CN103741546A - Wallpaper with corn particle effect and production process of wallpaper - Google Patents
Wallpaper with corn particle effect and production process of wallpaper Download PDFInfo
- Publication number
- CN103741546A CN103741546A CN201410019601.7A CN201410019601A CN103741546A CN 103741546 A CN103741546 A CN 103741546A CN 201410019601 A CN201410019601 A CN 201410019601A CN 103741546 A CN103741546 A CN 103741546A
- Authority
- CN
- China
- Prior art keywords
- particle effect
- corn particle
- liquid layer
- deck
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses wallpaper with a corn particle effect. The wallpaper is characterized in that a pre-coating liquid layer is formed on a substrate, and an uneven foaming slurry layer is formed on the pre-coating liquid layer and is obvious in unevenness and strong in granular sensation. Meanwhile, the invention discloses a production process of the wallpaper with the corn particle effect. The production process has the advantages that production materials are easily available, and the production cost is low.
Description
Technical field
The present invention relates to a kind of corn particle effect wallpaper and production technology thereof.
Background technology
In prior art, people improve constantly the requirement of house decorative material, and wallpaper is more and more subject to people's attention as the important component part of Modern Interior Decoration material, and wallpaper is also more and more diversified.Yet the wallpaper of prior art is comparatively single, major part is all plane, the fewer wallpaper that occurs that granular sensation is strong on market.
In view of the described defect of prior art wallpaper, inventor's further investigation, develops a kind of corn particle wallpaper and production technology thereof that overcomes described defect, and this case produces thus.
Summary of the invention
The object of the present invention is to provide a kind of corn particle effect wallpaper and production technology thereof, the wallpaper concave-convex sense that adopts this production technology to produce is obvious, and granular sensation is strong, and production material is easy to get and low cost of manufacture.
For reaching above-mentioned purpose, solution of the present invention is:
A corn particle effect wallpaper forms one deck precoating liquid layer on base material, forms one deck foamed slurry layer on precoating liquid layer, this foamed slurry layer concave-convex surface.
Further, described base material is body paper or non-woven paper.
A corn particle effect wallpaper production technology, comprises the following steps: on base material, be coated with one deck pre-coating solution and carry out surface treatment, dry and form precoating liquid layer; On precoating liquid layer, be coated with one deck slurry, this slurry is comprised of following compositions in weight percentage: PVC45-50%, plasticizer 25-30%, filler 18-22%, solvent 2-5%, the first blowing agent 0-3%, the second blowing agent 1-2% and stabilizing agent 1-3%, after 150-170 ℃ of temperature lower surface is dry, temperature is increased to 190-200 ℃, and applies 1.5 * 10
5-5.2 * 10
5the pressure of Pa, then dries, rolling, and normal temperature slaking forms one deck foamed slurry layer on precoating liquid layer, this foamed slurry layer concave-convex surface.
Further, pre-coating solution oven dry formation precoating liquid layer is to complete under 120 ℃ of-150 ℃ of environment in temperature.
Further, described plasticizer is DOP or TXIB or both mixing.
Further, described filler is CaCO
3or TiO
2or both mixing.
Further, described solvent is alkane solvent.
Further, described the first blowing agent is chemical foaming agent AC or chemical foaming agent AC-LC
2.
Further, described the second blowing agent is ACL-2.
Adopt after such scheme, the present invention adds inconsistent the first blowing agent of blowing temperature and the second blowing agent in slurry, the blowing agent that blowing temperature is lower first decomposites gas, make foamed slurry layer form abscess, progressively rising along with temperature, the blowing agent that blowing temperature is higher also starts to decomposite gas, by first up past extrapolation of the abscess of foaming, make the wallpaper surface that the present invention produces there is obvious granular sensation, be foamed slurry layer concave-convex surface, there is corn particle effect, simultaneously, corn particle effect wallpaper production technology of the present invention, it is produced material and is easy to get and low cost of manufacture.
Accompanying drawing explanation
Fig. 1 is invention corn particle effect wallpaper structural representation.
Label declaration
Base material 1 precoating liquid layer 2
Foamed slurry layer 3.
The specific embodiment
Below in conjunction with drawings and the specific embodiments, the present invention is described in detail.
Consult Fig. 1, a kind of corn particle effect wallpaper that the present invention discloses forms one deck precoating liquid layer 2 on base material 1, and described base material 1 is body paper or non-woven paper.On precoating liquid layer 2, form one deck foamed slurry layer 3, these foamed slurry layer 3 concave-convex surfaces.
The present invention also discloses described corn particle effect wallpaper production technology, comprise the following steps: on base material, be coated with one deck pre-coating solution and carry out surface treatment, pre-coating solution is a kind of conventional aqueous medium, industry universal name is called non-woven paper printing special assistant, its main component is: take crylic acid resin emulsion as matrix resin, water is solvent, and be added with the function additives such as coalescents, wetting agent, levelling agent, defoamer, thickener, on market, be common water-based printing material, main supply producer is east, Shanghai star, Dechang etc.In temperature, be under 120 ℃ of-150 ℃ of environment, to dry to form precoating liquid layer; On precoating liquid layer, be coated with one deck slurry, this slurry is comprised of following compositions in weight percentage: PVC45-50%, plasticizer 25-30%, filler 18-22%, solvent 2-5%, the first blowing agent 0-3%, the second blowing agent 1-2% and stabilizing agent 1-3%, after 150-170 ℃ of temperature lower surface is dry, temperature is increased to 190-200 ℃, and applies 1.5 * 10
5-5.2 * 10
5the pressure of Pa, then dries, rolling, and normal temperature slaking forms one deck foamed slurry layer 3 on precoating liquid layer 2, these foamed slurry layer 3 concave-convex surfaces.
Described plasticizer is DOP or TXIB or both mixing; Described filler is CaCO
3or TiO
2or both mixing; Described solvent is alkane solvent; Described the first blowing agent is chemical foaming agent AC or chemical foaming agent AC-LC
2; Described the second blowing agent is ACL-2.Wherein, AC, AC-LC
2be Celogen Az class blowing agent with ACL-2.DOP is o-phthalic acid dibutyl ester, and TXIB is 2,2,4-trimethyl-1,3-pentanediol diisobutyrate, and AC is Celogen Az, AC-LC
2also being Celogen Az with formal name used at school and the main component of ACL-2, is that AC is carried out to the product that modification obtains.
Embodiment mono-
Using body paper as base material 1, on base material 1, be coated with one deck pre-coating solution slurry and carry out surface treatment, after applying 130 ℃ of temperature, baking oven forms precoating liquid layer 2, PVC(resin) 50%, DOP19%, TXIB7%, CaCO on precoating liquid layer 2, with flower roller coat cloth one deck slurry, this slurry is comprised of following compositions in weight percentage:
313%, TiO
25%, alkane solvent 2%, chemical foaming agent AC-LC
21.5%, ACL-2 1% and stabilizing agent 1.5%, after baking oven applies the temperature surface drying of 155 ℃, then apply the temperature and 2.5 * 10 of 200 ℃
5after the pressure of Pa, dry, rolling, normal temperature slaking forms one deck foamed slurry layer 3 on precoating liquid layer 2, and these foamed slurry layer 3 concave-convex surfaces, have corn particle effect.
Embodiment bis-
Using non-woven paper as base material 1, on base material 1, be coated with one deck pre-coating solution slurry and carry out surface treatment, non-woven paper surface fiber is soaked, after applying 120 ℃ of temperature, baking oven forms precoating liquid layer 2, PVC(resin) 45%, DOP22%, TXIB3%, CaCO on precoating liquid layer 2, with flower roller coat cloth one deck slurry, this slurry is comprised of following compositions in weight percentage:
312%, TiO
210%, alkane solvent 4%, chemical foaming agent AC 1%, ACL-2 1.5% and stabilizing agent 1.5%, after baking oven applies the temperature surface drying of 160 ℃, then apply the temperature and 1.5 * 10 of 200 ℃
5after the pressure of Pa, dry, rolling, normal temperature slaking forms one deck foamed slurry layer 3 on precoating liquid layer 2, and these foamed slurry layer 3 concave-convex surfaces, have corn particle effect.
Embodiment tri-
Using non-woven paper as base material 1, on base material 1, be coated with one deck pre-coating solution slurry and carry out surface treatment, non-woven paper surface fiber is soaked, after applying 115 ℃ of temperature, baking oven forms precoating liquid layer 2, PVC(resin) 46%, DOP26%, CaCO on precoating liquid layer 2, with flower roller coat cloth one deck slurry, this slurry is comprised of following compositions in weight percentage:
312%, TiO
29%, alkane solvent 2%, chemical foaming agent AC 1.2%, ACL-2 1.8% and stabilizing agent 2%, after baking oven applies the temperature surface drying of 165 ℃, then apply the temperature and 2.0 * 10 of 195 ℃
5after the pressure of Pa, dry, rolling, normal temperature slaking forms one deck foamed slurry layer 3 on precoating liquid layer 2, and these foamed slurry layer 3 concave-convex surfaces, have corn particle effect.
Embodiment tetra-
Using non-woven paper as base material 1, on base material 1, be coated with one deck pre-coating solution slurry and carry out surface treatment, non-woven paper surface fiber is soaked, after applying 125 ℃ of temperature, baking oven forms precoating liquid layer 2, PVC(resin) 47%, DOP17%, TXIB8%, CaCO on precoating liquid layer 2, with flower roller coat cloth one deck slurry, this slurry is comprised of following compositions in weight percentage:
315%, TiO
26%, alkane solvent 2%, chemical foaming agent AC-LC
22%, ACL-2 2% and stabilizing agent 1%, after baking oven applies the temperature surface drying of 165 ℃, then apply the temperature and 2.1 * 10 of 200 ℃
5after the pressure of Pa, dry, rolling, normal temperature slaking forms one deck foamed slurry layer 3 on precoating liquid layer 2, and these foamed slurry layer 3 concave-convex surfaces, have corn particle effect.
The foregoing is only preferred embodiment of the present invention, the not restriction to this case design, all equivalent variations of doing according to the design key of this case, all fall into the protection domain of this case.
Claims (9)
1. a corn particle effect wallpaper, is characterized in that: on base material, form one deck precoating liquid layer, form one deck foamed slurry layer on precoating liquid layer, this foamed slurry layer concave-convex surface.
2. a kind of corn particle effect wallpaper as claimed in claim 1, is characterized in that: described base material is body paper or non-woven paper.
3. a kind of corn particle effect wallpaper production technology as claimed in claim 1 or 2, is characterized in that: comprise the following steps: on base material, be coated with one deck pre-coating solution and carry out surface treatment, dry and form precoating liquid layer; On precoating liquid layer, be coated with one deck slurry, this slurry is comprised of following compositions in weight percentage: PVC45-50%, plasticizer 25-30%, filler 18-22%, solvent 2-5%, the first blowing agent 0-3%, the second blowing agent 1-2% and stabilizing agent 1-3%, after 150-170 ℃ of temperature lower surface is dry, temperature is increased to 190-200 ℃, and applies 1.5 * 10
5-5.2 * 10
5the pressure of Pa, then dries, rolling, and normal temperature slaking forms one deck foamed slurry layer on precoating liquid layer, this foamed slurry layer concave-convex surface.
4. a kind of corn particle effect wallpaper production technology as claimed in claim 3, is characterized in that: pre-coating solution is dried and formed precoating liquid layer is to complete under 120 ℃ of-150 ℃ of environment in temperature.
5. a kind of corn particle effect wallpaper production technology as claimed in claim 3, is characterized in that: described plasticizer is DOP or TXIB or both mixing.
6. a kind of corn particle effect wallpaper production technology as claimed in claim 3, is characterized in that: described filler is CaCO
3or TiO
2or both mixing.
7. a kind of corn particle effect wallpaper production technology as claimed in claim 3, is characterized in that: described solvent is alkane solvent.
8. a kind of corn particle effect wallpaper production technology as claimed in claim 3, is characterized in that: described the first blowing agent is chemical foaming agent AC or chemical foaming agent AC-LC
2.
9. a kind of corn particle effect wallpaper production technology as claimed in claim 3, is characterized in that: described the second blowing agent is ACL-2.