CN103695122A - Lubricating agent of drawing lead-tin alloy steel-plating plate - Google Patents
Lubricating agent of drawing lead-tin alloy steel-plating plate Download PDFInfo
- Publication number
- CN103695122A CN103695122A CN201310701749.4A CN201310701749A CN103695122A CN 103695122 A CN103695122 A CN 103695122A CN 201310701749 A CN201310701749 A CN 201310701749A CN 103695122 A CN103695122 A CN 103695122A
- Authority
- CN
- China
- Prior art keywords
- lubricant
- plating plate
- metal steel
- steel plating
- terne metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a lubricant of a drawing lead-tin alloy steel-plating plate. 68# oil for a total loss system is adopted as base oil and matched with a plurality of composite additives. The lubricant comprises an oiliness agent, an antiwear agent, an extreme pressure agent, an anti-foaming agent, an antioxidant, a friction modifier, a metal deactivator and an antiwear assistant. The lubricant of the drawing lead-tin alloy steel-plating plate disclosed by the invention is good in lubricating property, strong in adhesiveness, good in wearing quality, viscosity-temperature characteristics and rinsing property, strong in extreme pressure property, good in cooling property, small in flow shear stress, and convenient to use and clean, the oil film strength in a deformation region is increased, the friction coefficient is reduced, coating falling powder attached to a steel die is reduced, stable strength and thickness performance of the oil film are kept, abrasion of a drawing tool and a drawing die is reduced, the surface glossiness and the specification accuracy of metal are improved, and the lubricant has proper flash point and ignition point.
Description
Technical field
The invention belongs to metal drawing processing and lubrication, the particularly field of lubricant of drawing terne metal steel plating plate.
Background technology
Drawing is one of main production method of tubing, bar, section bar and wire rod.Press goods cross-sectional shape, drawing can be divided into: solid material drawing and the large class of hollow material drawing two.Drawing terne metal (Pb:80%~80.5%, Sn:18%, Sb:1.5~2%) steel plating plate is that terne metal steel plating plate blank material is imposed to pulling force (load is greater than 700kPa), makes it by nib to obtain the plastic processing method with nib sectional dimension, goods that shape is identical.
In drawing process, the friction except between material, drawing-die and steel core, on contact surface, because drawing speed improves, will occurrence temperature sharply rise.In order reducing, in drawing process, to there is heavy wear or sintering, to reduce the coating powder that comes off and stick on punching block, thereby require lubricant to play antifriction and wear prevention, cooling, lubricated effect; Be improved drawing speed and section reduction rate, to improve output and the quality of drawing process processing simultaneously.
And the factor that affects the drawing of terne metal steel plating plate has conventionally: terne metal steel plating plate character (hardness, degree of cleaning, condition of surface); The material kind of drawing and drawing-die; The adaptability of drawing compound.Difference due to mode, condition and the range of product of drawing, also has difference to the requirement of lubricant.Therefore, drawing compound should meet many-sided requirements such as drawing process condition, industrial safety, economy, environmental friendliness, energy-conservation, reduction of discharging.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of lubricant of drawing terne metal steel plating plate, this lubricant should have good lubricity, increases oil film strength in distorted area, reduces frictional coefficient, reduce the coating powder that comes off and stick on punching block, keep oil film strength and thickness stable performance; Adhesivity is strong, and resistance to abrasion, sticky warm nature, to rinse performance good; Extreme pressure property is strong, cooling good, reduces the wearing and tearing of drawing device and drawing-die, has less mobile shear-stress, improves metallic surface smooth finish and specification precision, has suitable flash-point and point of ignition, easy to use and cleaning.
The present invention is usingd following technical scheme and is solved the problems of the technologies described above: employing be No. 68 total loss systems with oil as base oil, coordinate multiple composite additive, its each component and mass percent are:
Component | Content (mass percent) |
Base oil | Surplus |
Oiliness improver | 5.0%~8.0% |
Anti-wear agent | 8.0%~10.0% |
Extreme pressure agent | 5.0%~8.0% |
Kilfoam | 0.005%~0.01% |
Oxidation inhibitor | 0.5%~1.0% |
Friction improver | 3.0%~5.0% |
Metal passivator | 0.5%~1.0% |
Wear-resistant auxiliary agent | 0.3%~0.8% |
Base oil is No. 68 oil for total loss system.
Oiliness improver is sulfuration Oleum Gossypii semen.
Anti-wear agent is clorafin 42.
Extreme pressure agent is lead naphthenate.
Kilfoam is dimethyl silicone oil.
Oxidation inhibitor is N, the sub-Whitfield's ointment propylene diamine of N-.
Friction improver is phosphoric acid ester.
Metal passivator is thiadiazoles derivative.
Wear-resistant auxiliary agent is dialkyldithiocarbamacompositions tin.
The lubricant of drawing terne metal steel plating plate of the present invention, has good lubricity, increases oil film strength in distorted area, reduces frictional coefficient, reduces the coating powder that comes off and sticks on punching block, maintenance oil film strength and thickness stable performance; Adhesivity is strong, and resistance to abrasion, sticky warm nature, to rinse performance good; Extreme pressure property is strong, cooling good, reduces the wearing and tearing of drawing device and drawing-die, has less mobile shear-stress, improves metallic surface smooth finish and specification precision, has suitable flash-point and point of ignition, easy to use and cleaning.
Embodiment
Embodiment 1:
Following component is in harmonious proportion and is formed by mass percentage:
Component | Content (mass percent) |
No. 68 oil for total loss system | 66.19% |
Sulfuration Oleum Gossypii semen | 8.0% |
Clorafin 42 | 10.0% |
Lead naphthenate | 8.0% |
Dimethyl silicone oil | 0.01% |
N, the sub-Whitfield's ointment propylene diamine of N- | 1.0% |
Phosphoric acid ester | 5.0% |
Thiadiazoles derivative | 1.0% |
Dialkyldithiocarbamacompositions tin | 0.8% |
Above component summation is 100%.
Embodiment 2:
Following component is in harmonious proportion and is formed by mass percentage:
Component | Content (mass percent) |
No. 68 oil for total loss system | 71.9425% |
Sulfuration Oleum Gossypii semen | 6.5% |
Clorafin 42 | 9.0% |
Lead naphthenate | 6.5% |
Dimethyl silicone oil | 0.0075% |
N, the sub-Whitfield's ointment propylene diamine of N- | 0.75% |
Phosphoric acid ester | 4.0% |
Thiadiazoles derivative | 0.75% |
Dialkyldithiocarbamacompositions tin | 0.55% |
Above component summation is 100%.
Embodiment 3:
Following component is in harmonious proportion and is formed by mass percentage:
Component | Content (mass percent) |
No. 68 oil for total loss system | 77.695% |
Sulfuration Oleum Gossypii semen | 5.0% |
Clorafin 42 | 8.0% |
Lead naphthenate | 5.0% |
Dimethyl silicone oil | 0.005% |
N, the sub-Whitfield's ointment propylene diamine of N- | 0.5% |
Phosphoric acid ester | 3.0% |
Thiadiazoles derivative | 0.5% |
Dialkyldithiocarbamacompositions tin | 0.3% |
Above component summation is 100%.
The main physical and chemical index of embodiment 2 products is:
Project | Quality index |
Moisture, % | Vestige |
40 ℃ of kinematic viscosity mm 2/s | 73.6 |
Flash-point (opening) ℃, | 210 |
Mechanical impurity, % | Nothing |
Last non seizure load (Pb), Kg | 115 |
Pour point, ℃, | -5 |
Water soluble acid or alkali | Nothing |
Corrosion test (copper sheet, 100 ℃, 3h), level | 1 |
Viscosity index, is not less than | 90 |
Claims (10)
1. a lubricant for drawing terne metal steel plating plate, is characterized in that adopting No. 68 total loss systems as base oil, to coordinate multiple composite additive with oily, and its each component and mass percent are:
2. the lubricant of drawing terne metal steel plating plate as claimed in claim 1, is characterized in that base oil is No. 68 oil for total loss system.
3. the lubricant of drawing terne metal steel plating plate as claimed in claim 1, is characterized in that oiliness improver is sulfuration Oleum Gossypii semen.
4. the lubricant of drawing terne metal steel plating plate as claimed in claim 1, is characterized in that anti-wear agent is clorafin 42.
5. the lubricant of drawing terne metal steel plating plate as claimed in claim 1, is characterized in that extreme pressure agent is lead naphthenate.
6. the lubricant of drawing terne metal steel plating plate as claimed in claim 1, is characterized in that kilfoam is dimethyl silicone oil.
7. the lubricant of drawing terne metal steel plating plate as claimed in claim 1, is characterized in that in oxidation inhibitor be N, the sub-Whitfield's ointment propylene diamine of N-.
8. the lubricant of drawing terne metal steel plating plate as claimed in claim 1, is characterized in that friction improver is phosphoric acid ester.
9. the lubricant of drawing terne metal steel plating plate as claimed in claim 1, is characterized in that metal passivator is thiadiazoles derivative.
10. the lubricant of drawing terne metal steel plating plate as claimed in claim 1, is characterized in that wear-resistant auxiliary agent is dialkyldithiocarbamacompositions tin.