CN103817853A - Injection part surface treatment process - Google Patents
Injection part surface treatment process Download PDFInfo
- Publication number
- CN103817853A CN103817853A CN201210465500.3A CN201210465500A CN103817853A CN 103817853 A CN103817853 A CN 103817853A CN 201210465500 A CN201210465500 A CN 201210465500A CN 103817853 A CN103817853 A CN 103817853A
- Authority
- CN
- China
- Prior art keywords
- surface treatment
- base material
- working
- treatment according
- spraying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an injection part surface treatment process. The process comprises the following steps: spraying, coating a titanium metal layer, screen printing, electroplating and injection molding. A product treated by using the injection part surface treatment process disclosed by the invention has the remarkable effects of high corner angle and high stereoscopic impression in surface, better appearance, good hardness, wear-resisting property, chemical erosion resistance and ultraviolet resistance conforming to the corresponding standard and can be widely applied to plastic shells of cell phones, panel personal computers and other consumer electronics.
Description
Technical field
The present invention relates to a kind of moulding process of surface treatment.
Background technology
Along with the continuous lifting of people's living standard, the consumption electronic products such as mobile phone, panel computer are more and more universal, and on the basis of becoming stronger day by day in function, the texture of its plastic casing and the third dimension of pattern, also more and more become the index that consumer selects.In the time that being sprayed paint, product plastic casing there are at present following problems: (1) layer of paint is blocked up; (2) particle that sprays paint is excessively thick; (3) uniformity of spraying paint is poor; (4) wear no resistance; (5) spray paint and have dead angle; (6) the spray paint the problems of application of ground; (7) spray paint and affect the intensity of material; (8) the dirty point of lacquered surface.
In addition, also have poor effect when plastic casing is done to stereoeffect, third dimension is not strong, but cannot process for wedge angle and angular structures, has obvious limitation, is not suitable for batch production, the defects such as inefficiency.
Summary of the invention
The technical problem to be solved in the present invention is to provide that a kind of surface three-dimensional sense is good, the easy moulding process of surface treatment of processing procedure.
For solving the problems of the technologies described above, a kind of moulding process of surface treatment of the present invention, comprises the steps:
(1) spraying: at the two sides of base material coating resin class paint respectively, and be cured;
(2) be coated with titanium coating: vacuum splashing and plating titanium oxide metal level, the light transmittance of this titanium oxide metal level is 75~80%;
(3) screen painting: after mould is cleaned and spraying paint, dry, then by ink printing on the base material being coated with after titanium coating, after overcuring, rely on mould positioning mechanism location, in Mo Nei and together moulding of base material;
(4) electroplate: utilize electrode to pass through electric current, make the attached work of metal on substrate surface, then base material is carried out to die-cut formation sheet material;
(5) injection mo(u)lding: die-cut good sheet material is positioned in corresponding injection mold and carries out injection mo(u)lding, obtain finished product.
For improving spraying effect, when above-mentioned steps (1) spraying, also add paint thinner.
Above-mentioned base material is PC or PET.
The thickness of above-mentioned base material is 0.15~0.3 millimeter.
The thickness of above-mentioned titanium coating is 2~10 microns.
The invention has the beneficial effects as follows: the product surface of the treatment process processing of injecting products of the present invention has significant high corner angle, high relief effect, product is more attractive in appearance, and product has good hardness, anti-wear performance, resist chemical performance and anti-UV performance meet respective standard.Can be widely used in, on the plastic casing of mobile phone, panel computer and other consumption electronic products, greatly having promoted the competitiveness of product.
The specific embodiment
Improve an injection moulding process for working of plastics surface gloss, comprise the steps: a kind of moulding process of surface treatment, comprise the steps: (1) spraying: at the two sides of base material coating resin class paint respectively, and be cured; (2) be coated with titanium coating: vacuum splashing and plating titanium oxide metal level, the light transmittance of this titanium oxide metal level is 75~80%; (3) screen painting: after mould is cleaned and spraying paint, dry, then by ink printing being coated with after titanium coating on base material, after overcuring, rely on mould positioning mechanism location, in Mo Nei and together moulding of base material; (4) electroplate: utilize electrode to pass through electric current, make the attached work of metal on substrate surface, then base material is carried out to die-cut formation sheet material; (5) injection mo(u)lding: die-cut good sheet material is positioned in corresponding injection mold and carries out injection mo(u)lding, obtain finished product.
Final products are tested through hardness test, adhesion force test, wear-resisting test, anti-test chemical, anti-UV:
Wherein, hardness test condition is: load: 1Kgf, and effect angle: 45 °, using appliance: Mitsubishi 2H pencil, result shows does not have scratch.
Adhesion test: the method for testing of nondestructive testing: jerk after using 3M-595 adhesive tape 5cm length to be affixed on surface, result display surface dope layer can not be pulled up; The method of testing of destructive testing: mark grid (thermosetting 1mm × 1mm, thermoplasticity 2mm × 2mm) on surface with blade, then with jerking after on 3M-595 tape sticker, be less than 15% dope layer and be removed in grid.
Wear-resisting test: RCA tester table, use 11/16 wide banded blank sheet of paper, 17 circles per minute, loading is 175g, result demonstration loses polishing scratch.
Anti-test chemical: acid test, exposure time 24,48,72 hours, surface is through without any change; 60 ℃ of alkali tests, exposure time 24,48,72 hours, surface is through without any change.
Anti-UV test: at 60 ℃, the UV irradiation (wavelength 313nm) of 200 hours, surface is rear without any change after tested.
In sum, have good hardness by the moulding for the treatment of process processing of the present invention, anti-wear performance, resist chemical performance and anti-UV performance meet respective standard.
Claims (5)
1. a moulding process of surface treatment, is characterized in that comprising the steps:
(1) spraying: at the two sides of base material coating resin class paint respectively, and be cured;
(2) be coated with titanium coating: vacuum splashing and plating titanium oxide metal level, the light transmittance of this titanium oxide metal level is 75~80%;
(3) screen painting: mould is cleaned and spray paint after dry, then by ink printing on the base material being coated with after titanium coating, after overcuring, rely on mould positioning mechanism location, in Mo Nei and together moulding of base material;
(4) electroplate: utilize electrode to pass through electric current, make the attached work of metal on substrate surface, then base material is carried out to die-cut formation sheet material;
(5) injection mo(u)lding: die-cut good sheet material is positioned in corresponding injection mold and carries out injection mo(u)lding, obtain finished product.
2. a kind of working of plastics process of surface treatment according to claim 1, is characterized in that: when described step (1) spraying, also add paint thinner.
3. a kind of working of plastics process of surface treatment according to claim 1, is characterized in that: described base material is PC or PET.
4. a kind of working of plastics process of surface treatment according to claim 1, is characterized in that: the thickness of described base material is 0.15~0.3 millimeter.
5. a kind of working of plastics process of surface treatment according to claim 1, is characterized in that: the thickness of described titanium coating is 2~10 microns.