CN103668669B - A kind of thread water absorben perspiring shell fabric and preparation method thereof - Google Patents
A kind of thread water absorben perspiring shell fabric and preparation method thereof Download PDFInfo
- Publication number
- CN103668669B CN103668669B CN201310614059.5A CN201310614059A CN103668669B CN 103668669 B CN103668669 B CN 103668669B CN 201310614059 A CN201310614059 A CN 201310614059A CN 103668669 B CN103668669 B CN 103668669B
- Authority
- CN
- China
- Prior art keywords
- preparation
- shell fabric
- thread water
- present
- water absorben
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of thread water absorben perspiring shell fabric and preparation method thereof, thread water absorben perspiring shell fabric is made up of the raw material of following parts by weight: '-diphenylmethane diisocyanate 20-40 part, polymethyl methacrylate 80-90 part, cresols 10-20 part, polyvinyl resin 50-60 part, phosphate 20-25 part, honeysuckle 10-15 part, surfactant 10-18 part; Preparation method is by '-diphenylmethane diisocyanate, polymethyl methacrylate, cresols, polyvinyl resin, phosphate mixing, be heated into molten condition, add honeysuckle and surfactant mixing, extrude from spinnerets, form fiber, fibrage is become fabric.Moisture releasing rate of the present invention is between 11-13%, and when envionmental humidity is 50%, moisture releasing rate of the present invention is between 15-17%, and when envionmental humidity is 70%, moisture releasing rate of the present invention is between 19-20%.As from the foregoing, the present invention has good moisture absorbing and sweat releasing performance.
Description
Technical field
The present invention relates to fabric field, particularly relate to a kind of thread water absorben perspiring shell fabric and preparation method thereof.
Background technology
One of material that fabric is often used as people, has a significant impact the life of people.The function of fabric is also different, and some fabric is good hygroscopicity as cotton has, but cotton not easily not easily discharges moisture after moisture absorption, and people are worn uncomfortable, some fabric is good perspire effect as nylon facing material has, but moisture pick-up properties is good not.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, provide a kind of thread water absorben perspiring shell fabric, there is good moisture pick-up properties and moisture releasing performance simultaneously.
Thread water absorben perspiring shell fabric, is made up of the raw material of following parts by weight: '-diphenylmethane diisocyanate 20-40 part, polymethyl methacrylate 80-90 part, cresols 10-20 part, polyvinyl resin 50-60 part, phosphate 20-25 part, honeysuckle 10-15 part, surfactant 10-18 part.
As preferably, surfactant is the one in cetyl ester, isobutyl palmitate or cetyl stearic.
Present invention also offers a kind of preparation method of thread water absorben perspiring shell fabric, technique is simple, comprise the following steps: by '-diphenylmethane diisocyanate, polymethyl methacrylate, cresols, polyvinyl resin, phosphate mixing, be heated into molten condition, add honeysuckle and surfactant mixing, extrude from spinnerets, form fiber, fibrage is become fabric.
As preferably, the orifice diameter of spinnerets is 0.01-0.12mm.
As preferably, the warp density of thread water absorben perspiring shell fabric is 80-100 root/cm, and weft density is 50-80 root/cm.
Moisture releasing rate of the present invention is between 11-13%, and when envionmental humidity is 50%, moisture releasing rate of the present invention is between 15-17%, and when envionmental humidity is 70%, moisture releasing rate of the present invention is between 19-20%.As from the foregoing, the present invention has good moisture absorbing and sweat releasing performance.
Detailed description of the invention
Below by specific embodiment 1-3, the present invention is described in further detail:
Embodiment 1-3 adopts following raw material (unit is Kg):
| Embodiment 1 | Embodiment 2 | Embodiment 3 | |
| '-diphenylmethane diisocyanate | 20 | 40 | 30 |
| Polymethyl methacrylate | 80 | 90 | 85 |
| Cresols | 10 | 20 | 15 |
| Polyvinyl resin | 50 | 60 | 55 |
| Phosphate | 20 | 25 | 23 |
| Honeysuckle | 10 | 15 | 12 |
| Surfactant | 10 | 18 | 15 |
embodiment 1
Preparation method of the present invention, comprise the following steps: by '-diphenylmethane diisocyanate, polymethyl methacrylate, cresols, polyvinyl resin, phosphate mixing, be heated into molten condition, add honeysuckle and the mixing of surfactant cetyl ester, extrude from spinnerets (orifice diameter is 0.01mm), form fiber, according to warp density 80/cm, weft density 50/cm, becomes fabric by fibrage.
embodiment 2
Preparation method of the present invention, comprise the following steps: by '-diphenylmethane diisocyanate, polymethyl methacrylate, cresols, polyvinyl resin, phosphate mixing, be heated into molten condition, add honeysuckle and the mixing of surfactant isobutyl palmitate, extrude from spinnerets (orifice diameter is 0.12mm), form fiber, according to warp density 100/cm, weft density 80/cm, becomes fabric by fibrage.
embodiment 3
Preparation method of the present invention, comprise the following steps: by '-diphenylmethane diisocyanate, polymethyl methacrylate, cresols, polyvinyl resin, phosphate mixing, be heated into molten condition, add honeysuckle and surfactant cetyl stearic) mixing, extrude from spinnerets (orifice diameter is 0.09mm), form fiber, according to warp density 90/cm, weft density 70/cm, becomes fabric by fibrage.
test:
Test the performance parameter of fabric of the present invention:
The humidity absorption and release rate of fabric also has certain association with envionmental humidity, relative humidity is larger, moisture absorbing and sweat releasing effect is better, when envionmental humidity is 30%, hydroscopicity of the present invention is between 9-10%, and when envionmental humidity is 50%, hydroscopicity of the present invention is between 12-13%, when envionmental humidity is 70%, hydroscopicity of the present invention is between 17-19%; When envionmental humidity is 30%, moisture releasing rate of the present invention is between 11-13%, and when envionmental humidity is 50%, moisture releasing rate of the present invention is between 15-17%, and when envionmental humidity is 70%, moisture releasing rate of the present invention is between 19-20%.As from the foregoing, the present invention has good moisture absorbing and sweat releasing performance.
Claims (1)
1. a thread water absorben perspiring shell fabric, it is characterized in that, be made up of the raw material of following parts by weight: '-diphenylmethane diisocyanate 20-40 part, polymethyl methacrylate 80-90 part, cresols 10-20 part, polyvinyl resin 50-60 part, phosphate 20-25 part, honeysuckle 10-15 part, surfactant 10-18 part; Surfactant is the one in cetyl ester, isobutyl palmitate or cetyl stearic.
2.the preparation method of thread water absorben perspiring shell fabric according to claim 1, it is characterized in that, comprise the following steps: by '-diphenylmethane diisocyanate, polymethyl methacrylate, cresols, polyvinyl resin, phosphate mixing, be heated into molten condition, add honeysuckle and surfactant mixing, extrude from spinnerets, form fiber, fibrage is become fabric.
3.the preparation method of thread water absorben perspiring shell fabric according to claim 2, is characterized in that, the orifice diameter of spinnerets is 0.01-0.12mm.
4.the preparation method of thread water absorben perspiring shell fabric according to claim 2, is characterized in that, the warp density of thread water absorben perspiring shell fabric is 80-100 root/cm, and weft density is 50-80 root/cm.