CN103819130B - A kind of manufacture method of volcanic ash decorative material for internal wall - Google Patents
A kind of manufacture method of volcanic ash decorative material for internal wall Download PDFInfo
- Publication number
- CN103819130B CN103819130B CN201410079678.3A CN201410079678A CN103819130B CN 103819130 B CN103819130 B CN 103819130B CN 201410079678 A CN201410079678 A CN 201410079678A CN 103819130 B CN103819130 B CN 103819130B
- Authority
- CN
- China
- Prior art keywords
- volcanic ash
- internal wall
- decorative material
- manufacture method
- humidity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A manufacture method for volcanic ash decorative material for internal wall, belongs to the manufacture and exploit technical field of volcanic ash decorative material for internal wall.The technology of the present invention comprises technical formula and making method.With volcanic ash, mineral dye, calcined zeolite, slaked lime etc. for main raw material.Because the vesicular structure that volcanic ash self has, make product decoration indoor wall have vision soft, be smooth to the touch, coating firmly advantage, improve upholstery class.Adopt pozzolanic material, the relative humidity of the interior space can be made automatically to regulate 40% ~ 70%, between this humidity province that body sense is comfortable just.There is good heat-proof quality.This interval humidity also can prevent from condensing and the growing of mould.Especially volcanic ash processing treatment need only between 100-200 DEG C, and energy consumption is low, contrasts diatomaceous processing and considerably reduce production cost.And obtained product is all better than in every respect or is equivalent to diatomaceous earth products.Solve the energy consumption high problem that currently available products manufacture method exists in the course of processing.
Description
Technical field
The invention belongs to the manufacture and exploit technical field of volcanic ash decorative material for internal wall.
Background technology
Topsoil, interior decoration, mankind's activity etc. can cause room air pollution, are detrimental to health; The rise of Highrise buildings, reduce further the damping ability of buildings, exacerbates the discomfort that drying causes.Therefore, the finishing material with air-cleaning function and breathing humidity conditioning function is more and more subject to people's attention.For inner wall decoration, existing is adopt the ep-type material using diatomite as major function material mostly.The calcination process but present used diatomite need be fluxed through the high temperature of about 1000 DEG C, could by the organism in diatomite original ore and colour removal, remove simultaneously and be attached to the impurity such as the clay on diatomite surface, reach the object of purification, but above-mentioned high temperature is fluxed, calcination process need consume a large amount of energy, contaminate environment.Increase enterprise's production cost simultaneously.
Summary of the invention
For the problems referred to above, the object of this invention is to provide a kind of volcanic ash decorative material for internal wall that there is purifying air performance and breathe humidity conditioning function.This volcanic ash decorative material for internal wall is using volcanic ash as major function material, compare with diatomite, in the volcanic ash course of processing energy consumption low, solve the energy consumption high problem existed in the currently available products course of processing, in addition, pozzuolanic microcosmic class globosity makes volcanic ash decorative material for internal wall coating visually softer, and feel is more smooth.
Technical scheme of the present invention is as follows:
The technology of the present invention comprises technical formula and making method
Technical formula
Above volcanic ash is as functional materials, be obtained through process process such as 100-200 DEG C of drying, pulverizing, air classifications in volcanic ash ore deposit, outward appearance is pale yellow powder, and its loose bulk density is 0.18-0.23 gram/cc, particle appearance almost spherical, median size is 0.038-0.15mm.Dioxide-containing silica is greater than 85%.
Calcined zeolite is as aggregate, and its particle diameter is 0.1mm-1mm, and specific surface area is greater than 25 meters squared per gram, and whiteness is greater than 80%.
Its particle diameter of attapulgite powder is less than 0.045mm, and whiteness is greater than 80%.
Trevira is as anti-crack fiber, and its length is 2mm-3mm, and polyester is ethylene glycol terephthalate.Calcium perborate particle diameter is less than 0.1mm, and boron trioxide content is greater than 50%.Adipic dihydrazide content is greater than 95%.
Adipic dihydrazide is as formaldehyde-trapping agent, and its content is greater than 95%.。
Tourmalinite load nano-titanium dioxide is as purifying air catalyzer.
Inorganic environment-friendly pigment can adopt titanium dioxide, red iron oxide, iron oxide yellow etc.
Making method
By material each in above-mentioned technical formula, adopt general mixing equipment to mix in proportion, namely make powder decorative material for internal wall.The using method of product of the present invention is; Be in harmonious proportion evenly by powder body material and the water ratio by weight 1: 0.85, general coating tool such as employing trowel, spray gun etc. is coated on body of wall inwall.
The primary functional components of decorative material for internal wall of the present invention is volcanic ash.Volcanic ash is in fulminant volcanic activity, and solid stone and molten slurry are broken down into trickle particle and are formed.By volcanic ash ore deposit through process process such as 100-200 DEG C of drying, pulverizing, air classifications, can for the manufacture of decorative material for internal wall, because the Chemical Composition in volcanic ash contains a large amount of active SiO2 and Al2O3, in a humid environment with chemical reaction such as generation such as alkaline matter such as Ca (OH) 2 grade, generate the gum material such as hydrated calcium silicate, drated calcium aluminate, can enhancement be played to volcanic ash decorative material for internal wall coating.Again because volcanic ash has vesicular structure, during indoor humidity height, volcanic ash can by Vapor adsorption.When indoor humidity is low, steam desorption can discharge by volcanic ash.The relative humidity of the interior space is regulated automatically 40% ~ 70%, between this humidity province that body sense is comfortable just.Volcanic ash decorative material for internal wall can make the relative humidity of the interior space remain on less than 70%, can prevent condensation.Because volcanic ash has vesicular structure, the dry air in space has good heat-proof quality.As relative humidity then easily mildews bacterium more than 90%, relative humidity, below 70%, can prevent mould growth.The bait mould of acarid can not be produced, can anti-mite.The negative ion produced due to the tourmalinite load nano-titanium dioxide adopted has sterilizing function, and meanwhile, the strong basicity of slaked lime also can play good germicidal action.The adsorbable obnoxious flavour of volcanic ash decorative material for internal wall, the negative ion that tourmalinite load nano-titanium dioxide produces and being reacted by the obnoxious flavour adsorbed, decomposes nuisance, can deodorizing prevent finishing pollution syndromes.Produce negative ion be inhaled in body by respiratory tract, skin, in and harmful active oxygen, finishing pollution syndromes can be treated.Give soft, joyful, comfortable, loosen sensation, good conditioning and treating effect can be received, play the gentle field action of energy point.The inventive method is simple, easy to implement.In technical formula, have employed different materials improve and increase various function.As adopted calcined zeolite as aggregate, be because it has vesicular structure, the feature that specific surface area is large, the function that improve moisture adsorption and releasing He purify air.Adopt trevira as anti-crack fiber, add intensity, improve crack resistance, and can not go mouldy.Solve cellulose fiber peacekeeping polypropylene fibre Problems existing.Employing calcium perborate is sterilant, long-acting nontoxic.Solve inefficacy that tradition uses slaked lime to exist as sterilant and organic bactericide to volatilize the problem of poisonous gas.Be exactly adopt adipic dihydrazide and diatomite as formaldehyde-trapping agent in addition, adipic dihydrazide can carry out complex reaction with formaldehyde at normal temperatures and pressures, under the effect of tourmalinite load nano-titanium dioxide, Formaldehyde decomposition is become carbonic acid gas and water, carry out harmless treatment.In addition, volcanic ash decorative material for internal wall of the present invention adopts tourmalinite load nano-titanium dioxide as purifying air catalyzer, characteristic namely capable of releasing negative ion under utilizing tourmalinite normal temperature and pressure, activated nano titanium dioxide produces the katalysis that purifies air, no matter be at coatingsurface or at coat inside, all katalysis can be produced.This volcanic ash decorative material for internal wall is using volcanic ash as major function material, compare with diatomite, in the volcanic ash course of processing energy consumption low, solve the energy consumption high problem existed in the currently available products course of processing, in addition, pozzuolanic microcosmic class globosity makes the decorative material for internal wall coating vision made softer, and feel is more smooth.Improve upholstery class.
The present invention is without accompanying drawing.
Embodiment
Embodiment 1
Get volcanic ash 30kg, dioxide-containing silica is greater than 85%, median size is less than 0.074mm.Titanium dioxide 5kg, calcined zeolite 35kg, slaked lime 20kg, calcium hydroxide content are greater than 90%, and median size is less than 0.074mm.Ethene-vinyl acetate redispersible rubber powder 5kg, attapulgite powder 2kg, Vltra tears 0.6kg, trevira 0.3kg, calcium perborate 1kg, adipic dihydrazide 0.5kg, tourmalinite load nano-titanium dioxide 1kg.Processing units is general airtight mixing equipment, is dropped in proportion by above each material, and fully mixing can obtain powder finishing material.
Embodiment 2
Get volcanic ash 120kg, titanium dioxide 15kg, calcined zeolite 100kg, slaked lime 50kg, ethene-vinyl acetate redispersible rubber powder 15kg, attapulgite powder 10kg, Vltra tears 2kg, trevira 2kg, calcium perborate 2kg, adipic dihydrazide 2kg, tourmalinite load nano-titanium dioxide 5kg.Each constituent materials specification is with embodiment 1.Adopt embodiment 1 processing units and method, obtained powder finishing material.
Claims (2)
1. a manufacture method for volcanic ash decorative material for internal wall, is characterized in that: be made up of following material
By above-mentioned materials mixing and stirring, obtained powder body.
2. method according to claim 1, it is characterized in that, involved volcanic ash is that volcanic ash ore deposit obtains through 100-200 DEG C of drying, pulverizing, air classification process, outward appearance is pale yellow powder, its loose bulk density is 0.18-0.23 gram/cc, particle appearance is almost spherical, and median size is 0.038-0.15mm, and dioxide-containing silica is greater than 85%.