CN103757477B - 一种开关插座用铜镍锡合金及其制备方法 - Google Patents
一种开关插座用铜镍锡合金及其制备方法 Download PDFInfo
- Publication number
- CN103757477B CN103757477B CN201310751407.3A CN201310751407A CN103757477B CN 103757477 B CN103757477 B CN 103757477B CN 201310751407 A CN201310751407 A CN 201310751407A CN 103757477 B CN103757477 B CN 103757477B
- Authority
- CN
- China
- Prior art keywords
- copper
- switch socket
- nickel
- tin alloy
- incubated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明提供一种开关插座用铜镍锡合金及其制备方法，各组分的组成按重量百分比计分别为：Ni5~7%，Sn0.8~1.2%，P0.1~0.5%，余量为铜。制备该开关插座用铜镍锡合金的方法包括（1）、在氮气保护气氛下，将原料Ni、Sn、P、Cu加入到熔化炉中，加热至1180~1240℃，调整成分，成分符合配方比例后，将其保温，保温温度为1140~1200℃，保温40~90分钟；（2）、然后再取样分析，调整成份符合原料重量百分比后，将合金熔液浇入铸铁模中，冷却至室温即可；最后保温5小时，进行固溶处理得到铜镍锡合金。本发明提供的开关插座用铜镍锡合金弹性优异，强度好，适于作为开关插座铜材使用。
Description
技术领域
本发明涉及材料工程，具体涉及一种开关插座用铜镍锡合金及其制备方法。
背景技术
人们在购买开关插座时，通常都希望买到一款寿命长，质量好的产品，那么对于开关插座而言，其里面的铜片好坏就直接决定了它的质量。近年来，对开关内部铜材的导电率、耐力(降伏应力)、拉伸强度、弯曲加工性及抗应力松弛特性要求越来越高。
发明内容
鉴于上述信息，本发明的目的之一在于提供一种弹性好、导电性能良好的开关插座用铜镍锡合金。
本发明的另一目的在于提供一种上述开关插座用铜镍锡合金的制备方法。
本发明的技术方案是，一种开关插座用铜镍锡合金，各组分的组成按重量百分比计分别为：Ni5～7％，Sn0.8～1.2％，P0.1～0.5％，余量为铜。
所述各组分的组成按重量百分比计分别为：Ni5.5％，Sn0.9％，P0.2％，余量为铜。
一种开关插座用铜镍锡合金的制备方法，包括如下步骤：
(1)、在氮气保护气氛下，按重量百分比将原料Ni、Sn、P、Cu加入到熔化炉中，加热至1180～1240℃，将融化物料搅拌、捞渣、取样分析调整成分，成分符合配方比例后，将其转入保温炉内保温，保温温度为1140～1200℃，保温40～90分钟；
(2)、然后再取样分析，调整成份，成份符合原料重量百分比后，将合金熔液浇入铸铁模中，冷却至室温即可；最后对铸造所得合金在热处理炉内900℃下保温5小时，进行固溶处理得到铜镍锡合金。
本发明提供的开关插座用铜镍锡合金中，Ni能够显著提高强度、耐蚀性、硬度、电阻和热电性，并降低电阻率温度系数，Sn具有固溶强化和提高耐应力松弛性的作用，根据本发明的重量百分比制备得到的铜镍锡合金弹性优异，导电性能良好，适于作为开关插座铜材使用。
具体实施方式
下面的实施例可使本专业技术人员更全面地理解本发明，但不以任何方式限制本发明。
实施例1
在氮气保护气氛下，按重量百分比为：Ni5％，Sn0.9％，P0.5％，余量为铜的比例将原料加入到熔化炉中，加热至1180～1240℃，将融化物料搅拌、捞渣、取样分析调整成分，成分符合配方比例后，将其转入保温炉内保温，保温温度为1140～1200℃，保温40～90分钟；然后再取样分析，调整成份，成份符合原料重量百分比后，将合金熔液浇入铸铁模中，冷却至室温即可；最后对铸造所得合金在热处理炉内900℃下保温5小时，进行固溶处理得到铜镍锡合金Ⅰ。
实施例2
在氮气保护气氛下，按重量百分比为：Ni7％，Sn1.2％，P0.1％，余量为铜的比例将原料加入到熔化炉中，加热至1180～1240℃，将融化物料搅拌、捞渣、取样分析调整成分，成分符合配方比例后，将其转入保温炉内保温，保温温度为1140～1200℃，保温40～90分钟；然后再取样分析，调整成份，成份符合原料重量百分比后，将合金熔液浇入铸铁模中，冷却至室温即可；最后对铸造所得合金在热处理炉内900℃下保温5小时，进行固溶处理得到铜镍锡合金Ⅱ。
实施例3
在氮气保护气氛下，按重量百分比为：Ni5.5％，Sn0.9％，P0.2％，余量为铜的比例将原料加入到熔化炉中，加热至1180～1240℃，将融化物料搅拌、捞渣、取样分析调整成分，成分符合配方比例后，将其转入保温炉内保温，保温温度为1140～1200℃，保温40～90分钟；然后再取样分析，调整成份，成份符合原料重量百分比后，将合金熔液浇入铸铁模中，冷却至室温即可；最后对铸造所得合金在热处理炉内900℃下保温5小时，进行固溶处理得到铜镍锡合金Ⅲ。
实施例4
将得到的铜镍锡合金进行以下性能测试。
表1普通青铜和铜镍锡合金的基本性能
| 产品 | σe/MPa | δ/％ | E/GPa | HV | IACS/％ |
| 普通青铜 | 530 | 10 | 135 | 186 | 12.3 |
| 铜镍锡合金Ⅰ | 780 | 2 | 80 | 360 | 20.3 |
| 铜镍锡合金Ⅱ | 792 | 2 | 86 | 365 | 24.1 |
| 铜镍锡合金Ⅲ | 786 | 2 | 83 | 362 | 21.2 |
通过上述计算结果可知，铜镍锡合金Ⅰ～Ⅲ的弹性比功远大于普通青铜的弹性比功，并且导电性能也远大于普通青铜。由此可知，本发明的铜镍锡合金的基本性能达到中高弹性铜合金的要求。
Claims (2)
1.一种开关插座用铜镍锡合金，其特征在于，各组分的组成按重量百分比计分别为：Ni5.5%，Sn0.9%，P0.2%，余量为铜。
2.基于权利要求1所述的一种开关插座用铜镍锡合金的制备方法，其特征在于，包括如下步骤：
（1）、在氮气保护气氛下，按重量百分比将原料Ni、Sn、P、Cu加入到熔化炉中，加热至1180~1240℃，将融化物料搅拌、捞渣、取样分析调整成分，成分符合原料重量百分比后，将其转入保温炉内保温，保温温度为1140~1200℃，保温40~90分钟；
（2）、然后再取样分析，调整成份，成份符合原料重量百分比后，将合金熔液浇入铸铁模中，冷却至室温即可；最后对铸造所得合金在热处理炉内900℃下保温5小时，进行固溶处理得到铜镍锡合金。