CN103805277B - A kind of preparation method of wax temperature-sensing valve temperature sensing medium - Google Patents
A kind of preparation method of wax temperature-sensing valve temperature sensing medium Download PDFInfo
- Publication number
- CN103805277B CN103805277B CN201210440701.8A CN201210440701A CN103805277B CN 103805277 B CN103805277 B CN 103805277B CN 201210440701 A CN201210440701 A CN 201210440701A CN 103805277 B CN103805277 B CN 103805277B
- Authority
- CN
- China
- Prior art keywords
- temperature
- wax
- sensing
- cut
- sensing valve
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of preparation method of wax temperature-sensing valve temperature sensing medium.Object product of the present invention utilizes containing C
10~ C
18the petroleum wax substance of composition is raw material, gets cut and prepared by the techniques such as mixing through underpressure distillation, interval.The wax automatic temperature control valve using this product to prepare can be used for needs at 0 ~ 7 DEG C of scope temp, and requires the temperature-sensing valve of stroke homogenous linear, especially for the wax temperature-sensing valve being reached control apparatus element manipulation envrionment temperature by controlled cooling model medium temperature.
Description
Technical field
The invention belongs to special wax technical field, particularly relate to a kind of preparation method of wax temperature-sensing valve temperature sensing medium.Specifically, temperature sensing medium prepared by the present invention may be used for needs (0 ~ 7 DEG C) temperature control within the scope of narrower temperature control, and the temperature-sensing valve of stroke homogenous linear, this wax temperature-sensing valve can pass through controlled cooling model medium temperature, thus reaches the object of high precision control apparatus element manipulation envrionment temperature.
Background technology
With the valve that the temperature-sensing valve that Wax makes temperature sensing medium is a kind of self-forced type, be utilize volume change by-pass valve control aperture in wax class temperature sensing medium phase transition process thus reach the object controlling logistics flux, it has the several functions such as induction, execution, feedback, definite value simultaneously.This temperature-sensing valve has the temperature profile not considerable change with system pressure, physical strength is high, chemical stability good, easily mass-produced and install, the advantage such as cost is low, stable temperature control is reliable, thus in temperature control, be able to widespread use.
Electronic devices and components needs could be stablized under specific temperature environment, long term operation.Be inconvenient to keep in repair and in the very large situation of environmental temperature fluctuation scope, electronic devices and components must adopt heat-eliminating medium to control the temperature of its Working environment at some, could long-term stable operation.For this situation, the flow adopting active electric sub-control system to control special heat-eliminating medium in cold and hot fluid oil circuit at present controls the operating ambient temperature of electronic devices and components.This active electronic Control system architecture is complicated, weight lost efficacy greatly, easily, so be badly in need of improving.
Compared with controlling with current special electronic devices and components temperature the active electric sub-control system that adopts, if adopt wax temperature-sensing valve control temperature, will have that volume is little, lightweight, structure simply, the advantage such as dependable performance.Especially to being inconvenient to keep in repair and the Application Areas requiring working life longer, adopt wax temperature-sensing valve to ensureing that the work-ing life of electronic devices and components is significant.
Use the wax temperature-sensing valve prepared by wax temperature sensing medium prepared by prior art, temperature control scope is more than 10 ~ 15 DEG C; Existing technology of preparing means are single, are many with solvent method; And the linear degree of temperature control is very poor, or in relative wide temperature range stroke linear.Such as: DD 241,829, patent Introduction such as DD 241,830 grade are with solvent-extracted method, and the product of preparation is at 80 ~ 90 DEG C of scope temps.Wax temperature-sensing valve prepared by the product of the patent Introductions such as CN02109668.6, CN200310104909.3, CN200510046426.1, stroke homogenous linear in relative wide temperature range (25 DEG C even 50 DEG C).The preparation method of these patent Introductions or have pollution to environment, or the wax temperature-sensing valve that thus prepared by product only just can accomplish stroke homogenous linear in wide temperature control scope.
Character due to wax temperature sensing medium is the key factor determining wax temperature-sensing valve performance, therefore prepares the prerequisite that special temperature sensing medium is exploitation temperature-sensing valve.
Summary of the invention
One is the object of the present invention is to provide to be applicable to wax temperature-sensing valve temperature sensing medium, specifically can at 0 ~ 7 DEG C of scope temp, and the wax temperature sensing medium that the stroke value often spent is basically identical.Wax temperature sensing medium of the present invention, is particularly useful for the temperature automatically controlled device needing stroke homogenous linear, especially for passing through wax temperature-sensing valve controlled cooling model medium temperature, thus the field of control apparatus element manipulation envrionment temperature.
The temperature control scope of general wax temperature-sensing valve is more than 10 ~ 15 DEG C, and this is determined by the character of its temperature sensing medium used.As everyone knows, the character of wax temperature sensing medium is consisting of decision.The object of the invention product needs the character in narrow temperature control scope (0 ~ 7 DEG C) with stroke homogenous linear, and this just requires accurately to control its composition, make the carbon distribution of product narrower, and the ratio of the hydrocarbon component of various carbon number is close.
Common take oil as the Wax of raw material production, and main ingredient is normal paraffin and isoparaffin, and normal paraffin is more suitable for preparing temperature sensing medium, so the Wax that should normal paraffin content selected high is as raw material as far as possible.Suitable product commercially available at present mainly comprises with the Paraffin liquid heavy of urea dewaxing process production with the whiteruss of dewaxing by molecular sieve explained hereafter, because the normal paraffin content of whiteruss is higher than heavy liquid whiteruss, so preference liquids paraffin of the present invention is raw material.
The present invention is the water distilling apparatus (having 15 ~ 20 blocks of theoretical trays) utilizing separation efficiency lower, first produce the narrower cut of boiling range (boiling range is 5 ~ 10 DEG C), the mode that cut (choosing at least two cuts) carries out mixing is got again by interval, product composition is accurately controlled, thus realizes making product property meet the requirement of high precision control apparatus component temperature wax temperature-sensing valve.Prepare compared with the decomposite mode of high purity hydrocarbon with utilizing the rectifier unit of high separating efficiency, preparation method of the present invention more easily realizes.
The preparation method of a kind of wax temperature-sensing valve temperature sensing medium of the present invention, comprises following content:
(1) with containing C
10~ C
18the petroleum wax substance of composition is raw material, in the water distilling apparatus with 15 ~ 20 blocks of theoretical trays, raw material is produced 240 ~ 280 DEG C of cuts by the boiling range of 5 ~ 10 DEG C;
(2) in above-mentioned cut, choose suitable cut, choose at least two cuts by the mode of 1 or 2 cut in interval, ratio heating and melting equal by weight also mixes, and namely obtains wax temperature-sensing valve temperature sensing medium.
According to the preparation method of wax temperature-sensing valve temperature sensing medium of the present invention, wherein said raw material refers to that, containing the petroleum wax of carbonatoms at the normal paraffin of 10 ~ 18, especially whiteruss, particularly by the whiteruss of dewaxing by molecular sieve explained hereafter.
Suitable cut described in step (2), refers to that fusing point is the cut of-2 ~ 9 DEG C.Interval refers to discontinuously chooses cut, can 1, interval cut, also can 2, interval cut.The fusing point of at least two selected cuts distributes relatively uniform within the scope of-2 ~ 9 DEG C.
Advantage of the present invention is: by selecting the raw material be suitable for, and utilizes the water distilling apparatus of lower separation efficiency, and the mode of being got cut by interval reaches the object accurately controlling product composition and then reach control product property.The product performance of preparation method of the present invention are stablized, can at 0 ~ 7 DEG C of scope temp, and the stroke value often spent is basically identical, can be used for high precision control apparatus element manipulation envrionment temperature wax temperature-sensing valve.Physics, the stable chemical nature of wax temperature sensing medium of the present invention, during for the preparation of wax temperature-sensing valve, can obtain good result of use, and have longer work-ing life.
Accompanying drawing explanation
The expansion character curve of the wax temperature controlling valve temperature sensing medium that Fig. 1 and Fig. 2 is divided into embodiment 1 and embodiment 2 to prepare, in figure, X-coordinate is temperature, and ordinate zou is relative travel amount.
Embodiment
Utilize wax temperature-sensing valve to have temperature sensor to change and the characteristic making corresponding adjustment, the automatic adjustment of electronic devices and components operating ambient temperature can be applied to, its principle is by the mixed temperature of special heat-eliminating medium in its induction cold and hot fluid oil circuit, the flow of special heat-eliminating medium in automatic adjustment cold and hot fluid oil circuit, thus the object reaching the temperature automatically regulating blending agent.
Preparation method and the expansion character of wax temperature sensing medium of the present invention are described by the following examples.
Embodiment 1
(1) with the whiteruss of dewaxing by molecular sieve explained hereafter for raw material, in the water distilling apparatus with 17 blocks of theoretical trays, 1.33 × 10
3under Pa pressure, with 5 DEG C for the cut of 240 ~ 280 DEG C is prepared at interval, each section of cut product fusing point is as shown in table 1.
Table 1 each underpressure distillation product fusing point.
| Cut scope, DEG C | Product fusing point, DEG C |
| 240～245 | -3.1 |
| 245～250 | -1.5 |
| 250～255 | 0.4 |
| 255～260 | 2.8 |
| 260～265 | 5.0 |
| 265～270 | 6.9 |
| 270～275 | 9.0 |
| 275～280 | 11.0 |
From melting point data, 245 ~ 250 DEG C of cut to 270 ~ 275 cut fusing points, between-2 ~ 9 DEG C, are appropriate fractions.
(2) interval is got above-mentioned through underpressure distillation purification cut, i.e. 245 ~ 250 DEG C of cuts, 255 ~ 260 DEG C of cuts, 270 ~ 275 DEG C of cuts, and by proportional sampling heating and melting identical by weight for above-mentioned three kinds of cuts, mixes, obtain object product.
The expansion character curve of wax temperature-sensing valve temperature sensing medium made of product as shown in Figure 1 thus.
Embodiment 2
(1) take whiteruss as raw material, in the water distilling apparatus with 17 blocks of theoretical trays, 1.33 × 10
3under Pa pressure, with 10 DEG C for the cut of 240 ~ 280 DEG C is prepared at interval, each section of cut product fusing point is as shown in table 2.
Table 2 each component underpressure distillation product fusing point.
| Cut scope/DEG C | Product fusing point/DEG C |
| 240～250 | -1.8 |
| 250～260 | 2.4 |
| 260～270 | 6.2 |
| 270～280 | 10.1 |
From melting point data, 240 ~ 250 DEG C of cut to 260 ~ 270 cut fusing points, between-2 ~ 9 DEG C, are appropriate fractions.
(2) interval is got above-mentioned through underpressure distillation purification cut, i.e. 240 ~ 250 DEG C of cuts, 260 ~ 270 DEG C of cuts, and by proportional sampling heating and melting identical by weight for above-mentioned two kinds of cuts, mixes, obtain object product.
The expansion character curve of wax temperature-sensing valve temperature sensing medium made of product as shown in Figure 2 thus.
Claims (5)
1. a preparation method for wax temperature-sensing valve temperature sensing medium, comprises following content:
(1) with containing C
10~ C
18the petroleum wax substance of composition is raw material, in the water distilling apparatus with 15 ~ 20 blocks of theoretical trays, raw material is produced 240 ~ 280 DEG C of cuts by the boiling range of 5 ~ 10 DEG C;
(2) in above-mentioned cut, choose the cut that fusing point is-2 ~ 9 DEG C, choose at least two cuts by the mode of 1 or 2 cut in interval, ratio heating and melting equal by weight also mixes, and namely obtains wax temperature-sensing valve temperature sensing medium.
2. in accordance with the method for claim 1, it is characterized in that, described petroleum wax substance is whiteruss.
3. in accordance with the method for claim 2, it is characterized in that, described whiteruss is the whiteruss of dewaxing by molecular sieve explained hereafter or the Paraffin liquid heavy of urea dewaxing process production.
4. in accordance with the method for claim 1, it is characterized in that, described interval refers to discontinuously chooses cut.
5. the wax temperature-sensing valve temperature sensing medium that obtains of claim 1-4 either method, it is at 0 ~ 7 DEG C of scope temp, and the stroke value often spent is basically identical.