A kind of antibacterial makrolon composite plastic
Technical field
The invention belongs to plastic applications, specifically a kind of antibacterial makrolon composite plastic.
Background technology
Antibiotic plastic be a class in environment for use itself to stain bacterium on plastics, mould, the female bacterium of alcohol, algae even virus etc. rise and suppress or the plastics of killing action, keep itself clean by suppressing the breeding of microorganism.At present, antibiotic plastic obtains mainly through the method for adding a small amount of antiseptic-germicide in common plastics.Prior art antibiotic plastic antibacterial effect is undesirable, and antiseptic-germicide addition is comparatively large, and cost is higher.
Summary of the invention
The object of the present invention is to provide a kind of antibacterial makrolon composite plastic.
Object of the present invention can be achieved through the following technical solutions:
A kind of antibacterial makrolon composite plastic, it is characterized in that, these antibacterial carbonic ether plastics are made up of the feed composition of following weight part: polycarbonate 100-120 part, polyethylene terephthalate 50-60 part, chitosan 5-8 part, dispersion agent 0.1-0.5 part, nano titanium oxide 10-15 part, quaternary ammonium salt 5-7 part, oxidation inhibitor 1-2 part, compatilizer 0.2-0.6 part, coupling agent 0.3-0.7 part.
As preferred further, these antibacterial carbonic ether plastics are made up of the feed composition of following weight part: polycarbonate 110 parts, polyethylene terephthalate 55 parts, chitosan 6.5 parts, dispersion agent 0.3 part, nano titanium oxide 12 parts, quaternary ammonium salt 6 parts, 1.5 parts, oxidation inhibitor, compatilizer 0.4 part, coupling agent 0.5 part.
Oxidation inhibitor of the present invention is antioxidant 1010, and described coupling agent is silane coupling agent.
Beneficial effect of the present invention: the present invention adopts nano-titanium oxide and quaternary ammonium salt to be antiseptic-germicide, nano titanium oxide good dispersity, has stronger adsorption to microorganism, the adsorbable electronegative bacterium of quaternary ammonium salt antiseptic-germicide, cause cell wall structure to damage, content is exposed and kills bacterium; Antibacterial range is wide, and antiseptic-germicide usage quantity is few, good anti-bacterial effect.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further detail.
In specific embodiment of the invention 1-3, oxidation inhibitor is antioxidant 1010, and coupling agent is silane coupling agent.
Embodiment 1
A kind of antibacterial makrolon composite plastic, these antibacterial carbonic ether plastics are made up of the feed composition of following weight part: polycarbonate 110 parts, polyethylene terephthalate 55 parts, chitosan 6.5 parts, dispersion agent 0.3 part, nano titanium oxide 12 parts, quaternary ammonium salt 6 parts, 1.5 parts, oxidation inhibitor, compatilizer 0.4 part, coupling agent 0.5 part.
Embodiment 2
A kind of antibacterial makrolon composite plastic, these antibacterial carbonic ether plastics are made up of the feed composition of following weight part: polycarbonate 120 parts, polyethylene terephthalate 50 parts, chitosan 5 parts, dispersion agent 0.5 part, nano titanium oxide 15 parts, quaternary ammonium salt 7 parts, 2 parts, oxidation inhibitor, compatilizer 0.6 part, coupling agent 0.7 part.
Embodiment 3
A kind of antibacterial makrolon composite plastic, these antibacterial carbonic ether plastics are made up of the feed composition of following weight part: polycarbonate 100 parts, polyethylene terephthalate 60 parts, chitosan 8 parts, dispersion agent 0.1 part, nano titanium oxide 10 parts, quaternary ammonium salt 5 parts, 1 part, oxidation inhibitor, compatilizer 0.2 part, coupling agent 0.3 part.