CN103881526A - Efficient anticorrosive coating - Google Patents
Efficient anticorrosive coating Download PDFInfo
- Publication number
- CN103881526A CN103881526A CN201210565289.2A CN201210565289A CN103881526A CN 103881526 A CN103881526 A CN 103881526A CN 201210565289 A CN201210565289 A CN 201210565289A CN 103881526 A CN103881526 A CN 103881526A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- coating
- anticorrosive coating
- kerosene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an efficient anticorrosive coating. The efficient anticorrosive coating comprises, by weight, 30-60 parts of epoxy resin, 5-10 parts of butyl rubber, 10-15 parts of a fire retardant, 1-2 parts of dimethyl ethanolamine, 10-20 parts of sodium silicate, 10-15 parts of a thickening agent, 5-10 parts of bentonite, 1-3 parts of butyl latex and 10-15 parts of deionized water. A coat obtained by using the coating has no changes after the coat is immersed in a mixed solution of acid, alkali, brine solution, gasoline, kerosene, diesel oil and water at normal temperature for a long term. The coating has a long service life, can be widely applied to the inner walls of oil tanks of crude oil, kerosene, gasoline and the like, and oil convey pipelines, and is also suitable for the anticorrosion of chemical industry equipment and the inner walls of pipelines.
Description
Technical field
The present invention relates to a kind of high-efficiency anticorrosive paint.
Background technology
The common conduction Antistatic Paint of the anticorrosion general use of inner wall of petroleum storage tank at present, it is quiet that it efficiently solves petroleum products
The leakage problem of electric charge, has stopped petroleum static electricity fire outburst accident, the corrosion that has alleviated equipment.But, along with petroleum products
The development of storing technology, oil static electricity conductive anticorrosive paint in use also exposes some fatal weakness, has affected use.
Its weakness is to meet fiery easy firing, and water tolerance is poor, petroleum storage tank bottom seriously corroded.Be not suitable for petroleum tank, crude oil is from underground
While exploiting out, be a kind of oil-water mixture, the inwall of petroleum storage tank is had to strong corrosive nature.General static coating bubbled or comes off in several days to two months.
Summary of the invention
The deficiency existing for prior art, technical problem to be solved by this invention is, provide one be applicable to metallic oil tank and pipe laying inwall have fire-retardant, lead the good combination properties such as static, heatproof, oil resistant, resistant to chemical media, cost is low, easy construction, long service life, safe and reliable high-efficiency anticorrosive paint.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of high-efficiency anticorrosive paint, is grouped into by the one-tenth of following weight part:
Epoxy resin 30～60;
Isoprene-isobutylene rubber 5～10;
Fire retardant 10～15;
Dimethylethanolamine 1～2;
Water glass 10～20;
Thickening material 10～15;
Wilkinite 5～10;
Butyl latex 1～3;
Deionized water 10～15.
The advantage of high-efficiency anticorrosive paint of the present invention is: the long-term immersion in the mixed solution of normal temperature acid, alkali, salts solution, gasoline, kerosene, diesel oil, water of this coating is unchanged.Long service life, can be widely used in storage tank and the pipe laying inwalls such as crude oil, kerosene, gasoline, also applicable to the inner wall anti-corrosive of chemical industry equipment, pipeline.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further details;
A kind of high-efficiency anticorrosive paint, is grouped into by the one-tenth of following weight part:
Epoxy resin 30～60;
Isoprene-isobutylene rubber 5～10;
Fire retardant 10～15;
Dimethylethanolamine 1～2;
Water glass 10～20;
Thickening material 10～15;
Wilkinite 5～10;
Butyl latex 1～3;
Deionized water 10～15.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, variation, remodeling, interpolation or the replacement made, all should belong to protection scope of the present invention.
Claims (1)
1. a high-efficiency anticorrosive paint, is characterized in that, is grouped into by the one-tenth of following weight part:
Epoxy resin 30～60;
Isoprene-isobutylene rubber 5～10;
Fire retardant 10～15;
Dimethylethanolamine 1～2;
Water glass 10～20;
Thickening material 10～15;
Wilkinite 5～10;
Butyl latex 1～3;
Deionized water 10～15.