Technical field
The present invention relates to the field of a kind of metal-derusting and protection, especially the patina removal on mobile phone surface and the preparation of protective agent.
Technical background
Due to the outstanding reflecting feel of metal, on market, still having a lot of mobile phones is metal or metallizing shell, this mobile phone seem better appearance and anti-pollution characteristic relatively good, therefore obtain a lot of cellphone subscribers' favor.But in use, due to the corrosion of hand perspiration and other liquid, after the long period, the metal on mobile phone shell surface will be corroded and even get rusty, and especially has some green patinas in the place of seldom being touched by hand.Copper as a kind of color and gold the spitting image of metal have well ornamental, and easily tooling cost is low, usually be applied in the manufacture of metal hand casing, but because the erosion resistance of copper is poor, so green patina can be born in mobile phone shell surface after longer duration of service.
The main component of this patina is ventilation breather (Cu
2(OH)
2cO
3), ventilation breather has pungency to human body skin and mucous membrane.Mobile phone is as people's articles for daily use, and its security is extremely important to user, and the patina on mobile phone surface easily contacts with human body, if can not effectively remove these patinas, can produce potential harm and affect the attractive in appearance of mobile phone human body.Also do not have in the market specially for the mobile phone surface removal of patina and the product of protection.The general patina of using the mode of common wiping or hard thing polishing to remove mobile phone surface of people, although that this means can simply be removed patina is not thorough, and causes to damage to metal and has accelerated the formation of patina next time.Therefore, removal and the protective agent of mobile phone surface patina will meet this demand of people, and fill a hole in the market.
Summary of the invention
The object of the present invention is to provide a kind of patina that can thoroughly remove mobile phone surface and dirt and can prevent that metal from being corroded again, and esy to use, safe and reliable, environmentally safe,, removal and protective agent to metal harmless environment-friendly type mobile phone surface patina non-stimulated to human body.
The present invention comprises rust removing solution, scavenging solution, protective liquid, and the solution of these three kinds of difference in functionalitys is immersed in respectively in three blocks of non-woven fabrics and puts into three packing bags.User only need can complete rust cleaning, cleaning, three kinds of functions of protection to mobile phone with three non-woven fabrics wiping mobile phone shell surfaces successively.
Realizing the technical scheme that object of the present invention takes is:
Rust removing solution is formed by the preparation of raw material of following weight part: 10~20 parts of weak erosive acid, 0.05~0.1 part of acid inhibitor, 3~5 parts, tensio-active agent, 0.1~0.5 part, natural phant essence, 75~85 parts of deionized waters.Scavenging solution is formed by the preparation of raw material of following weight part: 95~97 parts of solvents, 3~5 parts, tensio-active agent, 0.1~0.5 part, natural phant essence.Protective liquid is formed by the preparation of raw material of following weight part: 0.02~0.04 part of inhibiter, 0.1~0.5 part, natural phant essence, 1.5~3.5 parts of lustering agents, 96~99 parts of solvents.
20~30 parts, the tartrate that described weak erosive acid is 99% for concentration, 70~80 parts of mixing acid that form of phosphoric acid that concentration is 85%.
Described acid inhibitor is Lan-826 or Lan-926 or urotropine.
Described tensio-active agent is Sodium dodecylbenzene sulfonate or sodium lauryl sulphate or lauryl alcohol phosphoric acid ester potassium.
Described natural phant essence is cream jasmin france or rose compound.
Described inhibiter is a kind of the formed mixture in a kind of and tertiary sodium phosphate, tripoly phosphate sodium STPP in trolamine, monoethanolamine, and its mass ratio is 1: 1.
Described lustering agent is polydimethylsiloxane or benzylideneacetone.
Preparation method of the present invention is: (1) is dissolved in weak erosive acid, acid inhibitor, tensio-active agent, natural phant essence in deionized water, stirs and is mixed evenly and obtains rust removing solution; (2) tensio-active agent, natural phant essence are dissolved in the solvent by ethanol and deionized water preparation, are uniformly mixed and obtain scavenging solution; (3) inhibiter, natural phant essence, lustering agent are dissolved in the solvent by ethanol and deionized water preparation, are uniformly mixed and obtain protective liquid; (4) three kinds of solution are immersed respectively in three blocks of non-woven fabrics and make product of the present invention.
Beneficial effect of the present invention: (1) the present invention adopts the weak erosive acid collocation acid inhibitor of 10~20% ratios both can thoroughly remove patina, the dirt on mobile phone surface, again can corroding metal; (2) inhibiter that the present invention adopts can form in metallic surface the stable protective membrane of one deck and prevent that metal from being corroded again; (3) the present invention is easy to use, only need with three non-woven fabrics wiping mobile phone metallic surfaces having immersed solution, can reach successively the object of rust cleaning and protection; (4) the present invention is not containing any strong acid, highly basic, nontoxic, and stable performance is safe and reliable.The non-woven fabrics adopting is environment-friendly degradable material, environmentally safe.
Embodiment
In order to understand better the present invention, with specific examples, describe technical scheme of the present invention in detail below, but the present invention is not limited thereto.
Embodiment 1.
In container A, add successively the deionized water of 85 parts, 2 parts of tartrate, 8 parts of phosphoric acid, 5 parts of sodium lauryl sulphate, 0.05 part of Lan-826,0.2 part of natural cream jasmin france, dispersed with stirring evenly obtains rust removing solution.To add successively 70 parts of deionized waters, 27 parts of ethanol in container B and stir, 3 parts of lauryl alcohol phosphoric acid ester potassium, 0.2 part of natural rose essence, dispersed with stirring evenly obtains scavenging solution.In container C, add successively 30 parts of ethanol, 0.01 part of trolamine, 0.01 part of tripoly phosphate sodium STPP, 2 parts of polydimethylsiloxanes, the deionized water of 68 parts, 0.2 part of natural rose essence, dispersed with stirring evenly obtains protective liquid.Three kinds of solution are immersed respectively in three blocks of non-woven fabrics.
Embodiment 2.
In container A, add successively the deionized water of 80 parts, 5 parts of tartrate, 11 parts of phosphoric acid, the sodium lauryl sulphate of 4 parts, the Lan-826 of 0.07 part, 0.2 part of natural cream jasmin france, dispersed with stirring evenly obtains rust removing solution.In container B, add successively the deionized water of 65 parts, 30 parts of ethanol, 5 parts of lauryl alcohol phosphoric acid ester potassium, 0.1 part of natural rose essence, dispersed with stirring evenly obtains scavenging solution.To adding successively 25 parts of ethanol, 0.015 part of trolamine, 0.015 part of tripoly phosphate sodium STPP, 2.5 parts of polydimethylsiloxanes, water and 0.3 part of natural rose essence of 72 parts in container C, dispersed with stirring evenly obtains protective liquid.Three kinds of solution are immersed respectively in three blocks of non-woven fabrics.
Embodiment 3.
In container A, add successively the deionized water of 75 parts, 7 parts of tartrate, 15 parts of phosphoric acid, the sodium lauryl sulphate of 3 parts, the Lan-826 of 0.1 part, 0.4 part of natural cream jasmin france, dispersed with stirring evenly obtains rust removing solution.In container B, add successively the deionized water of 77 parts, 20 parts of ethanol, 3 parts of lauryl alcohol phosphoric acid ester potassium, 0.3 part of natural rose essence, dispersed with stirring evenly obtains scavenging solution.To adding successively 20 parts of ethanol, 0.02 part of trolamine, 0.02 part of tripoly phosphate sodium STPP, 3 parts of polydimethylsiloxanes, water and 0.3 part of natural rose essence of 70 parts in container C, dispersed with stirring evenly obtains protective liquid.Three kinds of solution are immersed respectively in three blocks of non-woven fabrics.
Product performance test: three that use the product of three embodiment respectively rusting rate to be approached are eliminated rust, clean, protect with money mobile phone with metal shell with brand.Using method is: successively mobile phone metal shell is carried out to wiping with three blocks of non-woven fabrics in product of the present invention.After rust cleaning and protective treatment, check the rust cleaning effect of three sections of mobile phone metal shells, then normal three sections of mobile phones use is checked again to the situation of getting rusty of its metallic surface after eight months.Its test result is in Table 1.
Table 1: each embodiment product performance test result
Project |
Security |
Patina removal effect |
Metal protection performance |
Embodiment 1 |
Non-corrosiveness, safety |
Thoroughly remove fast |
Using after 8 months has a small amount of patina to produce |
Embodiment 2 |
Non-corrosiveness, safety |
Thoroughly remove fast |
Use and without patina, produce after 8 months |
Embodiment 3 |
Non-corrosiveness, safety |
Thoroughly remove fast |
Use and without patina, produce after 8 months |