CN103657711B - A kind of catalytic cracking catalyst and preparation method thereof - Google Patents
A kind of catalytic cracking catalyst and preparation method thereof Download PDFInfo
- Publication number
- CN103657711B CN103657711B CN201210341383.XA CN201210341383A CN103657711B CN 103657711 B CN103657711 B CN 103657711B CN 201210341383 A CN201210341383 A CN 201210341383A CN 103657711 B CN103657711 B CN 103657711B
- Authority
- CN
- China
- Prior art keywords
- rare earth
- molecular sieve
- zeolite
- weight
- catalytic cracking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of catalytic cracking catalyst and preparation method thereof, this catalytic cracking catalyst contains cracking activity constituent element, clay and binding agent; Wherein, described cracking activity constituent element comprises three kinds of Y zeolites, first Y zeolite is rare earth Y type molecular sieve, its content of rare earth counts the heavy % of 10-25 with rare earth oxide, lattice constant is 2.440-2.472nm, degree of crystallinity is 35-65%, framework silicon-aluminum atomic ratio is 2.5-5.0, in this molecular sieve X-ray diffraction spectrogram the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at ° peak, 2 θ=11.8 ± 0.1 ratio (I1/I2) and molecular sieve in be greater than 50 in the product value of the rare earth weight percentage of rare earth oxide; Second Y zeolite is the gas phase super-stable Y molecular sieves containing rare earth; 3rd Y zeolite is the DASY molecular sieve containing rare earth.The preparation method of described catalyst comprises preparation and comprises the slurries of cracking activity constituent element, binding agent and clay, spray-dired step.Catalyst of the present invention has higher conversion ratio and gasoline yield, can reduce molecular sieve consumption, reduce costs.
Description
Background technology
Catalytic cracking (FCC) is important crude oil secondary processing process, occupies very important status in petroleum refining industry.In catalytic cracking process, the residual oil of heavy end as vacuum distillate or more heavy constituent reacts in the presence of a catalyst, be converted into the high value added products such as liquefied gas, gasoline, diesel oil, usually need in this process to use the catalysis material with high cracking activity.Micro-pore zeolite catalysis material, owing to having excellent shape selective catalysis performance and very high cracking reaction activity, is widely used in petroleum refining and processing industry.Wherein Y zeolite is since last century, the sixties used first, is just the chief active constituent element of catalytic cracking catalyst always.Especially remarkable effect is had through the improvement of rare earth modified Y zeolite to acidic zeolite and structural stability.
In recent years, because rare earth price rapidly goes up, considerably increase the production cost of rare-earth modified molecular-sieve, cause no small pressure to manufacturing enterprise.In order to effectively utilize rare earth resources, reduce the molecular sieve production cost of molecular sieve production cost, particularly high rare-earth content, the rare earth utilization rate in modifying process must be improved, reduce rare earth to run off, also will ensure the cracking performance of molecular sieve simultaneously, improve the activity stability of molecular sieve as far as possible.
Current rare earth Y type molecular sieve is used widely in catalytic cracking catalyst as active component, such as in olefine lowering catalyst, two roasting techniques are handed in general employing two, i.e. twice liquid phase rare earth ion exchanged and twice high-temperature roasting, molecular sieve Rare-Earth Content reaches the heavy % of 16-22, there is higher hydrogen transfer activity, Olefin decrease successful, but it is high to there is coke yield, affects the problem of octane number and diesel yield.
A kind of olefine lowering catalyst and preparation method thereof is disclosed in CN1317547A, this catalyst mainly containing content of rare earth be the heavy % of 12-20, degree of crystallinity be greater than 50% REY molecular sieve and content of rare earth be the heavy % of 2-12, phosphorus content is the composite modified PREY molecular sieve of the heavy % of 0.2-3, the phosphorus of lattice constant 2.445-2.465nm and rare earth, compared with conventional catalyst, this catalyst Olefin decrease successful and product slates and octane number can be ensured.
A kind of hyperastable Y-type RE molecular sieve is disclosed in CN1506161A, two roasting techniques are handed in same employing two, namely after a roasting rare earth sodium Y is handed in acquisition one, substep reacts with rare earth and phosphorus containg substances again, and carry out second time roasting, obtain the composite modified Y molecular sieve of content of rare earth 8-25 heavy %, phosphorus content 0.1-3.0 heavy %, degree of crystallinity 30-55%, lattice constant 2.455-2.477nm, this molecular sieve has the significant effect reducing gasoline olefin, coke yield is moderate, diesel yield is high, and the utilization rate of modifying element is high.
Two molecular sieves handing over two roasting techniques to prepare are adopted also to have some other feature, can the molecular sieve improving coking behavior and preparation method thereof disclosed in CN101537366A, two friendships two are still adopted to roast technique, this molecular sieve phosphorus content 0.05-5.0%, content of rare earth is few, be only 0.05-4.0%, lattice constant 2.430-2.440nm, degree of crystallinity 35-55%.
A kind of modcfied faujasite and the hydrocarbon cracking catalyzer containing this zeolite is disclosed in CN1436727A, one is adopted to hand over a roasting technique, namely NaY first carries out an exchange reaction with phosphorus compound and ammonium compounds, add again subsequently earth solution continue reaction, more after filtration, washing and hydrothermal calcine obtain, this preparation process flow process is short, by the catalyst activity good stability of this molecular sieve, gasoline yield is high, and coke yield is low, has stronger heavy oil cracking ability and preventing from heavy metal pollution ability.
A kind of high silicon rare earth Y type zeolite is disclosed in CN1382631A, by the gas-phase reaction of rare earth Y type zeolite and silicon tetrachloride, obtain a kind of intracrystalline content of rare earth 4-15 heavy %, lattice constant 2.450-2.458nm, collapse temperature 1000-1056 DEG C, silica alumina ratio 8.3-8.8, sodium oxide content is less than the rare earth Y type zeolite of 1.0 heavy %, and this zeolite has good heavy oil cracking activity and selective, can improve yield of light oil, improve quality of gasoline, and there is good coke selectivity.
A kind of modified Y molecular sieve is disclosed in CN101823726A, one is adopted to hand over a roasting technique, namely NaY first carries out an exchange reaction with earth solution, add phosphorus compound subsequently again and continue reaction, more after filtration, washing and hydrothermal calcine obtain, its content of rare earth is about the heavy % of 11-23, rare earth major part is arranged in sodalite cage, molecular sieve stability improves, simultaneously adjustable change acidic zeolite, and the catalyst containing this molecular sieve has the advantages that heavy oil conversion performance is strong, coke selectivity is good.
Disclose a kind of rare-earth Y molecular sieve and preparation method thereof in CN100344374C, content of rare earth counts the heavy % of 12-22 with rare earth oxide, and rare earth ion is all arranged in the little cage of molecular sieve, in its 27AlMASNMR spectrogram, is that 0ppm goes out not have peak to occur in chemical shift.Said preparation method is that a roasting technique is handed in employing one, regulate pH value of solution to 8-11 with alkaline solution after handing over one, carry out again filtering, wash, dry and roasting, or isolated molecule sieving cake after handing over, collect filtrate, in filtrate, add alkaline solution regulates pH value of solution to 8-11, then the making beating that the rare earth hydrate filter cake obtained and molecular sieve filter cake added water, filtration, washing, dry and roasting.This technique makes rare earth ion precipitation unnecessary in solution avoid rare earth run off and can ensure that rare earth ion is all arranged in the little cage of molecular sieve.CN1322928C discloses a kind of catalyst being active component with this molecular sieve, significantly can reduce catalytic cracking gasoline olefine content, has excellent heavy oil conversion performance simultaneously.
In prior art, no matter adopt two friendships two to roast technique or one and hand over the rare-earth Y molecular sieve that obtains of a roasting technique, content of rare earth in its product is always lower than the total rare earth (TRE) amount dropped into, as CN1053808A, CN1069553C, disclosed in CN1026225C, several rare-earth Y molecular sieve all has this feature, even if there is more rare earth ion to be positioned in little cage, but inevitably have part rare earth ion to be still present in supercage, rare earth ion in supercage can by under backwash in follow-up washing process, cause rare earth to run off, cause the reduction of rare earth utilization rate.
Summary of the invention
The object of this invention is to provide a kind of catalytic cracking catalyst and preparation method thereof.Compared with prior art, catalyst of the present invention has higher conversion ratio and gasoline yield, can reduce molecular sieve consumption in the catalyst, reduces Catalyst Production cost.
The invention provides a kind of catalytic cracking catalyst, described catalytic cracking catalyst contains the binding agent of the cracking activity constituent element of 10-60 % by weight, the clay of 10-60 % by weight and 10-60 % by weight.Described cracking activity constituent element comprises the 3rd Y zeolite of first Y zeolite of 25-70 % by weight, second Y zeolite of 10-70 % by weight and 5-30 % by weight; Described first Y zeolite is a kind of rare earth Y type molecular sieve, its content of rare earth counts 10-25 % by weight with rare earth oxide, lattice constant is 2.440-2.472nm, degree of crystallinity is 35-65%, framework silicon-aluminum atomic ratio is 2.5-5.0, in this molecular sieve X-ray diffraction spectrogram the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at ° peak, 2 θ=11.8 ± 0.1 ratio (I1/I2) and molecular sieve in be greater than 50 in the product value of the rare earth weight percentage of rare earth oxide.In embodiments of the invention, this product value is preferably greater than 55 further.
The first described Y zeolite, under preferable case, content of rare earth counts the heavy % of 11-23 with rare earth oxide, and lattice constant is 2.450-2.470nm, and degree of crystallinity is 40-60%.
Described first Y zeolite is a kind of rare earth Y type molecular sieve, is through two friendship two roastings, obtains in conjunction with deposition of rare-earth process.More particularly, obtain through following preparation process: the mixed solution of NaY molecular sieve and earth solution or earth solution and ammonium salt is carried out contact pairs, after filtration, washing, after drying, carry out first time calcination process, obtain rare earth sodium Y molecular sieve; Then by rare earth sodium Y molecular sieve making beating and with ammonium salt solution or acid solution contact pairs, mix with earth solution again after filtration, and regulates the pH value of slurries to be 6-10, filter or do not filter, drying, carry out second time calcination process, obtain described rare earth Y type molecular sieve.
In above-mentioned preparation process, the sial atomic ratio of raw material NaY molecular sieve is preferably greater than 2.5 and degree of crystallinity is greater than 80%.The said mixed solution by NaY molecular sieve and earth solution or earth solution and ammonium salt carries out in the process of contact pairs, earth solution is 0.06-0.14 in rare earth oxide with the part by weight of NaY molecular sieve butt, preferred 0.08-0.12, adjustment pH is 3.0-5.0, control water sieve weight ratio at 5-30, preferably 8-15, the process of said contact pairs is at room temperature-100 DEG C, preferably 70-95 DEG C, carry out 0.3-3.0 hour, preferred 0.5-1.5 hour.
In above-mentioned preparation process, said first time calcination process, be calcination process 0.5-4.0 hour, preferred 1.0-3.0 hour under 500-650 DEG C, 0-100% water vapor conditions.Wherein calcination process is preferred embodiment carry out under 100% water vapor conditions for the first time.
In above-mentioned preparation process, said by the making beating of rare earth sodium Y molecular sieve and with the process of ammonium salt solution contact pairs be at room temperature-100 DEG C, preferably 60-80 DEG C, process 0.3-3.0 hour, preferred 0.5-1.5 hour, its middle rare earth sodium Y molecular sieve, by molecular sieve butt, is 1:(0.05-0.5 with the part by weight of ammonium salt and water): (5-30), preferably 1:(0.1-0.4): (8-15).Said by the making beating of rare earth sodium Y molecular sieve and with the process of acid solution contact pairs be at room temperature-100 DEG C, preferably 60-80 DEG C, process 0.3-2.0 hour, preferred 0.5-1.0 hour, its middle rare earth sodium Y molecular sieve, by molecular sieve butt, is 1:(003-0.2 with the part by weight of acid and H2O): (5-30), preferably 1:(0.05-0.1): (8-15).Said ammonium salt is selected from the mixture of any one or more in ammonium chloride, ammonium sulfate, ammonium nitrate, ammonium carbonate, carbonic hydroammonium.Said acid can be inorganic acid or organic acid, and inorganic acid can be selected from one or more the mixture in sulfuric acid, hydrochloric acid or nitric acid, and organic acid can be selected from one or more the mixture in oxalic acid, acetic acid, citric acid or tartaric acid.
In above-mentioned preparation process, by adding, akaline liquid adjustment slurry pH value is 6-10, preferable ph is 7-9, makes rare earth ion all precipitate formation rare-earth hydroxide, i.e. the process of deposition of rare-earth.Said akaline liquid can be selected from one or more the mixture in ammoniacal liquor, waterglass, sodium metaaluminate or sodium hydroxide solution.
In above-mentioned preparation process, said second time calcination process, be 500-650 DEG C, process 0.5-4 hour under 0-100% water vapor conditions, preferred 1-3 hour.Wherein second time calcination process is preferred embodiment carry out under 100% water vapor conditions.
In above-mentioned preparation process, rare earths material is well known to those skilled in the art, rare earth chloride or nitric acid rare earth can be selected from, can be rare earth chloride or the nitric acid rare earth of Rare Earth Elements Determination composition, wherein commonly comprise lanthanum chloride, lanthanum nitrate, cerium chloride or cerous nitrate etc., also can be the mishmetal of different rare earth element ratio, as rich cerium type or rich lanthanum type mishmetal.
In above-mentioned preparation process, preferred embodiment is that to have at least in wherein said double roasting process be once carry out under the water vapor conditions of 1-100%, more preferably 20-100%, most preferably 100%, steam treatment impels rare earth ion to move to little cage from molecular sieve supercage, therefore, the most preferred embodiment is the said double roasting process of preparation process is all carry out under the water vapor conditions of 100%.
In catalytic cracking catalyst provided by the invention, also containing other Y zeolite beyond the first described Y zeolite, other described Y zeolite such as the second Y zeolite and the 3rd Y zeolite, the second described Y zeolite is a kind of gas phase super-stable Y molecular sieves containing rare earth; Described 3rd Y zeolite is the DASY molecular sieve containing rare earth, and its content of rare earth is preferably 1.5-3 % by weight.
The present invention also provides a kind of preparation method of described catalytic cracking catalyst, and the method comprises: by cracking activity constituent element, clay and binding agent mixing making beating, then carry out spraying dry, washing, filtration and drying successively.
A kind of rare earth Y type molecular sieve of the active component that catalyst provided by the invention contains, by a liquid phase rare earth ion exchanged and a solid phase ion transition process, adopt the mode of deposition of rare-earth, through calcination process, rare earth ion is moved to little cage from supercage again, rare earth does not run off, molecular sieve structure good stability is (particularly through 800 DEG C, 100% steam burin-in process is after 17 hours, crystallization of molecular sieves reservation degree is high), activity stability better (light oil micro-reactor MA value), this preparation process can modulation content of rare earth flexibly, accurate control, simple to operate, and rare earth utilization rate is high, can more than 98% be reached, save rare earth resources, reduce production cost.
Compared with prior art, catalyst provided by the invention has higher activity stability, when content of rare earth quite or slightly low, than prior art, there is higher cracking activity, gasoline yield is high, or still can obtain higher catalytic activity and good product slates when molecular sieve content is lower in the catalyst, therefore also reduce the production cost of catalyst.
Detailed description of the invention
According to catalytic cracking catalyst provided by the invention, described cracking activity constituent element contains a kind of rare earth Y type molecular sieve, it is characterized in that, content of rare earth counts the heavy % of 10-25 with rare earth oxide, lattice constant is 2.440-2.472nm, degree of crystallinity is 35-65%, framework silicon-aluminum atomic ratio is 2.5-5.0, in this molecular sieve X-ray diffraction spectrogram the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at ° peak, 2 θ=11.8 ± 0.1 ratio (I1/I2) and molecular sieve in be greater than 50 in the product value of the rare earth weight percentage of rare earth oxide, in embodiments of the invention, this product value is preferably greater than 55 further.
According to catalytic cracking catalyst provided by the invention, also containing second and the 3rd Y zeolite in described cracking activity constituent element.Wherein:
Described second Y zeolite is the gas phase super-stable Y molecular sieves containing rare earth, its preparation method comprises: under agitation, Y zeolite containing rare earth is contacted with silicon tetrachloride, the temperature of contact is 100-500 DEG C, the time of contact is 0.1-10 hour, and described is 1:0.05-0.5 containing the Y zeolite of rare earth and the weight ratio of silicon tetrachloride.The concrete preparation method of described second gas phase super-stable Y molecular sieves can with reference to patent application CN1683244A, particularly embodiment 5,6 and 8 wherein;
In the present invention, described 3rd Y zeolite is the DASY molecular sieve containing rare earth, and the described DASY molecular sieve containing rare earth is the hydro-thermal super stable molecular sieve containing rare earth, wherein with RE
2o
3the content of rare earth that (rare earth oxide) is counted is preferably 1.5-3.0 % by weight.The described DASY molecular sieve containing rare earth can be various commercially available prod, such as, can be the DASY2.0 molecular sieve purchased from catalyst asphalt in Shenli Refinery of China Petrochemical Industry.
In the present invention, described clay can be clay conventional in catalytic cracking catalyst, such as, can be one or more in kaolin, halloysite, imvite, diatomite, galapectite, saponite, rectorite, sepiolite, attapulgite, hydrotalcite and bentonite.
In the present invention, described binding agent can be the conventional various binding agents used in catalytic cracking catalyst, such as can one or more for being selected from Ludox, Alumina gel and boehmite, is preferably the double aluminium binder of Alumina gel and boehmite.
In preferred situation, catalytic cracking catalyst provided by the invention, with the butt weight of described catalytic cracking catalyst for benchmark, described cracking activity constituent element in the content of butt for 20-50 % by weight, described clay in the content of butt for 20-50 % by weight, described binding agent in the content of butt for 10-50 % by weight.More preferably, with the butt weight of described catalytic cracking catalyst for benchmark, described cracking activity constituent element in the content of butt for 20-45 % by weight is such as 30-42 % by weight, described clay in the content of butt for 30-45 % by weight is such as 35-45 % by weight, described binding agent in the content of butt for 15-40 % by weight is such as 20-35 % by weight or for 25-32 % by weight.Described cracking activity constituent element comprises described 3rd Y zeolite of described first Y zeolite of 25-70 % by weight, described second Y zeolite of 10-70 % by weight and 5-25 % by weight, and such as described cracking activity constituent element can comprise described 3rd Y zeolite of described first Y zeolite of 30-65 % by weight, described second Y zeolite of 15-65 % by weight and 5-20 % by weight.
The preparation method of catalytic cracking catalyst provided by the invention, preferably includes following steps:
(1) mixed solution of NaY molecular sieve and earth solution or earth solution and ammonium salt is carried out contact pairs, after filtration, washing, after drying, carry out first time calcination process, obtain rare earth sodium Y molecular sieve; Then by rare earth sodium Y molecular sieve making beating and with ammonium salt solution or acid solution contact pairs, mix with earth solution again after filtration, and regulate the pH value of slurries to be 6-10, filter or do not filter, dry, carry out second time calcination process, obtain rare earth Y type molecular sieve of the present invention (the first Y zeolite);
(2) by cracking activity constituent element, clay and binding agent mixing making beating, then carry out spraying dry, washing, filtration and drying successively, wherein, described cracking activity constituent element comprises the first described Y zeolite, the second Y zeolite and the 3rd Y zeolite.
In above-mentioned preparation process, the sial atomic ratio of raw material NaY molecular sieve is preferably greater than 2.5 and degree of crystallinity is greater than 80%.The said mixed solution by NaY molecular sieve and earth solution or earth solution and ammonium salt carries out in the process of contact pairs, earth solution is 0.06-0.14 in rare earth oxide with the part by weight of NaY molecular sieve butt, preferred 0.08-0.12, adjustment pH is 3.0-5.0, control water sieve weight ratio at 5-30, preferably 8-15, the process of said contact pairs is at room temperature-100 DEG C, preferably 70-95 DEG C, carry out 0.3-3.0 hour, preferred 0.5-1.5 hour.
In above-mentioned preparation process, the first time calcination process described in step (1) is calcination process 0.5-4.0 hour, preferred 1.0-3.0 hour under 500-650 DEG C, 0-100% water vapor conditions.Wherein calcination process is preferred embodiment carry out under 100% water vapor conditions for the first time.
In above-mentioned preparation process, described in step (1) by the making beating of rare earth sodium Y molecular sieve and with the process of ammonium salt solution contact pairs be at room temperature-100 DEG C, preferably 60-80 DEG C, process 0.3-3.0 hour, preferred 0.5-1.5 hour, its middle rare earth sodium Y molecular sieve, by molecular sieve butt, is 1:(0.05-0.5 with the part by weight of ammonium salt and water): (5-30), preferably 1:(0.1-0.4): (8-15).Said by the making beating of rare earth sodium Y molecular sieve and with the process of acid solution contact pairs be at room temperature-100 DEG C, preferably 60-80 DEG C, process 0.3-2.0 hour, preferred 0.5-1.0 hour, its middle rare earth sodium Y molecular sieve by molecular sieve butt, with acid and H
2the part by weight of O is 1:(0.03-0.2): (5-30), preferably 1:(0.05-0.1): (8-15).Said ammonium salt is selected from the mixture of any one or more in ammonium chloride, ammonium sulfate, ammonium nitrate, ammonium carbonate, carbonic hydroammonium.Said acid can be inorganic acid or organic acid, and inorganic acid can be selected from one or more the mixture in sulfuric acid, hydrochloric acid or nitric acid, and organic acid can be selected from one or more the mixture in oxalic acid, acetic acid, citric acid or tartaric acid.
In above-mentioned preparation process, in step (1), by adding, akaline liquid adjustment slurry pH value is 6-10, preferable ph is 7-9, makes rare earth ion all precipitate formation rare-earth hydroxide, i.e. the process of deposition of rare-earth.Said akaline liquid can be selected from one or more the mixture in ammoniacal liquor, waterglass, sodium metaaluminate or NaOH.
In above-mentioned preparation process, the second time calcination process described in step (1), be 500-650 DEG C, process 0.5-4 hour under 0-100% water vapor conditions, preferred 1-3 hour.Wherein second time calcination process is preferred embodiment carry out under 100% water vapor conditions.
In above-mentioned preparation process, rare earths material is well known to those skilled in the art, rare earth chloride or nitric acid rare earth can be selected from, can be rare earth chloride or the nitric acid rare earth of Rare Earth Elements Determination composition, wherein commonly comprise lanthanum chloride, lanthanum nitrate, cerium chloride or cerous nitrate etc., also can be the mishmetal of different rare earth element ratio, as rich cerium type or rich lanthanum type mishmetal.
In above-mentioned preparation process, preferred embodiment is that to have at least in the double roasting process described in step (1) be once carry out under the water vapor conditions of 1-100%, more preferably 20-100%, most preferably 100%, steam treatment impels rare earth ion to move to little cage from molecular sieve supercage, therefore, the most preferred embodiment is the said double roasting process of preparation process is all carry out under the water vapor conditions of 100%.
According to the preparation method of catalytic cracking catalyst provided by the invention, by described cracking activity constituent element, mesoporous silica-alumina materials, clay and binding agent mixing making beating, and follow-up spraying dry, washing, filtration and drying, the implementation method of these operations all can adopt conventional method to implement, their specific implementation method such as has detailed description in patent application CN1916166A, CN1362472A, CN1727442A, CN1132898C, CN1727445A and CN1098130A, introduces in the present invention with for referencial use in the lump here.
The invention will be further described by the following examples.
In the following Examples and Comparative Examples,
Second Y zeolite obtains according to the method for CN1683244A embodiment 5.
3rd Y zeolite is DASY2.0 molecular sieve, and produced by catalyst asphalt in Shenli Refinery of China Petrochemical Industry, its content of rare earth is 2 % by weight, and sial atomic ratio (mol ratio) is 4.1;
Alumina gel is produced by catalyst asphalt in Shenli Refinery of China Petrochemical Industry, the Al of Alumina gel
2o
3content is 21.5 % by weight;
Kaolin is purchased from Suzhou China Kaolin Co., Ltd;
Boehmite is purchased from Shandong Aluminum Plant;
In each embodiment and comparative example, the chemical composition of molecular sieve measures (see " Petrochemical Engineering Analysis method (RIPP experimental technique) ", the volumes such as Yang Cuiding, Science Press, nineteen ninety publication) with x-ray fluorescence method.The thing phase of molecular sieve and crystallinity data adopt X-ray diffraction method to measure, and the framework silicon-aluminum atomic ratio of molecular sieve adopts NMR method to measure.
Embodiment 1
(1) preparation of rare earth Y type molecular sieve
Get 2.6 kilograms of NaY molecular sieve (Shandong catalyst plant, igloss 22.5 weighs %, silica alumina ratio 2.7, degree of crystallinity 88%, lower same) and 15 kilograms of deionized waters mixing making beating, add 1.0 liters of concentration 160gRE
2o
3the re chloride of/L and 0.24 kilogram of chloride solid, be warming up to 70 DEG C after stirring evenly and regulate slurries pH to 4.0 with watery hydrochloric acid, continue exchange 1.5 hours, after filtration, washing, drying, in 550 DEG C of roastings 2 hours under 100% water vapor conditions, obtain a friendship one and roast rare earth sodium Y molecular sieve Y-A1, the chemical composition of Y-A1 is the heavy % of sodium oxide molybdena 5.1, the heavy % of rare earth oxide 7.8.Then molecular sieve is pressed: NH
4cl:H
2the ratio of O=1:0.2:10 is pulled an oar and is exchanged 1 hour in 70 DEG C, and after filtering washing, reslurry also adds 0.27 liter of concentration 300gRE
2o
3the re chloride of/L, ensure concentration of slurry 400-450g/L, add ammoniacal liquor after stirring evenly and regulate slurries pH to 7.5 and continue stirring 10 minutes, after drying under 100% steam in 600 DEG C of roastings 2 hours, obtain rare earth Y type molecular sieve finished product of the present invention, be designated as Y-A.
The heavy % of sodium oxide molybdena 1.5 in Y-A, the heavy % of rare earth oxide 11.8, degree of crystallinity 50.3%, lattice constant 2.458nm, framework silicon-aluminum atomic ratio 3.5.In the ratio (I1/I2) of the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at its ° peak, 2 θ=11.8 ± 0.1 and molecular sieve in the product value of the rare earth weight percentage of rare earth oxide for 89.7.
(2) preparation of catalytic cracking catalyst
Pull an oar mixing with deionized water in the boehmite of 19 weight portions of butt, and in the slurries obtained, add the hydrochloric acid peptization that concentration is 36 % by weight, acid aluminum ratio (described 36 % by weight hydrochloric acid with in the weight ratio of the boehmite of butt) is 0.20, be warming up to 65 DEG C of acidifyings 1 hour, add in the slurries of 40 parts by weight kaolin clay of butt respectively, in the Alumina gel of 8 weight portions of butt, stir 20 minutes, add in the rare earth Y type molecular sieve Y-A of 18 weight portions of butt with in the second Y zeolite of butt 12 weight portion and in the DASY2.0 molecular sieve mixed serum of butt 10 weight portion afterwards more wherein, stir the slurries obtaining solid content 30 % by weight for 30 minutes, spraying dry makes microspherical catalyst.By the roasting 1 hour at 500 DEG C of this microspherical catalyst, then with (NH at 60 DEG C
4)
2sO
4washing ((NH
4)
2sO
4: microspherical catalyst: H
2o weight ratio=0.05:1:10) to Na
2o content is less than 0.25 % by weight, finally uses deionized water drip washing, microspherical catalyst: H
2o weight ratio=1:10, dries after filtration, obtains catalytic cracking catalyst C1 at 110 DEG C.
Embodiment 2
Pull an oar mixing with deionized water in the boehmite of 20 weight portions of butt, and in the slurries obtained, add the hydrochloric acid peptization that concentration is 36 % by weight, acid aluminum ratio (described 36 % by weight hydrochloric acid with in the weight ratio of the boehmite of butt) is 0.20, be warming up to 65 DEG C of acidifyings 1 hour, add in the slurries of 39 parts by weight kaolin clay of butt respectively, in the Alumina gel of 9 weight portions of butt, stir 20 minutes, add in the rare earth Y type molecular sieve Y-A of 15 weight portions of butt with in the second Y zeolite of butt 15 weight portion and in the DASY2.0 molecular sieve mixed serum of butt 2 weight portion afterwards more wherein, stir the slurries obtaining solid content 30 % by weight for 30 minutes, spraying dry makes microspherical catalyst.By the roasting 1 hour at 500 DEG C of this microspherical catalyst, then with (NH at 60 DEG C
4)
2sO
4washing ((NH
4)
2sO
4: microspherical catalyst: H
2o weight ratio=0.05:1:10) to Na
2o content is less than 0.25 % by weight, finally uses deionized water drip washing, microspherical catalyst: H
2o weight ratio=1:10, dries after filtration, obtains catalytic cracking catalyst C2 at 110 DEG C.
Embodiment 3
(1) preparation of rare earth Y type molecular sieve
Get 2.6 kilograms of NaY molecular sieve and 18 kilograms of deionized water mixing making beating, add 1.25 liters of concentration 160gRE
2o
3the re chloride of/L and 0.12 kilogram of chloride solid, be warming up to 80 DEG C after stirring evenly and regulate slurries pH to 3.8 with watery hydrochloric acid, continue exchange 1 hour, after filtration, washing, drying, in 570 DEG C of roastings 2 hours under 50% water vapor conditions, obtain a friendship one and roast rare earth sodium Y molecular sieve Y-C1, the chemical composition of Y-C1 is the heavy % of sodium oxide molybdena 4.9, the heavy % of rare earth oxide 9.9.Then molecular sieve is pressed: NH
4cl:H
2the ratio of O=1:0.15:12 is pulled an oar and is exchanged 1 hour in 75 DEG C, and after filtering washing, reslurry also adds 0.27 liter of concentration 300gRE
2o
3the re chloride of/L, ensure concentration of slurry 400-450g/L, add waterglass after stirring evenly and regulate slurries pH to 8.0 and continue stirring 10 minutes, in air atmosphere in 570 DEG C of roastings 2 hours after drying, obtain rare earth Y type molecular sieve finished product of the present invention, be designated as Y-C.
The heavy % of sodium oxide molybdena 1.3 in Y-C, the heavy % of rare earth oxide 13.9, degree of crystallinity 48.8%, lattice constant 2.465nm, framework silicon-aluminum atomic ratio 3.1.The intensity I at its ° peak, 2 θ=11.8 ± 0.1
1with the intensity I at ° peak, 2 θ=12.3 ± 0.1
2ratio (I
1/ I
2) with molecular sieve in the product value of the rare earth weight percentage of rare earth oxide for 55.6.
(2) preparation of catalytic cracking catalyst
Pull an oar mixing with deionized water in the boehmite of 18 weight portions of butt, and in the slurries obtained, add the hydrochloric acid peptization that concentration is 36 % by weight, acid aluminum ratio (described 36 % by weight hydrochloric acid with in the weight ratio of the boehmite of butt) is 0.20, be warming up to 65 DEG C of acidifyings 1 hour, add in the slurries of 42 parts by weight kaolin clay of butt respectively, in the Alumina gel of 8 weight portions of butt, stir 20 minutes, add in the rare earth Y type molecular sieve Y-C of 10 weight portions of butt with in the second Y zeolite of butt 20 weight portion and in the DASY2.0 molecular sieve mixed serum of butt 2 weight portion afterwards more wherein, stir the slurries obtaining solid content 30 % by weight for 30 minutes, spraying dry makes microspherical catalyst.By the roasting 1 hour at 500 DEG C of this microspherical catalyst, then with (NH at 60 DEG C
4)
2sO
4washing ((NH
4)
2sO
4: microspherical catalyst: H
2o weight ratio=0.05:1:10) to Na
2o content is less than 0.25 % by weight, finally uses deionized water drip washing, microspherical catalyst: H
2o weight ratio=1:10, dries after filtration, obtains catalytic cracking catalyst C3 at 110 DEG C.
Embodiment 4
(1) preparation of rare earth Y type molecular sieve
Get 2.6 kilograms of NaY molecular sieve and 18 kilograms of deionized water mixing making beating, add 1.25 liters of concentration 160gRE
2o
3the re chloride of/L and 0.12 kilogram of chloride solid, be warming up to 80 DEG C after stirring evenly and regulate slurries pH to 3.8 with watery hydrochloric acid, continue exchange 1 hour, after filtration, washing, drying, in air atmosphere in 600 DEG C of roastings 1.5 hours, obtain a friendship one and roast rare earth sodium Y molecular sieve Y-D1, the chemical composition of Y-D1 is the heavy % of sodium oxide molybdena 4.9, the heavy % of rare earth oxide 9.9; Then molecular sieve is pressed: NH
4cl:H
2the ratio of O=1:0.15:12 is pulled an oar and is exchanged 1 hour in 75 DEG C, after filtering washing, reslurry also adds the re chloride of 0.4 liter of concentration 300gRE2O3/L, ensure concentration of slurry 400-450g/L, add waterglass after stirring evenly regulate slurries pH to 8.0 and continue stirring 10 minutes, after drying under 100% steam in 570 DEG C of roastings 3 hours, obtain rare earth Y type molecular sieve finished product of the present invention, be designated as Y-D.
The heavy % of sodium oxide molybdena 1.3 in Y-D, the heavy % of rare earth oxide 15.9, degree of crystallinity 46.9%, lattice constant 2.466nm, framework silicon-aluminum atomic ratio 3.0.In the ratio (I1/I2) of the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at its ° peak, 2 θ=11.8 ± 0.1 and molecular sieve in the product value of the rare earth weight percentage of rare earth oxide for 57.2.
(2) preparation of catalytic cracking catalyst
Pull an oar mixing with deionized water in the boehmite of 22 weight portions of butt, and in the slurries obtained, add the hydrochloric acid peptization that concentration is 36 % by weight, acid aluminum ratio (described 36 % by weight hydrochloric acid with in the weight ratio of the boehmite of butt) is 0.20, be warming up to 65 DEG C of acidifyings 1 hour, add in the slurries of 36 parts by weight kaolin clay of butt respectively, in the Alumina gel of 10 weight portions of butt, stir 20 minutes, add in the rare earth Y type molecular sieve Y-D of 21 weight portions of butt with in the second Y zeolite of butt 5 weight portion and in the DASY2.0 molecular sieve mixed serum of butt 6 weight portion afterwards more wherein, stir the slurries obtaining solid content 30 % by weight for 30 minutes, spraying dry makes microspherical catalyst.By the roasting 1 hour at 500 DEG C of this microspherical catalyst, then with (NH at 60 DEG C
4)
2sO
4washing ((NH
4)
2sO
4: microspherical catalyst: H
2o weight ratio=0.05:1:10) to Na
2o content is less than 0.25 % by weight, finally uses deionized water drip washing, microspherical catalyst: H
2o weight ratio=1:10, dries after filtration, obtains catalytic cracking catalyst C4 at 110 DEG C.
Embodiment 5
(1) preparation of rare earth Y type molecular sieve
Get 2.6 kilograms of NaY molecular sieve and 20 kilograms of deionized water mixing making beating, add 1.5 liters of concentration 160gRE
2o
3the re chloride of/L, be warming up to 75 DEG C after stirring evenly and regulate slurries pH to 3.5 with watery hydrochloric acid, continue exchange 1 hour, after filtration, washing, drying, in 600 DEG C of roastings 2 hours under 100% water vapor conditions, obtain a friendship one and roast rare earth sodium Y molecular sieve Y-E1, the chemical composition of Y-E1 is the heavy % of sodium oxide molybdena 4.8, the heavy % of rare earth oxide 11.9; Then molecular sieve is pressed: NH
4cl:H
2the ratio of O=1:0.3:10 is pulled an oar and is exchanged 1 hour in 70 DEG C, and after filtering washing, reslurry also adds 0.4 liter of concentration 300gRE
2o
3the re chloride of/L, ensures concentration of slurry 400-450g/L, adds ammoniacal liquor and regulate slurries pH to 7.9 and continue stirring 10 minutes after stirring evenly, filter washing, after drying under 80% steam in 600 DEG C of roastings 2 hours, obtain rare earth Y type molecular sieve finished product of the present invention, be designated as Y-E.
The heavy % of sodium oxide molybdena 1.3 in Y-E, the heavy % of rare earth oxide 17.9, degree of crystallinity 45.2%, lattice constant 2.467nm, framework silicon-aluminum atomic ratio 3.2.In the ratio (I1/I2) of the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at its ° peak, 2 θ=11.8 ± 0.1 and molecular sieve in the product value of the rare earth weight percentage of rare earth oxide for 62.6.
(2) preparation of catalytic cracking catalyst
Pull an oar mixing with deionized water in the boehmite of 18 weight portions of butt, and in the slurries obtained, add the hydrochloric acid peptization that concentration is 36 % by weight, acid aluminum ratio (described 36 % by weight hydrochloric acid with in the weight ratio of the boehmite of butt) is 0.20, be warming up to 65 DEG C of acidifyings 1 hour, add in the slurries of 41 parts by weight kaolin clay of butt respectively, in the Alumina gel of 9 weight portions of butt, stir 20 minutes, add in the rare earth Y type molecular sieve Y-E of 18 weight portions of butt with in the second Y zeolite of butt 9 weight portion and in the DASY2.0 molecular sieve mixed serum of butt 5 weight portion afterwards more wherein, stir the slurries obtaining solid content 30 % by weight for 30 minutes, spraying dry makes microspherical catalyst.By the roasting 1 hour at 500 DEG C of this microspherical catalyst, then with (NH at 60 DEG C
4)
2sO
4washing ((NH
4)
2sO
4: microspherical catalyst: H
2o weight ratio=0.05:1:10) to Na
2o content is less than 0.25 % by weight, finally uses deionized water drip washing, microspherical catalyst: H
2o weight ratio=1:10, dries after filtration, obtains catalytic cracking catalyst C5 at 110 DEG C.
Embodiment 6
(1) preparation of rare earth Y type molecular sieve
Get 2.6 kilograms of NaY molecular sieve and 20 kilograms of deionized water mixing making beating, add 1.5 liters of concentration 160gLa
2o
3the lanthanum chloride solution of/L, be warming up to 75 DEG C after stirring evenly and regulate slurries pH to 3.5 with watery hydrochloric acid, continue exchange 1 hour, after filtration, washing, drying, in air atmosphere in 620 DEG C of roastings 2 hours, obtain a friendship one and roast rare earth sodium Y molecular sieve Y-F1, the chemical composition of Y-F1 is the heavy % of sodium oxide molybdena 4.8, the heavy % of lanthana 11.9; Then molecular sieve is pressed: oxalic acid: H
2the ratio of O=1:0.08:12 is pulled an oar and is exchanged 1 hour in 65 DEG C, and after filtering washing, reslurry also adds 0.67 liter of concentration 300gLa
2o
3the lanthanum chloride solution of/L, ensure concentration of slurry 400-450g/L, add ammoniacal liquor after stirring evenly and regulate slurries pH to 8.2 and continue stirring 10 minutes, after drying under 100% steam in 620 DEG C of roastings 3 hours, obtain rare earth Y type molecular sieve finished product of the present invention, be designated as Y-F.
The heavy % of sodium oxide molybdena 1.5 in Y-F, the heavy % of lanthana 21.9, degree of crystallinity 41.7%, lattice constant 2.470nm, framework silicon-aluminum atomic ratio 3.1.In the ratio (I1/I2) of the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at its ° peak, 2 θ=11.8 ± 0.1 and molecular sieve in the product value of the rare earth weight percentage of rare earth oxide for 70.1.
(2) preparation of catalytic cracking catalyst
Pull an oar mixing with deionized water in the boehmite of 17 weight portions of butt, and in the slurries obtained, add the hydrochloric acid peptization that concentration is 36 % by weight, acid aluminum ratio (described 36 % by weight hydrochloric acid with in the weight ratio of the boehmite of butt) is 0.20, be warming up to 65 DEG C of acidifyings 1 hour, add in the slurries of 43 parts by weight kaolin clay of butt respectively, in the Alumina gel of 8 weight portions of butt, stir 20 minutes, add in the rare earth Y type molecular sieve Y-F of 16 weight portions of butt with in the second Y zeolite of butt 12 weight portion and in the DASY2.0 molecular sieve mixed serum of butt 4 weight portion afterwards more wherein, stir the slurries obtaining solid content 30 % by weight for 30 minutes, spraying dry makes microspherical catalyst.By the roasting 1 hour at 500 DEG C of this microspherical catalyst, then with (NH at 60 DEG C
4)
2sO
4washing ((NH
4)
2sO
4: microspherical catalyst: H
2o weight ratio=0.05:1:10) to Na
2o content is less than 0.25 % by weight, finally uses deionized water drip washing, microspherical catalyst: H
2o weight ratio=1:10, dries after filtration, obtains catalytic cracking catalyst C6 at 110 DEG C.
Comparative example 1
(1) preparation of rare earth Y type molecular sieve
This comparative example is the rare-earth Y molecular sieve prepared according to method described in CN1053808A.
By NaY molecular sieve and re chloride (160gRE
2o
3/ L) and deionized water mixing, regulate slurries pH to 3.5 and exchange 1 hour in 90 DEG C, filtering, washing, filter cake being put into when pipe type calciner is warming up to 200 DEG C and pass into steam, continue to be warming up to 550 DEG C of roastings 2 hours, by gained molecular sieve and (NH
4)
2sO
4and H
2o pulls an oar in the ratio of 1:0.2:40 and exchanges 15 minutes in 60 DEG C, and filtration drying obtains comparative sample, is designated as DB-1.
The chemical composition of DB-1 is the heavy % of sodium oxide molybdena 1.3, the heavy % of rare earth oxide 12.1, degree of crystallinity 56.7%, lattice constant 2.468nm, framework si-al ratio 4.2.In the ratio (I1/I2) of the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at its ° peak, 2 θ=11.8 ± 0.1 and molecular sieve in the product value of the rare earth weight percentage of rare earth oxide for 33.9.
(2) preparation of catalytic cracking catalyst
Identical with the preparation method of embodiment 1 catalyst, just rare earth Y type molecular sieve Y-A slurries are wherein replaced with comparative example rare earth Y type molecular sieve DB-1 slurries, obtain catalytic cracking catalyst and be designated as DC-1.
Comparative example 2
(1) preparation of rare earth Y type molecular sieve
This comparative example conveniently two hands over two roasting methods to prepare rare-earth Y molecular sieve.
By NaY molecular sieve and re chloride (160gRE
2o
3/ L) and deionized water mix by a certain percentage, exchange 1 hour at 90 DEG C, filter, washing, after drying, roasting 2 hours under 520 DEG C of air atmospheres, by gained molecular sieve again with re chloride and H
2o pulls an oar in proportion and exchanges 1 hour in 90 DEG C, and filtration drying again carries out calcination process and obtains comparative sample, is designated as DB-2.
The chemical composition of DB-2 is the heavy % of sodium oxide molybdena 1.9, the heavy % of rare earth oxide 18.2, degree of crystallinity 43.6%, lattice constant 2.469nm, framework si-al ratio 2.7.In the ratio (I1/I2) of the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at its ° peak, 2 θ=11.8 ± 0.1 and molecular sieve in the product value of the rare earth weight percentage of rare earth oxide for 16.4.
(2) preparation of catalytic cracking catalyst
Identical with the preparation method of embodiment 4 catalyst, just rare earth Y type molecular sieve Y-D slurries are wherein replaced with comparative example rare earth Y type molecular sieve DB-2 slurries, obtain catalytic cracking catalyst and be designated as DC-2.
Comparative example 3
(1) preparation of rare earth Y type molecular sieve
This comparative example is the rare-earth Y molecular sieve prepared according to method described in CN100344374C.
NaY molecular sieve is mixed with deionized water and is warming up to 90 DEG C, add ammonium sulfate and use salt acid for adjusting pH to 3.5-4.0, exchange after 1 hour, filter cake adds water to pull an oar again and adds re chloride in proportion, salt acid for adjusting pH, to 3.5-5.5, in stirred at ambient temperature 1 hour, then adds ammoniacal liquor and stirs 5 minutes, after washing and drying, when weight space velocity 0.1
-1lower 540 DEG C of roastings of steam 1.5 hours; Molecular sieve after roasting 60 DEG C of ammonium chloride solutions are washed 10 minutes, and drying obtains comparative sample, is designated as DB-3.
The chemical composition of DB-3 is the heavy % of sodium oxide molybdena 0.2, the heavy % of rare earth oxide 20.6, degree of crystallinity 50.7%, lattice constant 2.472nm, framework si-al ratio 3.7.In the ratio (I1/I2) of the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at its ° peak, 2 θ=11.8 ± 0.1 and molecular sieve in the product value of the rare earth weight percentage of rare earth oxide for 26.8.
(2) preparation of catalytic cracking catalyst
Identical with the preparation method of embodiment 5 catalyst, just rare earth Y type molecular sieve Y-E slurries are wherein replaced with comparative example rare earth Y type molecular sieve DB-3 slurries, obtain catalytic cracking catalyst and be designated as DC-3.
Comparative example 4
(1) preparation of rare earth Y type molecular sieve
This comparative example is the rare-earth Y molecular sieve prepared according to method described in CN100344374C.
NaY molecular sieve is mixed with deionized water and pulls an oar, then add the re chloride of metering, stir at 60 DEG C after 5 minutes with between salt acid for adjusting pH to 3.5-5.5, continue stirring after 1 hour, add ammoniacal liquor and stir filtration in 5 minutes, after washing and drying, when weight space velocity 0.2
-1lower 600 DEG C of roastings of steam 1.5 hours; Molecular sieve after roasting 90 DEG C of ammonium chloride solutions are washed 10 minutes, and drying obtains comparative sample, is designated as DB-4.
The chemical composition of DB-4 is the heavy % of sodium oxide molybdena 0.8, the heavy % of rare earth oxide 11.8, degree of crystallinity 56.5%, lattice constant 2.465nm, framework si-al ratio 3.3.In the ratio (I1/I2) of the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at its ° peak, 2 θ=11.8 ± 0.1 and molecular sieve in the product value of the rare earth weight percentage of rare earth oxide for 40.1.
(2) preparation of catalytic cracking catalyst
Pull an oar mixing with deionized water in the boehmite of 19 weight portions of butt, and in the slurries obtained, add the hydrochloric acid peptization that concentration is 36 % by weight, acid aluminum ratio (described 36 % by weight hydrochloric acid with in the weight ratio of the boehmite of butt) is 0.20, be warming up to 65 DEG C of acidifyings 1 hour, add in the slurries of 38 parts by weight kaolin clay of butt respectively, in the Alumina gel of 8 weight portions of butt, stir 20 minutes, add in the DB-4 molecular sieve of 20 weight portions of butt with in the second Y zeolite of butt 12 weight portion and in the DASY2.0 molecular sieve mixed serum of butt 3 weight portion afterwards more wherein, stir the slurries obtaining solid content 30 % by weight for 30 minutes, spraying dry makes microspherical catalyst.By the roasting 1 hour at 500 DEG C of this microspherical catalyst, then with (NH at 60 DEG C
4)
2sO
4washing ((NH
4)
2sO
4: microspherical catalyst: H
2o weight ratio=0.05:1:10) to Na
2o content is less than 0.25 % by weight, finally uses deionized water drip washing, microspherical catalyst: H
2o weight ratio=1:10, dries after filtration, obtains catalytic cracking catalyst DC-4 at 110 DEG C.
Comparative example 5
(1) preparation of rare earth Y type molecular sieve
This comparative example is the rare-earth Y molecular sieve prepared according to method described in CN100344374C.
NaY molecular sieve is mixed with deionized water and pulls an oar, then add the re chloride of metering, stir at 60 DEG C after 5 minutes with between salt acid for adjusting pH to 3.5-5.5, continue stirring after 1 hour, add ammoniacal liquor and stir filtration in 5 minutes, after washing and drying, 550 DEG C of roastings 1.5 hours; Molecular sieve after roasting 60 DEG C of ammonium chloride solutions are washed 10 minutes, and drying obtains comparative sample, is designated as DB-5.
The chemical composition of DB-5 is the heavy % of sodium oxide molybdena 1.0, the heavy % of rare earth oxide 15.7, degree of crystallinity 52.9%, lattice constant 2.467nm, framework si-al ratio 3.6.In the ratio (I1/I2) of the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at its ° peak, 2 θ=11.8 ± 0.1 and molecular sieve in the product value of the rare earth weight percentage of rare earth oxide for 30.9.
(2) preparation of catalytic cracking catalyst
Pull an oar mixing with deionized water in the boehmite of 22 weight portions of butt, and in the slurries obtained, add the hydrochloric acid peptization that concentration is 36 % by weight, acid aluminum ratio (described 36 % by weight hydrochloric acid with in the weight ratio of the boehmite of butt) is 0.20, be warming up to 65 DEG C of acidifyings 1 hour, add in the slurries of 34 parts by weight kaolin clay of butt respectively, in the Alumina gel of 10 weight portions of butt, stir 20 minutes, add in the DB-5 molecular sieve of 23 weight portions of butt with in the second Y zeolite of butt 5 weight portion and in the DASY2.0 molecular sieve mixed serum of butt 6 weight portion afterwards more wherein, stir the slurries obtaining solid content 30 % by weight for 30 minutes, spraying dry makes microspherical catalyst.By the roasting 1 hour at 500 DEG C of this microspherical catalyst, then with (NH at 60 DEG C
4)
2sO4 washs ((NH
4)
2sO4: microspherical catalyst: H
2o weight ratio=0.05:1:10) to Na
2o content is less than 0.25 % by weight, finally uses deionized water drip washing, microspherical catalyst: H
2o weight ratio=1:10, dries after filtration, obtains catalytic cracking catalyst DC-5 at 110 DEG C.
Embodiment 7
The present embodiment summarizes the rare earth availability data of the rare earth Y type molecular sieve in embodiment 1-6 and comparative example 1-5.The rare earth utilization rate of molecular sieve is listed in table 1
Table 1
| Sieve sample | Theoretical RE 2O 3Inventory/% | RE in product 2O 3Content/% | Rare earth utilization rate/% |
| Y-A | 12.0 | 11.8 | 98.3 |
| Y-B | 12.0 | 11.9 | 99.2 |
| Y-C | 14.0 | 13.9 | 99.3 |
| Y-D | 16.0 | 15.9 | 99.4 |
| Y-E | 18.0 | 17.9 | 99.4 |
| Y-F | 22.0 | 21.9 | 99.5 |
| DB-1 | 14.0 | 12.1 | 86.4 |
| DB-2 | 24.0 | 18.2 | 75.8 |
| DB-3 | 23.0 | 20.6 | 89.6 |
| DB-4 | 13.0 | 11.8 | 90.7 |
| DB-5 | 17.5 | 15.7 | 89.7 |
From table 1, the rare earth utilization rate of the molecular sieve that embodiment provides is all more than 98%, and comparative example middle rare earth utilization rate is lower, and the rare earth utilization rate of comparative example 2 only about 75%, the utilization rate of other comparative examples is slightly high, but basic below 90%.Adopt of the present invention two to hand over the technique of two roastings and deposition of rare-earth effectively to improve rare earth utilization rate, decrease the waste of rare earth resources.
Embodiment 8
The present embodiment is in order to illustrate that rare earth Y type molecular sieve in embodiment 1-6 and comparative example 1-5 is through 800 DEG C, the physicochemical data of burin-in process after 17 hours under 100% water vapor conditions.
By the molecular sieve in above-described embodiment and comparative example and ammonium chloride solution hybrid switching, by Na wherein
2o content is washed till 0.3 heavy below %, after filtration drying, 800 DEG C, burin-in process 17 hours under 100% water vapor conditions, carries out materialization sign and measures light oil microactivity MA.Light oil micro-reactor appreciation condition: molecular sieve loading amount 2g, feedstock oil is huge port straight distillation light diesel oil, oil inlet quantity 1.56g, reaction temperature 460 DEG C.
The physico-chemical property characterization result of molecular sieve is in table 2.
Table 2
| Sieve sample | RE 2O 3Content/% | Structure cell/nm | Crystallization reservation degree/% | MA |
| Y-A | 11.7 | 2.436 | 45.4 | 63 |
| Y-B | 11.8 | 2.436 | 45.9 | 63 |
| Y-C | 13.8 | 2.438 | 46.0 | 65 |
| Y-D | 15.9 | 2.439 | 46.3 | 67 |
| Y-E | 17.9 | 2.441 | 47.8 | 70 |
| Y-F | 21.8 | 2.445 | 46.0 | 72 |
| DB-1 | 11.8 | 2.433 | 27.1 | 56 |
| DB-2 | 17.1 | 2.438 | 35.0 | 65 |
| DB-3 | 19.5 | 2.441 | 39.6 | 68 |
| DB-4 | 11.8 | 2.433 | 34.9 | 56 |
| DB-5 | 14.9 | 2.436 | 38.4 | 63 |
From table 2, after sodium is washed in the friendship of molecular sieve through ammonium described in embodiment, content of rare earth does not change substantially, illustrate that rare earth ion is mainly positioned in the little cage of molecular sieve, can not be got off by anticommuting, be in rare earth ion in little cage owing to generating double-core octahedral coordination structure, to molecular sieve structure, there is significant stabilization, crystallization reservation degree more than more than 45%, the active contrast sample suitable higher than content of rare earth of light oil.
Embodiment 9
The present embodiment is in order to illustrate the Catalytic Cracking Performance of the catalyst of embodiment 1-6 and comparative example 1-5.Respectively by catalytic cracking catalyst C1-C6 and DC1-DC5 of above-mentioned preparation, at 800 DEG C, under the condition of 100% water vapour aging 12 hours, be filled in the reactivity worth evaluating catalytic cracking catalyst in fixed fluidized bed FFB device (being manufactured by The Earth S. A. of Sinopec Research Institute of Petro-Chemical Engineering) afterwards, the amount of fill of catalyst is 150g.Then, reaction temperature be 520 DEG C, weight (hourly) space velocity (WHSV) is 16h
-1, oil ratio (weight) is under the condition of 6, by the feedstock oil shown in table 3, inject described fixed fluidized bed FFB device and carry out catalytic cracking reaction.The composition of analytical reactions product, and go out conversion ratio according to following formulae discovery, the catalytic cracking reaction results of property of catalyst is as shown in table 4 below:
Table 3
| Density (20 DEG C)/(kg/m 3) | 917.1 |
| Condensation point/DEG C | 20 |
| Carbon residue/% by weight | 1.91 |
| Four composition composition/% by weight | |
| Saturated hydrocarbons | 59.6 |
| Aromatic hydrocarbons | 27.3 |
| Colloid | 13.1 |
| Asphalitine | <0.1 |
| Element composition/% by weight | |
| C | 85.96 |
| H | 12.37 |
| S | 1.0 |
| N | 0.35 |
| Tenor/(μ g/g) | |
| Al | 4.9 |
| Ca | 8.3 |
| Fe | 12.3 |
| Na | 0.9 |
| Ni | 4.7 |
| V | 0.4 |
Table 4
From table 4, identical at prepared catalyst formula, when the content of rare earth of Y-shaped molecular sieve containing rare earth used is suitable, catalytic cracking catalyst of the present invention shows higher activity in residual oil cracking process, cracking reaction transforms remarkable rate and improves, and gasoline yield significantly increases (comparison see embodiment 1 and comparative example 1); When content of rare earth in catalyst rare earth Y type molecular sieve used is lower, still can obtain higher conversion ratio and good gasoline yield (see embodiment 4 and comparative example 2, the comparison of embodiment 5 and comparative example 3); Suitable at the content of rare earth of embodiment and comparative example rare earth Y type molecular sieve used, when the consumption of embodiment Middle molecule sieve is less, still can obtain with comparative example quite or higher conversion ratio, and when conversion ratio is more or less the same, the gasoline yield of embodiment is higher (by embodiment 1 and comparative example 4, relatively can finding out of embodiment 4 and comparative example 5), therefore not only the gasoline yield of catalyst of the present invention is higher, and can reduce the production cost of catalyst.
Claims (9)
1. a catalytic cracking catalyst, containing cracking activity constituent element, clay and binding agent, wherein, described cracking activity constituent element comprises the first Y zeolite, second Y zeolite and the 3rd Y zeolite, the content of rare earth of described first Y zeolite counts the heavy % of 10-25 with rare earth oxide, lattice constant is 2.440-2.472nm, degree of crystallinity is 35-65%, framework silicon-aluminum atomic ratio is 2.5-5.0, in this molecular sieve X-ray diffraction spectrogram the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at ° peak, 2 θ=11.8 ± 0.1 ratio (I1/I2) and molecular sieve in be greater than 50 in the product value of the rare earth weight percentage of rare earth oxide, the second described Y zeolite is a kind of gas phase super-stable Y molecular sieves containing rare earth, described 3rd Y zeolite is the DASY molecular sieve containing rare earth.
2. according to catalytic cracking catalyst according to claim 1, it is characterized in that, described catalytic cracking catalyst contains 10-60 % by weight cracking activity constituent element, 10-60 % by weight clay and 10-60 % by weight binding agent; Described cracking activity constituent element comprises described 3rd Y zeolite of described first Y zeolite of 25-70 % by weight, described second Y zeolite of 10-70 % by weight and 5-30 % by weight.
3. according to the catalytic cracking catalyst of claim 1, it is characterized in that, the content of rare earth of described first Y zeolite counts the heavy % of 11-23 with rare earth oxide, and lattice constant is 2.450-2.470nm, and degree of crystallinity is 40-60%.
4., according to the catalytic cracking catalyst of claim 1, it is characterized in that, described first Y zeolite through 800 DEG C, the crystallization reservation degree of 100% steam burin-in process after 17 hours be greater than 45%.
5. according to the catalytic cracking catalyst of claim 1, it is characterized in that, described first Y zeolite is through two friendships two and roasts and obtain in conjunction with deposition of rare-earth process.
6. according to the catalytic cracking catalyst of claim 5, it is characterized in that, said two hand over two to roast and rare earth utilization rate in conjunction with deposition of rare-earth process is greater than 98%.
7. according to the catalytic cracking catalyst of claim 1, wherein, in said first Y zeolite X-ray diffraction spectrogram the intensity I 2 at ° peak, intensity I 1 and 2 θ=12.3 ± 0.1 at ° peak, 2 θ=11.8 ± 0.1 ratio (I1/I2) and molecular sieve in be greater than 55 in the product value of the rare earth weight percentage of rare earth oxide.
8. the preparation method of the arbitrary described catalytic cracking catalyst of claim 1-7, the method comprises: the first Y zeolite described in preparation; Preparation comprises the slurries of described first Y zeolite, the second Y zeolite, the 3rd Y zeolite, clay and binding agent; By prepared slurries spraying dry.
9. according to the preparation method of catalytic cracking catalyst according to claim 8, it is characterized in that, the preparation method of the first described Y zeolite comprises: the mixed solution of NaY molecular sieve and earth solution or earth solution and ammonium salt is carried out contact pairs, after filtration, after washing, drying, carry out first time calcination process, obtain rare earth sodium Y molecular sieve; Then by rare earth sodium Y molecular sieve making beating and with ammonium salt solution or acid solution contact pairs, mix with earth solution again after filtration, and regulates the pH value of slurries to be 6-10, filter or do not filter, drying, carry out second time calcination process, obtain described first Y zeolite; The said mixed solution by NaY molecular sieve and earth solution or earth solution and ammonium salt carries out in the process of contact pairs, earth solution in the part by weight of rare earth oxide and NaY molecular sieve butt for 0.06-0.14, adjustment pH is 3.0-5.0, control water sieve weight ratio at 5-30, the process of said contact pairs carries out 0.3-3.0 hour room temperature-100 DEG C; Said first time calcination process, be calcination process 0.5-4.0 hour under 500-650 DEG C, 0-100% water vapor conditions; Said by rare earth sodium Y molecular sieve making beating and be process 0.3-3.0 hour room temperature-100 DEG C with the process of ammonium salt solution contact pairs, its middle rare earth sodium Y molecular sieve, by molecular sieve butt, is 1:(0.05-0.5 with the part by weight of ammonium salt and water): (5-30); Said by rare earth sodium Y molecular sieve making beating and be process 0.3-2.0 hour at room temperature-100 DEG C with the process of acid solution contact pairs, its middle rare earth sodium Y molecular sieve by molecular sieve butt, with acid and H
2the part by weight of O is 1:(0.03-0.2): (5-30); Said second time calcination process, be 500-650 DEG C, process 0.5-4 hour under 0-100% water vapor conditions.