CN103789606A - Flexible uncoated tinplate base - Google Patents
Flexible uncoated tinplate base Download PDFInfo
- Publication number
- CN103789606A CN103789606A CN201210435190.0A CN201210435190A CN103789606A CN 103789606 A CN103789606 A CN 103789606A CN 201210435190 A CN201210435190 A CN 201210435190A CN 103789606 A CN103789606 A CN 103789606A
- Authority
- CN
- China
- Prior art keywords
- tinplate base
- uncoated tinplate
- soft
- steel
- als
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a flexible uncoated tinplate base. The uncoated tinplate base comprises the following chemical components in percentage by weight: 0.05 to 0.09% of C, 0.15 to 0.25% of Si, 0.20 to 0.40% of Mn, not greater than 0.008% of P, not greater than 0.01% of S, 0.02 to 0.040% of Als, 0.04 to 0.08% of Ce, not greater than 0.005% of N, and the balance of Fe and inevitable impurities.
Description
Technical field
The present invention relates to technical field of ferrous metallurgy, relate in particular to a kind of soft uncoated tinplate base.
Background technology
Annealed cold-rolling tinning original plate, still there is the free C of part, N atom, if annealed steel plate is at normal temperatures through placing for a long time, or slightly under high-temperature, carrying out short period of time heating, can produce yield point elongation, and yield-point itself also can improve, this performance variation along with institute's elapsed time and generation, is called timeliness.Exist the tin plate of yield point elongation when stamping, can produce wrinkle on its surface, affect quality product and even cause workpiece to scrap attractive in appearance with product.Adopt the tin plate of continuous annealing because annealing time is shorter, uncombined carbon, nitrogen amount are more, and therefore ageing resistance is poor.
At present, processing characteristics is good both at home and abroad, hardness rank is as being TH52, TH55, the soft tin-plate of TH57, all adopts continuous annealing mode (CA), as Korean patent No. is: the patent documentation of KR100285643, its chemical composition providing is C:0.003～0.007 for (wt.%), S≤0.012, N:0.001～0.004, Mn:0.10～0.40, Al:0.03～0.06, has added Al in addition, the elements such as N, have " 2 the sheet zip-top cans soft zinc-plated blackboard of aluminium killed steel and the manufacture method " of excellent processability and compressive property, Korean patent No. is: the patent documentation of KR100340504, and its chemical composition is that (wt.%) is C≤0.004, Mn:0.2～0.5, Al:0.02～0.06, P:0.02～0.04, Cr:0.02～0.06, N≤0.003, N, and S≤0.01, Ti:0.01～0.03, has the zinc-plated blackboard of aluminium killed steel and the production method of excellent processability and ductility after annealing, Japanese Patent No. is: JP58027933 patent documentation, and the carbon aluminium-killed steel chemical composition (%) that it provides is C:0.02～0.09, N≤0.006, solAl:0.002～0.15, adopts continuous casting → hot rolling → cold rolling → continuous annealing (CA) treatment process to produce, and especially in annealing process, in the time of >=680 ℃, is incubated tin plate and production method more than 20sec, the employing cold air dynamic spraying technology spraying plating tin or the tin alloy coat that also have domestic Baoshan Iron and Steel Company to provide, then form the bright and clean stanningmetal plate of surfacing through smooth or cold-rolling treatment, process through soft heat the manufacture method that forms brilliant tin plate again, and the chemical composition of employing IF steel is (wt%) C≤0.006, Mn:0.10～0.20, Al:0.025～0.075, Si≤0.03, Ti:0.03～0.08, P≤0.015, S≤0.015, N≤0.003, O≤0.004, surplus is Fe and inevitable impurity element, adopt steel-making → continuous casting → hot rolling → acid to roll associating → continuous annealing → smooth → tin plating technique and produce the document of soft tin-plate and manufacture method thereof, its common ground adopts continuous annealing (CA) thermal regulation to produce soft tin-plate exactly, and in these patent documentations, all do not relate to the ageing resistance energy problem of tin plate, only have Baosteel to propose employing continuous annealing R-OA, Iinterstitial Atom-Free is processed and the control of material grains size, effectively slows down or eliminates the generation of tin plate timeliness.Produce the deficiency of soft tin-plate with continuous annealing furnace (CA): because uncoated tinplate base is very thin, IF steel or carbon aluminium-killed steel material are soft, add high temperature annealing, the problems such as hot wooden dipper song, broken belt easily occur in the time of steel belt continuous annealing.For fear of the generation of the problems such as hot wooden dipper song, broken belt, people generally adopt and reduce the measure of unit production rate and for it, it causes again production efficiency and lumber recovery to reduce, the problem that production cost is high.
Summary of the invention
The object of the invention is to propose a kind of soft uncoated tinplate base, this soft uncoated tinplate base pressworkability is good, ageing resistance can be good.
For reaching this object, the present invention by the following technical solutions:
A kind of soft uncoated tinplate base, the chemical composition of described uncoated tinplate base is by weight percentage: C:0.05-0.09, Si:0.15-0.25, Mn:0.20-0.40, P :≤0.008, S :≤0.01, Als:0.02-0.040, Ce:0.04-0.08, N :≤0.005, and all the other are Fe and inevitable impurity.
Preferably, the chemical composition of described uncoated tinplate base is by weight percentage: C:0.06-0.08, Si:0.18-0.22, Mn:0.25-0.35, P :≤0.008, S :≤0.01, Als:0.025-0.035, Ce:0.05-0.07, N :≤0.005, and all the other are Fe and inevitable impurity.
Most preferably, the chemical composition of described uncoated tinplate base is by weight percentage: C:0.07, Si:0.20, Mn:0.30, P :≤0.008, S :≤0.01, Al s:0.030, Ce:0.06, N :≤0.005, and all the other are Fe and inevitable impurity.
The principle of design of the each element of the present invention is:
C: well-known, carbon is the most effective strengthening element, therefore, along with the increase carbon steel hardening gradually of carbon content, but its cold working simultaneously (punching press, drawing) and welding property degenerate; Because cementite is negative electrode with respect to carbon steel (matrix is ferrite), therefore, in the time that carbon content increases, negative electrode quantity and area are increased, correspondingly its corrosion current has increased, thereby causes pickling time lag (PL) to increase, for this reason, determine that the soft uncoated tinplate base of resistance to timeliness selects carbon aluminium-killed steel, carbon content control is 0.05-0.09%.
Si: silicon can significantly improve the elastic limit of steel, yield-point and tensile strength, but the content of uncoated tinplate base Si is higher, the SiO of the oxidized generation of silicon
2content increases thereupon, the SiO of surface of steel plate
2content is higher, and the adhesivity of coating is poorer.Therefore, consider, Si content is controlled to 0.15-0.25%.
Mn:Mn energy reinforced ferrite, but also solid solution increases the hardness of tin plate base material.Therefore, soft tin-plate Mn content 0.20-0.40%.
P: the most basic requirement of metallic substance is the homogeneity of performance and tissue, otherwise just easy to crack when punching press, formability also there will be problem.Because segregation easily occurs phosphorus, so phosphorus content will strictly be controlled.Therefore, P content≤0.008%.
S: in general, S is detrimental impurity element in steel, therefore, S content≤0.01%.
Als: in steel, can form acid-soluble aluminium and sour insoluble aluminium adding of Al, and Als comprises solid solution aluminium and AlN, and the AlN particle of disperse can stop growing up of austenite crystal, crystal grain thinning, thus contribute to improve the processing forming of steel plate.But for aluminium killed steel, along with the increase of Als, the Al2O3 the amount of inclusions in steel increases, inclusion size also will become greatly, will cause corrosion resisting property and the coating adhesion variation of tin plate, and PL value is larger; But in order to guarantee the surface quality of the complete deoxidation of molten steel and continuously cast bloom, Als should guarantee >=0.005%.Therefore Als content is chosen in 0.02-0.04%.
Ce: can change composition, form, distribution and the character of steel inclusion, thereby improve toughness and the punching performance of steel.
N: content≤0.005%, N is the same with C, is also solid solution element.Along with the increase of N content in steel, will cause its pressworkability to degenerate (as n, r value decline), simultaneously, solid solution N is the major cause that causes tin plate finished product timeliness, particularly, for the strain aging effect after smooth, the impact of nitrogen is especially large, therefore requires N as far as possible low.
The present invention has following beneficial effect.
1) on the basis of great many of experiments, the component of the product to prior art is adjusted and is redesigned, and particularly adds appropriate rare earth element ce, improves toughness and the punching performance of uncoated tinplate base; More than its Erichsen number 8.0mm, be applicable to preparation deep-draw tank body.
2) soft uncoated tinplate base of the present invention also has the feature that ageing resistance is strong.
Embodiment
Embodiment mono-
A kind of soft uncoated tinplate base, the chemical composition of described uncoated tinplate base is by weight percentage: C:0.05, Si:0.25, Mn:0.20, P :≤0.008, S :≤0.01, Al s:0.040, Ce:0.04, N :≤0.005, and all the other are Fe and inevitable impurity.
Embodiment bis-
A kind of soft uncoated tinplate base, the chemical composition of described uncoated tinplate base is by weight percentage: C:0.09, Si:0.15, Mn:0.40, P :≤0.008, S :≤0.01, Al s:0.02, Ce:0.08, N :≤0.005, and all the other are Fe and inevitable impurity.
Embodiment tri-
A kind of soft uncoated tinplate base, the chemical composition of described uncoated tinplate base is by weight percentage: C:0.06, Si:0.22, Mn:0.25, P :≤0.008, S :≤0.01, Als:0.035, Ce:0.05, N :≤0.005, and all the other are Fe and inevitable impurity.
Embodiment tetra-
A kind of soft uncoated tinplate base, the chemical composition of described uncoated tinplate base is by weight percentage: C:0.08, Si:0.18, Mn:0.35, P :≤0.008, S :≤0.01, Als:0.025, Ce:0.07, N :≤0.005, and all the other are Fe and inevitable impurity.
Embodiment five
A kind of soft uncoated tinplate base, the chemical composition of described uncoated tinplate base is by weight percentage: C:0.07, Si:0.20, Mn:0.30, P :≤0.008, S :≤0.01, Als:0.03, Ce:0.06, N :≤0.005, and all the other are Fe and inevitable impurity.
Claims (3)
1. a soft uncoated tinplate base, it is characterized in that, the chemical composition of described uncoated tinplate base is by weight percentage: C:0.05-0.09, Si:0.15-0.25, Mn:0.20-0.40, P :≤0.008, S :≤0.01, Als:0.02-0.040, Ce:0.04-0.08, N :≤0.005, and all the other are Fe and inevitable impurity.
2. the soft uncoated tinplate base of one as claimed in claim 1, it is characterized in that, the chemical composition of described uncoated tinplate base is by weight percentage: C:0.06-0.08, Si:0.18-0.22, Mn:0.25-0.35, P :≤0.008, S :≤0.01, Als:0.025-0.035, Ce:0.05-0.07, N :≤0.005, and all the other are Fe and inevitable impurity.
3. the soft uncoated tinplate base of one as claimed in claim 2, it is characterized in that, the chemical composition of described uncoated tinplate base is by weight percentage: C:0.07, Si:0.20, Mn:0.30, P :≤0.008, S :≤0.01, Als:0.030, Ce:0.06, N :≤0.005, and all the other are Fe and inevitable impurity.