CN103665610A - Black sidewall rubber of radial tire of passenger car - Google Patents
Black sidewall rubber of radial tire of passenger car Download PDFInfo
- Publication number
- CN103665610A CN103665610A CN201310620708.2A CN201310620708A CN103665610A CN 103665610 A CN103665610 A CN 103665610A CN 201310620708 A CN201310620708 A CN 201310620708A CN 103665610 A CN103665610 A CN 103665610A
- Authority
- CN
- China
- Prior art keywords
- parts
- passenger car
- black
- paraffin
- rubbers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the technical field of tires, in particular to black sidewall rubber of a radial tire of a passenger car. The black sidewall rubber of the radial tire of the passenger car comprises raw materials in parts by weight as follows: chlorinated butyl rubber, ethylene propylene diene monomer rubber, butadiene styrene rubber, zinc oxide, stearic acid, carbon black N550, paraffin oil, paraffin, alkyl phenol disulfide and sulfur. The black sidewall rubber is wear-resistant, aging-resistant, puncture-resistant and resistant to dryness, wetness and skid and has lower hysteresis loss.
Description
Technical field
The invention belongs to the technical field of tire, be specifically related to a kind of black sidewall glue of radial tyre of passenger car.
Background technology
Half-steel meridian tyre refers to that body cord and crown center are 90 ° of angles or approaches that 90 ° of angles are arranged and with the pneumatic tyre of belt banding carcass.The fetus face bit position of half-steel meridian tyre or all adopt steel wire cord as supporting material, carcass adopts the radial of the filamentary materials such as nylon, polyester.Car half-steel meridian tyre comprises that tyre surface, band, belt, sidewall, the wear-resisting glue in rim of the mouth, carcass, air retaining wall, tyre bead, triangle rubber, rim of the mouth protect cloth.Car half-steel meridian tyre constructional feature is the single sizing material of the general employing of tyre surface, can not do hierarchial design; On belt, increase by one to two-layer fiber band, improve tire high speed performance; Sidewall is soft, and warping strength fatigability and anti-light aging performance are good; Tubeless design, air retaining wall requires to have extremely low ventilation property; For improving the rigidity of bead region, adopt large and hard triangle rubber stamen.
Car half-steel meridian tyre has following characteristics: 1, at a high speed; 2, fuel-economizing; 3, wear-resisting; 4, ride comfort; 5. handle
Stable; 6, low noise.
When the travel speed of tire is high, the wriggling between tyre surface and ground is very little, and tractive force and side force are higher, therefore requires tread rubber will have higher hardness, wear resistance, traction property, lower rolling resistance preferably.
Summary of the invention
The object of the invention is to provide for the defect of above-mentioned existence a kind of black sidewall glue of radial tyre of passenger car, wear-resisting, ageing-resistant, the resistance to puncture of this black sidewall glue, anti-dry wet and slippery, there is lower hysteresis loss.
Technical scheme of the present invention is: a kind of black sidewall glue of radial tyre of passenger car, is comprised of following raw materials in parts by weight proportioning:
22~30 parts of chlorinated butyl rubbers
18~20 parts of terpolymer EP rubbers
5~12 parts, styrene-butadiene rubber(SBR)
1~3 part, zinc oxide
1~5 part of stearic acid
40~50 parts of carbon black N550
10~12 parts of paraffin oils
1.0~1.5 parts, paraffin
1.0~1.3 parts of alkyl phenol disulfides
0.5~1.0 part of Sulfur.
The black sidewall glue of described radial tyre of passenger car, is comprised of following raw materials in parts by weight proportioning:
23.5 parts of chlorinated butyl rubbers
18.2 parts of terpolymer EP rubbers
6.2 parts, styrene-butadiene rubber(SBR)
1.5 parts, zinc oxide
2.5 parts of stearic acid
43.5 parts of carbon black N550
11.2 parts of paraffin oils
1.1 parts, paraffin
1.2 parts of alkyl phenol disulfides
0.6 part of Sulfur.
The black sidewall glue of described radial tyre of passenger car, is comprised of following raw materials in parts by weight proportioning:
27.8 parts of chlorinated butyl rubbers
19.2 parts of terpolymer EP rubbers
8.7 parts, styrene-butadiene rubber(SBR)
2.1 parts, zinc oxide
3.8 parts of stearic acid
46.3 parts of carbon black N550
10.8 parts of paraffin oils
1.3 parts, paraffin
1.18 parts of alkyl phenol disulfides
0.74 part of Sulfur.
The black sidewall glue of described radial tyre of passenger car, is comprised of following raw materials in parts by weight proportioning:
29.7 parts of chlorinated butyl rubbers
18.8 parts of terpolymer EP rubbers
10.6 parts, styrene-butadiene rubber(SBR)
2.7 parts, zinc oxide
4.8 parts of stearic acid
49.2 parts of carbon black N550
11.7 parts of paraffin oils
1.47 parts, paraffin
1.25 parts of alkyl phenol disulfides
0.85 part of Sulfur.
Beneficial effect of the present invention is: the hardness of the black sidewall glue of radial tyre of passenger car of the present invention (Shao Shi A) is 75~78,300% stress at definite elongation is 17.6~18.6MPa, tensile strength is 16.8~18MPa, tensile yield is 337~350%, be permanently deformed to 16~21%, elasticity is 27~30%, and Akron abrasion is 0.049~0.056, under speed 120km/h condition, rolling resistance is 54~58N.
In sum, wear-resisting, ageing-resistant, the resistance to puncture of described black sidewall glue, anti-dry wet and slippery, there is lower hysteresis loss.
Embodiment
Below by specific embodiment, the present invention will be described in detail.
Embodiment 1
A black sidewall glue for radial tyre of passenger car, is comprised of following raw materials in parts by weight proportioning:
22 parts of chlorinated butyl rubbers
18 parts of terpolymer EP rubbers
5 parts, styrene-butadiene rubber(SBR)
1 part, zinc oxide
1 part of stearic acid
40 parts of carbon black N550
10 parts of paraffin oils
1.0 parts, paraffin
1.0 parts of alkyl phenol disulfides
0.5 part of Sulfur.
Described in employing embodiment 1, the hardness (Shao Shi A) of the black sidewall glue of radial tyre of passenger car is 75,300% stress at definite elongation is 17.6MPa, tensile strength is 16.8MPa, tensile yield is 337%, be permanently deformed to 16%, elasticity is 27%, and Akron abrasion is 0.049, under speed 120km/h condition, rolling resistance is 58N.
Embodiment 2
The black sidewall glue of described radial tyre of passenger car, is comprised of following raw materials in parts by weight proportioning:
23.5 parts of chlorinated butyl rubbers
18.2 parts of terpolymer EP rubbers
6.2 parts, styrene-butadiene rubber(SBR)
1.5 parts, zinc oxide
2.5 parts of stearic acid
43.5 parts of carbon black N550
11.2 parts of paraffin oils
1.1 parts, paraffin
1.2 parts of alkyl phenol disulfides
0.6 part of Sulfur.
Described in employing embodiment 2, the hardness (Shao Shi A) of the black sidewall glue of radial tyre of passenger car is 76.8,300% stress at definite elongation is 17.8MPa, tensile strength is 17.1MPa, tensile yield is 339.1%, be permanently deformed to 17.2%, elasticity is 28.1%, and Akron abrasion is 0.050, under speed 120km/h condition, rolling resistance is 55.6N.
Embodiment 3
The black sidewall glue of described radial tyre of passenger car, is comprised of following raw materials in parts by weight proportioning:
27.8 parts of chlorinated butyl rubbers
19.2 parts of terpolymer EP rubbers
8.7 parts, styrene-butadiene rubber(SBR)
2.1 parts, zinc oxide
3.8 parts of stearic acid
46.3 parts of carbon black N550
10.8 parts of paraffin oils
1.3 parts, paraffin
1.18 parts of alkyl phenol disulfides
0.74 part of Sulfur.
Described in employing embodiment 3, the hardness (Shao Shi A) of the black sidewall glue of radial tyre of passenger car is 77.3,300% stress at definite elongation is 18.2MPa, tensile strength is 17.23MPa, tensile yield is 341.2%, be permanently deformed to 18.26%, elasticity is 28.14%, and Akron abrasion is 0.052, under speed 120km/h condition, rolling resistance is 56.87N.
Embodiment 4
The black sidewall glue of described radial tyre of passenger car, is comprised of following raw materials in parts by weight proportioning:
29.7 parts of chlorinated butyl rubbers
18.8 parts of terpolymer EP rubbers
10.6 parts, styrene-butadiene rubber(SBR)
2.7 parts, zinc oxide
4.8 parts of stearic acid
49.2 parts of carbon black N550
11.7 parts of paraffin oils
1.47 parts, paraffin
1.25 parts of alkyl phenol disulfides
0.85 part of Sulfur.
Described in employing embodiment 4, the hardness (Shao Shi A) of the black sidewall glue of radial tyre of passenger car is 77.53,300% stress at definite elongation is 18.45MPa, tensile strength is 17.68MPa, tensile yield is 348.7%, be permanently deformed to 20.47%, elasticity is 28.76%, and Akron abrasion is 0.055, under speed 120km/h condition, rolling resistance is 56.47N.
Embodiment 5
A black sidewall glue for radial tyre of passenger car, is comprised of following raw materials in parts by weight proportioning:
30 parts of chlorinated butyl rubbers
20 parts of terpolymer EP rubbers
12 parts, styrene-butadiene rubber(SBR)
3 parts, zinc oxide
5 parts of stearic acid
50 parts of carbon black N550
12 parts of paraffin oils
1.5 parts, paraffin
1.3 parts of alkyl phenol disulfides
1.0 parts of Sulfurs.
Described in employing embodiment 5, the hardness (Shao Shi A) of the black sidewall glue of radial tyre of passenger car is 78,300% stress at definite elongation is 18.6MPa, tensile strength is 18MPa, tensile yield is 350%, be permanently deformed to 21%, elasticity is 30%, and Akron abrasion is 0.056, under speed 120km/h condition, rolling resistance is 54N.
Claims (4)
1. a black sidewall glue for radial tyre of passenger car, is characterized in that, following raw materials in parts by weight proportioning, consists of:
22~30 parts of chlorinated butyl rubbers
18~20 parts of terpolymer EP rubbers
5~12 parts, styrene-butadiene rubber(SBR)
1~3 part, zinc oxide
1~5 part of stearic acid
40~50 parts of carbon black N550
10~12 parts of paraffin oils
1.0~1.5 parts, paraffin
1.0~1.3 parts of alkyl phenol disulfides
0.5~1.0 part of Sulfur.
2. the black sidewall glue of radial tyre of passenger car according to claim 1, is characterized in that, following raw materials in parts by weight proportioning, consists of:
23.5 parts of chlorinated butyl rubbers
18.2 parts of terpolymer EP rubbers
6.2 parts, styrene-butadiene rubber(SBR)
1.5 parts, zinc oxide
2.5 parts of stearic acid
43.5 parts of carbon black N550
11.2 parts of paraffin oils
1.1 parts, paraffin
1.2 parts of alkyl phenol disulfides
0.6 part of Sulfur.
3. the black sidewall glue of radial tyre of passenger car according to claim 1, is characterized in that, following raw materials in parts by weight proportioning, consists of:
27.8 parts of chlorinated butyl rubbers
19.2 parts of terpolymer EP rubbers
8.7 parts, styrene-butadiene rubber(SBR)
2.1 parts, zinc oxide
3.8 parts of stearic acid
46.3 parts of carbon black N550
10.8 parts of paraffin oils
1.3 parts, paraffin
1.18 parts of alkyl phenol disulfides
0.74 part of Sulfur.
4. the black sidewall glue of radial tyre of passenger car according to claim 1, is characterized in that, following raw materials in parts by weight proportioning, consists of:
29.7 parts of chlorinated butyl rubbers
18.8 parts of terpolymer EP rubbers
10.6 parts, styrene-butadiene rubber(SBR)
2.7 parts, zinc oxide
4.8 parts of stearic acid
49.2 parts of carbon black N550
11.7 parts of paraffin oils
1.47 parts, paraffin
1.25 parts of alkyl phenol disulfides
0.85 part of Sulfur.