CN103805732A - Converter smelting slag pressing method - Google Patents
Converter smelting slag pressing method Download PDFInfo
- Publication number
- CN103805732A CN103805732A CN201210440505.0A CN201210440505A CN103805732A CN 103805732 A CN103805732 A CN 103805732A CN 201210440505 A CN201210440505 A CN 201210440505A CN 103805732 A CN103805732 A CN 103805732A
- Authority
- CN
- China
- Prior art keywords
- slag
- converter
- converter smelting
- high pressure
- pressure nitrogen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A converter smelting slag pressing method comprises: blowing high pressure nitrogen into a converter by an oxygen lance, and destroying foamed slag by high pressure nitrogen jet to realize the purpose of smooth slag pouring. The method of the invention solves the problem that liquid slag is severe in foaming and cannot be poured out smoothly, needs no feeding of slag materials into the converter for slag pressing, saves the resources, does not increase the smelting cost, and is simple in operation. The method of the invention can be widely used as a steel-making converter smelting slag pressing method.
Description
Technical field:
The present invention relates to the improvement of steel-making converter smelting technology.
Background technology:
In converter steelmaking process, need deslagging operation midway, but liquid steel slag foamed is serious sometimes, can not pour out smoothly slag, need presses slag operation to dropping into slag charge in stove, waste resource, increases smelting cost.Address this problem and become urgent need.
Summary of the invention:
Overcome the deficiencies in the prior art, propose a kind of liquid steel slag foamed and spumescence slag is destroyed, realized when serious the converter smelting of smooth deslagging and press slag method.Converter smelting presses slag method to be: in stove, be blown into high pressure nitrogen with oxygen rifle, utilize high pressure nitrogen jet, by spumescence slag destruction, reach the object of smooth deslagging.The invention solves liquid steel slag foamed and seriously can not pour out smoothly the problem of slag, do not need to drop into slag charge in stove and press slag, saved resource, do not increase smelting cost, simple to operate.
Embodiment:
A most preferred embodiment of the present invention, smelts midway, before deslagging, if judge that slag foamed is serious, in stove, is blown into high pressure nitrogen by oxygen rifle, utilizes high pressure nitrogen jet that spumescence slag is destroyed, and can pour out smoothly slag.
Claims (1)
1. converter smelting is pressed a slag method, it is characterized in that: in stove, be blown into high pressure nitrogen with oxygen rifle, utilize high pressure nitrogen jet, by spumescence slag destruction, reach the object of smooth deslagging.