CN103866650A - High-temperature-resistant paper and preparation process thereof - Google Patents
High-temperature-resistant paper and preparation process thereof Download PDFInfo
- Publication number
- CN103866650A CN103866650A CN201410114556.3A CN201410114556A CN103866650A CN 103866650 A CN103866650 A CN 103866650A CN 201410114556 A CN201410114556 A CN 201410114556A CN 103866650 A CN103866650 A CN 103866650A
- Authority
- CN
- China
- Prior art keywords
- resistant paper
- density polyethylene
- temperature resistant
- high temperature
- particle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses high-temperature-resistant paper which is prepared from the following raw materials in parts by weight of dry substances: 70-100 parts of low-density polyethylene plastic particles, 10-50 parts of high-density polyethylene plastic particles, 1-5 parts of brominated flame retardants, 3-10 parts of hot melt glue and 2-5 parts of stabilizers. The invention also discloses a preparation process of the high-temperature resistant paper. Given the shortcomings of the original technology, the density of the low-density polyethylene is increased, and the coating density is increased along; and therefore, the water vapor transmission rate is reduced, the brightness, stiffness and tensile strength of the flame retardant paper are improved, high-quality flame retardant paper is obtained, and customers are highly satisfied.
Description
Technical field
The present invention relates to film technical field, be specifically related to a kind of high temperature resistant paper and preparation technology thereof.
Background technology
Existing film process using LEPD directly drenches on paper by film machine film head high temperature melt, airtight paper space firmly, be then coated with silicon, no problem qualitatively, but brightness ratio is dimer in appearance, and feel deflection is inadequate, heat resistance is not fine, and flame retardant effect is not good.
Summary of the invention
Goal of the invention: in order to overcome the deficiencies in the prior art, the invention provides high temperature resistant paper and the preparation technology thereof of a kind of high brightness, high-stiffness, high-tensile, good flame retardation effect.
For achieving the above object, the technical solution used in the present invention is: a kind of high temperature resistant paper, comprises that by dry matter weight umber following raw material makes: LDPE (Low-density polyethylene plastics) particle 70-100 part, high-density polyethylene plastics particle 10-50 part, bromide fire retardant 1-5 part, hot melt adhesive 3-10 part, stabilizing agent 2-5 part.
Wherein, above-mentioned LDPE (Low-density polyethylene plastics) particle is LDPE IC7A.
Wherein, above-specified high density vinyon particle is HDPE 80064.
Wherein, above-mentioned bromide fire retardant is one or more in PBDEs, tetrabromobisphenol A or hexabromo-Cyclododecane.
Wherein, aforementioned stable agent is mercaptan tin octylate 17MOK.
A preparation technology for high temperature resistant paper, comprises the following steps:
1), by LDPE (Low-density polyethylene plastics) particle and high-density polyethylene plastics mix particles, stir with mixer;
2) in step 1), add bromide fire retardant, hot melt adhesive, stabilizing agent, 500-1800 rev/min of stirring is heated to 135-150 ℃ simultaneously and obtains membrane coating material again;
3) membrane coating material is obtained to high temperature resistant paper by film machine die head co-extrusion in fire retardant papers, co-extrusion temperature is 240 ~ 300 ℃, and back pressure is 500pa ~ 1000pa, and co-extrusion speed is 110 ~ 130m/min.
Above-mentioned steps 1) LDPE (Low-density polyethylene plastics) particle and high-density polyethylene plastics mass particle be than being 7:3.
Above-mentioned steps 3) to be applied to high temperature resistant paper one side amount be 16-20g/ ㎡ for membrane coating material that fire retardant papers is carried out to film.
Beneficial effect: the present invention has the following advantages: the present invention is directed to the deficiency in original technical matters, increase the density of low density polyethylene (LDPE), thereby be coated with film density also increases thereupon, therefore water vapor transmittance reduces, brightness, deflection and the tensile strength of fire retardant papers are improved, obtain high-quality fire retardant papers, obtained client's high satisfaction.By improving raw material and technique, paper flame retardant effect and stability are all greatly improved simultaneously.
The specific embodiment
Below in conjunction with the specific embodiment, the present invention is further illustrated.
What LDPE of the present invention adopted is the Yanshan Mountain, Beijing LDPE IC7A plastic pellet, and what HDPE of the present invention adopted is HDPE 80064 plastic pellets in the Yanshan Mountain, Beijing.
Embodiment 1:
A kind of high temperature resistant paper, comprises that by dry matter weight umber following raw material makes: 70 parts, LDPE (Low-density polyethylene plastics) particle, 30 parts, high-density polyethylene plastics particle, 1 part of bromide fire retardant, 3 parts of hot melt adhesive, 2 parts of stabilizing agents.
A preparation technology for high temperature resistant paper, comprises the following steps:
LDPE (Low-density polyethylene plastics) particle LDPE IC7A is mixed take mass ratio as 7:3 with high-density polyethylene plastics particle HDPE 80064, stir with mixer; Add bromide fire retardant, hot melt adhesive, stabilizing agent, 500 revs/min of stirrings are heated to 135 ℃ simultaneously and obtain membrane coating material again; Membrane coating material is obtained to high temperature resistant paper by film machine die head co-extrusion in fire retardant papers, and co-extrusion temperature is 240 ℃, and back pressure is 500pa, and co-extrusion speed is 110m/min.Wherein, it is 16g/ ㎡ that the membrane coating material that fire retardant papers is carried out to film is applied to high temperature resistant paper one side amount.
Embodiment 2:
A kind of high temperature resistant paper, comprises that by dry matter weight umber following raw material makes: 100 parts, LDPE (Low-density polyethylene plastics) particle, 50 parts, high-density polyethylene plastics particle, 5 parts of bromide fire retardants, 10 parts of hot melt adhesive, 5 parts of stabilizing agents.
A preparation technology for high temperature resistant paper, comprises the following steps:
LDPE (Low-density polyethylene plastics) particle LDPE IC7A is mixed take mass ratio as 2:1 with high-density polyethylene plastics particle HDPE 80064, stir with mixer; Add bromide fire retardant, hot melt adhesive, stabilizing agent, 1000 revs/min of stirrings are heated to 145 ℃ simultaneously and obtain membrane coating material again; Membrane coating material is obtained to high temperature resistant paper by film machine die head co-extrusion in fire retardant papers, and co-extrusion temperature is 270 ℃, and back pressure is 7500pa, and co-extrusion speed is 120m/min.Wherein, it is 18g/ ㎡ that the membrane coating material that fire retardant papers is carried out to film is applied to high temperature resistant paper one side amount.
Embodiment 3:
A kind of high temperature resistant paper, comprises that by dry matter weight umber following raw material makes: 80 parts, LDPE (Low-density polyethylene plastics) particle, 10 parts, high-density polyethylene plastics particle, 3 parts of bromide fire retardants, 6 parts of hot melt adhesive, 3 parts of stabilizing agents.
A preparation technology for high temperature resistant paper, comprises the following steps:
LDPE (Low-density polyethylene plastics) particle LDPE IC7A is mixed take mass ratio as 8:1 with high-density polyethylene plastics particle HDPE 80064, stir with mixer; Add bromide fire retardant, hot melt adhesive, stabilizing agent, 1800 revs/min of stirrings are heated to 150 ℃ simultaneously and obtain membrane coating material again; Membrane coating material is obtained to high temperature resistant paper by film machine die head co-extrusion in fire retardant papers, and co-extrusion temperature is 300 ℃, and back pressure is 1000pa, and co-extrusion speed is 130m/min.Wherein, it is 20g/ ㎡ that the membrane coating material that fire retardant papers is carried out to film is applied to high temperature resistant paper one side amount.
Mass parameter is as follows after testing for the high temperature resistant paper of the embodiment of the present invention 1 ~ 3:
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (8)
1. a high temperature resistant paper, it is characterized in that, comprise that by dry matter weight umber following raw material makes: LDPE (Low-density polyethylene plastics) particle 70-100 part, high-density polyethylene plastics particle 10-50 part, bromide fire retardant 1-5 part, hot melt adhesive 3-10 part, stabilizing agent 2-5 part.
2. the high temperature resistant paper of one according to claim 1, is characterized in that, described LDPE (Low-density polyethylene plastics) particle is LDPE IC7A.
3. the high temperature resistant paper of one according to claim 1, is characterized in that, described high-density polyethylene plastics particle is HDPE 80064.
4. the high temperature resistant paper of one according to claim 1, is characterized in that, described bromide fire retardant is one or more in PBDEs, tetrabromobisphenol A or hexabromo-Cyclododecane.
5. the high temperature resistant paper of one according to claim 1, is characterized in that, described stabilizing agent is mercaptan tin octylate 17MOK.
6. the preparation technology of a kind of high temperature resistant paper described in claim 1 ~ 5 any one, is characterized in that, comprises the following steps:
1), by LDPE (Low-density polyethylene plastics) particle and high-density polyethylene plastics mix particles, stir with mixer;
2) in step 1), add bromide fire retardant, hot melt adhesive, stabilizing agent, 500-1800 rev/min of stirring is heated to 135-150 ℃ simultaneously and obtains membrane coating material again;
3) membrane coating material is obtained to high temperature resistant paper by film machine die head co-extrusion in fire retardant papers, co-extrusion temperature is 240 ~ 300 ℃, and back pressure is 500pa ~ 1000pa, and co-extrusion speed is 110 ~ 130m/min.
7. the preparation technology of high temperature resistant paper according to claim 6, is characterized in that, described step 1) LDPE (Low-density polyethylene plastics) particle is 7:3 with high-density polyethylene plastics mass particle ratio.
8. the preparation technology of high temperature resistant paper according to claim 6, is characterized in that, it is 16-20g/ ㎡ that the membrane coating material that described step 3) is carried out film to fire retardant papers is applied to high temperature resistant paper one side amount.