CN103695119B - Composition of ricinus communis-based weather-proof anti-rust anti-salt mist steel wire rope lubricating grease - Google Patents
Composition of ricinus communis-based weather-proof anti-rust anti-salt mist steel wire rope lubricating grease Download PDFInfo
- Publication number
- CN103695119B CN103695119B CN201310701742.2A CN201310701742A CN103695119B CN 103695119 B CN103695119 B CN 103695119B CN 201310701742 A CN201310701742 A CN 201310701742A CN 103695119 B CN103695119 B CN 103695119B
- Authority
- CN
- China
- Prior art keywords
- agent
- steel wire
- wire rope
- rust
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a composition of ricinus communis-based weather-proof anti-rust anti-salt mist steel wire rope lubricating grease. The base oil of HVIW500# lubricating oil serving as the base oil is matched with multiple composite additives. The ricinus communis-based weather-proof anti-rust anti-salt mist steel wire rope lubricating grease disclosed by the invention is applicable to all-weather environment and has the characteristics of corrosion protection, rusting resistance, dust prevention, moisture resistance, salt mist resistance and ultraviolet resistance; and moreover, the lubricating grease can reduce the abrasion of a steel wire rope and realize uniform stress acting on the steel wire rope, thereby reducing friction in the using process as well as the phenomenon of oil throwing.
Description
Technical field
The invention belongs to the composition of the weather-proof antirust Defend salt fog wire-rope grease of a kind of castor-oil plant base, belong to lubricating grease field.
Background technology
The intensity of wireline is large, from heavy and light, not easily suddenly fractures, reliable operation; Be widely used in lifting machine, fishery, mine, harbour, oil field, oceanographic engineering and engineering construction, in national economy, play huge effect.Wireline applying working condition is usually relatively more severe, often because of the reasons such as burn into unbalance stress and lack of lubrication cause steel rope fault, the situation of scrapping happens occasionally.
Wire-rope grease is coated on wireline surface usually, is reduce wireline friction in use on the one hand, reduces the wearing and tearing of wireline; Be protect wireline in transport, storage and use procedure on the other hand, dust-proof, windproof, moisture proof is not corroded.The surface lubrication fat that different wireline adopts also has larger difference.The kinestate (static stretching still bends repeatedly) of wireline, just whether applied environment (fishery, oceanographic engineering, mining or building structure steel wire rope) and dress trial run all can have different requirements to wire-rope grease.Both at home and abroad for different particular case, use the wire-rope grease of different size, and make great efforts to make grease product seriation and specificity.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind ofly has protection against corrosion, rust protection, dust-proof, moisture proof, Defend salt fog, antiultraviolet but also have the wearing and tearing reducing wireline, make wireline uniform force, reduce friction in use, reduce the composition getting rid of the weather-proof antirust Defend salt fog wire-rope grease of castor-oil plant base that oily phenomenon occurs.
The present invention solves the problems of the technologies described above by following technical scheme: adopt oil based on HVIW500 lubricant base, coordinate multiple composite additive, its each component and mass percent are:
| Component | Content (mass percent) |
| Base oil | Surplus |
| Saponifying agent | 8.0%～13.0% |
| Colloid tranquilizer | 2.0%～5.0% |
| Saponification auxiliary agent | 2.0%～3.0% |
| Alkaline agent | 1.0%～5.0% |
| Oxidation inhibitor | 0.5%～1.5% |
| Viscosity index improver | 3.0%～5.0% |
| Rust-preventive agent | 0.5%～2.0% |
| Anti-wear agent | 2.0%～3.0% |
| Strengthening agent | 6.0%～12.0% |
Base oil is the base oil of HVIW500 lubricating oil.
Saponifying agent is 12-oxystearic acid.
Colloid tranquilizer is sebacic acid.
Saponification auxiliary agent is boric acid.
Alkaline agent is lithium hydroxide.
Oxidation inhibitor is the 2,6 ditertiary butyl p cresol of mass ratio 50% ~ 40% and the 124 Triazole derivative compound of 50% ~ 60%.
Viscosity index improver is polymethacrylate.
Rust-preventive agent is the benzotriazole of mass ratio 50% ~ 40% and the dinonyl naphthalene sulfonate barium compound of 50% ~ 60%.
Anti-wear agent is boronation phosphamidon ester.
Strengthening agent mass ratio is the montanin wax of 50% ~ 40% and the ceresine compound of 50% ~ 60%.
The weather-proof antirust Defend salt fog wire-rope grease of castor-oil plant base of the present invention, be not only applicable to round-the-clock environment, there is protection against corrosion, rust protection, dust-proof, moisture proof, Defend salt fog, antiultraviolet characteristic, but also can reduce wireline wearing and tearing, make wireline uniform force, reduce friction in use, reduce the generation of getting rid of oily phenomenon.
Embodiment
Embodiment 1:
Following component is in harmonious proportion by mass percentage and forms:
| Component | Content (mass percent) |
| The base oil of HVIW500 lubricating oil | 50.5% |
| 12-oxystearic acid | 13.0% |
| Sebacic acid | 5.0% |
| Boric acid | 3.0% |
| Lithium hydroxide | 5.0% |
| The 2,6 ditertiary butyl p cresol of mass ratio 50% and the 124 Triazole derivative compound of 50% | 1.5% |
| Polymethacrylate | 5.0% |
| The benzotriazole of mass ratio 40% and the dinonyl naphthalene sulfonate barium compound of 60% | 2.0% |
| Boronation phosphamidon ester | 3.0% |
| The montanin wax of mass ratio 45% and the ceresine compound of 55% | 12.0% |
Above component summation is 100%.
Embodiment 2:
Following component is in harmonious proportion by mass percentage and forms:
| Component | Content (mass percent) |
| The base oil of HVIW500 lubricating oil | 58.0% |
| 12-oxystearic acid | 12.50% |
| Sebacic acid | 4.0% |
| Boric acid | 3.0% |
| Lithium hydroxide | 4.0% |
| The 2,6 ditertiary butyl p cresol of mass ratio 40% and the 124 Triazole derivative compound of 60% | 1.0% |
| Polymethacrylate | 3.0% |
| The benzotriazole of mass ratio 45% and the dinonyl naphthalene sulfonate barium compound of 55% | 1.5% |
| Boronation phosphamidon ester | 2.0% |
| The montanin wax of mass ratio 50% and the ceresine compound of 50% | 11.0% |
Above component summation is 100%.
Embodiment 3:
Following component is in harmonious proportion by mass percentage and forms:
| Component | Content (mass percent) |
| The base oil of HVIW500 lubricating oil | 55.5% |
| 12-oxystearic acid | 11.5% |
| Sebacic acid | 4.0% |
| Boric acid | 2.5% |
| Lithium hydroxide | 5.0% |
| The 2,6 ditertiary butyl p cresol of mass ratio 45% and the 124 Triazole derivative compound of 55% | 1.5% |
| Polymethacrylate | 4.0% |
| The benzotriazole of mass ratio 50% and the dinonyl naphthalene sulfonate barium compound of 50% | 1.5% |
| Boronation phosphamidon ester | 2.5% |
| The montanin wax of mass ratio 40% and the ceresine compound of 60% | 12.0% |
Above component summation is 100%.
The typical physical and chemical index of embodiment 1 product is:
| Project | Quality index |
| Outward appearance (15 DEG C ~ 25 DEG C) | Brown paste |
| Full cone penetration/unit | 96 |
| Dropping point/DEG C | 97 |
| Landing test (80 DEG C) | Qualified |
| Low-temperature performance (-30 DEG C) | Qualified |
| Salt-fog test (No. 45 steel, 7d)/level | B |
| No. 45 steel corrosions (100 DEG C, 3h) | Qualified |
| T 3Copper sheet (24h) | A level |
| H 62Number latten(-tin) (24h) | A level |
Claims (1)
1. the weather-proof antirust Defend salt fog wire-rope grease of castor-oil plant base, oil based on the base oil that it is characterized in that adopting HVIW500 lubricating oil, coordinate multiple composite additive, its each component and mass percent are:
Wherein:
Saponifying agent is 12-oxystearic acid;
Colloid tranquilizer is sebacic acid;
Saponification auxiliary agent is boric acid;
Alkaline agent is lithium hydroxide;
Oxidation inhibitor is mass ratio is the 2,6 ditertiary butyl p cresol of 50% ~ 40% and the 124 Triazole derivative compound of 50% ~ 60%;
Viscosity index improver is polymethacrylate;
Anti-wear agent is boronation phosphamidon ester;
Rust-preventive agent is the benzotriazole of mass ratio 50% ~ 40% and the dinonyl naphthalene sulfonate barium compound of 50% ~ 60%;
Strengthening agent is the montanin wax of mass ratio 50% ~ 40% and the ceresine compound of 50% ~ 60%.