1:80.
And then carry out microwave treatment, and microwave frequency is 600～650MHz, microwave treatment time is 2～3min; Finally make with pulverizer or hydraulic press the charcoal particle that diameter is 4-6mm.
Negative ion powder formula: 15 parts, sea-gull stone; 5 parts of Tourmalines; 30 parts, opal; 2 parts, serpentine; 4 parts of medical stones; 4 parts, strange ice stone; 1 part of hokutolite; 5 parts of doctor Wang Shis; 1 part, shell; 12 parts, diatomite; 5 parts of zirconias; 4 parts of basic zirconium phosphates.
Negative ion powder preparation: described sea-gull stone, Tourmaline, opal, serpentine, medical stone, strange ice stone, hokutolite, doctor Wang Shi, shell, diatomite, zirconia and basic zirconium phosphate are mixed, ultra-fine grinding to grain diameter is 15nm, sieve, microwave treatment: microwave frequency is 500MHz, microwave treatment time is 1min.
Embodiment tri-
Glue is made up of the raw material of following parts by weight: 28 parts of phthalic anhydrides, 11 parts of triethylene glycols, 17 parts of glutaric acids, 9 parts of butantriols, 6 parts of Zinc Oxides, 4 parts, magnesia, 18 parts of neoprenes, 85 parts of elastic plastics, 2.5 parts of softening oils, 18 parts of dimethyl carbonates, 25 parts, ethylbenzene, 2 parts of fire retardants.
Fire retardant is counted composed of the following components by weight: 40 parts of ammonium low polyphosphates, 15 parts, ammonium phosphate, 10 parts of ammonium pyrophosphates, 15 parts, ammonium sulfate, 8 parts of boric acid, 18 parts, water.
The plant material that the present embodiment bamboo charcoal preparation adopts is pine tree, ingresses after pine tree is removed to epidermis impurity, and length control is no more than 15cm.
Plant material is sent in microwave vacuum tank, and being evacuated to vacuum is-0.01～-0.005MPa, then carries out microwave treatment, and microwave frequency is 550MHz, and microwave treatment time is 1.2-2min;
To experience successively dry, pre-charing, charing, calcining and cooling through the plant material of pre-treatment gained, the temperature of each point for measuring temperature, dry section is 180 ℃, pre-char zone is 325 ℃, char zone is 530 ℃, control the combustion zone temperature experiencing in bamboo folding process, control combustion is warming up to 900 ℃ and be incubated 50min with the speed of 10 ℃/min, and then be warming up to 1600 ℃ and be incubated 5h with the speed of 10 ℃/min, then be cooled to 330-380 ℃ with the speed of 20-23 ℃/min, cool to again room temperature with the furnace, obtain elementary charcoal; Then carry out activation processing: then the Potassium Oxalate Solution that activation processing is is 9% by elementary gained charcoal with mass fraction 1:3.5 mixing submergence 4h is in mass ratio neutral by washed with de-ionized water to pH value; Then adopt vacuum pressed flame treatment, in processing procedure, first the elementary charcoal of gained after activation processing being packed into vacuum pressed tank vacuumizes and makes its vacuum for-0.02Mpa, then fire retardant is added in tank and by pressure in tank and adds to 0.6Mpa, the fire retardant of use is counted composed of the following components by weight: 30 parts of ammonium low polyphosphates, 15 parts, ammonium phosphate, 8 parts of ammonium pyrophosphates, 15 parts, ammonium sulfate, 8 parts of boric acid, 15 parts, water;
Then carry out bamboo vinegar processing, bamboo vinegar processing comprises a bamboo vinegar processing and the processing of secondary bamboo vinegar, a bamboo vinegar processing is that charcoal is immersed in to 40min in the bamboo vinegar treatment fluid of 50 ℃, the bamboo vinegar aqueous solution that bamboo vinegar treatment fluid is 30g/L, the processing of secondary bamboo vinegar is to continue charcoal to be immersed in 30min in the secondary bamboo vinegar treatment fluid of 80 ℃, secondary bamboo vinegar treatment fluid is the mixed solution of bamboo vinegar, chelating agent and the water composition of weight ratio 1:0.2:100, and wherein chelating agent is the disodium edta of 1:1 weight ratio and the mixture of ethylenediamine tetra-acetic acid;
And then carry out microwave treatment, and microwave frequency is 550～600MHz, microwave treatment time is 1.2～2min; Finally make with hydraulic press the charcoal particle that diameter is 0.5-2mm.
Negative ion powder formula: 20 parts, sea-gull stone; 10 parts of Tourmalines; 5 parts, opal; 6 parts, serpentine; 6 parts of medical stones; 6 parts, strange ice stone; 2 parts of hokutolites; 7 parts of doctor Wang Shis; 3 parts, shell; 18 parts, diatomite; 8 parts of zirconias; 6 parts of basic zirconium phosphates.
Negative ion powder preparation: described sea-gull stone, Tourmaline, opal, serpentine, medical stone, strange ice stone, hokutolite, doctor Wang Shi, shell, diatomite, zirconia and basic zirconium phosphate are mixed, ultra-fine grinding to grain diameter is 30nm, sieve, microwave treatment: microwave frequency is 650MHz, microwave treatment time is 3min.
Negative ion powder performance test of the present invention is as follows: get the negative ion powder that 500g the present invention makes and be placed in seal box, negative ion powder is evenly spread out, airtight 24 hours, with AIC-100 anion detector every 1 hour detect once, get 20 data at every turn, try to achieve the mean value of each data as final detection result, test result is in table 1.
Table 1 negative ion concentration test data table
This specific embodiment is only explanation of the invention; it is not limitation of the present invention; those skilled in the art are reading after this description and can make to the present embodiment the modification that there is no creative contribution as required, but as long as within the scope of claim of the present invention, are all subject to the protection of Patent Law.
Claims (9)
1. a health-care cushion, comprises a basic unit (1) and is arranged on the bed course (2) of described basic unit (1) top, it is characterized in that: described bed course (2) below is at least disposed with the first heath care layer (3) and the second heath care layer (4);
Described the first heath care layer (3) comprises bamboo-carbon layer (31) and tourmaline particle and/or the anion bisque (32) of interlaced arrangement; Concrete arrangement mode is that described the first heath care layer (3) top one side is bamboo-carbon layer (31), and opposite side is tourmaline particle and/or anion bisque (32); Described heath care layer (3) bottom and to be positioned under described bamboo-carbon layer (31) be tourmaline particle and/or anion bisque (32), described heath care layer (3) bottom and be positioned at described tourmaline particle and/or anion bisque (32) under be bamboo-carbon layer (31);
The flexible magnetic strips (42) that described the second heath care layer (4) comprises flexible magnet massage bead (41) and circumferentially arranges along described the second heath care layer (4), described flexible magnetic strips (42) is arranged on described basic unit (1) inside or basic unit (1) surface by elastica (43) company of wearing; Described flexible magnetic strips (42) by inlaying, mode coated or adhesion is fixed in described basic unit (1).
2. a kind of health-care cushion according to claim 1, is characterized in that: described flexible magnet massage bead (41) entirety is Tai Ji and distributes.
3. a kind of health-care cushion according to claim 2, it is characterized in that: described bed course (2) hooks face (51) and VELCRO hair side (52) by including VELCRO VELCRO (5) with described the first heath care layer (3) is removably connected, described VELCRO hooks face (51) by bonding described bed course (2) back side that is arranged on of glue, and described VELCRO hair side (52) is by bonding described the first heath care layer (3) surface that is arranged on of glue.
4. a kind of health-care cushion according to claim 4, is characterized in that: described glue is made up of the raw material of following parts by weight:
Phthalic anhydride 25-35 part, triethylene glycol 10-12 part, glutaric acid 15-18 part, butantriol 8-10 part, Zinc Oxide 5-7 part, magnesia 3-5 part, neoprene 15-25 part, elastic plastic 70-95 part, softening oil 2-3 part, dimethyl carbonate 15-20 part, ethylbenzene 20-30 part, fire retardant 1-3 part.
5. according to a kind of health-care cushion described in claim 1-4 any one, it is characterized in that: described bamboo charcoal is prepared from by following steps:
(1) raw material pre-treatment: plant material is sent in microwave vacuum tank, be evacuated to vacuum for-0.02MPa～-0.001MPa, then carry out microwave treatment, microwave frequency is 300MHz～950MHz, and microwave treatment time is 1～3min;
(2) elementary charcoal preparation: will experience successively dry, pre-charing, charing, calcining and cooling through the plant material of raw material pre-treatment gained, control combustion is warming up to 700-750 ℃ or 900-1000 ℃ and is incubated 40-80min with the speed of 5-15 ℃/min, and then be warming up to 1000-1500 ℃ or 1600-1800 ℃ and be incubated 2-8h with the speed of 5-15 ℃/min, then be cooled to 300-400 ℃ with the speed of 18-25 ℃/min, cool to again room temperature with the furnace, obtain elementary charcoal;
(3) then activation processing: the Potassium Oxalate Solution that is 8-10% with mass fraction by elementary gained charcoal is 1:3-4 mixing submergence 3-5h is in mass ratio neutral by washed with de-ionized water to pH value;
(4) dipping flame treatment: adopt vacuum pressed flame treatment, in processing procedure, first the elementary charcoal of gained after activation processing is packed into vacuum pressed tank and vacuumize and make its vacuum for-0.015MPa～-0.025MPa, then fire retardant is added in tank and by pressure to add to 0.1MPa～0.8MPa;
(5) bamboo vinegar processing: comprise a bamboo vinegar processing and the processing of secondary bamboo vinegar, a bamboo vinegar processing is that the charcoal after flame treatment is immersed in 20-40min in the bamboo vinegar treatment fluid of 40-50 ℃ by dipping, the processing of secondary bamboo vinegar is submergence 10-30min in the secondary bamboo vinegar treatment fluid of 55-80 ℃, the bamboo vinegar aqueous solution that a described bamboo vinegar treatment fluid is 20-30g/L, the mixed solution of bamboo vinegar, chelating agent and water composition that described secondary bamboo vinegar treatment fluid is weight ratio 1:0.1-0.2:60-100;
(6) microwave treatment: bamboo vinegar is processed to gained material and carry out microwave treatment, microwave frequency is 500～650MHz, and microwave treatment time is 1～3min;
(7) carbon granule preparation: the material after microwave treatment is made to the charcoal particle that diameter is 0.5-2mm with pulverizer or hydraulic press.
6. a kind of health-care cushion according to claim 5, is characterized in that: described step (1) plant material is corncob, bamboo or pine tree.
7. according to a kind of health-care cushion described in claim 1-4 any one, it is characterized in that: described negative ion powder is made up of following components in mass portion: sea-gull stone 15-20 part; Tourmaline 5-10 part; Opal 30-35 part; Serpentine 2-6 part; Medical stone 4-6 part; Strange ice stone 4-6 part; Hokutolite 1-2 part; Doctor Wang Shi 5-7 part; Shell 1-3 part; Diatomite 12-18 part; Zirconia 5-8 part; Basic zirconium phosphate 4-6 part.
8. a kind of health-care cushion according to claim 7, it is characterized in that: described sea-gull stone, Tourmaline, opal, serpentine, medical stone, strange ice stone, hokutolite, doctor Wang Shi, shell, diatomite, zirconia and basic zirconium phosphate are mixed, ultra-fine grinding to grain diameter is 15-30nm, sieve, microwave treatment.
9. a kind of health-care cushion according to claim 8, is characterized in that: microwave frequency is 500～650MHz, and microwave treatment time is 1～3min.