CN103849240A - Method for processing watercolor pencil leads of wax pencils - Google Patents
Method for processing watercolor pencil leads of wax pencils Download PDFInfo
- Publication number
- CN103849240A CN103849240A CN201210510168.8A CN201210510168A CN103849240A CN 103849240 A CN103849240 A CN 103849240A CN 201210510168 A CN201210510168 A CN 201210510168A CN 103849240 A CN103849240 A CN 103849240A
- Authority
- CN
- China
- Prior art keywords
- wax
- retractable pencil
- watercolor
- clay
- working method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for processing watercolor pencil leads of wax pencils. The method is characterized by comprising the following steps: (1) using first class talcum powder of 2000 mesh and wet clay as main materials for later use; (2) adding 40-55kg of water soluble wax, 25-35kg of polymeric wax, 15-20kg of pigment, 5-10kg of titanium dioxide, 15-20kg of magnesium stearate and 5-10kg of EVA hot melt adhesive in 110kg of main materials; (3) evenly stirring the materials of step (2); (4) grinding the kneaded material in a stone rolling machine for 3-4 hours; (5) storing the grinded material in a storage tank for 72 hours; (6) putting the material of the step (5) in a pencil lead pressing machine to press watercolor pencil leads with specifications of phi 5.0. The method has the positive effects that the process is simplified and improved on the basis of the existing manufacturing process and no machine equipment is improved, so that the process can be directly applied to the existing manufacturing process, and is simple and feasible.
Description
Technical field
The present invention relates to pencil manufacture field, relate in particular to a kind of wax crayon watercolor lead for retractable pencil working method.
Background technology
Existing watercolor pencil shortcoming is that moisture is inhomogeneous, excessively unnatural, and dichromatism is bad mediation together, and the moisture that the time of adding has been grown in the watercolor shaft of a writing brush is easy to kill, so be generally applicable to picture children's stories, be grown up and have the people of foundation of painting to use.
Summary of the invention
The object of the invention is the defect for prior art, provides for the deficiencies in the prior art.The invention provides a kind of watercolor lead for retractable pencil working method, its objective is and utilize existing pencil processing technology, with talcum powder, clay is raw material, through other materials batching, produces a kind of watercolor lead for retractable pencil, realize the transformation of pencil high added value, for the deep processing of pencil creates direction.
The present invention is achieved through the following technical solutions, and has developed a kind of wax crayon watercolor lead for retractable pencil working method, is characterized in being to comprise the following steps:
(1) be 2000 orders by one-level talcum powder order number, clay is wet clay, for subsequent use as major ingredient; .
(2) water soluble wax 40-55kg will be placed in major ingredient 110kg, polymer wax 25-35kg, pigment 15-20kg, titanium dioxide 5-10kg, Magnesium Stearate 15-20kg, EVA hot melt adhesive 5-10kg;
(3) batching of step (2) is stirred, be placed on and in kneader, mediate 5-6 hour;
(4) by kneaded material with rolling 3-4 hour in stone rolling machine;
(5) material rolling is put in hold-up vessel and stored 72 hours, allow material further moisten with for subsequent use;
(6) material of step (5) is put into the core machine of pressing, extruding specification is the watercolor lead for retractable pencil of Φ 5.0, dries.
In described step (1), talcum powder clay is wet clay, and moisture content is in 20% left and right.
Described step (3) kneader temperature is 50-55 degree Celsius.
Described step (4) its to become thickness be 0.5-0.8 millimeter
The positively effect of invention is: the present invention is with talcum powder, clay, polymeric gel is basis, auxiliary formula accurately, by the production technique of science, adopt the production technique of common production lead for retractable pencil pencil, a kind of new high grade colorful lead for retractable pencil of exploitation, is that thinking has further been expanded in the high added value production of pencil.And because technique of the present invention is to simplify improvedly on the basis of existing technological process, machinery equipment is not improved, therefore can directly apply to existing production technique, simple.
Specific embodiment:
Embodiment 1:
First prepare major ingredient: fineness is 2000 object talcum powder, clay is that wet clay 110kg will place water soluble wax 50kg, polymer wax 25g in major ingredient 110kg, pigment 15kg, titanium dioxide 5kg, Magnesium Stearate 10kg, EVA hot melt adhesive 5kg, mediates 6 hours, and temperature is 35 degrees Celsius, then roll as 0.6 millimeter of thickness with stone rolling machine, the thin slice of moisture content 20%, in the storage of carrying out 72 hours, extrudes the wax crayon watercolor lead for retractable pencil of Φ 5.0 finally by overvoltage core machine, carry out nature and dry, for subsequent use to do.
Embodiment 2:
First prepare major ingredient: fineness is 2000 object talcum powder, and clay is wet clay 110kg.Water soluble wax 45kg will be placed, polymer wax 30g, pigment 15kg, titanium dioxide 5kg, Magnesium Stearate 15kg, PVA hot melt adhesive 5k in major ingredient 110kg.Above material is stirred, mediate 7 hours, temperature is 45 degrees Celsius, then roll as 0.7 millimeter of thickness with stone rolling machine, the thin slice of moisture content 20, in the storage of carrying out 72 hours, the wax crayon watercolor lead for retractable pencil that extrudes Φ 5.0 finally by overvoltage core machine, carries out nature and dries, for subsequent use to do.
In actual applications; those skilled in the art completely can be in technical field scheme of the present invention; in actual applications; those skilled in the art is completely in technical scheme of the present invention; other parameters of choose reasonable; but the technical scheme substance of protecting with the present invention is identical, still falls within the scope of protection of the present invention.
Claims (4)
1. a wax crayon watercolor lead for retractable pencil working method, is characterized in being to comprise the following steps:
(1) be 2000 orders by one-level talcum powder order number, clay is wet clay, for subsequent use as major ingredient;
(2) water soluble wax 40-55kg will be placed in major ingredient 110kg, polymer wax 25-35kg, pigment 15-20kg, titanium dioxide 5-10kg, Magnesium Stearate 15-20kg, EVA hot melt adhesive 5-10kg;
(3) batching of step (2) is stirred, be placed on and in kneader, mediate 5-6 hour;
(4) by kneaded material with rolling 3-4 hour in stone rolling machine;
(5) material rolling is put in hold-up vessel and stored 72 hours, allow material further moisten with for subsequent use;
(6) material of step (5) is put into the core machine of pressing, extruding specification is the watercolor lead for retractable pencil of Φ 5.0, dries.
2. according to a kind of wax crayon watercolor lead for retractable pencil working method described in claims 1, it is characterized in that in step (1), talcum powder clay is wet clay, moisture content is in 20% left and right.
3. according to a kind of wax crayon watercolor lead for retractable pencil working method described in claims 1, it is characterized in that step (3) kneader temperature is 50-55 degree Celsius.
4. according to a kind of wax crayon watercolor lead for retractable pencil working method described in claims 1, it is characterized in that step (4) its to become thickness be 0.5-0.8 millimeter.