CN103862830A - Producing method of waterproof warm-keeping coral fleece composite fabric - Google Patents
Producing method of waterproof warm-keeping coral fleece composite fabric Download PDFInfo
- Publication number
- CN103862830A CN103862830A CN201210546780.0A CN201210546780A CN103862830A CN 103862830 A CN103862830 A CN 103862830A CN 201210546780 A CN201210546780 A CN 201210546780A CN 103862830 A CN103862830 A CN 103862830A
- Authority
- CN
- China
- Prior art keywords
- coral fleece
- coral
- film
- fleece blanket
- blanket fabrics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a producing method of waterproof warm-keeping coral fleece composite fabric. Coral fleece fabric produced by using ultrafine polyester low-stretch yarn as a raw material is preferably adopted. The method includes: a step of cleaning, finishing and setting the coral fleece fabric; a step of selecting a composite material that is preferably thermoplastic polyurethane (TPU) film having a thickness of 0.015 mm; a step of coating the film with glue by adoption of a coating method of rubber dots and a rubber roll, then preheating the film; and a step of subjecting the coral fleece fabric and the TPU film to thermocompression bonding, and cooling to obtain a finished product. The preheating temperature of the film is 30-40 DEG C. The thermocompression bonding temperature is 70 DEG C and the thermocompression bonding pressure is 5.5 KPa. The composite fabric is fine in texture, soft in handfeel, nonirritating to skin, free of allergy, waterproof and warm-keeping.
Description
Technical field
The invention belongs to cloth processing technology field, be specifically related to a kind of production method of thermal insulating and water-proof coral suede composite material-feeding.
Background technology
Coral suede be a kind of colorful, spreadability is good is coralloid fabric fabric, there is quality exquisiteness, soft, do not fall hair, not balling-up, do not fade and to skin without any stimulation, not irritated feature, is in recent years and spins industry and more and more favored, be received by the market, just progressively replace at present traditional bedding.Coral flannelette material carries out deep processing, becomes functional cloth, is the trend of following coral flannelette material development.
Summary of the invention
The above-mentioned technical problem existing in order to overcome prior art field, the object of the invention is to, and a kind of production method of thermal insulating and water-proof coral suede composite material-feeding is provided, technique is simple, and gained composite material-feeding quality exquisiteness is soft, not balling-up, does not fade, waterproof, warming.
The production method of thermal insulating and water-proof coral suede composite material-feeding provided by the invention, comprises the following steps:
(1) coral fleece blanket fabrics, the coral fleece blanket fabrics of preferably producing as raw material taking terylene super fine low stretch yarn fiber;
(2) coral fleece blanket fabrics processing, clears up coral fleece blanket fabrics, repair, shape;
(3) select composite, preferably the thermoplastic polyurethane TPU film of 0.015mm;
(4) film processing, adopts the coating method of glue point rubber roll to the gluing of TPU film, carries out the pre-heat treatment after gluing;
(5) coral fleece blanket fabrics and TPU film are carried out to hot pressing, the cooling finished product that obtains afterwards.
Described film preheat temperature is 30～40 DEG C, and hot pressing temperature is 70 DEG C, and pressure is 5.5Kpa..
The production method of thermal insulating and water-proof coral suede composite material-feeding provided by the invention, its beneficial effect is, the coral fleece blanket fabrics of preferably producing as raw material taking terylene super fine low stretch yarn fiber, quality exquisiteness, soft, without any stimulation, not irritated to skin; The preferably thermoplastic polyurethane TPU film of 0.015mm, environment-protecting asepsis, antimildew and antibacterial and recyclable degraded, breathable moisture permeability is good; Reasonably preheat temperature and pressure, guarantee that material property is good; Have good washing fastness, the washing of 60 DEG C can be washed 40 times, still can have good performance.
Detailed description of the invention
Below in conjunction with an embodiment, the production method of thermal insulating and water-proof coral suede composite material-feeding provided by the invention is described in detail.
Embodiment
The production method of the thermal insulating and water-proof coral suede composite material-feeding of the present embodiment, comprises the following steps:
(1) coral fleece blanket fabrics, the coral fleece blanket fabrics of preferably producing as raw material taking terylene super fine low stretch yarn fiber;
(2) coral fleece blanket fabrics processing, clears up coral fleece blanket fabrics, repair, shape;
(3) select composite, preferably the thermoplastic polyurethane TPU film of 0.015mm;
(4) film processing, adopts the coating method of glue point rubber roll to the gluing of TPU film, carries out the pre-heat treatment after gluing;
(5) coral fleece blanket fabrics and TPU film are carried out to hot pressing, the cooling finished product that obtains afterwards.
Described film preheat temperature is 30～40 DEG C, and hot pressing temperature is 70 DEG C, and pressure is 5.5Kpa.
Claims (2)
1. a production method for thermal insulating and water-proof coral suede composite material-feeding, is characterized in that comprising the following steps:
Select coral fleece blanket fabrics, the coral fleece blanket fabrics of preferably producing as raw material taking terylene super fine low stretch yarn fiber;
Coral fleece blanket fabrics processing, clears up coral fleece blanket fabrics, repair, shape;
Select composite, preferably the thermoplastic polyurethane TPU film of 0.015mm;
Film processing, adopts the coating method of glue point rubber roll to the gluing of TPU film, carries out the pre-heat treatment after gluing;
Coral fleece blanket fabrics and TPU film are carried out to hot pressing, the cooling finished product that obtains afterwards.
2. the production method of thermal insulating and water-proof coral suede composite material-feeding according to claim 1, is characterized in that: described film preheat temperature is 30～40 DEG C, hot pressing temperature is 70 DEG C, and pressure is 5.5Kpa.