CN103804768A - 一种可双向拉伸的聚乙烯电容器金属化膜及其制备方法 - Google Patents
一种可双向拉伸的聚乙烯电容器金属化膜及其制备方法 Download PDFInfo
- Publication number
- CN103804768A CN103804768A CN201310708080.1A CN201310708080A CN103804768A CN 103804768 A CN103804768 A CN 103804768A CN 201310708080 A CN201310708080 A CN 201310708080A CN 103804768 A CN103804768 A CN 103804768A
- Authority
- CN
- China
- Prior art keywords
- parts
- metalized film
- film
- capacitor metalized
- way stretchable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种可双向拉伸的聚乙烯电容器金属化膜,其特征在于,由下列重量份的原料制成:茂金属线性低密度聚乙烯200、明矾1-2、氧化镁1-2、蔗糖脂肪酸酯3-4、亚磷酸二正丁酯2-3、薄荷醇1-2、橘子油1-2、苯并三氮唑1-2、三聚氰胺2-3、助剂5-6;本发明加工工艺简单,并且用其制作的薄膜电容器接触电阻小,从而使得产品特性好。本发明具有良好的高热封强度,耐高温性能好;通过过滤,去除原料中的杂质,使原料性能好,降低了薄膜的报废率,不易破裂;采用电晕处理,提高了薄膜的耐压强度,防止击穿。
Description
技术领域
本发明涉及电容器制造领域,特别是一种可双向拉伸的聚乙烯电容器金属化膜及其制备方法。
背景技术
薄膜电容器是以金属箔当电极,将其和聚乙酯,聚丙烯,聚笨乙烯或聚碳酸酯等塑料薄膜,从两端重叠后,卷绕成圆筒状的构造之电容器 ;在所有的塑料薄膜电容当中,聚丙烯(PP)电容和聚苯乙烯(PS)电容的特性最为显著,当然这两种电容器的价格也比较高,电容器的薄膜质量直接影响电容器的使用寿命和产品性能,电容器薄膜的需求量大、种类多,采用单一原料生产的薄膜很难适应市场的要求,但每种原料都有其不足之处,所以生产出来的薄膜很难满足各种情况的需求。
发明内容
本发明的目的是提供一种可双向拉伸的聚乙烯电容器金属化膜及其制备方法。
为了实现本发明的目的,本发明通过以下方案实施:
一种可双向拉伸的聚乙烯电容器金属化膜,由下列重量份的原料制成:茂金属线性低密度聚乙烯200、明矾1-2、氧化镁1-2、蔗糖脂肪酸酯3-4、亚磷酸二正丁酯2-3、薄荷醇1-2、橘子油1-2、苯并三氮唑1-2、三聚氰胺2-3、助剂5-6;
所述助剂由下列重量份的原料制成:茂金属线性低密度聚乙烯12-15、甲基三乙氧基硅烷1-2、二茂铁1-2、椴木灰烬1-2、促进剂TMTD 1-2;制备方法是将茂金属线性低密度聚乙烯加热至熔融状态,加入其它成分,搅拌分散均匀,冷却,造粒,即得。
本发明所述可双向拉伸的聚乙烯电容器金属化膜,由以下具体步骤制成:
(1)将茂金属线性低密度聚乙烯、明矾、氧化镁、蔗糖脂肪酸酯、亚磷酸二正丁酯加热熔融,再加入助剂以及其余剩余成分充分搅拌,送入挤出机熔融、过滤,然后再通过挤出机挤出片状熔体,过滤>1200目,所述挤出机的温度为220-250℃;
(2)将步骤(1)制成的片状熔体通过激冷辊及风淋室冷却定型后制得铸片,依次进行纵向拉伸、横向拉伸、粗化面电晕处理;
(3)收卷、第一次时效处理、第二次时效处理;
(4)真空蒸发金属化膜,粗化面形成金属化层。
本发明加工工艺简单,并且用其制作的薄膜电容器接触电阻小,从而使得产品特性好。本发明具有良好的高热封强度,耐高温性能好;通过过滤,去除原料中的杂质,使原料性能好,降低了薄膜的报废率,不易破裂;采用电晕处理,提高了薄膜的耐压强度,防止击穿。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种可双向拉伸的聚乙烯电容器金属化膜,由下列重量份(公斤)的原料制成:茂金属线性低密度聚乙烯200、明矾1、氧化镁1、蔗糖脂肪酸酯3、亚磷酸二正丁酯2、薄荷醇1、橘子油1、苯并三氮唑1、三聚氰胺2、助剂5;
所述助剂由下列重量份(公斤)的原料制成:茂金属线性低密度聚乙烯12、甲基三乙氧基硅烷1、二茂铁1、椴木灰烬1、促进剂TMTD 1;制备方法是将茂金属线性低密度聚乙烯加热至熔融状态,加入其它成分,搅拌分散均匀,冷却,造粒,即得。
本发明所述可双向拉伸的聚乙烯电容器金属化膜,由以下具体步骤制成:
(1)将茂金属线性低密度聚乙烯、明矾、氧化镁、蔗糖脂肪酸酯、亚磷酸二正丁酯加热熔融,再加入助剂以及其余剩余成分充分搅拌,送入挤出机熔融、过滤,然后再通过挤出机挤出片状熔体,过滤>1200目,所述挤出机的温度为220-250℃;
(2)将步骤(1)制成的片状熔体通过激冷辊及风淋室冷却定型后制得铸片,依次进行纵向拉伸、横向拉伸、粗化面电晕处理;
(3)收卷、第一次时效处理、第二次时效处理;
(4)真空蒸发金属化膜,粗化面形成金属化层。
本发明实施例的金属化薄膜的技术指标如下 :
(1)横向收缩率≤ 0.2%、纵向收缩率≤ 2.5%
(2)横向拉伸强度≥ 19Mpa、纵向拉伸强度≥ 14Mpa ;
(3)最小击穿电压 600Vv/um 。
Claims (2)
1.一种可双向拉伸的聚乙烯电容器金属化膜,其特征在于,由下列重量份的原料制成:茂金属线性低密度聚乙烯200、明矾1-2、氧化镁1-2、蔗糖脂肪酸酯3-4、亚磷酸二正丁酯2-3、薄荷醇1-2、橘子油1-2、苯并三氮唑1-2、三聚氰胺2-3、助剂5-6;
所述助剂由下列重量份的原料制成:茂金属线性低密度聚乙烯12-15、甲基三乙氧基硅烷1-2、二茂铁1-2、椴木灰烬1-2、促进剂TMTD 1-2;制备方法是将茂金属线性低密度聚乙烯加热至熔融状态,加入其它成分,搅拌分散均匀,冷却,造粒,即得。
2.根据权利要求1所述可双向拉伸的聚乙烯电容器金属化膜,其特征在于,由以下具体步骤制成:
(1)将茂金属线性低密度聚乙烯、明矾、氧化镁、蔗糖脂肪酸酯、亚磷酸二正丁酯加热熔融,再加入助剂以及其余剩余成分充分搅拌,送入挤出机熔融、过滤,然后再通过挤出机挤出片状熔体,过滤>1200目,所述挤出机的温度为220-250℃;
(2)将步骤(1)制成的片状熔体通过激冷辊及风淋室冷却定型后制得铸片,依次进行纵向拉伸、横向拉伸、粗化面电晕处理;
(3)收卷、第一次时效处理、第二次时效处理;
(4)真空蒸发金属化膜,粗化面形成金属化层。