CN103788913A - Polyaspartic acid ester sealant for petroleum pipeline end socket and preparation method thereof - Google Patents
Polyaspartic acid ester sealant for petroleum pipeline end socket and preparation method thereof Download PDFInfo
- Publication number
- CN103788913A CN103788913A CN201410076892.3A CN201410076892A CN103788913A CN 103788913 A CN103788913 A CN 103788913A CN 201410076892 A CN201410076892 A CN 201410076892A CN 103788913 A CN103788913 A CN 103788913A
- Authority
- CN
- China
- Prior art keywords
- end socket
- pipe line
- line end
- type seal
- polyaspartic ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a polyaspartic acid ester sealant for a petroleum pipeline end socket and a preparation method of the polyaspartic acid ester sealant. The polyaspartic acid ester sealant for the petroleum pipeline end socket comprises, by weight ratio, including a constituent A and a constituent B, wherein the constituent A includes 20-70 parts of aliphatic isocyanate and 20-65 parts of polyether polyol; the constituent B includes 30-70 parts of asparaginic acid resin, 30-44 parts of a steric hindrance chain extender, 5-50 parts of padding, 2-4 parts of an addition agent, 1-3 parts of a pigment and 4-10 parts of a plasticizing agent; the mass ratio of the constituent A to the constituent B is 1:1-1.3:1. The polyaspartic acid ester sealant for the petroleum pipeline end socket has the advantages that the formula is scientific and reasonable; the oil resistance, the liquid medium resistance, the weather resistance and the ageing resistance of the polyaspartic acid ester sealant are excellent; the mechanical property of the polyaspartic acid ester sealant is approximately the same as that of anti-corrosion polyurea of a pipeline, so that the adhesive force of the polyaspartic acid ester sealant is excellent.
Description
Technical field
The present invention relates to polyureas technology, relate in particular to a kind of petroleum pipe line end socket polyaspartic ester type seal gum and preparation method thereof.
Background technology
Along with the development of national economy, the advantage of pipeline oil transportation highlights day by day.General the employing built on stilts or buried two kinds of modes on the ground of laying of oil pipeline.But no matter take that mode, in the time that metallic conduit contacts with surrounding medium, cause its surface corrosion owing to there is chemical action or electrochemical action.This phenomenon is very general.After metallic conduit is corroded, all will change in profile, color and luster and mechanical property, and affect the quality of institute's oil transportation product, and shorten the work-ing life of oil pipeline, and seriously may cause leakage, contaminate environment, even can not be used.
The common corrosion of petroleum pipe line comprises chemical corrosion and galvanic corrosion.Chemical corrosion: exposed metal/bare metal, in air, while contact, generates corresponding compound (oxide compound, sulfide, muriate etc.) with airborne oxygen, sulfurous gas, chlorine etc. on metallic surface.The organic sulfide (sulphur, hydrogen sulfide, mercaptan, thioether, epithio ether, disulphide, thiophene etc.) that simultaneously contains various ways in oil product, naphthenic acid etc. also can produce chemical corrosion to metallic oil pipeline.Galvanic corrosion: when metal contacts with electrolyte solution, the corrosion being caused by electrochemistry.Metallic conduit and the atmosphere that contains moisture, soil, ocean contact, carbonic acid gas, sulfurous gas, hydrogenchloride, sodium-chlor and the dust containing in these media is all the electrolyte solution of different concns.
Oil pipeline end socket is the most important structure in whole pipeline, due to the complicacy of its structure, construction and use, in pipe laying, be the position that suffers chemical corrosion the most serious, be also oil seepage, leak the position usually occurring, therefore the sealing at end socket place is extremely important.Find a kind of corrosion-resistant, good sealing effect, and have the sealing material of fine consistency very important with polyurea materials.
At present, protective system for inner and outer walls of pipeline mainly contains the multiple materials such as petroleum pitch, coal tar enamel, clinkery epoxy powder, double-deck welding epoxy powder, 3PE structural anticorrosion layer and spray polyurea material, wherein polyurea materials has more advantage than other materials, having broken traditional preservative coat need to heat and be wound around the defect of bringing, one time coating thickness can reach 1-2mm, this greatly simplifies its coating process, and can guarantee the overall antiseptic property of pipeline.Polyurea materials is that a kind of curing molding growing up is in recent years fast, the ep-type material of constructability.It is high with tensile strength, snappiness good, and the premium properties such as waterproof, protection against corrosion, wear-resisting, anti-slippery, heat shock resistance, low temperature resistant and good decorative property, be subject to people and more and more favor, show unique characteristics at ready coating aspect aspect the big area such as corrosion protection coating and wear-resistant coating.Polyurea materials has excellent physicals, antiseptic property and workability concurrently, is the preferred material in inner and outer walls of pipeline antiseptic project.
Spray polyurea speed of response is fast, gel time is short (only having short tens seconds), can be at comparatively smooth inner and outer walls of pipeline rapid shaping.But spray polyurea is not suitable for complex structure, flex point, the cap that node is many.This be because spray polyurea in the time that cap is constructed, because set time is fast, gel time is short, trickling property is poor, easily causes drain spray and spraying uneven; Wetting property is poor, poorly sealed, and the problem such as easily come off.
The main polyurethane sealant that adopts of petroleum pipe line end socket sealing at present, polyurethane sealant is bonding stable, excellent spring, anti tear, wear-resisting, anti-puncture, does not pollute base material, acid and alkali-resistance, resistance to liquid medium, corrosion-free to concrete, steel substrate etc.Price is gathered sulphur, organosilicon sealant is cheap, and has good consistency (this is that other sealing materials do not possess) with polyurea materials.
Polyurethane sealant is by single component, two kinds of base types of two-pack.The basal component of single-component product is end NCO base performed polymer, and the hydroxyl isoreactivity group generation chemical reaction that can exist with the water of substrate surface absorption and surface after bonding finally generates urea bond structure and solidifies.Single-component mist-solidifying polyurethane sealant is a kind ofly to utilize in air micro-moisture as crosslinking accelerator and curing response type seal gum.Single-component product at room temperature can carry out moisture-curable, operation is easy, but there is following shortcoming in it: single component sealant package stability packed and ectocine larger, conventionally solidify slower, under high humid and warm environment, solidify and may produce bubble and crackle, affect use properties and work-ing life, and many occasions need primary coat.
Double Component Polyurethane Sealant is solidified by the NCO base of base polyurethane prepolymer for use as and the active hydrogen compounds cross-linking reaction of another component.Self-vulcanizing speed is faster than single component, and cost value is lower, but still has following shortcoming as the sealing material at petroleum pipe line end socket place:
A. the more anticorrosion polyureas of sticking power is poor.Polyurethane sealant and polyurea materials belong to polyurethane system, the consistency of bi-material is better, but also there is certain difference in the two: the tensile strength >=20MPa of polyurea materials for pipeline corrosion protection, elongation at break >=10%, hardness is high, in polyurethane system, belong to rigid material, to the sticking power excellence (sticking power >=9MPa) of steel substrate.Tensile strength >=the 6Mpa of polyurethane sealant, elongation at break >=100%, hardness is low, belongs to flexible materials in polyurethane system, in without primary coat situation, the poor adhesive force (sticking power >=2.5MPa) to steel substrate.
B. resistance to liquid medium, oil-proofness are not as polyurea materials.In polyurethane sealant, contain a large amount of amino-formate bonds, this bond polarity can not show a candle to urea bond polarity in polyurea materials.Therefore polyurea materials is finer and close, oil resistant, resistance to liquid medium more.Can not show a candle to polyurea materials at polyurethane sealant aspect this.
C. in polyurethane sealant, contain a large amount of aromatic isocyanate polymkeric substance, xanthochromia is serious, and weather resisteant is poor, and resistance of aging is poor.
Summary of the invention
The object of the invention is to, for above-mentioned current polyurethane sealant poor adhesive force; Resistance to liquid medium, oil-proofness are not good; Weather resisteant is poor, the problem that resistance of aging is poor, proposes a kind of petroleum pipe line end socket polyaspartic ester type seal gum, when oil resistant, resistance to liquid medium, weathering resistance and ageing resistance are superior, reach unanimity with the mechanical property of pipeline corrosion protection polyureas, sticking power excellence.
For achieving the above object, the technical solution used in the present invention is: polyaspartic ester type seal gum for a kind of petroleum pipe line end socket, comprises each component that weight proportion is following:
A component:
Aliphatic isocyanates 20-70 part, is preferably 45-70 part; Polyether glycol 20-65 part, is preferably 30-55 part;
B component:
Poly-aspartic-acid resin 30-70 part, is preferably 45-70 part; Steric hindrance ammonia chainextender 30-44 part, is preferably 25-40 part; Filler 5-50 part, is preferably 25-40 part; Auxiliary agent 2-4 part, is preferably 2-3 part; Pigment 1-3 part, is preferably 1-2 part; Softening agent 4-10 part, is preferably 5-10 part;
The mass ratio of described A component and B component is 1:1~1.3:1, and preferred mass ratio is 1:1.
Steric hindrance ammonia chainextender of the present invention refers to the compound that contains multiple secondary amino groups.
Further, described aliphatic isocyanates is one or more in HMDI (HMDI), hexamethylene diisocyanate trimer, isophorone diisocyanate (IPDI), phenylenedimethylidyne isocyanic ester (XDI) and cyclohexanedimethyleterephthalate vulcabond (H6XDI).
Further, described polyether glycol is polyoxytrimethylene ethoxylated polyhydric alcohol and/or polytetrahydrofuran polyvalent alcohol.Preferred described polyether glycol is that molecular weight is respectively 1000,2000,3000 polyoxytrimethylene ether glycol, polyoxytrimethylene ether trivalent alcohol and molecular weight and is respectively one or more in 650,1000,2000 polytetrahydrofuran diol.
Further, described polyaspartic ester is one or more in Desmophen NH1420, Desmophen NH1520 and Desmophen NH1220.
Further, described steric hindrance ammonia chainextender is 4,4'-diamino-3,3'-dichloro diphenyl methane (MOCA), steric hindrance ammonia Unilink4200(4,4 '-bis-Zhong Ding ADP methylmethanes), Unilink4100(4,4 '-bis-Zhong Ding amino-benzenes), Clearlink1000(4,4 '-bis-Zhong Ding amino bicyclic hexyl methane), Clearlink3000(3,3 '-dimethyl-4,4 '-bis-Zhong Ding amino bicyclic hexyl methane), one or more in Jefflink555 and Jefflink754.
Further, described filler is one or more in fine particle calcium carbonate, coarse whiting, talcum powder, calcium hydroxide, zinc phosphate and mica powder, and described filler order number is more than 800 orders.
Further, described auxiliary agent is one or more in oxidation inhibitor, photostabilizer and defoamer.Described oxidation inhibitor is: one or more in oxidation inhibitor-264, antioxidant 1010 and antioxidant 1076, consumption accounts for 5/1000ths of the total system of manual polyureas.Described photostabilizer be in UV-9, UV-24, UV-49, UV-531 and UV-328 one or more, consumption accounts for 5/1000ths of the total system of manual polyureas.Described defoamer is one or more in BYK-066N, BYK-054 and BYK-5500, and consumption accounts for 5/1000ths of the total system of manual polyureas.
Further, described pigment is one or more in titanium dioxide, iron oxide red, molybdenum red, indigo-blue indigo plant and carbon black.
Further, described softening agent is one or more in dioctyl phthalate (DOP), dibutyl phthalate and Di Iso Decyl Phthalate.When solid packing in system and auxiliary agent are when more, system viscosity can raise, and suitably adds softening agent can realize following advantage: the viscosity that 1. reduces melt; 2. increase the snappiness of superpolymer; 3. increase the elongation at break of superpolymer; 4. reduce the forming process temperature of superpolymer; 5. improve the forming process characteristic of superpolymer; 6. improve the impact property of superpolymer; 7. improve the low temperature flexibility of superpolymer; 8. reduce the surface hardness of superpolymer.
Another object of the present invention also provides the preparation method of a kind of petroleum pipe line end socket polyaspartic ester type seal gum, comprises the following steps:
The preparation of A component: as in container, (stirring makes it to be heated evenly, and is conducive to removing of moisture to open stirring by polyether glycol; When polyether glycol is while being multiple, stirring can also make multiple polyether glycol mix), be heated to 110~120 ℃, vacuum hydro-extraction is removed raw water to water ratio and is reached below 3/10000ths, and being cooled to liquid material temperature is 20-30 ℃, is preferably 25 ℃.Isocyanate ester compound is joined in container, and stirring at normal temperature reaction, after 1-2 hour, is preferably after 1 hour, is slowly warming up to 80~90 ℃, detects NCO% value and reaches after design load 98-102%, cooling discharge.
Vacuum of the present invention adopts vacuum pump to realize, and vacuum tightness is-0.1~-0.08MPa; Described slow intensification is, in time of 0.5 hour-1 hour, to rise to 80-90 ℃ by room temperature.Along with the rising of temperature, reaction aggravation, is prone to implode, therefore need slowly to heat up, speed of response is little by little accelerated; Conventionally after being warming up to 80~90 ℃, keep reaction 2h, NCO% value can be qualified.NCO% design load of the present invention is to calculate theoretical nco value by formulating of recipe.
Add after aromatic isocyanate after first normal-temperature reaction for some time, again normal-temperature reaction be because: after aromatic isocyanate adds, at once will with steric hindrance ammonia, polyether glycol exothermic heat of reaction, and heat release is obvious, easily there is implode to hot words if extraneous, cause the failure of an experiment, therefore need to stir 1-2 hour under normal temperature, after initial reaction heat release finishes, pass through again heating unit temperature reaction.
The preparation of B component: polyaspartic ester, steric hindrance ammonia chainextender are placed in to container and mix; Filler and pigment are joined in container and mixed, and mixing time is 20-60min, is preferably 30min; Then add auxiliary agent to mix (auxiliary agent is volatile, adds in the later stage, can reduce its volatile quantity), mixing time is 20-60min, be preferably 30min, to product, moisture and outward appearance detects, and water ratio reaches below 5/10000ths, and outward appearance is without layering, without loose colour, qualified discharging.
Polyaspartic ester type sealant formula science for petroleum pipe line end socket of the present invention, rationally, preparation method simply, easily go, has the following advantages compared with prior art:
(1), gel time of the present invention reaches 20-120 minutes, and then extended operable time, application property is strong.The longer operating time can make form of construction work simple and convenient, can realize manual blade coating, brushing and cast.Can in narrow, complicated operating mode, construct, especially in node, flex point or the construction of cap place.The manual material construction of the present invention is simple, successful, can reduce use cost for the sealing of cap, improves the working efficiency of complex working condition.
(2), A component of the present invention replaces the aromatic isocyanate of prior art with aliphatic isocyanates, improved oil-proofness, resistance to medium, resistance to xanthochromia and the ageing-resistant performance of material.Petroleum pipe line end socket of the present invention can be used in conjunction with at oil pipeline end socket place and polyurea materials with polyaspartic ester type seal gum.
(3) resin, in existing polyurethane sealant B component is often take polyether glycol, micromolecular hydroxyl compound as main, under catalyst action with A component curing cross-linked.Catalyzer can accelerate to solidify, again can accelerated material aging.And existing polyurethane sealant only contains amino-formate bond, and mechanical property is general.The present invention replaces polyether glycol with polyaspartic ester resin, with steric hindrance ammonia chainextender synthetic B component jointly, thereby in seal gum, introduces a large amount of urea keys, and curing reaction, without catalyzer, increases the mechanics effect of material, improves the sticking power with base material.Without primary coat in the situation that, the sticking power >=9MPa on steel substrate, considerably beyond existing polyurethane type seal gum.The introducing of a large amount of urea keys also makes the performance of seal gum and pipeline corrosion protection polyureas reach unanimity, tensile strength >=20MPa, and elongation at break >=10%, tear strength >=70N/mm, has promoted the consistency of polyureas and seal gum.
(4), petroleum pipe line end socket of the present invention does not contain solvent with polyaspartic ester type seal gum, VOC free discharge, Environmental Safety.
(5), preparation method of the present invention simply, easily go, can realize petroleum pipe line end socket polyaspartic ester type seal gum suitability for industrialized production.
Embodiment
Below in conjunction with embodiment, the present invention is further described:
Embodiment 1:
The present embodiment discloses a kind of petroleum pipe line end socket polyaspartic ester type seal gum, comprises each component that weight proportion is following:
A component:
65.7 parts of hexamethylene diisocyanate trimer HDI;
34.3 parts of polytetrahydrofuran ethoxylated polyhydric alcohol PTMG-1000;
B component:
Sealing glue is prepared from by following steps:
The preparation of A component: the polytetrahydrofuran ethoxylated polyhydric alcohol PTMG-1000 of 34.3g is joined in container, by liquid material stirring at low speed after 5 minutes, be heated to 110~120 ℃, open vacuum pump, vacuum tightness is-0.1~-0.08MPa, and vacuum hydro-extraction 2h removes a small amount of water containing in raw material, detect water ratio and reach below 3/10000ths, being cooled to liquid material temperature is 25 ℃ of left and right.The hexamethylene diisocyanate HDI tripolymer of 65.7g is joined in container, stirring at normal temperature reaction 1 hour, question response heat release finishes to be slowly warming up to 80~90 ℃ afterwards, keeps reaction 2h, sampling, detect NCO% value qualified after, cooling discharge.
The preparation of B component: first by the polyaspartic ester Desmophen NH1420 of 60g, 4.5g dioctyl phthalate (DOP) adds in mixing tank, stirring at low speed running is after 5 minutes, 31g800 order fine particle calcium carbonate and 2g carbon black are added in mixing tank and high speed dispersion 30 minutes, by 1g UV-49, 1g oxidation inhibitor-264, 0.5g defoamer BYK-066N adds in mixing tank high speed dispersion 30 minutes again, the object of mixing is like this for better B component being uniformly dispersed, to product, moisture and outward appearance detects, water ratio reaches below 5/10000ths, and outward appearance is without layering, without loose colour, qualified discharging.
After being uniformly mixed than 1:1 with B constituent mass by A component when use, get final product manual application.
Use polyaspartic ester type seal gum at 25 ℃ to the petroleum pipe line end socket of above-mentioned preparation, under humidity 65% environment, carry out Mechanics Performance Testing, detected result is as shown in table 1.
The mechanical experimental results of table 1 embodiment 1 seal gum
Petroleum pipe line end socket polyaspartic ester type seal gum prepared by visible the present embodiment has excellent oil-proofness and resistance to liquid medium performance, good sealing effect; Reach unanimity with the polyureas performance on pipeline, compatible effect is good; Also there is longer gel time 30min, can realize manual blade coating.
Embodiment 2:
The present embodiment discloses a kind of petroleum pipe line end socket polyaspartic ester type seal gum, comprises each component that weight proportion is following:
A component:
50.4 parts of HMDI HMDI;
49.6 parts of polyoxytrimethylene ethoxylated polyhydric alcohol PPG-1000;
B component:
Sealing glue is prepared from by following steps:
The preparation of A component: the polyoxytrimethylene ethoxylated polyhydric alcohol PPG-1000 of 49.6g is joined in container, by liquid material stirring at low speed after 5 minutes, be heated to 110~120 ℃, open vacuum pump, vacuum tightness is-0.1~-0.08MPa, and vacuum hydro-extraction 2h removes a small amount of water containing in raw material, detect water ratio and reach below 3/10000ths, being cooled to liquid material temperature is 25 ℃ of left and right.The HMDI HMDI of 50.4g is joined in container, stirring at normal temperature reaction 1 hour, question response heat release finishes to be slowly warming up to 80~90 ℃ afterwards, keeps reaction 2h, sampling, detect NCO% value qualified after, cooling discharge.
The preparation of B component: first the Desmophen NH1520 of Desmophen NH1420, the 34.6g of 33g is added in mixing tank, stirring at low speed running is after 5 minutes, 27.9g800 order talcum powder and 2g carbon black are added in mixing tank and high speed dispersion 30 minutes, by 1g UV-49,1g oxidation inhibitor-264,0.5g defoamer BYK-066N adds in mixing tank high speed dispersion 30 minutes again, the object of mixing is like this for better B component being uniformly dispersed, to product, moisture and outward appearance detects, water ratio reaches below 5/10000ths, qualified discharging.
After being uniformly mixed than 1:1 with B constituent mass by A component when use, get final product manual application.
Use polyaspartic ester type seal gum at 25 ℃ to the petroleum pipe line end socket of above-mentioned preparation, under humidity 65% environment, carry out Mechanics Performance Testing by the experimental technique GB/T16777-2008 of architectural waterproof material, detected result is as shown in table 2.
The mechanical experimental results of table 2 embodiment 2 seal gums
Petroleum pipe line end socket polyaspartic ester type seal gum prepared by visible the present embodiment has excellent oil-proofness and resistance to liquid medium performance, good sealing effect; Reach unanimity with the polyureas performance on pipeline, compatible effect is good; Also there is longer gel time 45min, can realize manual blade coating.
Embodiment 3:
The present embodiment discloses a kind of petroleum pipe line end socket polyaspartic ester type seal gum, comprises each component that weight proportion is following:
A component:
69.3 parts of hexamethylene diisocyanate HDI tripolymers;
30.7 parts of polyoxytrimethylene ethoxylated polyhydric alcohol PPG-1000;
B component:
Sealing glue is prepared from by following steps:
The preparation of A component: the polyoxytrimethylene ethoxylated polyhydric alcohol PPG-1000 of 30.7g is joined in container, by liquid material stirring at low speed after 5 minutes, be heated to 110~120 ℃, open vacuum pump, vacuum tightness is-0.1~-0.08MPa, and vacuum hydro-extraction 2h removes a small amount of water containing in raw material, detect water ratio and reach below 3/10000ths, being cooled to liquid material temperature is 25 ℃ of left and right.The hexamethylene diisocyanate HDI tripolymer of 69.3g is joined in container, stirring at normal temperature reaction 1 hour, question response heat release finishes to be slowly warming up to 80~90 ℃ afterwards, keeps reaction 2h, sampling, detect NCO% value qualified after, cooling discharge.
The preparation of B component: first by the Desmophen NH1420 of 45.3g, the Unilink4200 of 8.5g adds in mixing tank, stirring at low speed running is after 5 minutes, light 31.7g800 order talcum powder and 2g iron oxide red are added in mixing tank and high speed dispersion 30 minutes, by 1g UV-49, 1g oxidation inhibitor-264, 0.5g defoamer BYK-066N adds in mixing tank high speed dispersion 30 minutes again, the object of mixing is like this for better B component being uniformly dispersed, to product, moisture and outward appearance detects, water ratio reaches below 5/10000ths, and outward appearance is without layering, without loose colour, qualified discharging.Two components in mass ratio 1:1 are uniformly mixed and are mixed to get polyaspartic ester type seal gum of the present invention.
After testing, the petroleum pipe line end socket polyaspartic ester type seal gum that prepared by the present embodiment has excellent oil-proofness and resistance to liquid medium performance, good sealing effect; Reach unanimity with the polyureas performance on pipeline, compatible effect is good; Also there is longer gel time 1h, can realize manual blade coating.
The present invention is not limited to petroleum pipe line end socket polyaspartic ester type seal gum and preparation method thereof that above-described embodiment is recorded, the wherein change of each composition weight proportioning, and the change of preparation condition is all within protection scope of the present invention.
Finally it should be noted that: above each embodiment, only in order to technical scheme of the present invention to be described, is not intended to limit; Although the present invention is had been described in detail with reference to aforementioned each embodiment, those of ordinary skill in the art is to be understood that: its technical scheme that still can record aforementioned each embodiment is modified, or some or all of technical characterictic is wherein equal to replacement; And these modifications or replacement do not make the essence of appropriate technical solution depart from the scope of various embodiments of the present invention technical scheme.
Claims (10)
1. a polyaspartic ester type seal gum for petroleum pipe line end socket, is characterized in that, comprises each component that weight proportion is following:
A component:
Aliphatic isocyanates 20-70 part;
Polyether glycol 20-65 part;
B component:
The mass ratio of described A component and B component is 1:1~1.3:1.
2. polyaspartic ester type seal gum for petroleum pipe line end socket according to claim 1, it is characterized in that, described aliphatic isocyanates is one or more in HMDI, hexamethylene diisocyanate trimer, isophorone diisocyanate, phenylenedimethylidyne isocyanic ester and cyclohexanedimethyleterephthalate vulcabond.
3. polyaspartic ester type seal gum for petroleum pipe line end socket according to claim 1, is characterized in that, described polyether glycol is polyoxytrimethylene ethoxylated polyhydric alcohol and/or polytetrahydrofuran polyvalent alcohol.
4. polyaspartic ester type seal gum for petroleum pipe line end socket according to claim 1, is characterized in that, described polyaspartic ester is one or more in Desmophen NH1420, Desmophen NH1520 and Desmophen NH1220.
5. polyaspartic ester type seal gum for petroleum pipe line end socket according to claim 1, it is characterized in that, described steric hindrance ammonia chainextender is 4,4'-diamino-3, one or more in 3'-dichloro diphenyl methane, Unilink4200, Unilink4100, Clearlink1000, Clearlink3000, Jefflink555 and Jefflink754.
6. polyaspartic ester type seal gum for petroleum pipe line end socket according to claim 1, it is characterized in that, described filler is one or more in fine particle calcium carbonate, coarse whiting, talcum powder, calcium hydroxide, zinc phosphate and mica powder, and described filler order number is more than 800 orders.
7. polyaspartic ester type seal gum for petroleum pipe line end socket according to claim 1, is characterized in that, described auxiliary agent is one or more in oxidation inhibitor, photostabilizer and defoamer; Described oxidation inhibitor is: one or more in oxidation inhibitor-264, antioxidant 1010 and antioxidant 1076; Described photostabilizer be in UV-9, UV-24, UV-49, UV-531 and UV-328 one or more; Described defoamer is one or more in BYK-066N, BYK-054 and BYK-5500.
8. polyaspartic ester type seal gum for petroleum pipe line end socket according to claim 1, is characterized in that, described pigment is one or more in titanium dioxide, iron oxide red, molybdenum red, indigo-blue indigo plant and carbon black.
9. polyaspartic ester type seal gum for petroleum pipe line end socket according to claim 1, is characterized in that, described softening agent is one or more in dioctyl phthalate (DOP), dibutyl phthalate and Di Iso Decyl Phthalate.
10. a preparation method for petroleum pipe line end socket use polyaspartic ester type seal gum described in claim 1-9 any one, comprises the following steps:
The preparation of A component: polyether glycol, as in container, is heated to 110~120 ℃, and vacuum hydro-extraction is removed raw water to water ratio and reached below 3/10000ths, and being cooled to liquid material temperature is 20-30 ℃; Isocyanate ester compound is joined in container, and stirring at normal temperature reaction, after 1-2 hour, is slowly warming up to 80~90 ℃, detects NCO% value and reaches after design load 98-102%, cooling discharge;
The preparation of B component: polyaspartic ester, steric hindrance ammonia chainextender are placed in to container and mix; Filler and pigment are joined in container and mixed, and mixing time is 20-60min; Then add auxiliary agent to mix, mixing time is 20-60min, and to product, moisture and outward appearance detects, and water ratio reaches below 5/10000ths, and outward appearance is without layering, without loose colour, and qualified discharging.