CN103834771B - The heat treating method of wearable cast steel - Google Patents

The heat treating method of wearable cast steel Download PDF

Info

Publication number
CN103834771B
CN103834771B CN201410081973.2A CN201410081973A CN103834771B CN 103834771 B CN103834771 B CN 103834771B CN 201410081973 A CN201410081973 A CN 201410081973A CN 103834771 B CN103834771 B CN 103834771B
Authority
CN
China
Prior art keywords
cast steel
heat treating
wearable cast
temperature
wearable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201410081973.2A
Other languages
Chinese (zh)
Other versions
CN103834771A (en
Inventor
沈文宝
童小燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huzhou Qianjin Baoyun Machinery Casting Co Ltd
Original Assignee
Huzhou Qianjin Baoyun Machinery Casting Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huzhou Qianjin Baoyun Machinery Casting Co Ltd filed Critical Huzhou Qianjin Baoyun Machinery Casting Co Ltd
Priority to CN201410081973.2A priority Critical patent/CN103834771B/en
Publication of CN103834771A publication Critical patent/CN103834771A/en
Application granted granted Critical
Publication of CN103834771B publication Critical patent/CN103834771B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of heat treating method of wearable cast steel, the chemical composition of described cast steel and mass percent thereof are: C:0.32-0.34; Mn:0.90-0.95; Si:1.1-1.3; Cr:1.8-2.1; Ni:0.3.5-5; Ti:0.02-0.03; V:0.18-0.22; Surplus is iron; Described heat treating method comprises: 1. normalizing: described wearable cast steel being placed in temperature is that the normalizing furnace of 1060 DEG C is incubated 24h, in normalizing furnace, be chilled to room temperature; 2. quench: be incubated 30min in the quenching furnance of 920-960 DEG C in temperature, take out water-cooled to room temperature; 3. tempering: be incubated 2h in the tempering stove of temperature 260 DEG C, takes out air cooling to room temperature.The present invention, while guarantee high rigidity, has good toughness, and technique simple and stable.<pb pnum="1" />

Description

The heat treating method of wearable cast steel
Technical field
The present invention relates to a kind of heat treating method of wearable cast steel, particularly a kind of heat treating method with the wearable cast steel of high hard toughness.
Background technology
Wearing and tearing are many industrial sector ubiquities and become the major reason causing equipment failure or material damage, and it also consumes a large amount of energy and material simultaneously.The various engineering excavation machine manufactured by wear-resistant alloy cast steel and shovel loader bucket tooth, various Wearproof transfer piping, various grinder hammerhead and jaw, various grip-pad, owing to being in the working conditions such as high strength, atrocious weather, its wear pattern is more serious.
Usually adopt vacuum heat treatment or annealing thermal treatment in existing foundry engieering, take polishing or machining mode to process steel casting after thermal treatment, the aftertreatment cost of steel casting can be increased like this, increase the workload of workpeople simultaneously; And complex process is unstable.
Summary of the invention
The object of the invention is to, a kind of heat treating method of wearable cast steel is provided.The present invention, while guarantee high rigidity, has good toughness, and technique simple and stable.
Technical scheme of the present invention: the heat treating method of wearable cast steel, is characterized in that: the chemical composition of described cast steel and mass percent thereof are: C:0.32-0.34; Mn:0.90-0.95; Si:1.1-1.3; Cr:1.8-2.1; Ni:0.3.5-5; Ti:0.02-0.03; V:0.18-0.22; Surplus is iron;
Described heat treating method comprises:
1. normalizing: described wearable cast steel being placed in temperature is that the normalizing furnace of 1060 DEG C is incubated 24h, is chilled to room temperature in normalizing furnace;
2. quench: be incubated 30min in the quenching furnance of 920-960 DEG C in temperature, take out water-cooled to room temperature;
3. tempering: be incubated 2h in the tempering stove of temperature 260 DEG C, takes out air cooling to room temperature.
In the heat treating method of aforesaid wearable cast steel, the hardness of described wearable cast steel: 48-50HRC, impelling strength Akv13-15J.
In the heat treating method of aforesaid wearable cast steel, the tissue of described wearable cast steel is mainly tempering lath martensite, residual austenite and a small amount of carbide.
In the heat treating method of aforesaid wearable cast steel, the size of described carbide is at 30-40nm.
Compared with prior art, steel casting thermal treatment process provided by the invention, its beneficial effect is, this technique is easily understood, and improves the mechanical property of steel casting, and thermal treatment cost is very low, and cast(ing) surface aftertreatment workload is little, and casting dimension accuracy is high.Adopt the combination of quenching and low-temperaturetempering, technological operation is simple, superior performance.The present invention can eliminate the dendritic segregation produced in castingprocesses, makes microstructure homogenization, reduces directivity, comparatively stable.
The invention has the advantages that: 1, microalloy treatment technique is advanced, good stability; 2, thermal treatment process is simple, and low-temperaturetempering process, has saved the energy, reduced production cost; 3, the coupling of rational alloying element is adopted, high without hardness, and good toughness; 4, rational chromium content, can improve matrix, improves hardening capacity.
Embodiment
Below in conjunction with embodiment, the present invention is further illustrated, but not as the foundation limited the present invention.
Embodiment.The heat treating method of wearable cast steel, feature is: the chemical composition of described cast steel and mass percent thereof are: C:0.32-0.34; Mn:0.90-0.95; Si:1.1-1.3; Cr:1.8-2.1; Ni:0.3.5-5; Ti:0.02-0.03; V:0.18-0.22; Surplus is iron;
Described heat treating method comprises:
1. normalizing: described wearable cast steel being placed in temperature is that the normalizing furnace of 1060 DEG C is incubated 24h, is chilled to room temperature in normalizing furnace;
2. quench: be incubated 30min in the quenching furnance of 920-960 DEG C in temperature, take out water-cooled to room temperature;
3. tempering: be incubated 2h in the tempering stove of temperature 260 DEG C, takes out air cooling to room temperature.
The hardness of described wearable cast steel: 48-50HRC, impelling strength Akv13-15J.The tissue of described wearable cast steel is mainly tempering lath martensite, residual austenite and a small amount of carbide.The size of described carbide is at 30-40nm.

Claims (4)

1. the heat treating method of wearable cast steel, is characterized in that: the chemical composition of described cast steel and mass percent thereof are: C:0.32-0.34%; Mn:0.90-0.95%; Si:1.1-1.3%; Cr:1.8-2.1%; Ni:5%; Ti:0.02-0.03%; V:0.18-0.22%; Surplus is iron;
Described heat treating method comprises:
1. normalizing: described wearable cast steel being placed in temperature is that the normalizing furnace of 1060 DEG C is incubated 24h, is chilled to room temperature in normalizing furnace;
2. quench: be incubated 30min in the quenching furnance of 920-960 DEG C in temperature, take out water-cooled to room temperature;
3. tempering: be incubated 2h in the tempering stove of temperature 260 DEG C, takes out air cooling to room temperature.
2. the heat treating method of wearable cast steel according to claim 1, is characterized in that: the hardness of described wearable cast steel: 48-50HRC, impelling strength Akv13-15J.
3. the heat treating method of wearable cast steel according to claim 1 and 2, is characterized in that: the tissue of described wearable cast steel is mainly tempering lath martensite, residual austenite and a small amount of carbide.
4. the heat treating method of wearable cast steel according to claim 3, is characterized in that: the size of described carbide is at 30-40nm.
CN201410081973.2A 2014-03-07 2014-03-07 The heat treating method of wearable cast steel Expired - Fee Related CN103834771B (en)