CN103820611A - 核电压紧弹性环用马氏体不锈钢锻件的热处理方法 - Google Patents

核电压紧弹性环用马氏体不锈钢锻件的热处理方法 Download PDF

Info

Publication number
CN103820611A
CN103820611A CN201210470097.3A CN201210470097A CN103820611A CN 103820611 A CN103820611 A CN 103820611A CN 201210470097 A CN201210470097 A CN 201210470097A CN 103820611 A CN103820611 A CN 103820611A
Authority
CN
China
Prior art keywords
forging
stainless steel
insulation
nuclear
heat treatment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201210470097.3A
Other languages
English (en)
Other versions
CN103820611B (zh
Inventor
李向
张智峰
涂而兴
李守江
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Electric Heavy Forging Co. Ltd.
Shanghai Heavy Machinery Plant Co Ltd
Original Assignee
Shanghai Heavy Machinery Plant Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Heavy Machinery Plant Co Ltd filed Critical Shanghai Heavy Machinery Plant Co Ltd
Priority to CN201210470097.3A priority Critical patent/CN103820611B/zh
Publication of CN103820611A publication Critical patent/CN103820611A/zh
Application granted granted Critical
Publication of CN103820611B publication Critical patent/CN103820611B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种核电压紧弹性环用马氏体不锈钢锻件的热处理方法,用于对AP1000核电堆内构件压紧弹性环用F6NM马氏体不锈钢锻件进行性能热处理,采用电加热环形炉,电加热环形炉的温度控制精度为±10℃;包括如下步骤:第一步,正火;第二步,第一次回火;第三步,第二次回火。本发明采用正火+两次回火的热处理工艺,能够获得回火马氏体+少量奥氏体的混合组织,从而获得良好的强度和韧性,所得到的F6NM压紧弹性环锻件能够符合AP1000核电堆内构件锻件规范的性能要求。

Description

核电压紧弹性环用马氏体不锈钢锻件的热处理方法
技术领域
本发明涉及一种热处理方法,具体涉及一种核电压紧弹性环用马氏体不锈钢锻件的热处理方法。
背景技术
压紧弹性环是核岛一回路压力容器中的重要部件,也是最大的马氏体不锈钢锻件,法国RCC-M标准采用Z12CN13钢(接近于国标的1Cr13NiMo)制造压紧弹性环锻件,在二代改进型1000MW核电上已有成功的应用。RCC-M标准对Z12CN13钢成分要求如表1所示:
  C   Mn   P   S   Si   Ni   Cr   Mo
  ≤0.15   ≤1.00   ≤0.020   ≤0.020   ≤0.50   1.0~2.0   11.5~13.0   0.40~0.60
表1
二代改进型核电压紧弹性环锻件的性能要求如表2所示:
Figure BDA00002426175000011
表2
AP1000核电属于第三代压水堆核电,设计寿命较二代改进型的40年延长至60年,发电功率从二代改进型的1000MW增大至1250MW,故对压紧弹性环锻件的性能要求提出了更高的要求,AP1000核电压紧弹性环锻件的性能要求如表3所示:
Figure BDA00002426175000012
表3
美国西屋公司在设计第三代AP1000核电时,先后选择了F6a、改良型403制造压紧弹性环,由于性能要求尤其是夏比冲击试验要求较二代加有较大提高,全球范围内未有锻件制造企业成功地制造出满足其强韧性要求的锻件,故只能再次更改材料。根据西屋公司最新设计文件,AP1000核电压紧弹性环锻件材料已更改为F6NM。F6NM在核电核岛主设备大锻件上属于首次应用。F6NM压紧弹性环锻件的成分要求如表4所示:
Figure BDA00002426175000021
表4
由成分可见,F6NM与二代改进型核电压紧弹性环用Z12CN13钢有显著差异,故现有的Z12CN13锻件热处理技术已不再适用于AP1000核电,需要根据F6NM的材料特性和压紧弹性环锻件的技术特点开发出新的热处理工艺。
发明内容
本发明所要解决的技术问题是提供一种核电压紧弹性环用马氏体不锈钢锻件的热处理方法,它可以获得满足技术规范要求的机械性能。
为解决上述技术问题,本发明核电压紧弹性环用马氏体不锈钢锻件的热处理方法的技术解决方案为:
用于对AP1000核电堆内构件压紧弹性环用F6NM马氏体不锈钢锻件进行性能热处理,采用电加热环形炉,电加热环形炉的温度控制精度为±10℃;包括如下步骤:
第一步,正火;
将锻件进炉加热至450~500℃后保温,保温时间为每100mm壁厚保温0.3~0.8小时;然后以≤150℃/小时的升温速度加热至1010~1040℃之间保温,保温时间为每100mm壁厚保温2~3小时;之后出炉空冷至锻件表面低于95℃;
第二步,第一次回火;
将锻件进炉以≤80℃/小时的升温速度加热至580~600℃之间保温,保温时间为每100mm壁厚保温2~3小时;之后出炉空冷至锻件表面低于95℃;
第三步,第二次回火;
将锻件进炉以≤80℃/小时的升温速度加热至550~570℃之间保温,保温时间为每100mm壁厚保温2~3小时;之后出炉空冷至锻件表面低于95℃。
所述热处理方法所得到的AP1000核电堆内构件压紧弹性环用F6NM马氏体不锈钢锻件,其屈服强度Rp0.2为680~690MPa,抗拉强度Rm为820~830MPa,10℃夏比冲击侧膨胀量为2.0~2.2mm。
本发明可以达到的技术效果是:
本发明采用正火+两次回火的热处理工艺,能够获得回火马氏体+少量奥氏体的混合组织,从而获得良好的强度和韧性。
本发明的热处理方式为正火+回火;奥氏体化温度为≥1010℃;冷却介质为空气;淬火后的工件冷却至≤95℃;回火温度为560~600℃,所得到的F6NM压紧弹性环锻件能够符合AP1000核电堆内构件锻件规范的性能要求。
下面结合具体实施方式对本发明作进一步详细的说明:
具体实施方式
本发明核电压紧弹性环用马氏体不锈钢锻件的热处理方法,用于对AP1000核电堆内构件压紧弹性环用F6NM马氏体不锈钢锻件进行性能热处理,采用电加热环形炉,电加热环形炉的温度控制精度为±10℃;包括如下步骤:
第一步,正火;
将锻件进炉加热至450~500℃后保温,保温时间为每100mm壁厚保温0.3~0.8小时;然后以≤150℃/小时的升温速度加热至1010~1040℃之间保温,保温时间为每100mm壁厚保温2~3小时;之后出炉空冷至锻件表面低于95℃;
第二步,第一次回火;
将锻件进炉以≤80℃/小时的升温速度加热至580~600℃之间保温,保温时间为每100mm壁厚保温2~3小时;之后出炉空冷至锻件表面低于95℃;
第三步,第二次回火;
将锻件进炉以≤80℃/小时的升温速度加热至550~570℃之间保温,保温时间为每100mm壁厚保温2~3小时;之后出炉空冷至锻件表面低于95℃。
采用本发明所得到的AP1000核电堆内构件压紧弹性环用F6NM马氏体不锈钢锻件,其屈服强度Rp0.2为680~690MPa,抗拉强度Rm为820~830MPa,10℃夏比冲击侧膨胀量为2.0~2.2mm,各项力学性能指标均优于考核要求。

Claims (3)

1.一种核电压紧弹性环用马氏体不锈钢锻件的热处理方法,其特征在于,用于对AP1000核电堆内构件压紧弹性环用F6NM马氏体不锈钢锻件进行性能热处理,包括如下步骤:
第一步,正火;
将锻件进炉加热至450~500℃后保温,保温时间为每100mm壁厚保温0.3~0.8小时;然后以≤150℃/小时的升温速度加热至1010~1040℃之间保温,保温时间为每100mm壁厚保温2~3小时;之后出炉空冷至锻件表面低于95℃;
第二步,第一次回火;
将锻件进炉以≤80℃/小时的升温速度加热至580~600℃之间保温,保温时间为每100mm壁厚保温2~3小时;之后出炉空冷至锻件表面低于95℃;
第三步,第二次回火;
将锻件进炉以≤80℃/小时的升温速度加热至550~570℃之间保温,保温时间为每100mm壁厚保温2~3小时;之后出炉空冷至锻件表面低于95℃。
2.根据权利要求1所述的核电压紧弹性环用马氏体不锈钢锻件的热处理方法,其特征在于,所述热处理方法采用电加热环形炉;电加热环形炉的温度控制精度为±10℃。
3.根据权利要求1所述的核电压紧弹性环用马氏体不锈钢锻件的热处理方法,其特征在于,所述热处理方法所得到的AP1000核电堆内构件压紧弹性环用F6NM马氏体不锈钢锻件,其屈服强度Rp0.2为680~690MPa,抗拉强度Rm为820~830MPa,10℃夏比冲击侧膨胀量为2.0~2.2mm。
CN201210470097.3A 2012-11-19 2012-11-19 核电压紧弹性环用马氏体不锈钢锻件的热处理方法 Active CN103820611B (zh)