CN103752817A - Wear-resisting plate and production method thereof - Google Patents
Wear-resisting plate and production method thereof Download PDFInfo
- Publication number
- CN103752817A CN103752817A CN201310746761.7A CN201310746761A CN103752817A CN 103752817 A CN103752817 A CN 103752817A CN 201310746761 A CN201310746761 A CN 201310746761A CN 103752817 A CN103752817 A CN 103752817A
- Authority
- CN
- China
- Prior art keywords
- wear
- plate
- steel plate
- cover
- resisting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to a wear-resisting plate. The wear-resisting plate comprises a steel plate, a gridding cover and wear-resisting material powder. The wear-resisting plate is characterized in that the steel plate is the bottom layer base body; the gridding cover warps the steel plate inside a cover body; the wear-resisting powder fills inside the remaining space inside the cover body of the gridding cover. The invention provides a production method of the wear-resisting plate. According to the wear-resisting plate and the production method thereof, the steel plate, the gridding cover and the wear-resisting material powder are sintered into a whole, the wear-resisting plate obtained through sintering is thick in wear-resisting plastic layer thickness and strong in sintering fastness, and accordingly suitability and wear resistance of the wear-resisting plate material are improved.
Description
Technical field
The invention belongs to high-abrasive material field, be specifically related to a kind of with general steel plate, prepare the preparation method of wearing plate.
Background technology
In recent years, domestic market was supported in order to steel plate conventionally, spreads high-abrasive material and plastify sintering on steel plate, then make the wear-resisting guide rail of lathe, but there are the following problems: the Wear-resistant plastic bed of material is thin, and the wear-resisting time is short.If the thickening Wear-resistant plastic bed of material, can cause wear-resistant material layer sintering insecure, peeling, even comes off.
Summary of the invention
In order to address the aforementioned drawbacks, technical scheme of the present invention is as follows:
A wearing plate, includes grid cover and high-abrasive material powder on steel plate, steel plate, and steel plate is bottom matrix, and described grid cover is wrapped in steel plate in its cover body, and described high-abrasive material powder is filled remaining space in described grid cover cover body.
Described steel plate is cold-rolled steel sheet.
Net on described grid cover is steel wire.
Wearing plate preparation method based on above-mentioned wear-resisting plate structure, described step is as follows:
The first step, using described steel plate as bottom matrix, steel plate is wrapped in cover body by grid cover;
Second step, fills remaining space in described grid cover cover body with high-abrasive material powder, makes workpiece to be sintered;
The 3rd step, puts into vacuum drying oven workpiece and carries out sintering;
The 4th step, sintering finishes rear taking-up workpiece, waits it fast coolingly can obtain described wearing plate.
Described high-abrasive material powder quality percentage is: powder of stainless steel 76%, tungsten powder 5.5%, carborundum 7%, chromium 5%, cobalt 3.5%, surplus are nickel-based solder.
Described sintering temperature is controlled at 95～105 ° of C.
Described sintering time is controlled at 1 hour.
The vacuum of described vacuum-sintering need reach 6.7X10
-3pa.
Wearable plate in the present invention is that steel plate, grid cover and Wear-resistant plastic powder three are sintered into one, the thickness that the wearable plate making by sintering has the Wear-resistant plastic bed of material is thick, the feature that sintering fastness is strong, thus suitability and the anti-wear performance of wearable plate improved.
Accompanying drawing explanation
Fig. 1 is the structural representation of wearing plate.
The specific embodiment
A kind of wearing plate as shown in Figure 1, it is characterized in that: include grid cover 2 and high-abrasive material powder on steel plate 1, steel plate, steel plate 1 is bottom matrix, and described grid cover 2 is wrapped in steel plate 1 in its cover body, and described high-abrasive material powder is filled remaining space in described grid cover 2 cover bodies.
Described steel plate 1 is cold-rolled steel sheet.
Net on described grid cover 2 is steel wire.
Wearing plate preparation method based on above-mentioned wear-resisting plate structure, described step is as follows:
The first step, using described steel plate 1 as bottom matrix, steel plate 1 is wrapped in cover body by grid cover 2;
Second step, fills remaining space in described grid cover 2 cover bodies with high-abrasive material powder, makes workpiece to be sintered;
The 3rd step, puts into vacuum drying oven workpiece and carries out sintering;
The 4th step, sintering finishes rear taking-up workpiece, waits it fast coolingly can obtain described wearing plate.
Described high-abrasive material powder quality percentage is: powder of stainless steel 76%, tungsten powder 5.5%, carborundum 7%, chromium 5%, cobalt 3.5%, surplus are nickel-based solder.
Described sintering temperature is controlled at 95～105 ° of C, and described sintering time is controlled at 1 hour, and vacuum during described vacuum-sintering need reach 6.7X10
-3pa.
Claims (8)
1. a wearing plate, it is characterized in that: include grid cover (2) and high-abrasive material powder on steel plate (1), steel plate, steel plate (1) is bottom matrix, described grid cover (2) is wrapped in steel plate (1) in its cover body, and described high-abrasive material powder is filled remaining space in described grid cover (2) cover body.
2. according to the wearing plate described in claim 1, it is characterized in that: described steel plate (1) is cold-rolled steel sheet.
3. according to the wearing plate described in claim 1, it is characterized in that: the net on described grid cover (2) is steel wire.
4. the wearing plate preparation method of the wear-resisting plate structure based on claim 1, is characterized in that: described step is as follows:
The first step, using described steel plate (1) as bottom matrix, steel plate (1) is wrapped in its cover body by grid cover (2);
Second step, fills remaining space in described grid cover (2) cover body with high-abrasive material powder, makes workpiece to be sintered;
The 3rd step, puts into vacuum drying oven workpiece and carries out sintering;
The 4th step, taking-up workpiece after sintering completes, waits it fast coolingly can obtain described wearing plate.
5. the preparation method of wearing plate according to claim 4, is characterized in that: described high-abrasive material powder quality percentage is: powder of stainless steel 76%, tungsten powder 5.5%, carborundum 7%, chromium 5%, cobalt 3.5%, surplus are nickel-based solder.
6. the preparation method of wearing plate according to claim 4, is characterized in that: described sintering temperature is controlled at 95～105 ° of C.
7. the preparation method of wearing plate according to claim 4, is characterized in that: described sintering time is controlled at 1 hour.
8. the preparation method of wearing plate according to claim 4, is characterized in that: the vacuum of described vacuum-sintering need reach 6.7X10
-3pa.