CN103773012A - 一种沥青防水材料 - Google Patents
一种沥青防水材料 Download PDFInfo
- Publication number
- CN103773012A CN103773012A CN201410023413.1A CN201410023413A CN103773012A CN 103773012 A CN103773012 A CN 103773012A CN 201410023413 A CN201410023413 A CN 201410023413A CN 103773012 A CN103773012 A CN 103773012A
- Authority
- CN
- China
- Prior art keywords
- parts
- hours
- waterproofing material
- asphalt waterproofing
- aging agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种沥青防水材料,其组成成份以质量份数表示法为:石油沥青80-100份;氧化铁红10-15份;甲苯40-45份;云母粉5-8份;乳化剂10-20份;防老剂0.4-0.6份;氯丁橡胶60-80份;二硫化四甲基秋兰姆为0.1-0.3份;硬脂酸为1-3份;滑石粉15-18份;苯二甲酸二丁酯2-5份;氧化镁4-5份;二甲苯5-10份;产品表干2-3h,实干21-23h;耐水性好,0.5MPa、60min无渗漏;使用寿命长,耐100℃高温5h不起泡,0℃5h无裂纹;产品粘接强度>0.3,断裂伸长率>800%,可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于沥青材料领域,尤其涉及一种沥青防水材料。
背景技术
氯丁橡胶,由氯丁橡胶聚合而生产的合成橡胶,被广泛应用于用于抗风化产品、粘胶鞋底、涂料和火箭燃料,氯丁橡胶均以乳液聚合法生产,生产工艺流程多为单釜间歇聚合。聚合温度多控制在40~60℃,转化率则在90%左右。聚合温度、最终转化率过高或聚合过程中进入空气(氧气)均会导致产品质量下降。生产中用硫磺-秋兰姆(四烷基甲氨基硫羰二硫化物)体系调节分子量。硫磺-秋兰姆体系的主要缺点在于硫键不够稳定,这是影响贮存性的重要原因之一。若用硫醇调节分子量,则可改善此种性能。氯丁橡胶与一般合成橡胶不同,它不用硫磺硫化,而是用氧化锌、氧化镁等硫化。
沥青是一种天然的或人工生产的工程材料。它主要由沥青结合剂和级配骨料构成。主要应用于道路工程的路面铺设和加固、高层建筑中的地板铺面、水利工程中的密封材料。某些情况下也用于垃圾处理工程中的密封。出于工程技术和经济方面的原因,沥青构件具有不同的分层结构,主要包括沥青承载层、沥青联结层以及沥青面层。各层按照不同的厚度和所处位置,为紧密的结构主体提供不同的承载力。在化学上,沥青混凝土是一种具有热后可塑性的惰性材料,随着社会城市化、科技化、人性化的发展,设计一种强度高,防水强,耐老化的沥青防水材料以满足市场需求,是非常必要的。
发明内容
解决的技术问题:
本申请针对现有沥青防水材料强度低,防水性能低,不耐老化等技术问题,提供一种沥青防水材料。
技术方案:
一种沥青防水材料,由下列原料组成,以质量份数表示法为:石油沥青80-100份;氧化铁红10-15份;甲苯40-45份;云母粉5-8份;乳化剂10-20份;防老剂0.4-0.6份;氯丁橡胶60-80份; 二硫化四甲基秋兰姆为0.1-0.3份;硬脂酸为1-3份;滑石粉15-18份;苯二甲酸二丁酯2-5份;氧化镁4-5份;二甲苯5-10份。
作为本发明的一种优选技术方案:所述沥青防水材料,其组成成分,以质量份数表示法为:石油沥青80-100份;氧化铁红10-15份;甲苯40-45份;云母粉5-8份;乳化剂10-20份;防老剂0.4-0.6份;氯丁橡胶60-80份; 二硫化四甲基秋兰姆为0.1-0.3份;硬脂酸为1-3份;滑石粉15-18份;苯二甲酸二丁酯2-5份;氧化镁4-5份;二甲苯5-10份。
作为本发明的一种优选技术方案:所述乳化剂采用松香皂。
作为本发明的一种优选技术方案:所述防老剂采用尼奥宗-D。
有益效果:
本发明所述一种沥青防水材料采用以上技术方案与现有技术相比,具有以下技术效果:1、产品表干2-3h,实干21-23h;2、耐水性好,0.5MPa、60min无渗漏;3、使用寿命长,耐100℃高温5h不起泡,0℃5h无裂纹;4、产品粘接强度>0.3,断裂伸长率>800%,可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种沥青防水材料,其组成成份以质量份数表示法为:石油沥青80份;氧化铁红10份;甲苯40份;云母粉5份;松香皂乳化剂10份;防老剂尼奥宗-D0.4份;氯丁橡胶60份; 二硫化四甲基秋兰姆为0.1份;硬脂酸为1份;滑石粉15份;苯二甲酸二丁酯2份;氧化镁4份;二甲苯5份。将石油沥青在240℃下熔化脱水,除去杂质后加入其余组分,边加热边搅拌,2h后冷却至室温,即为成品。
产品表干3h,实干23h;耐水性好,0.3MPa、30min无渗漏;使用寿命长,耐80℃高温5h不起泡,0℃3h无裂纹;粘接强度0.3MPa,断裂伸长率800%。
实施例2:
一种沥青防水材料,其组成成份以质量份数表示法为:石油沥青100份;氧化铁红15份;甲苯45份;云母粉8份;松香皂乳化剂20份;防老剂尼奥宗-D0.6份;氯丁橡胶80份; 二硫化四甲基秋兰姆为0.3份;硬脂酸为3份;滑石粉18份;苯二甲酸二丁酯5份;氧化镁5份;二甲苯10份。将石油沥青在240℃下熔化脱水,除去杂质后加入其余组分,边加热边搅拌,2h后冷却至室温,即为成品。
产品表干2.5h,实干22h;耐水性好,0.4MPa、40min无渗漏;使用寿命长,耐90℃高温5h不起泡,0℃4h无裂纹;粘接强度0.4MPa,断裂伸长率850%。
实施例3:
一种沥青防水材料,其组成成份以质量份数表示法为:石油沥青100份;氧化铁红12.5份;甲苯42.5份;云母粉6.5份;松香皂乳化剂15份;防老剂尼奥宗-D 0.5份;氯丁橡胶70份; 二硫化四甲基秋兰姆为0.2份;硬脂酸为2份;滑石粉16份;苯二甲酸二丁酯3.5份;氧化镁4.5份;二甲苯7.5份。将石油沥青在240℃下熔化脱水,除去杂质后加入其余组分,边加热边搅拌,2h后冷却至室温,即为成品。
产品表干2h,实干21h;耐水性好,0.5MPa、60min无渗漏;使用寿命长,耐100℃高温5h不起泡,0℃5h无裂纹;粘接强度0.5MPa,断裂伸长率900%。
以上实施例中的所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述,而不是限制,因此在与本发明的权利要求书相当的含义和范围内的任何改变,都应该认为是包括在权利要求书的范围内。
Claims (4)
1.一种沥青防水材料,其特征在于:其组成成份以质量份数表示法为:石油沥青80-100份;氧化铁红10-15份;甲苯40-45份;云母粉5-8份;乳化剂10-20份;防老剂0.4-0.6份;氯丁橡胶60-80份; 二硫化四甲基秋兰姆为0.1-0.3份;硬脂酸为1-3份;滑石粉15-18份;苯二甲酸二丁酯2-5份;氧化镁4-5份;二甲苯5-10份。
2.根据权利要求1所述的一种沥青防水材料,其特征在于:其组成成份以质量份数表示法为:石油沥青100份;氧化铁红12.5份;甲苯42.5份;云母粉6.5份;乳化剂15份;防老剂0.5份;氯丁橡胶70份; 二硫化四甲基秋兰姆为0.2份;硬脂酸为2份;滑石粉16份;苯二甲酸二丁酯3.5份;氧化镁4.5份;二甲苯7.5份。
3.根据权利要求1所述的一种沥青防水材料,其特征在于:所述乳化剂采用松香皂。
4.根据权利要求1所述的一种沥青防水材料,其特征在于:所述防老剂采用尼奥宗-D。