CN103862825A - Production method of moisture-absorbing quick-drying composite fabric - Google Patents
Production method of moisture-absorbing quick-drying composite fabric Download PDFInfo
- Publication number
- CN103862825A CN103862825A CN201210546482.1A CN201210546482A CN103862825A CN 103862825 A CN103862825 A CN 103862825A CN 201210546482 A CN201210546482 A CN 201210546482A CN 103862825 A CN103862825 A CN 103862825A
- Authority
- CN
- China
- Prior art keywords
- fabric
- moisture
- quilting
- cloth
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method of moisture-absorbing quick-drying composite fabric. According to the production method, ultrahigh molecular weight polyethylene yarn is taken as suture line; composite fabric is made from bird eye quilting cloth, silk floss, and non-woven fabric; the composite fabric is washed with cold water and hot water, and is subjected to coating treatment so as to obtain coated fabric; the coated fabric is subjected to finish processing, silk floss is sandwiched by bird eye quilting cloth and non-woven fabric for layering processing, and then an obtained product is subjected to cutting, edge covering, and sparse quilting so as to obtain moisture-absorbing quilting cloth; a waterproof layer thin film is subjected to gluing preheat, and the moisture-absorbing quilting cloth and the waterproof layer thin film are subjected to hotpressing using combination machine, and the moisture-absorbing quick-drying composite fabric is obtained after cooling, wherein TPU thin film with a thickness of 0.015mm is selected as the waterproof layer thin film preferably. The production method is simple, and is suitable for batch production; the moisture-absorbing quick-drying composite fabric is light and soft, is capable of absorbing moisture, can be dried quickly, and is comfortable for using.
Description
Technical field
The invention belongs to cloth processing technology field, be specifically related to a kind of production method of hydroscopic fast-drying composite material-feeding.
Background technology
It is neat that quilting cloth has stitch, whole structure is attractive in appearance, the feature of good hand touch, and the water suction fast of bird eye fabric fabric, water delivery, diffusion and volatilization, relation between self-control underclothes and skin surface between moisture and humidity, pressure or tactility etc. when clothing and skin contact, thus dry and comfortable, the comfortableness of maintenance skin are the first-selections of fabric for sportswear.At present, changeable along with scientific and technical development and people's life requirement, Multifunction fabric becomes new demand.
Summary of the invention
Process in order to overcome prior art field cloth the above-mentioned technical problem existing, the object of the invention is to, a kind of production method of hydroscopic fast-drying composite material-feeding is provided, technique is simple, and cloth is attractive in appearance, good hand touch, and there is specific Moisture absorbing & quick drying property.
The production method of hydroscopic fast-drying composite material-feeding provided by the invention, comprises the following steps:
1) Compound Fabric suture is prepared: employing ultrahigh molecular weight polyethylene yarn is suture;
2) Compound Fabric fabric is selected: Compound Fabric fabric comprises bird's eye quilting cloth, silk floss and nonwoven;
3) fabric arranges: 3 kinds of fabrics described in step 2 are carried out to hot water or cold water's cleaning, then through coating processing, obtain the coat side bed of material;
4) compound laying: after 3 kinds of fabrics arrange, silk floss is placed between bird's eye quilting cloth and nonwoven layer of cloth, carries out laying;
5), by the fabric cutting after above-mentioned laying, bound edge, sparse quilting, obtain moisture absorption quilting cloth;
6) watertight composition pressing, preferably the thick TPU film of 0.015mm is watertight composition, by the preheating of TPU film gluing, carries out hot pressing with gained moisture absorption quilting cloth by compounding machine, after hot pressing is cooling, obtains hydroscopic fast-drying composite material-feeding.
The production method of hydroscopic fast-drying composite material-feeding provided by the invention, its beneficial effect is, preparation method is simple, is applicable to batch production; Compound Fabric fabric comprises bird's eye quilting cloth, silk floss and nonwoven, guarantees that Compound Fabric light weight, softness, hydroscopic fast-drying, the use of producing are comfortable; Adopting TPU film is watertight composition, wear-resisting, resistance toly subdues, low temperature resistant antimildew and antibacterial recyclable degraded.
Detailed description of the invention
Below in conjunction with an embodiment, the production method of hydroscopic fast-drying composite material-feeding provided by the invention is described in detail.
Embodiment
The production method of the hydroscopic fast-drying composite material-feeding of the present embodiment, comprises the following steps:
1) Compound Fabric suture is prepared: employing ultrahigh molecular weight polyethylene yarn is suture;
2) Compound Fabric fabric is selected: Compound Fabric fabric comprises bird's eye quilting cloth, silk floss and nonwoven;
3) fabric arranges: 3 kinds of fabrics described in step 2 are carried out to hot water or cold water's cleaning, then through coating processing, obtain the coat side bed of material;
4) compound laying: after 3 kinds of fabrics arrange, silk floss is placed between bird's eye quilting cloth and nonwoven layer of cloth, carries out laying;
5), by the fabric cutting after above-mentioned laying, bound edge, sparse quilting, obtain moisture absorption quilting cloth;
6) watertight composition pressing, preferably the thick TPU film of 0.015mm is watertight composition, by the preheating of TPU film gluing, carries out hot pressing with gained moisture absorption quilting cloth by compounding machine, after hot pressing is cooling, obtains hydroscopic fast-drying composite material-feeding.
Claims (1)
1. a production method for hydroscopic fast-drying composite material-feeding, is characterized in that comprising the following steps:
1) Compound Fabric suture is prepared: employing ultrahigh molecular weight polyethylene yarn is suture;
2) Compound Fabric fabric is selected: Compound Fabric fabric comprises bird's eye quilting cloth, silk floss and nonwoven;
3) fabric arranges: 3 kinds of fabrics described in step 2 are carried out to hot water or cold water's cleaning, then through coating processing, obtain the coat side bed of material;
4) compound laying: after 3 kinds of fabrics arrange, silk floss is placed between bird's eye quilting cloth and nonwoven layer of cloth, carries out laying;
5), by the fabric cutting after above-mentioned laying, bound edge, sparse quilting, obtain moisture absorption quilting cloth;
6) watertight composition pressing, preferably the thick TPU film of 0.015mm is watertight composition, by the preheating of TPU film gluing, carries out hot pressing with the common quilting cloth of gained by compounding machine, after hot pressing is cooling, obtains hydroscopic fast-drying composite material-feeding.