CN103773155A - Antibacterial heat insulation reflective coating and preparation method thereof - Google Patents
Antibacterial heat insulation reflective coating and preparation method thereof Download PDFInfo
- Publication number
- CN103773155A CN103773155A CN201410031302.5A CN201410031302A CN103773155A CN 103773155 A CN103773155 A CN 103773155A CN 201410031302 A CN201410031302 A CN 201410031302A CN 103773155 A CN103773155 A CN 103773155A
- Authority
- CN
- China
- Prior art keywords
- parts
- reflective coating
- antibacterial
- preparation
- heat insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to an antibacterial heat insulation reflective coating and a preparation method of the antibacterial heat insulation reflective coating and belongs to the technical field of coatings. The coating comprises the following components in parts by weight: 40-55 parts of silicone acrylic emulsion, 2-4 parts of nanometer titania, 1-2 parts of nano-zinc oxide, 1-3 parts of zinc pyrithione, 6-9 parts of vermiculite, 5-12 parts of sepiolite, 4-7 parts of organobentonite, 0.5-1 part of a dispersing agent, 0.5-2 parts of a defoaming agent and 18-30 parts of water. The preparation method is simple, and the prepared antibacterial heat insulation reflective coating is high in flexibility, high in adhesion force, high in heat reflectivity and good in heat insulation effect and has a good antibacterial effect. Meanwhile, the product is wide in application range, can be used for life-saving equipment such as life jackets and also can be used for other textiles, pipelines and ships.
Description
Technical field
The invention belongs to technical field of coatings, be specifically related to a kind of antibacterial adiabatic reflective coating and preparation method thereof.
Background technology
Personal life-saving appliance, as vestlifejacket, generally adopts porous plastics or cork etc. to make, and is through and has enough buoyancy with it, and drowning people's head can be surfaced.But in icy water, human body temperature declines and is exceedingly fast, therefore, be badly in need of developing the better heat preservation that how to make vestlifejacket.
Most thermal insulation coatings is applied to construction engineering technical field in the market, and snappiness, compactness and the sticking power of this class coating are generally poor, should not be coated on textile surface, and also more single, do not there is anti-microbial effect.Therefore how overcoming the deficiencies in the prior art is current technical field of coatings problem demanding prompt solutions.
Summary of the invention
The object of the invention is in order to solve the deficiencies in the prior art, a kind of antibacterial adiabatic reflective coating and preparation method thereof is provided.Product snappiness of the present invention is good, strong adhesion, and heat reflectivity is high, and insulation effect is good, has good antibacterial effect.
The technical solution used in the present invention is as follows:
A kind of antibacterial adiabatic reflective coating, comprises the following component according to parts by weight meter: 40 ~ 55 parts of organosilicon crylic acid latexs, 2 ~ 4 parts of nano titanium oxides, 1 ~ 2 part of nano zine oxide, 1 ~ 3 part of Zinc Pyrithione, 6 ~ 9 parts of vermiculites, 5 ~ 12 parts of sepiolites, 4 ~ 7 parts of organobentonites, 0.5 ~ 1 part of dispersion agent, 0.5 ~ 2 part of defoamer, 18 ~ 30 parts, water.
Described dispersion agent is dispersion agent 5040.
Described defoamer is mineral oil defoaming agent.
The present invention also provides a kind of preparation method of antibacterial adiabatic reflective coating, comprises the steps:
Step (1): vermiculite, sepiolite and organobentonite are ground to 120 ~ 200 orders;
Step (2): organosilicon crylic acid latex is added to the water, then adds wherein dispersion agent and defoamer, after being stirred to and mixing, then add step (1) ground vermiculite, sepiolite and organobentonite, continue to stir, obtain slurry;
Step (3): nano titanium oxide, nano zine oxide and Zinc Pyrithione are joined in the slurry of step (2), continue to be stirred to and mix, obtain antibacterial adiabatic reflective coating of the present invention.
The constructional method of this coating is similar to the constructional method of general coating, can adopt plasma spraying, electrostatic spraying, brushing, dip coating, roll roller coat apply etc., can be according to different coating processs, adjusting coating viscosity.
compared with prior art, its beneficial effect is in the present invention:preparation method of the present invention is simple, and the antibacterial adiabatic reflective coating snappiness making is good, strong adhesion, and heat reflectivity is high, and insulation effect is good, has good antibacterial effect; Meanwhile, product application scope of the present invention is wider, not only can, on the survival equipment such as vestlifejacket, can also be used for other textiless and pipeline, boats and ships etc.
Specific embodiment
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1
A kind of antibacterial adiabatic reflective coating, comprises the following component according to parts by weight meter: 40 parts of organosilicon crylic acid latexs, 2 parts of nano titanium oxides, 1 part of nano zine oxide, 1 part of Zinc Pyrithione, 6 parts of vermiculites, 5 parts of sepiolites, 4 parts of organobentonites, 5,040 0.5 parts of dispersion agents, 0.5 part of mineral oil defoaming agent, 18 parts, water.
The preparation method of the antibacterial adiabatic reflective coating of the present embodiment, comprises the steps:
Step (1): vermiculite, sepiolite and organobentonite are ground to 120 ~ 200 orders;
Step (2): organosilicon crylic acid latex is added to the water, then adds wherein dispersion agent 5040 and mineral oil defoaming agent, after being stirred to and mixing, then add step (1) ground vermiculite, sepiolite and organobentonite, continue to stir, obtain slurry;
Step (3): nano titanium oxide, nano zine oxide and Zinc Pyrithione are joined in the slurry of step (2), continue to be stirred to and mix, obtain the antibacterial adiabatic reflective coating of the present embodiment.
Embodiment 2
A kind of antibacterial adiabatic reflective coating, comprises the following component according to parts by weight meter: 55 parts of organosilicon crylic acid latexs, 4 parts of nano titanium oxides, 2 parts of nano zine oxides, 3 parts of Zinc Pyrithione, 9 parts of vermiculites, 12 parts of sepiolites, 7 parts of organobentonites, 5,040 1 parts of dispersion agents, 2 parts of mineral oil defoaming agents, 30 parts, water.
The preparation method of the antibacterial adiabatic reflective coating of the present embodiment is identical with the preparation method of embodiment 1.
Embodiment 3
A kind of antibacterial adiabatic reflective coating, comprises the following component according to parts by weight meter: 48 parts of organosilicon crylic acid latexs, 3.1 parts of nano titanium oxides, 1.6 parts of nano zine oxides, 2 parts of Zinc Pyrithione, 8 parts of vermiculites, 9 parts of sepiolites, 5 parts of organobentonites, 5,040 0.9 parts of dispersion agents, 1.2 parts of mineral oil defoaming agents, 26 parts, water.
The preparation method of the antibacterial adiabatic reflective coating of the present embodiment is identical with the preparation method of embodiment 1.
performance Detection
To the performance test of the embodiment of the present invention 1 ~ 3 products obtained therefrom, result is as shown in table 1.
Table 1 embodiment of the present invention 1 ~ 3 product performance test data
, the sterilizing rate of embodiment 1 ~ 3 product is detected, detected result is as shown in table 2 meanwhile.
The sterilizing rate detected result of table 2 embodiment 1 ~ 3 product
Claims (4)
1. an antibacterial adiabatic reflective coating, is characterized in that comprising the following component according to parts by weight meter: 40 ~ 55 parts of organosilicon crylic acid latexs, 2 ~ 4 parts of nano titanium oxides, 1 ~ 2 part of nano zine oxide, 1 ~ 3 part of Zinc Pyrithione, 6 ~ 9 parts of vermiculites, 5 ~ 12 parts of sepiolites, 4 ~ 7 parts of organobentonites, 0.5 ~ 1 part of dispersion agent, 0.5 ~ 2 part of defoamer, 18 ~ 30 parts, water.
2. antibacterial adiabatic reflective coating according to claim 1, is characterized in that described dispersion agent is dispersion agent 5040.
3. antibacterial adiabatic reflective coating according to claim 1, is characterized in that described defoamer is mineral oil defoaming agent.
4. the preparation method of antibacterial adiabatic reflective coating claimed in claim 1, is characterized in that comprising the steps:
Step (1): vermiculite, sepiolite and organobentonite are ground to 120 ~ 200 orders;
Step (2): organosilicon crylic acid latex is added to the water, then adds wherein dispersion agent and defoamer, after being stirred to and mixing, then add step (1) ground vermiculite, sepiolite and organobentonite, continue to stir, obtain slurry;
Step (3): nano titanium oxide, nano zine oxide and Zinc Pyrithione are joined in the slurry of step (2), continue to be stirred to and mix, obtain antibacterial adiabatic reflective coating of the present invention.