CN103880366A - Low-water-absorption cement-based joint filling agent - Google Patents

Low-water-absorption cement-based joint filling agent Download PDF

Info

Publication number
CN103880366A
CN103880366A CN201310556564.9A CN201310556564A CN103880366A CN 103880366 A CN103880366 A CN 103880366A CN 201310556564 A CN201310556564 A CN 201310556564A CN 103880366 A CN103880366 A CN 103880366A
Authority
CN
China
Prior art keywords
filling agent
parts
joint filling
spackling
low water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310556564.9A
Other languages
Chinese (zh)
Inventor
沈廉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Southeast University
Original Assignee
Southeast University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Southeast University filed Critical Southeast University
Priority to CN201310556564.9A priority Critical patent/CN103880366A/en
Publication of CN103880366A publication Critical patent/CN103880366A/en
Pending legal-status Critical Current

Abstract

The invention discloses a low-water-absorption cement-based joint filling agent, which comprises the following components in parts by weight: 40-60 parts of hydraulic cementing materials, 10-20 parts of mineral admixture, 5-8 parts of antioxidant 1010, 1-3 parts of 107 organic silicon rubber and 3-5 parts of tackifier. According to the invention, since 107 organic silicon rubber is added into the basic formula of the tile-seam filling agent, the hydrophobicity and hydrophobicity transfer of the joint filling agent can effectively be enhanced; therefore, the joint filling agent has a self-cleaning performance, hardly causes dust attachment, the use effect of the joint filling agent is ensured; due to use of the antioxidant 1010, oxidization capability of the joint filling agent is strengthened, the service life of the joint filling agent is prolonged, and the replacement cost is reduced.

Description

A kind of low water absorbable cement based spackling
Technical field
The present invention relates to a kind of tile grout, especially relate to a kind of tile grout of low water absorbable, belong to spackling technical field.
Background technology
Traditional tile grout, because the hydrophobic nature of its formula is not strong, therefore dust is very easy to be adsorbed on the surface of spackling, makes its self-cleaning not strong, easily dirty, not only affects attractive in appearancely, but also has increased the cost that need to again construct.
Summary of the invention
In order to overcome the deficiencies in the prior art, the object of the present invention is to provide the low water absorbable cement based spackling that high, the antifouling ability of a kind of self-cleaning is strong.
The present invention is achieved through the following technical solutions:
A kind of low water absorbable cement based spackling, is characterized in that, comprises that the parts by weight of following component and each component are:
Hydraulicity gelatinous material: 40-60 part;
Mineral admixture: 10-20 part;
Antioxidant 1010: 5-8 part;
107 organo-silicone rubbers: 1-3 part;
Tackifier: 3-5 part.
Further, described hydraulicity gelatinous material is silicate cement.
And, strength grade >=42.5 of described silicate cement
And described described mineral admixture is silicon ash or flyash.
In addition described tackifier are γ-aminopropyl triethoxysilane.
The invention has the beneficial effects as follows: the present invention is by the basic components of tile grout, increase by 107 organo-silicone rubbers, can effectively strengthen hydrophobic nature and the migration of hydrophobicity of spackling, therefore make spackling there is self-cleaning property, be difficult for adhesive dust, guaranteed the result of use of spackling; Meanwhile, the application of antioxidant 1010, makes spackling resistance of oxidation strong, has extended its work-ing life, has saved replacement cost.
Embodiment
Below in conjunction with specific embodiment, describe the specific embodiment of the present invention in detail:
Embodiment 1:
Low water absorbable cement based spackling, comprises that the parts by weight of following component and each component are: silicate cement: 40g; Mineral admixture silicon ash: 10g; Antioxidant 1010: 8g; 107 organo-silicone rubber 1g; γ-aminopropyl triethoxysilane: 5g.In the present embodiment, strength grade >=42 of described silicate cement.
Embodiment 2:
Low water absorbable cement based spackling, comprises that the parts by weight of following component and each component are: silicate cement: 60g; Coal ash: 20g; Antioxidant 1010: 5g; 107 organo-silicone rubbers: 3g; γ-aminopropyl triethoxysilane: 3g.In the present embodiment, strength grade >=42 of described silicate cement.
Embodiment 3:
Low water absorbable cement based spackling, comprises that the parts by weight of following component and each component are: silicate cement: 50g; Coal ash: 15g; Antioxidant 1010: 6g; 107 organo-silicone rubbers: 2g; γ-aminopropyl triethoxysilane: 4g.In the present embodiment, strength grade >=42 of described silicate cement.
The present invention, by the basic components of tile grout, increases by 107 organo-silicone rubbers, can effectively strengthen hydrophobic nature and the migration of hydrophobicity of spackling, therefore makes spackling have self-cleaning property, is difficult for adhesive dust, has guaranteed the result of use of spackling; Meanwhile, the application of antioxidant 1010, makes spackling resistance of oxidation strong, has extended its work-ing life, has saved replacement cost.
Below disclose the present invention with preferred embodiment, so it is not intended to limiting the invention, and all employings are equal to replaces or the technical scheme that obtains of equivalent transformation mode, within all dropping on protection scope of the present invention.

Claims (5)

1. a low water absorbable cement based spackling, is characterized in that, comprises that the parts by weight of following component and each component are:
Hydraulicity gelatinous material: 40-60 part;
Mineral admixture: 10-20 part;
Antioxidant 1010: 5-8 part;
107 organo-silicone rubbers: 1-3 part;
Tackifier: 3-5 part.
2. a kind of low water absorbable cement based spackling according to claim 1, is characterized in that, described hydraulicity gelatinous material is silicate cement.
3. a kind of low water absorbable cement based spackling according to claim 2, is characterized in that strength grade >=42.5 of described silicate cement.
4. a kind of low water absorbable cement based spackling according to claim 1, is characterized in that, described described mineral admixture is silicon ash or flyash.
5. a kind of low water absorbable cement based spackling according to claim 3, is characterized in that, described tackifier are γ-aminopropyl triethoxysilane.
CN201310556564.9A 2013-11-11 2013-11-11 Low-water-absorption cement-based joint filling agent Pending CN103880366A (en)