CN103788816A - Coating for universal node - Google Patents
Coating for universal node Download PDFInfo
- Publication number
- CN103788816A CN103788816A CN201410023424.XA CN201410023424A CN103788816A CN 103788816 A CN103788816 A CN 103788816A CN 201410023424 A CN201410023424 A CN 201410023424A CN 103788816 A CN103788816 A CN 103788816A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- universal joint
- powder
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a coating for a universal node. The coating is prepared from the following components in parts by weight: 100 parts of epoxy resin, 14-16 parts of melamine, 20-30 parts of zinc powder, 10-15 parts of aluminum powder, 8-10 parts of dimethylformamide, 1-2 parts of carbon black, 25-35 parts of glycol ether, 10-12 parts of modifier, 8-10 parts of acetone and 1-1.5 parts of talcum powder. The surface drying time of the coating product is 2-3h and the solid drying time is 10-15h; and the coating resists the high temperature of 371 DEG C for 5 days, resists salt mist for 500h, resists acid and alkali, is high in the impact strength, is long in the service life, can be widely produced and can be used for continuously replacing the existing materials.
Description
Technical field
The application belongs to metallic paint field, relates in particular to a kind of universal joint coating.
Background technology
So-called universal joint refers to devices such as utilizing ball-type and exports with the axle power of realizing different directions, and it is also on automobile one very vitals.Universal joint and transmission shaft combination, be called cardan gear.On the vehicle of front-mounted engine rear wheel drive, cardan gear is arranged between transmission output shaft and main reducing gear of drive axle input shaft; And the vehicle of front-mounted engine front-wheel drive has omitted transmission shaft, universal joint is arranged between not only responsible driving but also the front axle half shaft of being responsible for turning to and wheel; Between the variator and drive axle of engine behind front wheel rear wheel drive truck.When distant between variator and drive axle, transmission shaft should be divided into two sections of even multistages, and add intermediate support.Between the transfer gear of many shaft-driven automobiles and drive axle or between drive axle and drive axle.Due to the distortion of vehicle frame, can cause between two drive disk assemblies that between axis, mutual alignment changes.Be depicted as between engine and variator.The structure of universal joint and effect are a little as the joint in human limb, and the angle between the part that it allows to be connected changes within the specific limits.The angle causing for the bob that meets transmission of power, adapts to produce while turning to automobilism changes, the drive axle of front drive automobile, and between semiaxis and wheel shaft, conventional universal joint is connected.But owing to being subject to the restriction of axial dimension, require drift angle larger again, the instantaneous angular velocity that single universal joint can not make output shaft and axle enter axle equates, easily cause vibration, the damage of aggravation parts, and produce very large noise, so extensively adopt constant velocity cardan joint miscellaneous.On front drive automobile, two constant velocity cardan joints for each semiaxis, are inboard universal joints near the universal joint of transaxle, and near axletree is outboard universal joint.On rear-drive automobile, engine, clutch coupling and variator are as a complete installation on vehicle frame, and drive axle is connected with vehicle frame by resilient suspension, has a distance between the two, need to connect.In automobilism, Uneven road produces and beats, the potential difference of load variations or two assembly installations etc., capital changes angle and the distance between transmission output shaft and main reducing gear of drive axle input shaft, therefore all adopt double Hooke's joint at the universal joint type of belt drive of rear-drive automobile, be exactly that transmission shaft two ends respectively have a universal joint, its effect is that the angle at transmission shaft two ends is equated, thereby guarantees that output shaft equates all the time with the instantaneous angular velocity of input shaft.
Epoxy resin is the organic high molecular compound that contains two or more epoxide groups in general reference molecule, and except indivedual, their relative molecular mass is not high.The molecular structure of epoxy resin is to contain active epoxide group in molecular chain as its feature, and epoxide group can be positioned at the end, centre of molecular chain or structure circlewise.Owing to containing active epoxide group in molecular structure, make them can form with polytype solidifying agent generation crosslinking reaction insoluble, the molten cancellated superpolymer of three-dimensional that has; The epoxy resin of domestic actual production only has several trades mark of bisphenol A-type.According to statistics, within 1997, national epoxy resin demand is about 110kt, and turnout is about 30kt, and import volume is about 60kt.The production kind trade mark of domestic epoxy is very single, is mainly bisphenol A-type.Due to domestic epoxy inferior quality, manyly require the high occasion must the external high-quality epoxy of import, as high-quality liquid epoxy, brominated epoxy, phenolic aldehyde epoxy etc.And universal along with humanity concept, and the formation of novel harmonious society, design a kind of universal joint coating and be very important.
Summary of the invention
the technical problem solving:
The application, for above-mentioned technical problem, provides a kind of universal joint coating, solves existing universal joint coating long time of drying, not salt spray resistance, the technical problems such as non-refractory.
technical scheme:
A kind of universal joint coating, be made up of following raw materials according, take mass fraction representation as 100 parts of epoxy resin; Trimeric cyanamide 14-16 part; Zinc powder 20-30 part; Aluminium powder 10-15 part; Dimethyl formamide 8-10 part; Carbon black 1-2 part; Ethylene glycol ethyl ether 25-35 part; Properties-correcting agent 10-12 part; Acetone 8-10 part; Talcum powder 1-1.5 part.
As a preferred technical solution of the present invention: its composition is take mass fraction representation as 100 parts of epoxy resin; Trimeric cyanamide 14-16 part; Zinc powder 20-30 part; Aluminium powder 10-15 part; Dimethyl formamide 8-10 part; Carbon black 1-2 part; Ethylene glycol ethyl ether 25-35 part; Properties-correcting agent 10-12 part; Acetone 8-10 part; Talcum powder 1-1.5 part.
As a preferred technical solution of the present invention: described properties-correcting agent adopts glycidyl methacrylate.
beneficial effect:
A kind of universal joint of the present invention adopts above technical scheme compared with prior art with coating, has following technique effect: 1, product surface drying 2-3h, does solid work 10-15h; 2, resistance to 371 ℃ of high temperature, 5 days; 3, salt spray resistance 500h, acid and alkali-resistance; 4, high, the long service life of product shock strength, can the not division of history into periods of widespread production for current material.
Embodiment
embodiment 1:
A kind of universal joint coating, its composition is take mass fraction representation as 100 parts of epoxy resin; 14 parts of trimeric cyanamides; 20 parts of zinc powders; 10 parts of aluminium powders; 8 parts of dimethyl formamides; 1 part of carbon black; 25 parts of ethylene glycol ethyl ethers; 10 parts of glycidyl methacrylate; 8 parts, acetone; 1 part of talcum powder.
Product surface drying 3h, does solid work 15h; Resistance to 371 ℃ of high temperature, 5 days; Salt spray resistance 500h.
embodiment 2:
A kind of universal joint coating, its composition is take mass fraction representation as 100 parts of epoxy resin; 16 parts of trimeric cyanamides; 30 parts of zinc powders; 15 parts of aluminium powders; 10 parts of dimethyl formamides; 2 parts of carbon blacks; 35 parts of ethylene glycol ethyl ethers; 12 parts of glycidyl methacrylate; 10 parts, acetone; 1.5 parts of talcum powder.
Product surface drying 2.5h, does solid work 12.5h; Resistance to 371 ℃ of high temperature, 5 days; Salt spray resistance 500h.
embodiment 3:
A kind of universal joint coating, its composition is take mass fraction representation as 100 parts of epoxy resin; 15 parts of trimeric cyanamides; 25 parts of zinc powders; 12.5 parts of aluminium powders; 9 parts of dimethyl formamides; 1.5 parts of carbon blacks; 30 parts of ethylene glycol ethyl ethers; 11 parts of glycidyl methacrylate; 9 parts, acetone; 1.2 parts of talcum powder.
Product surface drying 2h, does solid work 10h; Resistance to 371 ℃ of high temperature, 5 days; Salt spray resistance 500h.
Composition all components in above embodiment all can business be bought.
Above-described embodiment is just for content of the present invention is set forth, rather than restriction, and therefore any change in implication and the scope suitable with claims of the present invention, all should think to be included in the scope of claims.
Claims (3)
1. a universal joint coating, is characterized in that: its composition is take mass fraction representation as 100 parts of epoxy resin; Trimeric cyanamide 14-16 part; Zinc powder 20-30 part; Aluminium powder 10-15 part; Dimethyl formamide 8-10 part; Carbon black 1-2 part; Ethylene glycol ethyl ether 25-35 part; Properties-correcting agent 10-12 part; Acetone 8-10 part; Talcum powder 1-1.5 part.
2. a kind of universal joint coating according to claim 1, is characterized in that: its composition is take mass fraction representation as 100 parts of epoxy resin; 15 parts of trimeric cyanamides; 25 parts of zinc powders; 12.5 parts of aluminium powders; 9 parts of dimethyl formamides; 1.5 parts of carbon blacks; 30 parts of ethylene glycol ethyl ethers; 11 parts of properties-correcting agent; 9 parts, acetone; 1.2 parts of talcum powder.
3. a kind of universal joint coating according to claim 1, is characterized in that: described properties-correcting agent adopts glycidyl methacrylate.