CN103788839A - Glass bottle coating with degrading function and glass bottle - Google Patents
Glass bottle coating with degrading function and glass bottle Download PDFInfo
- Publication number
- CN103788839A CN103788839A CN201410025003.0A CN201410025003A CN103788839A CN 103788839 A CN103788839 A CN 103788839A CN 201410025003 A CN201410025003 A CN 201410025003A CN 103788839 A CN103788839 A CN 103788839A
- Authority
- CN
- China
- Prior art keywords
- wine bottle
- coating
- glass wine
- weight
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a glass bottle coating with a degrading function and a glass bottle. A thermosetting powder coating is sprayed on the glass bottle and cured to obtain the glass bottle coating, wherein the thermosetting powder coating comprises the following raw materials in parts by weight: 25-55 parts by weight of thermosetting resin, 4-20 parts by weight of curing agent, 15-50 parts by weight of degrading agent, 0.1-5 parts by weight of flatting agent and 5-20 parts by weight of pigment and filler. According to the glass bottle coating, on the premise of meeting the basic performance of the glass bottle coating, a better degrading function of the glass bottle coating is effectively realized, and environment pollution caused by a wasted glass bottle is avoided.
Description
Technical field
The present invention relates to a kind of glass wine bottle coating, be specifically related to a kind of glass wine bottle coating and glass wine bottle with degradation function.
Background technology
Thermosetting powder coating(s) is because it is containing organic solvent, and the feature of environmental protection is good, and utilization ratio is high, and the advantage such as storage, convenient transportation is widely used in each field.Human consumer wishes can automatically degrade after the product glass wine bottle coating after thermosetting powder coating(s) application is meeting life cycle, avoids scrap glass bottle to environment, improves environmental-protecting performance.But current business-like thermosetting powder coating(s) does not have from degradation function, thereby can give environment, the product especially short for life cycle, replacement frequency is high, such as glass wine bottle, this pollution is severeer; Further, in the normal use procedure of these products, more need to guarantee that product can not produce degraded, therefore want to avoid powder coating glass wine bottle coating to environment, needing to obtain and in life cycle, can automatically not degrade but reach after life cycle, is automatically degradable product when meeting certain environment condition.
Summary of the invention
In view of this, the object of the present invention is to provide a kind of glass wine bottle coating and glass wine bottle with degradation function, meeting under the prerequisite of glass wine bottle coating fundamental property, also effectively realizing the good degradation function of glass wine bottle coating, avoiding scrap glass bottle to environment.
The technical solution used in the present invention is as follows:
Have a glass wine bottle coating for degradation function, obtain after adopting thermosetting powder coating(s) spraying, solidification treatment on glass wine bottle, wherein, described thermosetting powder coating(s) comprises the raw material of following portions by weight:
Preferably, described degradation agents is polylactic resin.
But, along with the applicant finds through lot of experiments, although polylactic resin has good degradation function, the Chinese patent that is CN103160087A as publication number discloses a kind of degradable plasticized poly lactic acid resin and preparation method thereof, belongs to polymer modification field.This polylactic resin comprises: poly(lactic acid), plasticization modifier, nucleator, oxidation inhibitor.The mass ratio of described poly(lactic acid), plasticization modifier, nucleator and oxidation inhibitor is 100: (10～40): (0.3～1): (0.3～1).Polylactic resin melt flow rate (MFR) provided by the invention can be controlled in 5～30g/10min, and tension fracture elongation rate reaches 480%, and resistance to impact shock reaches 30.0KJ/m
2, reaching polylactic acid plasticize and toughness reinforcing object, material has higher clarity and degradable property simultaneously.If but it cannot be directly applied in thermosetting powder coating(s), the thermosetting powder coating(s) preparing cannot meet Essential Performance Requirements, the particularly mechanical property requirement of glass wine bottle coating, expertise and the lot of experiments of the applicant based on accumulating for many years at thermosetting powder coating(s) found, this is because the degradation materials such as polylactic resin itself exist film performance poor, and exist consistency poor with thermosetting resin, finally make polylactic resin directly applications well in thermosetting powder coating(s).
Therefore, the present invention further proposes optimal technical scheme and solves above-mentioned technical problem.
Preferably, described thermosetting powder coating(s) also comprises the polymkeric substance of 5-20 part parts by weight, and described polymkeric substance has the hydroxyl or the carboxyl functional group that carry out crosslinked action with described polylactic resin, for improving the mechanical property of glass wine bottle coating.
Preferably, described thermosetting powder coating(s) also comprises the polyether-modified silicone resin of 5-20 part parts by weight, for strengthening the consistency of described polylactic resin and described thermosetting resin.
Preferably, described thermosetting powder coating(s) also comprises the water-retaining agent of 5-20 part parts by weight, and described water-retaining agent is the polymkeric substance that contains hydrophilic radical, and described hydrophilic radical can be any one or a few in hydroxyl, carboxyl, ester bond, amino.
Preferably, described thermosetting resin is vibrin or epoxy resin.
Preferably, described thermosetting powder coating(s) also can add the auxiliary agent of 0-15 part parts by weight, and described auxiliary agent is any one or a few the mixing in matting agent, curing catalysts, expanding material, air release agent, defoamer.
Preferably, a kind of preparation method of degradable thermosetting powder coating(s) as above, wherein, its operation steps comprises as follows:
A), whole raw materials of parts by weight described above put into mixing tank mix, obtain batch mixing;
B), batch mixing that above-mentioned steps a) is obtained is placed in forcing machine and melt extrudes, and then after cooling process, obtains compressing tablet material;
C) the first coarse reduction of compressing tablet material, above-mentioned steps b) being obtained is ground and is obtained fine powder;
D), fine powder that above-mentioned steps c) is obtained separates by cyclonic separator, classification is sieved, and detects, finished product;
E), complete the preparation of degradable thermosetting powder coating(s).
Preferably, also can add the auxiliary agent of 0-15 part parts by weight in described step in a), described auxiliary agent is any one or a few the mixing in matting agent, curing catalysts, expanding material, air release agent, defoamer.
A kind of glass wine bottle, comprises glass wine bottle, is coated with glass wine bottle coating on described glass wine bottle, and wherein, described glass wine bottle coating adopts the glass wine bottle coating with degradation function as above.
The present invention is by proposing to realize at thermosetting powder coating(s) interpolation degradation agents the degradation function of glass wine bottle coating, particularly, adopt polylactic resin as degradation agents, in realizing good degradation function, the environmental protection characteristic that can also keep thermosetting powder coating(s) itself to possess, the present invention simultaneously considers because poly(lactic acid) itself exists film performance poor, and exist consistency poor with thermosetting resin, finally can make to prepare the thermosetting powder coating(s) that meets related request (particularly mechanical property of glass wine bottle coating etc.), thereby proposition adds the polymkeric substance of 5-20 part parts by weight in thermosetting powder coating(s), this polymkeric substance has the hydroxyl or the carboxyl functional group that carry out crosslinked action with polylactic resin, for improving the mechanical property of glass wine bottle coating, further, in thermosetting powder coating(s), add the polyether-modified silicone resin of 5-20 part parts by weight, for strengthening the consistency of polylactic resin and thermosetting resin, and then improve the surface tension of glass wine bottle coating, finally obtain level and smooth glass wine bottle coating, therefore the present invention is meeting under the prerequisite of thermosetting powder coating(s) fundamental property, realize the applications well of polylactic resin in thermosetting powder coating(s), finally realize the good degradation function of glass wine bottle coating, avoided scrap glass bottle to environment.
The present invention further preferably, proposes in thermosetting powder coating(s), to add the water-retaining agent with hydrophilic radical, further improves the degradation function of glass wine bottle coating of the present invention.
Accompanying drawing explanation
Accompanying drawing 1 is the preparation process block diagram of thermosetting powder coating(s) under the specific embodiment of the invention.
Embodiment
The embodiment of the invention discloses a kind of glass wine bottle coating with degradation function, obtain after adopting thermosetting powder coating(s) spraying, solidification treatment on glass wine bottle, wherein, thermosetting powder coating(s) comprises the raw material of following portions by weight:
The embodiment of the invention also discloses a kind of glass wine bottle, comprise glass wine bottle, be coated with glass wine bottle coating on glass wine bottle, wherein, glass wine bottle coating adopts the glass wine bottle coating with degradation function as above.
The embodiment of the present invention is by proposing to realize at thermosetting powder coating(s) interpolation degradation agents the degradation function of glass wine bottle coating, particularly, adopt polylactic resin as degradation agents, in realizing good degradation function, the environmental protection characteristic that can also keep thermosetting powder coating(s) itself to possess, the embodiment of the present invention is considered because poly(lactic acid) itself exists film performance poor simultaneously, and exist consistency poor with thermosetting resin, finally can make to prepare the thermosetting powder coating(s) that meets related request (particularly mechanical property of glass wine bottle coating etc.), thereby proposition adds the polymkeric substance of 5-20 part parts by weight in thermosetting powder coating(s), this polymkeric substance has the hydroxyl or the carboxyl functional group that carry out crosslinked action with polylactic resin, for improving the mechanical property of glass wine bottle coating, further, in thermosetting powder coating(s), add the polyether-modified silicone resin of 5-20 part parts by weight, for strengthening the consistency of polylactic resin and thermosetting resin, and then improve the surface tension of glass wine bottle coating, finally obtain level and smooth glass wine bottle coating, therefore the embodiment of the present invention is meeting under the prerequisite of thermosetting powder coating(s) fundamental property, realize the applications well of polylactic resin in thermosetting powder coating(s), finally realize the good degradation function of glass wine bottle coating, avoided scrap glass bottle to environment.
In order to be illustrated more clearly in the embodiment of the present invention or technical scheme of the prior art, to the accompanying drawing of required use in embodiment or description of the Prior Art be briefly described below, apparently, the accompanying drawing the following describes is only some embodiment that record in the present invention, for those of ordinary skills, do not paying under the prerequisite of creative work, can also obtain according to these accompanying drawings other accompanying drawing.
Embodiment 1:
There is a glass wine bottle coating for degradation function, obtain adopt thermosetting powder coating(s) spraying, solidification treatment on glass wine bottle after;
Wherein, thermosetting powder coating(s) comprises the raw material of following portions by weight:
35 parts of thermosetting resins, particularly, in the present embodiment, thermosetting resin adopts vibrin;
5 parts, solidifying agent, particularly, in the present embodiment, solidifying agent is triglycidyl isocyanurate;
20 parts of degradation agentss, wherein, specifically preferably, in the present embodiment, degradation agents is polylactic resin, particularly, the making processes of polylactic resin can adopt the preparation method of any one common practise to prepare, further particularly, in the present embodiment, its preparation method can adopt starch material to obtain glucose via saccharification, then makes highly purified lactic acid by glucose and certain strain fermentation, then is synthesized and obtained polylactic resin by chemical synthesis process;
1 part of flow agent;
8 parts of color stuffings;
The polymkeric substance of 10 parts of parts by weight, particularly, in the present embodiment, this polymkeric substance has the hydroxy functional group that carries out crosslinked action with polylactic resin, for improving the mechanical property of glass wine bottle coating, in reality, can adopt the polymkeric substance of any one common practise, more preferably, adopt the polymkeric substance of polyhydroxy functional groups;
The polyether-modified silicone resin of 10 parts of parts by weight, for strengthening the consistency of polylactic resin and vibrin, and then improves the surface tension of glass wine bottle coating, makes the glass wine bottle coating of acquisition level and smooth;
The water-retaining agent of 10 parts of parts by weight, water-retaining agent is the polymkeric substance that contains hydrophilic radical, hydrophilic radical can be hydroxyl, carboxyl, ester bond, any one or a few in amino, particularly, in the present embodiment, hydrophilic radical is hydroxyl, more specifically, polymkeric substance in the present embodiment also can be simultaneously as water-retaining agent, at this moment because the hydroxy functional group in polymkeric substance or carboxyl functional group both can produce crosslinked action with polylactic resin, also can be used as hydrophilic radical simultaneously, in the time that reality is used, hydroxy functional group in polymkeric substance or carboxyl functional group and polylactic resin,
The air release agent of 0.5 part of parts by weight;
The defoamer of 0.5 part of parts by weight.
In the present embodiment, flow agent, air release agent and defoamer all can adopt any one material in existing known technology, as flow agent can adopt homopolymer and multipolymer and the modified polyorganosiloxane of acrylate, as air release agent and defoamer can adopt wax, st-yrax.
Organic color stuffings such as color stuffing can be that coupling is red, thioindigo, castor quinone or azo or for inorganic color stuffings such as titanium dioxide, ferric oxide, magnesium oxide etc., can certainly adopt other well known materials, color stuffing can strengthen color and the opacifying power of powder coating, and can strengthen the texture of powder coating.
Natch, in other embodiments, thermosetting powder coating(s) provided by the invention can also add other auxiliary agents of certainweight umber, for example wax class matting agent, for regulating the gloss of thermosetting powder coating(s), obtain having the powder coating of various luster degree, also can add according to actual needs and promote curing curing catalysts, or add and promote the expanding material of the different components of thermosetting powder coating(s) in melt stage consistency, or add aluminum oxide growth agent auxiliary agent etc., particularly, wax class matting agent, curing catalysts, expanding material and aluminum oxide growth agent auxiliary agent all can adopt any one in existing commercially produced product.
Shown in Figure 1, in this embodiment, the preparation method of degradable thermosetting powder coating(s) as above, wherein, its operation steps comprises as follows:
A), whole raw materials of parts by weight described above put into mixing tank mix, obtain batch mixing;
B), batch mixing that above-mentioned steps a) is obtained is placed in forcing machine and melt extrudes, and then after cooling process, obtains compressing tablet material;
C) the first coarse reduction of compressing tablet material, above-mentioned steps b) being obtained is ground and is obtained fine powder;
D), fine powder that above-mentioned steps c) is obtained separates by cyclonic separator, classification is sieved, and detects, finished product;
E), complete the preparation of degradable thermosetting powder coating(s).
In this embodiment, a kind of glass wine bottle coating, obtains after adopting thermosetting powder coating(s) spraying, solidification treatment on glass wine bottle, and wherein, thermosetting powder coating(s) adopts degradable thermosetting powder coating(s) as above.
Embodiment 2:
In the present embodiment 2, thermosetting powder coating(s) comprises the raw material of following portions by weight:
The polymkeric substance of 5 parts of parts by weight, particularly, in the present embodiment, this polymkeric substance has the carboxyl functional group that carries out crosslinked action with polylactic resin, for improving the mechanical property of glass wine bottle coating;
The polyether-modified silicone resin of 5 parts of parts by weight;
The water-retaining agent of 5 parts of parts by weight, water-retaining agent is the polymkeric substance that contains hydrophilic radical, hydrophilic radical is carboxyl;
All the other technical schemes of the present embodiment 2 are identical with above-described embodiment 1.
Embodiment 3:
In the present embodiment 3, thermosetting powder coating(s) comprises the raw material of following portions by weight:
The polymkeric substance of 5 parts of parts by weight, particularly, in the present embodiment, this polymkeric substance has the carboxyl functional group that carries out crosslinked action with polylactic resin, for improving the mechanical property of glass wine bottle coating;
The polyether-modified silicone resin of 20 parts of parts by weight;
The water-retaining agent of 5 parts of parts by weight, water-retaining agent is the polymkeric substance that contains hydrophilic radical, hydrophilic radical is ester bond;
The air release agent of 0.5 part of parts by weight;
The defoamer of 0.5 part of parts by weight;
All the other technical schemes of the present embodiment 3 are identical with above-described embodiment 1.
Embodiment 4:
In the present embodiment 4, thermosetting powder coating(s) comprises the raw material of following portions by weight:
The polymkeric substance of 5 parts of parts by weight, particularly, in the present embodiment, this polymkeric substance has the carboxyl functional group that carries out crosslinked action with polylactic resin, for improving the mechanical property of glass wine bottle coating;
The polyether-modified silicone resin of 5 parts of parts by weight;
The water-retaining agent of 5 parts of parts by weight, water-retaining agent is the polymkeric substance that contains hydrophilic radical, hydrophilic radical is amino;
All the other technical schemes of the present embodiment 4 are identical with above-described embodiment 1.
Embodiment 5:
In the present embodiment 5, thermosetting powder coating(s) comprises the raw material of following portions by weight:
The polymkeric substance of 5 parts of parts by weight, particularly, in the present embodiment, this polymkeric substance has the carboxyl functional group that carries out crosslinked action with polylactic resin, for improving the mechanical property of glass wine bottle coating;
The polyether-modified silicone resin of 5 parts of parts by weight;
The water-retaining agent of 5 parts of parts by weight, water-retaining agent is the polymkeric substance that contains hydrophilic radical, hydrophilic radical is hydroxyl;
The air release agent of 0.5 part of parts by weight;
The defoamer of 0.5 part of parts by weight;
All the other technical schemes of the present embodiment 5 are identical with above-described embodiment 1.
Embodiment 6:
All the other technical schemes of the present embodiment 6 are identical with above-described embodiment 1, and difference is only following:
The polymkeric substance of 10 parts of parts by weight;
The polyether-modified silicone resin of 20 parts of parts by weight;
Do not contain water-retaining agent.
Embodiment 7:
All the other technical schemes of the present embodiment 7 are identical with above-described embodiment 1, and difference is only following:
The polymkeric substance of 20 parts of parts by weight;
The polyether-modified silicone resin of 10 parts of parts by weight;
Do not contain water-retaining agent.
Embodiment 8:
All the other technical schemes of the present embodiment 8 are identical with above-described embodiment 1, and difference is only following:
The polymkeric substance of 30 parts of parts by weight;
Do not contain polyether-modified silicone resin and water-retaining agent.
Embodiment 9:
All the other technical schemes of the present embodiment 9 are identical with above-described embodiment 1, and difference is only following:
The polyether-modified silicone resin of 30 parts of parts by weight;
Do not contain polymkeric substance and water-retaining agent.
Embodiment 10:
All the other technical schemes of the present embodiment 10 are identical with above-described embodiment 1, and difference is only following:
The polymkeric substance of 20 parts of parts by weight;
The water-retaining agent of 10 parts of parts by weight;
Do not contain polyether-modified silicone resin.
Embodiment 11:
All the other technical schemes of the present embodiment 11 are identical with above-described embodiment 1, and difference is only following:
The polyether-modified silicone resin of 20 parts of parts by weight;
The water-retaining agent of 10 parts of parts by weight;
Do not contain polymkeric substance.
Embodiment 12:
All the other technical schemes of the present embodiment 12 are identical with above-described embodiment 1, and difference is only following:
The water-retaining agent of 30 parts of parts by weight, wherein, the hydrophilic radical in water-retaining agent is amino;
Do not contain polymkeric substance and polyether-modified silicone resin.
Embodiment 13:
In the present embodiment 13, thermosetting powder coating(s) comprises the raw material of following portions by weight:
The air release agent of 0.5 part of parts by weight;
The defoamer of 0.5 part of parts by weight;
All the other technical schemes of the present embodiment 13 are identical with above-described embodiment 1.
Embodiment 14:
All the other technical schemes of the present embodiment 14 are identical with above-described embodiment 1, distinguish and are only, in the present embodiment 14, thermosetting resin adopts epoxy resin, and solidifying agent is the property class of diving; Primary, secondary amine; Acid anhydrides and compounds thereof; Or any one in resol class solidifying agent, particularly, in the present embodiment, adopt acid anhydride type curing agent.In other embodiment, can also adopt the thermosetting resin of other classifications, launch no longer one by one in this article to repeat.
Comparative example 1:
This comparative example 1 adopts existing business-like thermosetting powder coating(s), and all the other technical schemes are identical with above-described embodiment 1.
The present invention is directed to above-described embodiment and comparative example and carried out implementation result test, concrete test result is as following table 1.
All kinds of glass wine bottle coating performance of table 1 test result
High-pressure water boiling test described in the present invention is in full to test acquired results with reference to ENISO2409 standard, described cross-hatching sticking power is to test acquired results with reference to GB/T9286-1998 standard, and described 60 ° of gloss are to test acquired results with reference to GB/T9754-2007 standard.
Degradation time described in the present invention in full refers to that glass wine bottle coating glass wine bottle coating after this test duration departs from the time of base material completely, wherein, the first degradation time refers to glass wine bottle to be coated with to be placed on tests rear acquired results under outdoor physical environment, the second degradation time refers to glass wine bottle is coated with and is placed on pH=4.5, and relative humidity is greater than under 98% indoor conditions tests rear acquired results.
From table 1, data can obviously be found out, the embodiment of the present invention has all realized degradation function, wherein, glass wine bottle is coated with and is placed on pH=4.5, relative humidity is greater than degradation speed under 98% indoor conditions and is greater than it and is placed in the degradation speed under outdoor physical environment, and the degradation function that adds the embodiment of water-retaining agent is better than with respect to the embodiment that does not add water-retaining agent, this is because polylactic resin is under outdoor physical environment, be subject to nature microorganism Degradation, in conjunction with the ultraviolet irradiation in natural light, further strengthen degradation function simultaneously; And at acidic conditions, and under the environment of high humidity, both can there is hydrolytic deterioration in polylactic resin, find microbiological deterioration, therefore its degradation speed is faster than the glass wine bottle coating under outdoor physical environment, and adds after water-retaining agent simultaneously, when glass wine bottle coating is under physical environment or humidity environment, water-retaining agent in glass wine bottle coating will adsorb moisture content, thereby promotes the polylactic resin degraded that is hydrolyzed, thereby realizes the degradation function of glass wine bottle coating.
But embodiment 12 and embodiment 13 are difficult to meet the basic mechanical property demand of conventional industry for glass wine bottle coating, this is because poly(lactic acid) itself exists film performance poor, and exist consistency poor with thermosetting resin, and other embodiment have all added polymkeric substance in thermosetting powder coating(s), this polymkeric substance has the hydroxyl or the carboxyl functional group that carry out crosslinked action with polylactic resin, for improving the mechanical property of glass wine bottle coating; Or in thermosetting powder coating(s), add polyether-modified silicone resin, and for strengthening the consistency of polylactic resin and thermosetting resin, and then improve the surface tension of glass wine bottle coating, finally obtain level and smooth glass wine bottle coating; Therefore the embodiment of the present invention is meeting under the prerequisite of thermosetting powder coating(s) fundamental property, realize the applications well of polylactic resin in thermosetting powder coating(s), finally realize the good degradation function of thermosetting powder coating(s), avoided scrap glass bottle to environment.Wherein, from table 1, data also can obviously be found out, add polyether-modified silicone resin to be better than to add for the net effect that improves glass wine bottle coating performance and there is the effect of carrying out the hydroxyl of crosslinked action or the polymkeric substance of carboxyl functional group with polylactic resin, and add polyether-modified silicone resin simultaneously and there is the implementation result the best of carrying out the hydroxyl of crosslinked action or the polymkeric substance of carboxyl functional group with polylactic resin, can prepare high-quality glass wine bottle coating, be most preferred embodiment of the present invention.
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and in the situation that not deviating from spirit of the present invention or essential characteristic, can realize the present invention with other specific form.Therefore, no matter from which point, all should regard embodiment as exemplary, and be nonrestrictive, scope of the present invention is limited by claims rather than above-mentioned explanation, is therefore intended to all changes that drop in the implication and the scope that are equal to important document of claim to include in the present invention.Any Reference numeral in claim should be considered as limiting related claim.
In addition, be to be understood that, although this specification sheets is described according to embodiment, but be not that each embodiment only comprises an independently technical scheme, this narrating mode of specification sheets is only for clarity sake, those skilled in the art should make specification sheets as a whole, and the technical scheme in each embodiment also can, through appropriately combined, form other embodiments that it will be appreciated by those skilled in the art that.
Claims (10)
1. have a glass wine bottle coating for degradation function, obtain after adopting thermosetting powder coating(s) spraying, solidification treatment on glass wine bottle, it is characterized in that, described thermosetting powder coating(s) comprises the raw material of following portions by weight:
2. the glass wine bottle coating with degradation function as claimed in claim 1, is characterized in that, described degradation agents is polylactic resin.
3. the glass wine bottle coating with degradation function as claimed in claim 2, it is characterized in that, described thermosetting powder coating(s) also comprises the polymkeric substance of 5-20 part parts by weight, described polymkeric substance has the hydroxyl or the carboxyl functional group that carry out crosslinked action with described polylactic resin, for improving the mechanical property of glass wine bottle coating.
4. the glass wine bottle coating with degradation function as claimed in claim 2, it is characterized in that, described thermosetting powder coating(s) also comprises the polyether-modified silicone resin of 5-20 part parts by weight, for strengthening the consistency of described polylactic resin and described thermosetting resin.
5. the glass wine bottle coating with degradation function as described in claim 3 or 4, it is characterized in that, described thermosetting powder coating(s) also comprises the water-retaining agent of 5-20 part parts by weight, described water-retaining agent is the polymkeric substance that contains hydrophilic radical, and described hydrophilic radical can be any one or a few in hydroxyl, carboxyl, ester bond, amino.
6. the glass wine bottle coating with degradation function as claimed in claim 1, is characterized in that, described thermosetting resin is vibrin or epoxy resin.
7. the glass wine bottle coating with degradation function as claimed in claim 1, it is characterized in that, described thermosetting powder coating(s) also can add the auxiliary agent of 0-15 part parts by weight, and described auxiliary agent is any one or a few the mixing in matting agent, curing catalysts, expanding material, air release agent, defoamer.
8. the glass wine bottle coating with degradation function as described in claim 1-6 any one, is characterized in that, the operation steps of preparing described thermosetting powder coating(s) comprises as follows:
A), whole raw materials of parts by weight as described in claim 1-6 any one put into mixing tank mix, obtain batch mixing;
B), batch mixing that above-mentioned steps a) is obtained is placed in forcing machine and melt extrudes, and then after cooling process, obtains compressing tablet material;
C) the first coarse reduction of compressing tablet material, above-mentioned steps b) being obtained is ground and is obtained fine powder;
D), fine powder that above-mentioned steps c) is obtained separates by cyclonic separator, classification is sieved, and detects, finished product;
E), complete the preparation of degradable thermosetting powder coating(s).
9. the glass wine bottle coating with degradation function as claimed in claim 8, it is characterized in that, also can add the auxiliary agent of 0-15 part parts by weight in a) in described step, described auxiliary agent is any one or a few the mixing in matting agent, curing catalysts, expanding material, air release agent, defoamer.
10. a glass wine bottle, comprises glass wine bottle, is coated with glass wine bottle coating on described glass wine bottle, it is characterized in that, described glass wine bottle coating adopts the glass wine bottle coating with degradation function as described in any one in claim 1-9.