CN103755305A - Insulation board and making process thereof - Google Patents
Insulation board and making process thereof Download PDFInfo
- Publication number
- CN103755305A CN103755305A CN201310752558.0A CN201310752558A CN103755305A CN 103755305 A CN103755305 A CN 103755305A CN 201310752558 A CN201310752558 A CN 201310752558A CN 103755305 A CN103755305 A CN 103755305A
- Authority
- CN
- China
- Prior art keywords
- heat preservation
- plate material
- preservation plate
- parts
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an insulation board and a making process thereof, belonging to the field of building materials. The insulation board mainly comprises the following components in percentage by weight: 10-15 percent of inorganic reinforcing material, 10-30 percent of composite high-temperature adhesive, 1-5 percent of activating agent, 50-70 percent of lightweight aggregate and 15-20 percent of water. The insulation board has the characteristics of low volume weight, excellent insulation effect, high compressive strength and low making cost.
Description
Technical field
The present invention relates to building material field, especially a kind of heat preservation plate material and manufacture craft thereof.
Background technology
Along with going deep into of reform and opening-up, the economic fast development of China, people's material and cultural life is all greatly improved, and embodies a concentrated reflection of clothing, food, lodging and transportion--basic necessities of life aspect, especially aspect living, requires higher quality.This has just promoted the fast development of building trade.Material of construction expense accounts for more than 50% in fundamental construction total expenses, has sizable ratio, and the kind of material of construction and quality level are restricting Architecture and structure form and constructional method.In addition, material of construction directly affects safe reliability, weather resistance and the suitability of building and construction work.Therefore, the exploitation of New Building Materials, production and use, significant for promoting social progress, developing national economy.
The heat preservation plate material unit weight of present stage is high, and effect of heat insulation is poor and be not suitable for the needs of building trade development.
Summary of the invention
Goal of the invention of the present invention is: for the problem of above-mentioned existence, provide a kind of heat preservation plate material and manufacture craft thereof, have unit weight low, thermal insulation effect is good, and ultimate compression strength is high, the feature that cost of manufacture is low.
The technical solution used in the present invention is as follows: a kind of heat preservation plate material, it is mainly comprised of inorganic reinforcement, combined high temperature alite paste, promoting agent, aglite group and water, and its weight percent is: inorganic reinforcement 10%-15%, combined high temperature alite paste 10%-30%, promoting agent 1%-5%, aglite 50%-70%, water 15%-20%.
Such scheme is done further preferably, described inorganic reinforcement is mainly comprised of fibrous magnesium silicate, brucite, glass fibre, aluminium silicate fiber peacekeeping montmorillonite, and its weight percent is: fibrous magnesium silicate 20%-30%, brucite 10%-20%, glass fibre 10%-20%, aluminum silicate fiber 10%-20% and montmorillonite 10%-20%.
Such scheme is done further preferably, described combined high temperature alite paste is mainly by water glass, aluminium dihydrogen phosphate, silicone resin glue and silicon sol, and its weight percent is: water glass 10%-20%, aluminium dihydrogen phosphate 10%-20%, silicone resin glue 50%-60%, silicon sol 20%-30%.
Such scheme is done further preferably, and described promoting agent is one or more mixture of succinate sodium sulfonate and naphthalene sulfonic acidformaldehyde condensation product.
Such scheme is done further preferably, and described aglite is pearlstone, leca or haydites of book structure.
The manufacture craft of described a kind of heat preservation plate material is:
A, according to weight proportion, mix that to make inorganic reinforcement standby;
B, according to weight proportion, mix that to make combined high temperature alite paste standby;
C, according to weight proportion, mix and make the moulding slurry with cementability;
D, moulding slurry is injected in forming mould, compression moulding is dry by the demoulding, can obtain heat preservation plate material product after surface decoration.。
In sum, owing to having adopted technique scheme, the invention has the beneficial effects as follows: it is low that this heat preservation plate material has unit weight, thermal insulation effect is good, and ultimate compression strength is high, the feature that cost of manufacture is low.
Embodiment
Disclosed all features in this specification sheets, or the step in disclosed all methods or process, except mutually exclusive feature and/or step, all can combine by any way.
Disclosed arbitrary feature in this specification sheets (comprising any accessory claim, summary), unless narration especially all can be replaced by other equivalences or the alternative features with similar object.That is,, unless narration especially, each feature is an example in a series of equivalences or similar characteristics.
Embodiment 1
By 30 parts of fibrous magnesium silicates, 10 parts of brucites, 20 parts of glass fibre, 20 parts of aluminum silicate fibers, 20 parts of montmorillonites mix makes inorganic reinforcement; By 10 parts of water glass, 20 parts of aluminium dihydrogen phosphates, 50 parts of silicone resin glue, 20 parts of silicon sol mix makes combined high temperature alite paste; By 10 parts of inorganic reinforcements, 20 parts of combined high temperature alite pastes, 3 parts of succinate sodium sulfonates, 52 parts of pearlstones, 15 parts of water are made the moulding slurry with cementability; Moulding slurry is injected in forming mould, and compression moulding is dry by the demoulding, can obtain heat preservation plate material product after surface decoration.
Embodiment 2
By 20 parts of fibrous magnesium silicates, 20 parts of brucites, 20 parts of glass fibre, 20 parts of aluminum silicate fibers, 20 parts of montmorillonites mix makes inorganic reinforcement; By 10 parts of water glass, 10 parts of aluminium dihydrogen phosphates, 60 parts of silicone resin glue, 20 parts of silicon sol mix makes combined high temperature alite paste; By 15 parts of inorganic reinforcements, 10 parts of combined high temperature alite pastes, 5 parts of naphthalene sulfonic acidformaldehyde condensation products, 50 parts of lecas, 20 parts of water are made the moulding slurry with cementability; Moulding slurry is injected in forming mould, and compression moulding is dry by the demoulding, can obtain heat preservation plate material product after surface decoration.
Embodiment 3
By 25 parts of fibrous magnesium silicates, 20 parts of brucites, 20 parts of glass fibre, 20 parts of aluminum silicate fibers, 15 parts of montmorillonites mix makes inorganic reinforcement; By 15 parts of water glass, 10 parts of aluminium dihydrogen phosphates, 55 parts of silicone resin glue, 20 parts of silicon sol mix makes combined high temperature alite paste; By 12.5 parts of inorganic reinforcements, 15 parts of combined high temperature alite pastes, 1 part of succinate sodium sulfonate and 1.5 parts of naphthalene sulfonic acidformaldehyde condensation products, 55 parts of haydites of book structure, 15 parts of water are made the moulding slurry with cementability; Moulding slurry is injected in forming mould, and compression moulding is dry by the demoulding, can obtain heat preservation plate material product after surface decoration.
After testing, a kind of heat preservation plate material Main physical performance of embodiment 1-3 is as described in Table 1:
The present invention is not limited to aforesaid embodiment.The present invention expands to any new feature or any new combination disclosing in this manual, and the arbitrary new method disclosing or step or any new combination of process.
Claims (6)
1. a heat preservation plate material, it is characterized in that: it is mainly comprised of inorganic reinforcement, combined high temperature alite paste, promoting agent, aglite group and water, and its weight percent is: inorganic reinforcement 10%-15%, combined high temperature alite paste 10%-30%, promoting agent 1%-5%, aglite 50%-70%, water 15%-20%.
2. a kind of heat preservation plate material as claimed in claim 1, it is characterized in that: described inorganic reinforcement is mainly comprised of fibrous magnesium silicate, brucite, glass fibre, aluminium silicate fiber peacekeeping montmorillonite, and its weight percent is: fibrous magnesium silicate 20%-30%, brucite 10%-20%, glass fibre 10%-20%, aluminum silicate fiber 10%-20% and montmorillonite 10%-20%.
3. a kind of heat preservation plate material as claimed in claim 1, it is characterized in that: described combined high temperature alite paste is mainly by water glass, aluminium dihydrogen phosphate, silicone resin glue and silicon sol, and its weight percent is: water glass 10%-20%, aluminium dihydrogen phosphate 10%-20%, silicone resin glue 50%-60%, silicon sol 20%-30%.
4. a kind of heat preservation plate material as claimed in claim 1, is characterized in that: described promoting agent is one or more mixture of succinate sodium sulfonate and naphthalene sulfonic acidformaldehyde condensation product.
5. a kind of heat preservation plate material as claimed in claim 1, is characterized in that: described aglite is pearlstone, leca or haydites of book structure.
6. make a technique for a kind of heat preservation plate material as claimed in claim 1, it is characterized in that: comprise the following steps
A, weight proportion mixes that to make inorganic reinforcement standby according to claim 2;
B, weight proportion mixes that to make combined high temperature alite paste standby according to claim 3;
C, weight proportion mixes and makes the moulding slurry with cementability according to claim 1;
D, moulding slurry is injected in forming mould, compression moulding is dry by the demoulding, can obtain heat preservation plate material product after surface decoration.