CN103709580B - A kind of memory cushion and preparation method thereof - Google Patents
A kind of memory cushion and preparation method thereof Download PDFInfo
- Publication number
- CN103709580B CN103709580B CN201310749242.6A CN201310749242A CN103709580B CN 103709580 B CN103709580 B CN 103709580B CN 201310749242 A CN201310749242 A CN 201310749242A CN 103709580 B CN103709580 B CN 103709580B
- Authority
- CN
- China
- Prior art keywords
- cushion
- preparation
- surfactant
- parts
- memory cushion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of memory cushion and preparation method thereof, memory cushion comprises the raw material of following weight portion meter: kymene 0-40 part, magnesium hydroxide 20-40 part, methacrylic acid 10-20 part, ammonium chloride 10-20 part, tributyl phosphate 20-50 part, trimethylolpropane 40-50 part, surfactant 20-30 part. The preparation method of memory cushion: polyamide, magnesium hydroxide, methacrylic acid, ammonium chloride, tributyl phosphate and trimethylolpropane are mixed, be heated to 90-110 DEG C, add surfactant, reaction 30-40min, injection mo(u)lding. Memory cushion of the present invention is through pressing for a long time, indeformable, still keeps original elasticity, and elasticity and restorability are all fine.
Description
Technical field
The present invention relates to a kind of memory cushion and preparation method thereof.
Background technology
Cushion, can allow seat for a long time in clean state, is placed on and above stool, has warming and comfortable effect. The shape of cushion, according to supporting chair designs, mostly is square, circular and oval. Cushion can also be made to animal, personage, fruit and other interesting image, on pattern, also can make with reference to the pattern of the pattern of bedcover in bedroom or sofa, also can independently come out as an article. Cushion small volume, is widely used, but after existing cushion is sat for a long time, flattens and be difficult for recovering, and affects result of use.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, a kind of memory cushion is provided, rebound performance is good.
The present invention is by the following technical solutions:
One is remembered cushion, comprises the raw material of following weight portion meter: kymene 0-40 part, magnesium hydroxide 20-40 part, methacrylic acid 10-20 part, ammonium chloride 10-20 part, tributyl phosphate 20-50 part, trimethylolpropane 40-50 part, surfactant 20-30 part.
As preferably, surfactant is stearic acid or neopelex.
The present invention also provides the preparation method of above-mentioned memory cushion, comprise the following steps: polyamide, magnesium hydroxide, methacrylic acid, ammonium chloride, tributyl phosphate and trimethylolpropane are mixed, be heated to 90-110 DEG C, add surfactant, reaction 30-40min, injection mo(u)lding.
Beneficial effect of the present invention: memory cushion of the present invention is through pressing for a long time, indeformable, still keeps original elasticity, and elasticity and restorability are all fine.
Detailed description of the invention
Below by specific embodiment, the present invention is further explained in detail.
Embodiment 1
One is remembered cushion, comprises the raw material of following weight portion meter: 0 part of kymene, 20 parts of magnesium hydroxides, 10 parts of methacrylic acids, 10 parts of ammonium chlorides, 20 parts of tributyl phosphates, 40 parts of trimethylolpropanes, 20 parts of surfactant neopelexes.
Preparation method, comprises the following steps: polyamide, magnesium hydroxide, methacrylic acid, ammonium chloride, tributyl phosphate and trimethylolpropane are mixed, be heated to 90 DEG C, add surfactant, reaction 30min, injection mo(u)lding.
Embodiment 2
One is remembered cushion, comprises the raw material of following weight portion meter: 40 parts of polyamide, 40 parts of magnesium hydroxides, 20 parts of methacrylic acids, 20 parts of ammonium chlorides, 50 parts of tributyl phosphates, 50 parts of trimethylolpropanes, 30 parts of surfactant stearic acid.
Preparation method, comprises the following steps: polyamide, magnesium hydroxide, methacrylic acid, ammonium chloride, tributyl phosphate and trimethylolpropane are mixed, be heated to 110 DEG C, add surfactant, reaction 40min, injection mo(u)lding.
Embodiment 3
One is remembered cushion, comprises the raw material of following weight portion meter: 5 parts of kymenes, 30 parts of magnesium hydroxides, 15 parts of methacrylic acids, 15 parts of ammonium chlorides, 30 parts of tributyl phosphates, 45 parts of trimethylolpropanes, 25 parts of surfactant stearic acid.
Preparation method, comprises the following steps: polyamide, magnesium hydroxide, methacrylic acid, ammonium chloride, tributyl phosphate and trimethylolpropane are mixed, be heated to 100 DEG C, add surfactant, reaction 35min, injection mo(u)lding.
Performance parameter of the present invention:
As from the foregoing, memory cushion of the present invention is through pressing for a long time, indeformable, still keeps original elasticity, and elasticity and restorability are all fine.
Claims (2)
1. a memory cushion, is characterized in that: the raw material that comprises following weight portion meter: kymene 0-40 part, magnesium hydroxide 20-40 part, methacrylic acid 10-20 part, ammonium chloride 10-20 part, tributyl phosphate 20-50 part, trimethylolpropane 40-50 part, surfactant 20-30 part; Its preparation method is: polyamide, magnesium hydroxide, methacrylic acid, ammonium chloride, tributyl phosphate and trimethylolpropane are mixed, be heated to 90-110 DEG C, add surfactant, reaction 30-40min, injection mo(u)lding.
2. memory cushion according to claim 1, is characterized in that: surfactant is stearic acid or neopelex.