CN103789706A - High temperature resistant steel pipe material and preparation method thereof - Google Patents
High temperature resistant steel pipe material and preparation method thereof Download PDFInfo
- Publication number
- CN103789706A CN103789706A CN201410018615.7A CN201410018615A CN103789706A CN 103789706 A CN103789706 A CN 103789706A CN 201410018615 A CN201410018615 A CN 201410018615A CN 103789706 A CN103789706 A CN 103789706A
- Authority
- CN
- China
- Prior art keywords
- speed
- heated
- steel pipe
- pipe material
- tube material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high temperature resistant steel pipe material, which comprises the following chemical elements in percentage by weight: 0.08-0.11% of C, 1.4-1.6% of W, 0.02-0.04% of Sb, 0.7-1.0% of Mn, 0.6-0.9% of Si, 0.02-0.04% of Hf, 0.2-0.5% of Mo, 0.2-0.4% of Co, 0.02-0.03% of Ta, 0-0.015% of P, 0-0.002% of S, and the balance being Fe and inevitable impurity. The steel pipe material has the characteristics of high strength, good high-temperature resistance, good wear resistance, large conduction coefficient, small expansion coefficient, good anti-oxidation and good stress corrosion, and can be widely applied to high-temperature parts and fasteners. The heat process temperature is reasonably controlled, so as to improve the comprehensive mechanical property of the steel pipe material. A refining agent can fully perform the physicochemical reaction with the molten steel, thereby achieving deoxidation, desulfurization, dephosphorization and improvements of state of inclusions, and improving the purity of steel, the metal yield rate and the yield of steel tubes.
Description
Technical field
The present invention relates to field of alloy material, relate in particular to a kind of high temperaturesteel tube material and preparation method thereof.
Background technology
Steel pipe is not only for delivery of fluid and powdery solid, exchange heat energy, manufacturing machine part and container, it or a kind of economic steel.Manufacture from people's daily apparatus, furniture, water supply and sewage, air feed, ventilation and heating facility to various agricultural machinery apparatus, exploitation, national defence and the space flight firearms used of subterranean resource, bullet, guided missile, rocket etc. all be unable to do without steel pipe.
Along with production technology is constantly progressive, the raising of living standards of the people, specification of quality to steel pipe is more and more higher, not only require have higher intensity, hardness, erosion resistance, wear resistance, high temperature resistant, good springiness, counter-bending, shock-resistant, good toughness, be difficult for occurring crackle, improve safety performance, but also need to there is good processibility, reduce Financial cost, improve the competitive power of product, also need further to improve the quality of steel pipe, especially research and develop the tube material of different performances for different purposes.
Summary of the invention
The object of the present invention is to provide a kind of high temperaturesteel tube material and preparation method thereof, this tube material has that intensity is high, high temperature resistant, wear-resisting, thermal conductivity is large, the feature such as the coefficient of expansion is little, good in oxidation resistance, stress corrosion resistant are good.
Technical scheme of the present invention is as follows:
A kind of high temperaturesteel tube material, is characterized in that: chemical element composition and mass percent thereof that it contains are: C 0.08-0.11, W1.4-1.6, Sb0.02-0.04, Mn0.7-1.0, Si0.6-0.9, Hf0.02-0.04, Mo0.2-0.5, Co0.2-0.4, Ta0.02-0.03, P≤0.015, S≤0.002, surplus are Fe and inevitable impurity.
The production method of described high temperaturesteel tube material, is characterized in that comprising the following steps:
(1) pig iron is sent into and in stove, added refining agent and carry out initial refining, add alloying constituent, add refining agent and carry out secondary refining, survey and adjust chemical element component content to qualified, vacuum outgas, continuous casting circular tube blank, then carry out anneal, make blank;
(2) in alloying process, first alloy and the pig iron are cast to alloy block, then throw in batches; The composition of alloy block and release sequence are (1) Mn, Si, Fe; (2) W, Mo, Fe; (3) other alloying elements and Fe; Input interlude is 25-28 minute, and after throwing in, Argon stirs;
(3) add hot piercing, described blank heating is bored a hole at 1155-1165 ℃, obtain pipe, and control punch excentricity is less than 7%;
(4) thermal treatment.
Described thermal treatment is: pipe is heated to 760-770 ℃ with 23-25 ℃/s speed, and insulation 30-40 minute, then be heated to 1020-1030 ℃ with 25-27 ℃/s speed, insulation 7-9 minute; Cool to 50-90 ℃ with 240-260 ℃/h of speed again; Be heated to 930-940 ℃ with 23-25 ℃/s speed again, insulation 1-1.5 hour, again with 230-240 ℃/s speed spraying cooling to 320-330 ℃, again with 200-210 ℃/s speed spraying cooling to 80-100 ℃, be heated to 580-590 ℃ with 20-22 ℃/s speed again, insulation 2-3 hour, takes out air cooling and get final product.
Described refining agent is made up of the raw material of following weight part: scrap iron powder 20-24, nano titanium oxide 0.5-1, nano mica powder 0.5-1, monazite 3-5, barium oxide 2-4, calcium oxide 6-8, chromium sesquioxide 2-4, expanded graphite 4-6; Preparation method pulverizes monazite, is heated to molten state with scrap iron powder, adds monazite, barium oxide, calcium oxide, chromium sesquioxide, expanded graphite to stir, degassed in a vacuum; Gained powder is pressed into base under 0.7-1Kpa, then, at 1210-1240 ℃, calcines 1-2 hour, cooling after, then be ground into 100-200 order powder, mix with other remaining components, to obtain final product.
Beneficial effect of the present invention
Tube material of the present invention has added the elements such as W, Mo, Co, Sb, Ta, this steel pipe has that intensity is high, high temperature resistant, wear-resisting, thermal conductivity is large, the feature such as the coefficient of expansion is little, good in oxidation resistance, stress corrosion resistant are good, can be widely used in high-temperature component, fastening piece etc.; By reasonable control thermal treatment temp, improve the comprehensive mechanical property of tube material, improve safety coefficient; Refining agent of the present invention can carry out abundant physical reaction with molten steel, reaches deoxidation, desulfurization, dephosphorization, improves inclusion morphology object, improves the purity of steel, and recovery rate of iron and Tube yield are improved.
Embodiment
A kind of high temperaturesteel tube material, chemical element composition and mass percent thereof that it contains are: C 0.08-0.11, W1.4-1.6, Sb0.02-0.04, Mn0.7-1.0, Si0.6-0.9, Hf0.02-0.04, Mo0.2-0.5, Co0.2-0.4, Ta0.02-0.03, P≤0.015, S≤0.002, surplus are Fe and inevitable impurity.
The production method of described high temperaturesteel tube material, comprises the following steps:
(1) pig iron is sent into and in stove, added refining agent and carry out initial refining, add alloying constituent, add refining agent and carry out secondary refining, survey and adjust chemical element component content to qualified, vacuum outgas, continuous casting circular tube blank, then carry out anneal, make blank;
(2) in alloying process, first alloy and the pig iron are cast to alloy block, then throw in batches; The composition of alloy block and release sequence are (1) Mn, Si, Fe; (2) W, Mo, Fe; (3) other alloying elements and Fe; Throwing in interlude is 27 minutes, and after throwing in, Argon stirs;
(3) add hot piercing, by perforation at described blank heating to 1160 ℃, obtain pipe, and control punch excentricity is less than 7%;
(4) thermal treatment.
Described thermal treatment is: pipe is heated to 765 ℃ with 24 ℃/s speed, is incubated 35 minutes, then be heated to 1025 ℃ with 26 ℃/s speed, be incubated 8 minutes; Cool to 70 ℃ with 250 ℃/h of speed again; Be heated to 935 ℃ with 24 ℃/s speed again, be incubated 1.3 hours, then with 235 ℃/s speed spraying cooling to 325 ℃, then with 205 ℃/s speed spraying cooling to 90 ℃, then be heated to 585 ℃ with 21 ℃/s speed, and be incubated 2.5 hours, take out air cooling and get final product.
Described refining agent by following weight part (kilogram) raw material make: scrap iron powder 22, nano titanium oxide 0.7, nano mica powder 0.8, monazite 4, barium oxide 3, calcium oxide 7, chromium sesquioxide 3, expanded graphite 5; Preparation method pulverizes monazite, is heated to molten state with scrap iron powder, adds monazite, barium oxide, calcium oxide, chromium sesquioxide, expanded graphite to stir, degassed in a vacuum; Gained powder is pressed into base under 0.8Kpa, then, at 1230 ℃, calcines 1.5 hours, cooling after, then be ground into 150 order powder, mix with other remaining components, to obtain final product.
Adopt the high temperaturesteel tube material of the present embodiment to make the steel pipe that wall thickness is 4.2mm, can bear more than 20Mpa pressure and booster not, yield strength 740MPa, tensile strength is at 850MPa, hardness (HV) 246, impact absorbing energy 56J, impelling strength 64J/cm2, unit elongation 16.7%.
Claims (4)
1. a high temperaturesteel tube material, is characterized in that: chemical element composition and mass percent thereof that it contains are: C 0.08-0.11, W1.4-1.6, Sb0.02-0.04, Mn0.7-1.0, Si0.6-0.9, Hf0.02-0.04, Mo0.2-0.5, Co0.2-0.4, Ta0.02-0.03, P≤0.015, S≤0.002, surplus are Fe and inevitable impurity.
2. the production method of high temperaturesteel tube material according to claim 1, is characterized in that comprising the following steps:
(1) pig iron is sent into and in stove, added refining agent and carry out initial refining, add alloying constituent, add refining agent and carry out secondary refining, survey and adjust chemical element component content to qualified, vacuum outgas, continuous casting circular tube blank, then carry out anneal, make blank;
(2) in alloying process, first alloy and the pig iron are cast to alloy block, then throw in batches; The composition of alloy block and release sequence are (1) Mn, Si, Fe; (2) W, Mo, Fe; (3) other alloying elements and Fe; Input interlude is 25-28 minute, and after throwing in, Argon stirs;
(3) add hot piercing, described blank heating is bored a hole at 1155-1165 ℃, obtain pipe, and control punch excentricity is less than 7%;
(4) thermal treatment.
3. the production method of high temperaturesteel tube material according to claim 2, it is characterized in that: described thermal treatment is: pipe is heated to 760-770 ℃ with 23-25 ℃/s speed, insulation 30-40 minute, then be heated to 1020-1030 ℃ with 25-27 ℃/s speed, insulation 7-9 minute; Cool to 50-90 ℃ with 240-260 ℃/h of speed again; Be heated to 930-940 ℃ with 23-25 ℃/s speed again, insulation 1-1.5 hour, again with 230-240 ℃/s speed spraying cooling to 320-330 ℃, again with 200-210 ℃/s speed spraying cooling to 80-100 ℃, be heated to 580-590 ℃ with 20-22 ℃/s speed again, insulation 2-3 hour, takes out air cooling and get final product.
4. the production method of high temperaturesteel tube material according to claim 2, is characterized in that: described refining agent is made up of the raw material of following weight part: scrap iron powder 20-24, nano titanium oxide 0.5-1, nano mica powder 0.5-1, monazite 3-5, barium oxide 2-4, calcium oxide 6-8, chromium sesquioxide 2-4, expanded graphite 4-6; Preparation method pulverizes monazite, is heated to molten state with scrap iron powder, adds monazite, barium oxide, calcium oxide, chromium sesquioxide, expanded graphite to stir, degassed in a vacuum; Gained powder is pressed into base under 0.7-1Kpa, then, at 1210-1240 ℃, calcines 1-2 hour, cooling after, then be ground into 100-200 order powder, mix with other remaining components, to obtain final product.