CN103757361A - 镍镉废电池正负极混合材料的浸出方法 - Google Patents
镍镉废电池正负极混合材料的浸出方法 Download PDFInfo
- Publication number
- CN103757361A CN103757361A CN201310736558.1A CN201310736558A CN103757361A CN 103757361 A CN103757361 A CN 103757361A CN 201310736558 A CN201310736558 A CN 201310736558A CN 103757361 A CN103757361 A CN 103757361A
- Authority
- CN
- China
- Prior art keywords
- leaching
- nickel
- acid
- anode
- mixed materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明介绍的镍镉废电池正负极混合材料的浸出方法是将从镍镉废电池中分离出的并经焙烧预处理得到的正负极混合材料和麦草粉加入耐压、耐硫酸和硝酸腐蚀的反应釜中,加入硫酸和硝酸的混合溶液,并在密闭条件下进行搅拌浸出。
Description
技术领域
本发明涉及镍镉废电池正负极混合材料的一种浸出方法。
背景技术
镍镉电池是一类广泛使用的电池,该电池使用报废后将产生大量废电池。由于这类电池含有大量重金属,若弃入环境,将对环境产生很大的直接和潜在危害。镍镉废电池正负极混合材料主要含镍、钴和镉,三者的总含量高达60%左右,很具回收价值。很具回收价值。目前从镍镉废电池正负极混合材料中回收镍、钴和镉的工艺主要有火法工艺和湿法工艺。火法工艺得到的产品为合金材料,很难获得较纯的镍、钴和镉。湿法工艺比较容易得到较纯的镍、钴和镉。浸出是湿法工艺中必不可少的一个过程。目前镍镉废电池正负极混合材料的浸出方法主要有盐酸浸出法、硫酸浸出法、硝酸浸出法和混酸(硫酸加硝酸)浸出法。盐酸浸出法,设备腐蚀大,酸雾产生量大而污染环境。硫酸浸出法消耗较昂贵的氧化剂(如双氧水等)。硝酸浸出法的硝酸消耗量大,而且会产生大量氮氧化物,污染环境。所有的湿法工艺都存在如何经济地提高浸出速度、提高金属浸出率、降低酸耗和其它辅料消耗的问题。虽然硝酸加工业纯氧浸出法和混酸加工业纯氧浸出法较好地解决了上述问题,但浸出设备较复杂,而且废电池浸出所需工业纯氧量不大,废电池处理企业就地生产工业纯氧自用不经济,工业纯氧的储存、运输和使用比较麻烦。开发设备腐蚀小、浸出速度快、浸出率高、酸耗和其它辅料消耗低、使用方便、基本无环境污染的镍镉废电池正负极混合材料的浸出方法具有较大实用价值。
发明内容
针对目前镍镉废电池正负极混合材料浸出的问题,本发明的目的是寻找一种金属浸出率高,浸出速度快,浸出率高,酸耗和其它辅料消耗低,使用方便,不用昂贵还原剂,基本无环境污染的镍镉废电池正负极混合材料的浸出方法,其特征在于将从镍镉废电池中分离出的并经焙烧预处理得到的正负极混合材料和≤1.5mm的麦草粉加入耐压、耐硫酸和硝酸腐蚀的反应釜中,加入硫酸和硝酸的混合溶液,并在密闭条件下进行搅拌浸出。浸出结束后 进行液固分离,得到所需浸出溶液。反应温度为50℃~80℃,浸出的硫酸初始浓度为1mol/L~4mol/L,硝酸的初始浓度为5g/L~10g/L 浸出时间为2h~4h,浸出过程进行搅拌,搅拌速度为30r/min~120r/min。硫酸加入量为加入反应容器的正负极混合材料中全部金属浸出的硫酸理论消耗量的110%~140%。麦草粉的加入量以干基计为正负极混合材料中镍、钴总质量的60%~75%。
本发明的目的是这样实现的:在密闭并有麦草粉和硝酸存在的条件下,硫酸浸出经焙烧预处理后的镍镉废电池正负极混合材料(材料中的镍和钴呈金属氧化物形态)时,浸出过程发生如下主要化学反应:
NiO + H2SO4 = NiSO4 + H2O
CoO + H2SO4 = CoSO4 + H2O
CdO + H2SO4 = CdSO4 + H2O
nC6H10O5 + nH2SO4 =n(C5H11O5)HSO4
n(C5H11O5)HSO4 + nH2O = nC6H12O6 + nH2SO4
C6H12O6 + 8HNO3 = 8NO + 6CO2 + 10H2O
nC6H10O5 + 8nHNO3 = 8nNO + 6nCO2 + 9nH2O
3Ni2O3 + 6H2SO4 + 2NO = 6NiSO4 + 2HNO3 + 5H2O
3Co2O3 + 6H2SO4 + 2NO = 6CoSO4 + 2HNO3 + 5H2O
Ni2O3和Co2O3的总反应为:
12nNi2O3 + nC6H10O5 + 24nH2SO4 = 24nNiSO4 + 6nCO2 + 29nH2O
12n Co2O3 + nC6H10O5 + 24nH2SO4 = 24nCoSO4 + 6nCO2 + 29nH2O
麦草粉中的其它有机物也与硝酸反应生成NO、CO2和H2O,生成的NO与Ni2O3和Co2O3按前述反应生成NiSO4 、CoSO4、HNO3和H2O。
由于硝酸与麦草粉的反应速度较快,产生的NO与Ni2O3和Co2O3的反应也较快,由此加快整个浸出过程,并实现Ni2O3和Co2O3较完全浸出。NO可以彻底破坏正负极混合材料中高价氧化物的层状结构,提高有价金属的浸出率。
相对于现有方法,本发明的突出优点是采用麦草粉作还原剂,硝酸作浸出加速剂浸出镍镉废电池正负极混合材料,反应速度快,反应酸度较低,硫酸和还原剂的消耗量小,并且麦草粉便宜;正负极混合材料中高价氧化物的层状结构破坏彻底,可提高金属浸出率;浸出液后续处理中不需要中和大量的酸,成本较低;浸出液后续处理中产生的废弃物量少,降低了污染治理费用,具有明显的经济效益和环境效益;过程在密闭条件下进行,避免了NO逸出产生的环境污染。
具体实施方法
实施例1:将100g镍镉废电池正负极混合材料(含镍30.5%、钴1.6%、镉28.1%)和≤1.5mm麦草粉19.5g加入容积为1L的衬钛压力反应釜中,加入硫酸浓度为1.5mol/L、硝酸浓度为5g/L的混酸溶液590ml,在50℃~60℃下搅拌(搅拌速度80r/min)浸出4h,浸出结束后进行液固分离,得到560ml浸出溶液(不含浸出渣洗涤水)。镍、钴和镉的浸出率分别为99.1%、98.5%和99.3%(按进入浸出溶液和浸出渣洗涤液中的镍、钴和镉计算)。
实施例2:将500g镍镉废电池正负极混合材料(含镍30.5%、钴1.6%、镉28.1%)≤1.5mm麦草粉120g加入容积为5L的衬钛压力反应釜中,加入硫酸浓度为2.5mol/L、硝酸浓度为10g/L的混酸溶液2200ml,,在70℃~80℃下搅拌(搅拌速度为70r/min)浸出2h,浸出结束后进行液固分离,得到2000ml浸出溶液(不含浸出渣洗涤水),镍、钴和镉的浸出率分别为99.3%、99.1%和99.4%(按进入浸出溶液和浸出渣洗涤液中的镍、钴和镉计算)。
Claims (1)
1.一种镍镉废电池正负极混合材料的浸出方法,其特征是将从镍镉废电池中分离出的并经焙烧预处理得到的正负极混合材料和≤1.5mm的麦草粉加入耐压、耐硫酸和硝酸腐蚀的反应釜中,加入硫酸和硝酸的混合溶液,并在密闭条件下进行搅拌浸出,浸出结束后 进行液固分离,得到所需浸出溶液,反应温度为50℃~80℃,浸出的硫酸初始浓度为1mol/L~4mol/L,硝酸的初始浓度为5g/L~10g/L 浸出时间为2h~4h,浸出过程进行搅拌,搅拌速度为30r/min~120r/min,硫酸加入量为加入反应容器的正负极混合材料中全部金属浸出的硫酸理论消耗量的110%~140%,麦草粉的加入量以干基计为正负极混合材料中镍、钴总质量的60%~75%。